A01.15 - Bars

ABSTRACT
This specification covers cold-finished carbon and alloy steel bars for heat treatment, machining into components, or for as-finished condition as shafting or in constructional applications. The steel materials shall be cold drawn, turned, ground, polished, hot wrought, cold rolled, and heat treated. The steel specimens shall undergo chemical analysis.
SCOPE
1.1 This specification covers cold-finished carbon and alloy steel bars produced in straight length and coil. Cold-finished bars are suitable for heat treatment, for machining into components, or for use in the as-finished condition as shafting, or in constructional applications, or for other similar purposes (Note 1). Grades of steel are identified by grade numbers or by chemical composition.
Note 1: A guide for the selection of steel bars is contained in Practice A400.  
1.2 Some end uses may require one or more of the available designations shown under Supplementary Requirements. Supplementary requirements shall apply only when specified individually by the purchaser.  
1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers hot-wrought special quality carbon steel bars. Special quality bar applications include forging, heat treating, cold drawing, machining, and many structural uses. The steel shall be made by one or more of the following primary processes: open-hearth, basic-oxygen, or electric furnace. The heat analysis shall conform to the requirements for chemical composition specified.
SCOPE
1.1 This specification covers hot-wrought special quality carbon steel bars. Special quality bar applications include forging, heat treating, cold drawing, machining, and many structural uses. A guide for the selection of steel bars is contained in Practice A400.  
1.2 The bars shall be furnished in the grades specified in Table 1. Sections and sizes of bar steel available are covered in Specification A29/A29M. Hot-wrought special quality carbon steel bars are produced in cut lengths and coils; the manufacturer should be consulted regarding sections and sizes available in coils, produced to a chemical composition.    
Rephosphorized and Resulfurized Carbon SteelE, G, H    
Designation  
Grade  
Carbon  
Manganese  
Phosphorus  
Sulfur  
Lead  
G12110  
1211  
0.13 max  
0.60–0.90  
0.07–0.12  
0.10–0.15  
...  
G12120  
1212  
0.13 max  
0.70–1.00  
0.07–0.12  
0.16–0.23  
...  
G12130  
1213  
0.13 max  
0.70–1.00  
0.07–0.12  
0.24–0.33  
...  
G12150  
1215  
0.09 max  
0.75–1.05  
0.04–0.09  
0.26–0.35  
...  
...  
12L14  
0.15 max  
0.85–1.15  
0.04–0.09  
0.26–0.35  
0.15–0.35    
1.3 Merchant quality hot-wrought carbon steel bars are covered in Specification A575.  
1.4 Some end uses may require superior surface quality, or special chemical restrictions, metallurgical characteristics, heat treatment, or surface finishes which the purchaser may obtain by designating one or more of the available Supplementary Requirements.  
1.5 The values stated in inch-pound units are to be regarded as standard.  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers hot-wrought merchant quality carbon steel bars and bar size shapes produced to mechanical property requirements and intended for noncritical constructional applications. The bars shall be available in round, square and hexagonal shapes. The steel shall be made by the open-hearth, basic-oxygen, or electric-furnace process. The specimens shall undergo a tension test to determine tensile strength, yield point and elongation. The merchant quality bars shall be from visible pipe; however, they may contain pronounced chemical segregation. Internal porosity, surface seams, and other surface irregularities may be present in this quality. The bars shall also be furnished as rolled and not pickled, blast cleaned, or oiled.
SCOPE
1.1 This specification covers hot-wrought merchant quality carbon steel bars and bar size shapes produced to mechanical property requirements and intended for noncritical constructional applications (see 8.2).  
1.2 Merchant quality hot-wrought steel bar is available in the following ranges of size and section:  
1.2.1 Rounds, squares, and hexagons with diameters or distance across flats under 3 in. [75 mm].  
1.2.2 Bar size shapes with maximum dimensions under 3 in. [75 mm].  
1.2.3 Other bar sections with weight per foot under 40.84 lb/ft [60.78 kg/m].  
1.2.4 Flats 6 in. [152 mm] or under in width, over 0.203 in. [over 5 mm in thickness up to 150 mm in width] in thickness, and under 40.84 lb/ft or 12 in.2 [77.4 cm2] in cross-sectional area.  
1.2.5 Flats over 6 in. to 8 in., inclusive in width, 0.230 in. and over [over 6 mm in thickness and over 50 mm through 200 mm in width] in thickness and under 40.84 lb/ft [60.78 kg/m] or 12 in.2 [77.4 cm2] in cross-sectional area.  
1.2.6 Hot-wrought merchant quality carbon steel bars subject to mechanical property requirements are hot wrought in straight lengths only.  
1.3 Some applications may require one or more of the available designations shown under supplementary requirements.  
Note 1: Special quality hot-wrought carbon steel bars subject to mechanical property requirements are covered in Specification A675/A675M.  
1.4 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
4.1 If the desired mechanical properties are as described in 5.1.1 for material identified as Classes P-1 through P-7, or in 5.1.2 for material identified as Classes Q-1 through Q-7, the strength level desired can be based on hardness or the equivalent tensile or yield strength as shown in Tables 1-4. If the desired mechanical properties are as set forth in 5.1.3 for material identified as Classes R-1 through R-6, the strength level is based on yield strength as shown in Tables 5 and 6.  
4.2 The user, after determining the mechanical property requirements of the critical section (that carrying the greatest stress) of the part, should select the composition or compositions from Tables 1-6 that fulfills these requirements and is most suitable for processing.
SCOPE
1.1 This practice covers the selection of steel bars according to section and to the mechanical properties desired in the part to be produced. This is not a specification for the procurement of steel. Applicable procurement specifications are listed in Section 6.  
1.2 Several steel compositions intended for various sections and mechanical property requirements are presented in Tables 1-6. The criteria for placing a steel composition in one of the three general class designations, Classes P, Q, and R (described in Section 5) are as follows:          
1.2.1 Classes P and Q  should be capable of developing the mechanical properties shown in Tables 1-4 by liquid quenching from a suitable austenitizing temperature, and tempering at 800 °F (427 °C) or higher. A hardness indicated by tests made at a location shown in Fig. 1, A, B, or C, is taken as evidence that a composition is capable of meeting other equivalent mechanical properties shown in the tables. Normal good shop practices are assumed, with control of austenitizing and tempering temperatures, and mild agitation of the part in the quenching bath.
FIG. 1 Locations in Typical Cross Sections of Steel Bars at Which Desired Properties Are Obtained  
1.2.2 Class R  should be capable of developing the mechanical properties shown in Tables 5 and 6 as hot rolled, by cold drawing, or by cold drawing with additional thermal treatment. The locations for obtaining tension tests are described in 7.2.  
1.3 It is not implied that the compositions listed in the tables are the only ones satisfactory for a certain class and mechanical property requirement. Steels with lower alloy contents are often satisfactory through the use of special processing techniques.  
1.4 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This guide covers a group of requirements for carbon and alloy steel bars under each of the following specifications: hot-rolled carbon steel bars, cold-finished carbon steel bars, hot-rolled alloy steel bars, and cold-finished alloy steel bars. Heat and product analysis shall be performed on several grades of carbon steel bars, wherein the material shall conform to the required chemical composition for carbon, manganese, phosphorus, and sulfur. Several grades of alloy steel bars shall also undergo heat and product analysis and shall meet the required chemical composition for carbon, manganese, phosphorus, sulfur, silicon, nickel, chromium, and molybdenum. When compositions other than those indicated in the specified chemical components are required, the composition limits shall be prepared using the specified ranges and limits for carbon steel and alloy steel. The material shall undergo grain size test and shall conform to the specified grain size requirement. Mechanical tests shall also be performed on the steel test specimens.
SCOPE
1.1 This specification2 covers a group of common requirements which, unless otherwise specified in the purchase order or in an individual specification, shall apply to carbon and alloy steel bars under each of the following ASTM specifications (or under any other ASTM specification which invokes this specification or portions thereof):    
Title of Specification  
ASTM
DesignationA  
Hot-Rolled Carbon Steel Bars:  
Steel Bars, Carbon, Quenched and Tempered  
A321    
Steel Bars and Shapes, Carbon Rolled from “T'' Rails  
A499    
Steel Bars, Carbon, Merchant Quality, M-Grades  
A575    
Steel Bars, Carbon, Hot-Wrought, Special Quality  
A576    
Steel Bars, Carbon, Merchant Quality, Mechanical Properties  
A663/A663M    
Steel Bars, Carbon, Hot-Wrought, Special Quality, Mechanical Properties  
A675/A675M    
Carbon and Alloy Steel Bars for Springs  
A689    
Cold-Finished Carbon Steel Bars:  
Steel Bar, Carbon and Alloy, Cold-Finished  
A108    
Cold-Drawn Stress-Relieved Carbon Steel Bars Subject to Mechanical Property Requirements  
A311/A311M  
Hot-Rolled Alloy Steel Bars:  
Steel Bars, Alloy, Standard Grades  
A322    
Carbon and Alloy Steel Bars Subject to End-Quench Hardenability Requirements  
A304    
Steel Bars, Alloy, Hot-Wrought or Cold-Finished, Quenched and Tempered  
A434/A434M    
Steel Bars, Alloy, Hot-Wrought, for Elevated Temperature or Pressure-Containing Parts, or Both  
A739    
Cold-Finished Alloy Steel Bars:  
Steel Bars, Alloy, Hot-Rolled or Cold-Finished, Quenched and Tempered  
A434/A434M    
Steel Bars, Carbon, Hot-Wrought or Cold-Finished, Special Quality, for Pressure Piping Components  
A696    
A These designations refer to the latest issue of the respective specifications, which appear either in the Annual Book of ASTM Standards, Vol 01.05, or as reprints obtainable from ASTM.  
1.2 In case of any conflict in requirements, the requirements of the purchase order, the individual material specification, and this general specification shall prevail in the sequence named.  
1.3 The values stated in either inch-pound units or SI units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall used independently of the other, and values from the two systems shall not be combined.  
1.4 For purposes of determining conformance to this specification and the various material specifications referenced in 1.1, dimensional values shall be rounded to the nearest unit in the right-hand place of figures used in expressing the limiting values in accordance with the rounding method of Practice E29.
Note 1: Specification A29/A29M previously listed dimensional tolerances for cold-finished bars; these are now found in Spe...

ABSTRACT
This specification covers hot-wrought and cold-finished special quality carbon steel bars, in straight lengths only, subject to mechanical property requirements and intended for use in manufacturing components for pressure piping and other pressure-containing applications. The steel bars are furnished in Grade B and Grade C and shall be made by melting, deoxidation, hot and cold working, heat treatment, and shall have special quality. Heat and product analyses shall be performed on the material and the chemical composition shall conform to the values required in carbon, manganese, phosphorus, sulfur, silicon, and lead. The carbon steel shall undergo tensile testing and conform to the required tensile strength, yield strength, and elongation.
SCOPE
1.1 This specification2 covers hot-wrought and cold-finished special quality carbon steel bars, in straight lengths only, subject to mechanical property requirements and intended for use in manufacturing components for pressure piping and other pressure-containing applications.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers flanged U-channel carbon steel posts having a nominal weight ranging from 0.75 to 6.0 lb/ft and a nominal width ranging from 1.25 to 4.0 in. These posts are furnished in the as-wrought condition intended for applications requiring high tensile strength or crashworthiness and with a lower carbon (LC) designation for use where higher ductility or improved weldability are required. This specification indicates that tension tests and tensile tests are conducted on the flanged steel U-channel posts, and notes that retesting for failed mechanical properties may be permitted.
SCOPE
1.1 This specification covers flanged U-channel carbon steel posts having a nominal weight ranging from 0.75 lb/ft to 6.0 lb/ft and a nominal width ranging from 1.25 in. to 4.0 in. These posts are furnished in the as-wrought condition intended for applications requiring high tensile strength or crashworthiness and with a lower carbon (LC) designation for use where higher ductility or improved weldability are required. These materials are available in multiple yield strength levels of 50 ksi, 60 ksi, 70 ksi, and 80 ksi (345 MPa, 420 MPa, 485 MPa, and 550 MPa). The 50 ksi and 60 ksi (345 MPa and 420 MPa) yield strength grades are available as lower carbon posts, designated as Grades 50LC or 60LC.
Note 1: This specification does not cover high-strength low-alloy (HSLA) post. Refer to Specification A572/A572M for HSLA. For structural Grade 36, refer to Specification A36/A36M.  
1.2 Units—The values stated in inch-pound units are to be regarded as the standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers standard specification for alloy steel bars, suitable for surface hardening by nitriding, designated as Classes A, B, C, and D. Class A and Class D bars are general-purpose bars; Class B bars are free-machining bars; Class C bars contain nickel and are characterized by higher core strength. All classes shall be furnished in the hot-rolled, quenched, and tempered condition. The steel shall be made by the electric-furnace process only. The microstructure resulting from heat treatment shall not show free ferrite in amounts exceeding the prescribed values. The maximum depth of total and partial decarburization of hot-rolled bars and heat-treated bars shall not exceed the amounts prescribed. Heat or cast analysis shall be performed on four classes of steel, wherein the material shall conform to the required chemical composition for carbon, manganese, phosphorus, sulfur, silicon, chromium, aluminum, molybdenum, selenium, and nickel. After quenching and tempering, the steel shall conform to one of the specified hardness ranges.
SCOPE
1.1 This specification covers alloy steel bars, suitable for surface hardening by nitriding, designated as Classes A, B, C, and D. Class A and Class D bars are general-purpose bars; Class B bars are free-machining bars; Class C bars contain 3.50 % nickel and are characterized by higher core strength. All classes are normally furnished in the hot-rolled, quenched, and tempered condition. However, centerless-ground or turned bars, in any of the classes, may be specified by the purchaser. Also, as-rolled, annealed, or unannealed bars suitable for forging may be purchased to this specification. When as-rolled, annealed, or unannealed bars are furnished, Sections 6, 10, and 11 are not applicable.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
4.1 It is anticipated that the ASTM Subcommittees A01.02, A01.03, A01.06, A01.09, A01.11, A01.15, A01.19, A01.22, and A01.28 will use the standard composition limits listed in this guide for the grades identified in their product specifications unless there is a specific technical justification for doing otherwise.  
4.2 The composition limits given in this guide are to be used as guides in determining limits for each of the elements included in the total composition of each grade. The composition limits have been established with the intent that each ASTM subcommittee will find it necessary to require only a minimum number of changes to reflect specific technical effects. Section 5 lists the general guidelines followed for determining the limits for each element; the limits established in this guide are based upon these guidelines.
SCOPE
1.1 This guide covers ASTM Subcommittees A01.02, A01.03, A01.06, A01.09, A01.11, A01.15, A01.19, A01.22, and A01.28 for specifying chemical composition limits of wrought carbon, low-alloy, and alloy steels. It is intended that these recommended grade composition limits be suitable for adoption by other standardization bodies that prepare standards for carbon, low-alloy, and alloy steel products, including discontinued steels.  
1.2 Included in this guide are the recommendations for determining the number of significant figures for specifying chemical composition.  
1.3 The carbon and alloy steel grades in all standards overseen by the aforementioned ASTM subcommittees have been included, except those grades applicable to restricted special end uses.  
1.4 Not addressed are minor composition modifications that a specific ASTM subcommittee may find necessary to accommodate effects of normal processing or to enhance fabricability by the producer or user, or both.  
1.5 Also not generally addressed (except where established by ASTM subcommittees) is a complete rationalization of all limits, especially where such would conflict with long-standing practices and is not justified by special technical effect.  
1.6 This guide does not address discontinued or formerly standard steel grades. A listing of such steel grades can be found in SAE J1249. Also excluded from this guide are cast materials and welding filler metals.  
1.7 In 1995, the AISI made the decision to transfer the responsibility of maintaining its numbering system to the Society of Automotive Engineers (SAE) for carbon and alloy steels (SAE J403 and SAE J404) and to ASTM International for stainless steels (Guide A959 and others). To inform users of this important event, historical information is included in the appendix of this standard.  
1.8 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.9 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers steel fence posts and assemblies manufactured from hot-wrought sections and intended for use in field and line fencing. Line posts shall be fabricated from steels A or B and assemblies from steels A, B, or C. The cross sections of the line post shall be T, U, or Y sections. One item from each lot shall be selected at random for testing. A lot shall consist of all posts or assemblies or both, of the same length offered for delivery at the same time.
SCOPE
1.1 This specification covers steel fence posts manufactured from hot-wrought sections and intended for use in field and line fencing.  
1.2 The posts are available as studded tee and are furnished painted or galvanized, unless otherwise specified.  
1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers hot-wrought, special quality microalloyed carbon steel bars intended for use as hot forging stock. The bars shall be hot-wrought, as-wrought, unless thermal treatment is necessary to ensure cold shearability. The steel specimens shall be killed and shall conform to the fine grain size requirement. Heat analysis and product analysis shall be performed wherein the specimens shall conform to the required chemical compositions of vanadium, columbium, and molybdenum.
SCOPE
1.1 This specification covers hot-wrought, special quality microalloyed carbon steel bars intended for use as hot forging stock. The bars shall be hot-wrought, as-wrought, unless thermal treatment is necessary to ensure cold shearability.  
1.2 The bars shall be furnished to chemical composition only. Chemical composition is based on standard carbon steel grades modified to include microalloying elements such as columbium (niobium), vanadium, or molybdenum. Desired mechanical properties are developed in the subsequent hot forging and controlled cooling operations.  
1.3 Sections and sizes of bar steel available are covered in Specification A29/A29M.  
1.4 Supplementary Requirements S1 to S6 are provided for use when additional controls or requirements are desired. These shall apply only when specified on the purchase order.  
1.5 The values stated in either inch-pound units or SI units are to be regarded separately as standard. Within the text and tables, SI units are shown in brackets. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.  
1.6 Unless the order specifies the applicable “M” specification designation, the material shall be furnished to the inch-pound units.  
1.7 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers hot-wrought, ferritic alloy steel bars for elevated temperature or pressure-containing parts suitable for fusion welding or both. The bars are furnished in two grades: Grade B 11 and Grade B 22. The steel shall be made by on or more of the following primary processes: open-hearth, basic-oxygen, or electric furnace. The bars shall be normalized and tempered. The heat analysis shall conform to the limits for chemical composition specified. The bars as represented by the test specimen shall conform to the tensile requirements specified.
SCOPE
1.1 This specification2 covers hot-wrought, ferritic alloy steel bars for elevated temperature or pressure-containing parts suitable for fusion welding or both.  
1.2 The bars are furnished in the following grades:    
Grade B 11: 1.25 % chromium, 0.55 % molybdenum  
Grade B 22: 2.25 % chromium, 1.00 % molybdenum  
1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
3.1 This test method covers the procedure for determining the hardenability of steel by the end-quench or Jominy test. The test consists of water quenching one end of a cylindrical test specimen 1.0 in. in diameter and measuring the hardening response as a function of the distance from the quenched end.
SCOPE
1.1 These test methods cover the identification and description of test methods for determining the hardenability of steels. The two test methods include the quantitative end-quench or Jominy Test and a method for calculating the hardenability of steel from the chemical composition based on the original work by M. A. Grossman.  
1.2 The selection of the test method to be used for determining the hardenability of a given steel shall be agreed upon between the supplier and user. The Certified Material Test Report shall state the method of hardenability determination.  
1.3 The calculation method described in these test methods is applicable only to the range of chemical compositions that follow:    
Element  
Range, %  
Carbon  
0.10–0.70  
Manganese  
0.50–1.65  
Silicon  
0.15–0.60  
Nickel  
1.50 max  
Chromium  
1.35 max  
Molybdenum  
0.55 max  
Copper  
0.35 max  
Vanadium  
0.20 max  
1.4 Hardenability is a measure of the depth to which steel will harden when quenched from its austenitizing temperature (Table 1). It is measured quantitatively, usually by noting the extent or depth of hardening of a standard size and shape of test specimen in a standardized quench. In the end-quench test the depth of hardening is the distance along the specimen from the quenched end which correlates to a given hardness level.    
1.5 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.6 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.7 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers the standard for carbon steel bars and shapes rolled from standard rail steel. The material shall be hot wrought from section “T” rails and shall be produced by hot forming slit railroad rail parts to yield straight lengths. One tension test and one hardness test shall be performed from each lot to determine the mechanical properties and shall conform to the requirement in tensile strength, elongation, Brinell hardness, and Rockwell B hardness.
SCOPE
1.1 This specification covers carbon steel bars and shapes produced from standard rail steel. These bars are furnished in the as-wrought condition intended for structural use, or bar and shape uses, where high tensile properties are applicable. These materials are available in four strength levels as Grade 50, Grade 60, Grade 70, and Grade 80.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers cold-drawn, stress-relieved carbon steel bars subject to mechanical property requirements. The bars are furnished in two classes, A and B. Class A are normal-draft cold-drawn and stress-relieved rounds, squares, hexagons, and flats. Class B are heavy-draft cold-drawn and stress-relieved rounds and hexagons. The steel shall be made by one or more of the following primary processes: open-hearth, basic-oxygen, or electric-furnace. The cast or heat analysis shall conform to the chemical composition requirements specified. Tension test shall be made to conform to the requirements specified.
SCOPE
1.1 This specification covers two classes, nine grades, and four conditions of stress-relieved cold-drawn carbon steel bars produced to mechanical property requirements. One class, B, is cold drawn with higher than normal (heavy) drafts to provide higher strength levels, and four grades provide improved machinability.  
1.2 Supplementary Requirements, S1 through S6, of an optional nature are provided.  
1.3 The values stated in either inch-pound units or SI units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers M-grade hot-wrought merchant quality carbon steel bars produced to a chemical composition. Merchant quality bars are used for structural and similar miscellaneous bar applications involving moderate cold bending, moderate hot forming, punching, and welding as used in the production of noncritical parts. Moderate cold bending involves generous bend radius with the axis of the bend transverse to the direction of rolling. Heat analysis shall conform to the requirements as to chemical composition.
SCOPE
1.1 This specification covers hot-wrought merchant quality carbon steel bars produced to a chemical composition. Merchant quality bars are used for structural and similar miscellaneous bar applications involving moderate cold bending, moderate hot forming, punching, and welding as used in the production of noncritical parts. Moderate cold bending involves a generous bend radius with the axis of the bend transverse to the direction of rolling.  
1.2 Special quality hot-wrought carbon steel bars are covered in Specification A576.  
1.3 Some end uses may require one or more of the available designations shown under Supplementary Requirements.  
1.4 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers carbon and alloy steel bars subject to end-quench hardenability requirements. The methods for estimating the hardness value of the material are presented. Method A is the minimum and maximum hardness values at any desired distance, Method B is the minimum and maximum distances at which any desired hardness value occurs, Method C is the two maximum hardness values at two desired distances, Method D is the two minimum hardness values at two desired distances, and Method E is any minimum hardness plus any maximum hardness. The heat analysis shall conform to the requirements as to chemical composition. The fine austenitic grain size requirements of the steel material are presented in details. The end-quench hardenability shall conform to the requirements specified on the purchase order. The test specimen requirements indicates that, the number and location of test specimens shall be in accordance with the manufacturers standard practice and shall adequately represent the hardenability of each heat, also, all forged or rolled hardenability test specimens must be normalized prior to testing. The grain size and end-quench hardenability test methods are presented in details.
SCOPE
1.1 This specification covers hot-worked alloy, carbon, and carbon-boron steels in a variety of compositions and sizes, which may attain specified depth of hardening in the end quench test. These steel compositions are identified by the suffix letter “H” added to the conventional grade number.  
1.2 This specification provides for analyses other than those listed under Tables 1 and 2. Special hardenability limits are also permissible when approved by the purchaser and manufacturer.    
1.3 The values stated in inch-pound units are to be regarded as standard. No other units of measurement are included in this standard.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers hot-worked alloy and carbon-boron steels designed to attain restricted depth of hardening in the end-quench test. These steel compositions are identified by the suffix letter “RH” added to the conventional grade number. The steel shall be made by one or more of the following primary processes: open-hearth, basic-oxygen, or electric furnace. The primary melting may incorporate separate degassing or ladle refining and may be followed by secondary melting using electroslag remelting or vacuum arc remelting. Where secondary melting is employed, the heat shall be defined as all the ingots remelted from a single primary heat. Immediately after hot working, the bars shall be allowed to cool when necessary to a temperature below the critical range under suitable conditions, to prevent injury by too rapid cooling. The steel shall have an austenitic grain size of five to eight. The grain structure shall be considered satisfactory when a minimum of 70% of the rated grains are within the specified size limits. Hardenability values specified are based on fine-grain steels and are not applicable to coarse-grain steel. All forged and rolled hardenability test specimens must be normalized prior to testing. Cast specimens need not be normalized.
SCOPE
1.1 This specification covers hot-worked alloy and carbon-boron steels designed to attain restricted depth of hardening in the end-quench test. These steel compositions are identified by the suffix letter “RH” added to the conventional grade number.  
1.2 In general, steels with restricted hardenability (RH steels) will exhibit a hardness range not greater than 5 HRC at the initial position on the end-quench hardenability bar and not greater than 65 % of the hardness range for standard H-band steels (Specification A304) in the inflection region. Generally the restricted hardenability band follows the middle of the corresponding standard H-band. An example of the RH band compared with the H band is given for Grade 4140 in Fig. 1.
FIG. 1 Comparison of H-Band and RH-Band for 4140 SteelA  
1.2.1 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.  
1.3 This specification is expressed in both inch-pound units and SI units. However, the material will be supplied to inch-pound units unless the purchase order specifies the “M” specification designation.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers standards for hot-wrought, special quality microalloyed carbon steel bars intended for use in applications where as-rolled mechanical properties are desired. A typical end use includes hydraulic cylinder shafts. The typical chemical composition of microalloyed carbon steel shall contain carbon, manganese, phosphorus, sulfur, and vanadium. Heat and product analyses shall be conducted wherein the material shall conform to the required chemical composition for vanadium, columbium (niobium), and molybdenum. The elements and specified chemical ranges shall not exceed the required limits. The steel bars shall undergo tension test and conform to the mechanical property requirements such as yield strength, tensile strength, and elongation.
SCOPE
1.1 This specification covers hot-wrought, special quality microalloyed carbon steel bars intended for use in applications where as-rolled mechanical properties are desired. A typical end use is hydraulic cylinder shafts.  
1.2 The bars shall be furnished to chemical composition and mechanical properties as provided herein. Chemical composition is based on standard carbon steel grades modified to include microalloying elements such as columbium (niobium), vanadium, or molybdenum. Three strength classes are available, designated 75 [520], 80 [550], and 100 [690], corresponding to the minimum yield strength in ksi.  
1.3 Sections and sizes of bar steels available are covered in Specification A29/A29M.  
1.4 Supplementary Requirements S1 to S5 are provided for use when additional controls or requirements are desired. These shall apply only when specified on the purchase order.  
1.5 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.  
1.6 Unless the order specifies the applicable “M” specification designation, the material shall be furnished to the inch-pound units.  
1.7 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This guide covers standard specification for hot-wrought special quality carbon steel bars and bar size shapes produced to mechanical property requirements and intended for general constructional applications. Heat analysis shall be performed wherein the material shall conform to the required chemical composition for phosphorus, sulfur, copper, and lead. The steel shall meet the required tensile properties such as tensile strength, yield strength, and elongation. The test specimen shall undergo mechanical tests such as tension test and bend test.
SCOPE
1.1 This specification2 covers hot-wrought special quality carbon steel bars and bar size shapes produced to mechanical property requirements and intended for general constructional applications.  
1.2 The bars are available in nine strength grades designated 45, 50, 55, 60, 65, 70, 75, 80, and 90 [310, 345, 380, 415, 450, 485, 515, 550, and 620] corresponding to the minimum ultimate tensile strength in ksi [MPa]. The chemical composition is selected by the manufacturer to develop the required mechanical properties.  
1.3 Hot-wrought special quality carbon steel bars subject to mechanical property requirements are hot wrought in straight lengths only. Sections and sizes available are covered in Specification A29/A29M.  
1.4 Some applications may require one or more of the available designations shown under Supplementary Requirements.  
Note 1: Merchant-quality hot-wrought carbon steel bars subject to mechanical property requirements are covered in Specification A663/A663M.  
1.5 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers hot-wrought steel bars for the manufacture of general purpose springs such as coil, torsion, and leaf. The steel shall be melt processed by using open-hearth, basic-oxygen, or electric furnace. The materials shall undergo heat analysis and shall conform to the required chemical compositions and hardenability. The steel specimens shall conform to the required values of rounded corner radii and cross section tolerances for round-edge flat bars.
SCOPE
1.1 This specification covers hot-wrought steel bars to be used for the manufacture of general-purpose springs such as coil, torsion, and leaf.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers hot-wrought alloy steel bars. The steel shall be made by one or more of the following primary processes: open-hearth, basic-oxygen, or electric-furnace. The primary melting may incorporate separate degassing or refining and may be followed by secondary melting using electro-slag remelting or vacuum arc remelting. Where secondary remelting is employed, the heat shall be defined as all of the cast product remelted from a single primary heat. The steel shall be furnished as strand cast or ingot cast. Immediately after hot forming, the bars shall be allowed to cool to a temperature below the critical range under suitable conditions to prevent imperfections caused by too rapid cooling. The bars shall be free of pipe, cracks, and flakes. Within the limits of good manufacturing and inspection practices, the bars shall be free of injurious seams, laps, segregation, or other imperfections which are due to their nature, degree, or extent, will interfere with the use of the material in machining or fabrication of suitable parts.
SCOPE
1.1 This specification covers hot-wrought alloy steel bars. Bar applications include forging, heat treating, cold drawing, machining and many structural components (Note 1).  
Note 1: A guide for the selection of steel bars is contained in Practice A400.  
1.2 The bars shall be furnished in the grades specified in Table 1. Sections and sizes of bar steel available are covered in Specification A29/A29M. Hot-wrought alloy steel bars are produced in cut lengths and coils; the manufacturer should be consulted regarding sections and sizes available in coils, produced to a chemical composition.  
1.3 Some applications may require superior surface quality, or special chemical restrictions, metallurgical characteristics, heat treatment, or surface finishes which the purchaser may obtain by designating one or more of the available Supplementary Requirements.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers the standard for hot-coiled, heat-treated helical compression springs with tapered, closed, squared and ground ends made of hot-wrought round steel bars. Cross sections for hot-wrought round, square, and round-cornered square bars of steel of the bar diameter shall be taken into consideration when designing and calculating the solid height, spring rate, solid stress, and solid capacity. The spring shall undergo quenching and tempering to have sufficiently high hardness and withstand the stresses developed in testing. Springs with specific indentation diameter shall not exceed the specified Brinell hardness numbers. The spring shall meet the metallurgical requirement, end construction, physical requirements such as measurements, solid height, free height, loaded height, permanent set, uniformity of pitch, outside diameter and calculations of solid capacity and uncorrected solid stress.
SCOPE
1.1 This specification covers hot-coiled, heat-treated helical compression springs with tapered, closed, squared and ground ends made of hot-wrought round steel bars 3/8 in. (9.5 mm) and larger in diameter.  
1.2 This specification also serves to inform the user of practical manufacturing limits, mechanical tests, and inspection requirements applicable to the type of spring described in 1.1.  
1.3 Supplementary Requirements S1 to S8 inclusive of an optional nature are provided. They shall apply only when specified by the purchaser. Details of these supplementary requirements shall be agreed upon by the manufacturer and purchaser.  
1.4 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers hot-wrought and cold-finished quenched and tempered alloy steel bars. The steel materials shall be melt processed by using open-heart, basic oxygen, or electric furnace and shall conform to the austenitic grain size requirement. Tension tests shall be performed wherein the steel specimens shall conform to the required values of yield strength, tensile strength, and elongation.
SCOPE
1.1 This specification covers hot-wrought and cold-finished quenched and tempered alloy steel bars.  
1.2 Hot-wrought bars are available in three strength level classes designated BB, BC, and BD, and cold-finished bars in two strength level classes designated BB and BC. The bars are available in the conditions specified in 4.4 subject to the size limitations shown.  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
3.1 This test method covers the procedure for determining the hardenability of steel by the end-quench or Jominy test. The test consists of water quenching one end of a cylindrical test specimen 1.0 in. in diameter and measuring the hardening response as a function of the distance from the quenched end.
SCOPE
1.1 These test methods cover the identification and description of test methods for determining the hardenability of steels. The two test methods include the quantitative end-quench or Jominy Test and a method for calculating the hardenability of steel from the chemical composition based on the original work by M. A. Grossman.  
1.2 The selection of the test method to be used for determining the hardenability of a given steel shall be agreed upon between the supplier and user. The Certified Material Test Report shall state the method of hardenability determination.  
1.3 The calculation method described in these test methods is applicable only to the range of chemical compositions that follow:    
Element  
Range, %  
Carbon  
0.10–0.70  
Manganese  
0.50–1.65  
Silicon  
0.15–0.60  
Nickel  
1.50 max  
Chromium  
1.35 max  
Molybdenum  
0.55 max  
Copper  
0.35 max  
Vanadium  
0.20 max  
1.4 Hardenability is a measure of the depth to which steel will harden when quenched from its austenitizing temperature (Table 1). It is measured quantitatively, usually by noting the extent or depth of hardening of a standard size and shape of test specimen in a standardized quench. In the end-quench test the depth of hardening is the distance along the specimen from the quenched end which correlates to a given hardness level.    
1.5 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.6 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.7 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This guide covers a group of requirements for carbon and alloy steel bars under each of the following specifications: hot-rolled carbon steel bars, cold-finished carbon steel bars, hot-rolled alloy steel bars, and cold-finished alloy steel bars. Heat and product analysis shall be performed on several grades of carbon steel bars, wherein the material shall conform to the required chemical composition for carbon, manganese, phosphorus, and sulfur. Several grades of alloy steel bars shall also undergo heat and product analysis and shall meet the required chemical composition for carbon, manganese, phosphorus, sulfur, silicon, nickel, chromium, and molybdenum. When compositions other than those indicated in the specified chemical components are required, the composition limits shall be prepared using the specified ranges and limits for carbon steel and alloy steel. The material shall undergo grain size test and shall conform to the specified grain size requirement. Mechanical tests shall also be performed on the steel test specimens.
SCOPE
1.1 This specification2 covers a group of common requirements which, unless otherwise specified in the purchase order or in an individual specification, shall apply to carbon and alloy steel bars under each of the following ASTM specifications (or under any other ASTM specification which invokes this specification or portions thereof):    
Title of Specification  
ASTM
DesignationA  
Hot-Rolled Carbon Steel Bars:  
Steel Bars, Carbon, Quenched and Tempered  
A321    
Steel Bars and Shapes, Carbon Rolled from “T'' Rails  
A499    
Steel Bars, Carbon, Merchant Quality, M-Grades  
A575    
Steel Bars, Carbon, Hot-Wrought, Special Quality  
A576    
Steel Bars, Carbon, Merchant Quality, Mechanical Properties  
A663/A663M    
Steel Bars, Carbon, Hot-Wrought, Special Quality, Mechanical Properties  
A675/A675M    
Steel Bars for Springs, Carbon and Alloy  
A689    
Cold-Finished Carbon Steel Bars:  
Steel Bars, Carbon and Alloy, Cold-Finished  
A108    
Cold-Drawn Stress-Relieved Carbon Steel Bars Subject to Mechanical Property Requirements  
A311/A311M  
Hot-Rolled Alloy Steel Bars:  
Steel Bars, Alloy, Standard Grades  
A322    
Carbon and Alloy Steel Bars Subject to End-Quench Hardenability Requirements  
A304    
Steel Bars, Alloy, Hot-Wrought or Cold-Finished, Quenched and Tempered  
A434/A434M    
Steel Bars, Alloy, Hot-Wrought, for Elevated Temperature or Pressure-Containing Parts, or Both  
A739    
Cold-Finished Alloy Steel Bars:  
Steel Bars, Alloy, Hot-Rolled or Cold-Finished, Quenched and Tempered  
A434/A434M    
Steel Bars, Carbon, Hot-Wrought or Cold-Finished, Special Quality, for Pressure Piping Components  
A696    
A These designations refer to the latest issue of the respective specifications, which appear either in the Annual Book of ASTM Standards, Vol 01.05, or as reprints obtainable from ASTM.  
1.2 In case of any conflict in requirements, the requirements of the purchase order, the individual material specification, and this general specification shall prevail in the sequence named.  
1.3 The values stated in either inch-pound units or SI units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall used independently of the other, and values from the two systems shall not be combined.  
1.4 For purposes of determining conformance to this specification and the various material specifications referenced in 1.1, dimensional values shall be rounded to the nearest unit in the right-hand place of figures used in expressing the limiting values in accordance with the rounding method of Practice E29.
Note 1: Specification A29/A29M previously listed dimensional tolerances for cold-finished bars; these are now found in ...

ABSTRACT
This specification covers cold-finished carbon and alloy steel bars for heat treatment, machining into components, or for as-finished condition as shafting or in constructional applications. The steel materials shall be cold drawn, turned, ground, polished, hot wrought, cold rolled, and heat treated. The steel specimens shall undergo chemical analysis.
SCOPE
1.1 This specification covers cold-finished carbon and alloy steel bars produced in straight length and coil. Cold-finished bars are suitable for heat treatment, for machining into components, or for use in the as-finished condition as shafting, or in constructional applications, or for other similar purposes (Note 1). Grades of steel are identified by grade numbers or by chemical composition.
Note 1: A guide for the selection of steel bars is contained in Practice A400.  
1.2 Some end uses may require one or more of the available designations shown under Supplementary Requirements. Supplementary requirements shall apply only when specified individually by the purchaser.  
1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers hot-wrought alloy steel bars. The steel shall be made by one or more of the following primary processes: open-hearth, basic-oxygen, or electric-furnace. The primary melting may incorporate separate degassing or refining and may be followed by secondary melting using electro-slag remelting or vacuum arc remelting. Where secondary remelting is employed, the heat shall be defined as all of the cast product remelted from a single primary heat. The steel shall be furnished as strand cast or ingot cast. Immediately after hot forming, the bars shall be allowed to cool to a temperature below the critical range under suitable conditions to prevent imperfections caused by too rapid cooling. The bars shall be free of pipe, cracks, and flakes. Within the limits of good manufacturing and inspection practices, the bars shall be free of injurious seams, laps, segregation, or other imperfections which are due to their nature, degree, or extent, will interfere with the use of the material in machining or fabrication of suitable parts.
SCOPE
1.1 This specification covers hot-wrought alloy steel bars. Bar applications include forging, heat treating, cold drawing, machining and many structural components (Note 1).  
Note 1: A guide for the selection of steel bars is contained in Practice A400.  
1.2 The bars shall be furnished in the grades specified in Table 1. Sections and sizes of bar steel available are covered in Specification A29/A29M. Hot-wrought alloy steel bars are produced in cut lengths and coils; the manufacturer should be consulted regarding sections and sizes available in coils, produced to a chemical composition.  
1.3 Some applications may require superior surface quality, or special chemical restrictions, metallurgical characteristics, heat treatment, or surface finishes which the purchaser may obtain by designating one or more of the available Supplementary Requirements.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers M-grade hot-wrought merchant quality carbon steel bars produced to a chemical composition. Merchant quality bars are used for structural and similar miscellaneous bar applications involving moderate cold bending, moderate hot forming, punching, and welding as used in the production of noncritical parts. Moderate cold bending involves generous bend radius with the axis of the bend transverse to the direction of rolling. Heat analysis shall conform to the requirements as to chemical composition.
SCOPE
1.1 This specification covers hot-wrought merchant quality carbon steel bars produced to a chemical composition. Merchant quality bars are used for structural and similar miscellaneous bar applications involving moderate cold bending, moderate hot forming, punching, and welding as used in the production of noncritical parts. Moderate cold bending involves a generous bend radius with the axis of the bend transverse to the direction of rolling.  
1.2 Special quality hot-wrought carbon steel bars are covered in Specification A576.  
1.3 Some end uses may require one or more of the available designations shown under Supplementary Requirements.  
1.4 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
3.1 This test method covers the procedure for determining the hardenability of steel by the end-quench or Jominy test. The test consists of water quenching one end of a cylindrical test specimen 1.0 in. in diameter and measuring the hardening response as a function of the distance from the quenched end.
SCOPE
1.1 These test methods cover the identification and description of test methods for determining the hardenability of steels. The two test methods include the quantitative end-quench or Jominy Test and a method for calculating the hardenability of steel from the chemical composition based on the original work by M. A. Grossman.  
1.2 The selection of the test method to be used for determining the hardenability of a given steel shall be agreed upon between the supplier and user. The Certified Material Test Report shall state the method of hardenability determination.  
1.3 The calculation method described in these test methods is applicable only to the range of chemical compositions that follow:    
Element  
Range, %  
Carbon  
0.10–0.70  
Manganese  
0.50–1.65  
Silicon  
0.15–0.60  
Nickel  
1.50 max  
Chromium  
1.35 max  
Molybdenum  
0.55 max  
Copper  
0.35 max  
Vanadium  
0.20 max  
1.4 Hardenability is a measure of the depth to which steel will harden when quenched from its austenitizing temperature (Table 1). It is measured quantitatively, usually by noting the extent or depth of hardening of a standard size and shape of test specimen in a standardized quench. In the end-quench test the depth of hardening is the distance along the specimen from the quenched end which correlates to a given hardness level.    
1.5 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.6 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.7 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers steel fence posts and assemblies manufactured from hot-wrought sections and intended for use in field and line fencing. Line posts shall be fabricated from steels A or B and assemblies from steels A, B, or C. The cross sections of the line post shall be T, U, or Y sections. One item from each lot shall be selected at random for testing. A lot shall consist of all posts or assemblies or both, of the same length offered for delivery at the same time.
SCOPE
1.1 This specification covers steel fence posts manufactured from hot-wrought sections and intended for use in field and line fencing.  
1.2 The posts are available as studded tee and are furnished painted or galvanized, unless otherwise specified.  
1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers hot-wrought merchant quality carbon steel bars and bar size shapes produced to mechanical property requirements and intended for noncritical constructional applications. The bars shall be available in round, square and hexagonal shapes. The steel shall be made by the open-hearth, basic-oxygen, or electric-furnace process. The specimens shall undergo a tension test to determine tensile strength, yield point and elongation. The merchant quality bars shall be from visible pipe; however, they may contain pronounced chemical segregation. Internal porosity, surface seams, and other surface irregularities may be present in this quality. The bars shall also be furnished as rolled and not pickled, blast cleaned, or oiled.
SCOPE
1.1 This specification covers hot-wrought merchant quality carbon steel bars and bar size shapes produced to mechanical property requirements and intended for noncritical constructional applications (see 7.2).  
1.2 Merchant quality hot-wrought steel bar is available in the following ranges of size and section:  
1.2.1 Rounds, squares, and hexagons with diameters or distance across flats under 3 in. [75 mm].  
1.2.2 Bar size shapes with maximum dimensions under 3 in. [75 mm].  
1.2.3 Other bar sections with weight per foot under 40.84 lb/ft [60.78 kg/m].  
1.2.4 Flats 6 in. [152 mm] or under in width, over 0.203 in. [over 5 mm in thickness up to 150 mm in width] in thickness, and under 40.84 lb/ft or 12 in.2 [77.4 cm2] in cross-sectional area.  
1.2.5 Flats over 6 in. to 8 in., inclusive in width, 0.230 in. and over [over 6 mm in thickness and over 50 mm through 200 mm in width] in thickness and under 40.84 lb/ft [60.78 kg/m] or 12 in.2 [77.4 cm2] in cross-sectional area.  
1.2.6 Hot-wrought merchant quality carbon steel bars subject to mechanical property requirements are hot wrought in straight lengths only.  
1.3 Some applications may require one or more of the available designations shown under supplementary requirements.  
Note 1: Special quality hot-wrought carbon steel bars subject to mechanical property requirements are covered in Specification A675/A675M.  
1.4 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers hot-wrought special quality carbon steel bars. Special quality bar applications include forging, heat treating, cold drawing, machining, and many structural uses. The steel shall be made by one or more of the following primary processes: open-hearth, basic-oxygen, or electric furnace. The heat analysis shall conform to the requirements for chemical composition specified.
SCOPE
1.1 This specification covers hot-wrought special quality carbon steel bars. Special quality bar applications include forging, heat treating, cold drawing, machining, and many structural uses. A guide for the selection of steel bars is contained in Practice A400.  
1.2 The bars shall be furnished in the grades specified in Table 1. Sections and sizes of bar steel available are covered in Specification A29/A29M. Hot-wrought special quality carbon steel bars are produced in cut lengths and coils; the manufacturer should be consulted regarding sections and sizes available in coils, produced to a chemical composition.    
Rephosphorized and Resulfurized Carbon SteelE, G, H    
Designation  
Grade  
Carbon  
Manganese  
Phosphorus  
Sulfur  
Lead  
G12110  
1211  
0.13 max  
0.60–0.90  
0.07–0.12  
0.10–0.15  
...  
G12120  
1212  
0.13 max  
0.70–1.00  
0.07–0.12  
0.16–0.23  
...  
G12130  
1213  
0.13 max  
0.70–1.00  
0.07–0.12  
0.24–0.33  
...  
G12150  
1215  
0.09 max  
0.75–1.05  
0.04–0.09  
0.26–0.35  
...  
...  
12L14  
0.15 max  
0.85–1.15  
0.04–0.09  
0.26–0.35  
0.15–0.35 (A) New designations established in accordance with Practice E527 and SAE J 1086.(B) Maximum unless otherwise indicated.(C) When silicon is required, the following ranges and limits are commonly specified: 0.10 %, max, 0.10 to 0.20 %, 0.15 to 0.35 %, or 0.20 to 0.40 %.(D) Copper can be specified when required as 0.20 % minimum.(E) When lead is required as an added element to a standard steel, a range of 0.15 to 0.35 % incl is specified. Such a steel is identified by inserting the letter “L” between the second and third numerals of the grade designation, for example, 10 L 45. A cast or heat analysis is not determinable when lead is added to the ladle stream.(F) When boron treatment is specified for killed steels, the steels can be expected to contain 0.0005 to 0.003 % boron.(G) The elements bismuth, calcium, selenium, or tellurium may be added as agreed between purchaser and supplier.(H) It is not common practice to produce these steels to specified limits for silicon because of its adverse effect on machinability.  
1.3 Merchant quality hot-wrought carbon steel bars are covered in Specification A575.  
1.4 Some end uses may require superior surface quality, or special chemical restrictions, metallurgical characteristics, heat treatment, or surface finishes which the purchaser may obtain by designating one or more of the available Supplementary Requirements.  
1.5 The values stated in inch-pound units are to be regarded as standard.  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers hot-wrought and cold-finished special quality carbon steel bars, in straight lengths only, subject to mechanical property requirements and intended for use in manufacturing components for pressure piping and other pressure-containing applications. The steel bars are furnished in Grade B and Grade C and shall be made by melting, deoxidation, hot and cold working, heat treatment, and shall have special quality. Heat and product analyses shall be performed on the material and the chemical composition shall conform to the values required in carbon, manganese, phosphorus, sulfur, silicon, and lead. The carbon steel shall undergo tensile testing and conform to the required tensile strength, yield strength, and elongation.
SCOPE
1.1 This specification2 covers hot-wrought and cold-finished special quality carbon steel bars, in straight lengths only, subject to mechanical property requirements and intended for use in manufacturing components for pressure piping and other pressure-containing applications.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
3.1 If the desired mechanical properties are as described in 4.1.1 for material identified as Classes P-1 through P-7, or in 4.1.2 for material identified as Classes Q-1 through Q-7, the strength level desired can be based on hardness or the equivalent tensile or yield strength as shown in Tables 1-4. If the desired mechanical properties are as set forth in 4.1.3 for material identified as Classes R-1 through R-6, the strength level is based on yield strength as shown in Tables 5 and 6.  
3.2 The user, after determining the mechanical property requirements of the critical section (that carrying the greatest stress) of the part, should select the composition or compositions from Tables 1-6 that fulfills these requirements and is most suitable for processing.
SCOPE
1.1 This practice covers the selection of steel bars according to section and to the mechanical properties desired in the part to be produced. This is not a specification for the procurement of steel. Applicable procurement specifications are listed in Section 5.  
1.2 Several steel compositions intended for various sections and mechanical property requirements are presented in Tables 1-6. The criteria for placing a steel composition in one of the three general class designations, Classes P, Q, and R (described in Section 4) are as follows:  (A) 1 psi = 0.006895 MPa.(B) Minimum as-quenched hardness for obtaining desired hardness after tempering at 800 °F (427 °C) or higher.(C) 1 in. = 25.4 mm.  (A) 1 psi = 0.006895 MPa.(B) Minimum as-quenched hardness for obtaining desired hardness after tempering at 800 °F (427 °C) or higher.(C) 1 in. = 25.4 mm.(D) These steels have insufficient hardenability for Class P-4, because of difference in test locations, but are satisfactory for other smaller sizes.  (A) 1 psi = 0.006895 MPa.(B) Minimum as-quenched hardness for obtaining desired hardness after tempering at 800 °F (427 °C) or higher.(C) 1 in. = 25.4 mm.  (A) 1 psi = 0.006895 MPa.(B) Minimum as-quenched hardness for obtaining desired hardness after tempering at 800 °F (427 °C) or higher.(C) 1 in. = 25.4 mm.(D) These steels have insufficient hardenability for Class Q-4 parts because of different location of test specimens, but are satisfactory for smaller sections.(E) For these steels, the yield to tensile-strength ratio will usually be lower than 80 %.  (A) Hot-rolled bars are indicated in table by prefix “HR.”(B) Cold-drawn bars are indicated in table by prefix “CD.” These bars are produced by normal practice in cold-drawing and with no stress relief. Bars cold-finished by turning, grinding, turning and polishing, etc., are not covered under cold-drawn bars, as such cold-finished bars have the properties of hot-rolled bars.(C) Classification of cold-drawn steels by size and yield-strength level in this table is based on yield-strength determinations at 0.2 % offset, or as determined by 0.005 in./in. elongation under load for yield strengths up to 90 000 psi, incl, and by 0.006 in./in. elongation under load for yield strengths above 90 000 psi.(D) 1 psi = 0.006895 MPa.(E) 1 in. = 25.4 mm.  (A) Conditions and treatments of bars are indicated in this table by the symbols shown below. Bars cold-finished by turning, grinding, turning and polishing, etc., are not covered, as such bars have the properties of hot-rolled bars. “CD” = Bars produced by normal practice in cold-drawing, and with no stress relief. “CDT” = Cold-drawn bars with subsequent thermal treatment. Heavier than normal drafts may be required.(B) Classification of cold-drawn steels by size and yield-strength level in this table is based on yield-strength determinations at 0.2 % offset or as determined by 0.005 in./in. elongation under load for yield strengths up to 90 000 psi, and by 0.006 in./in. elongation under load for yield strengths above 90 000 psi.(C) 1 psi = 0.006895 MPa.(D) 1 in. = 25.4 mm.  (A) 1 in. = 25.4 mm.  
1.2.1 Classes P and Q  should be capable of developing...

SIGNIFICANCE AND USE
4.1 It is anticipated that the ASTM Subcommittees A01.02, A01.03, A01.06, A01.09, A01.11, A01.15, A01.19, A01.22, and A01.28 will use the standard composition limits listed in this guide for the grades identified in their product specifications unless there is a specific technical justification for doing otherwise.  
4.2 The composition limits given in this guide are to be used as guides in determining limits for each of the elements included in the total composition of each grade. The composition limits have been established with the intent that each ASTM subcommittee will find it necessary to require only a minimum number of changes to reflect specific technical effects. Section 5 lists the general guidelines followed for determining the limits for each element; the limits established in this guide are based upon these guidelines.
SCOPE
1.1 This guide covers ASTM Subcommittees A01.02, A01.03, A01.06, A01.09, A01.11, A01.15, A01.19, A01.22, and A01.28 for specifying chemical composition limits of wrought carbon, low-alloy, and alloy steels. It is intended that these recommended grade composition limits be suitable for adoption by other standardization bodies that prepare standards for carbon, low-alloy, and alloy steel products, including discontinued steels.  
1.2 Included in this guide are the recommendations for determining the number of significant figures for specifying chemical composition.  
1.3 The carbon and alloy steel grades in all standards overseen by the aforementioned ASTM subcommittees have been included, except those grades applicable to restricted special end uses.  
1.4 Not addressed are minor composition modifications that a specific ASTM subcommittee may find necessary to accommodate effects of normal processing or to enhance fabricability by the producer or user, or both.  
1.5 Also not generally addressed (except where established by ASTM subcommittees) is a complete rationalization of all limits, especially where such would conflict with long-standing practices and is not justified by special technical effect.  
1.6 This guide does not address discontinued or formerly standard steel grades. A listing of such steel grades can be found in SAE J1249. Also excluded from this guide are cast materials and welding filler metals.  
1.7 In 1995, the AISI made the decision to transfer the responsibility of maintaining its numbering system to the Society of Automotive Engineers (SAE) for carbon and alloy steels (SAE J403 and SAE J404) and to ASTM International for stainless steels (Guide A959 and others). To inform users of this important event, historical information is included in the appendix of this standard.  
1.8 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.9 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This guide covers standard specification for alloy steel bars, suitable for surface hardening by nitriding, designated as Classes A, B, C, and D. Class A and Class D bars are general-purpose bars; Class B bars are free-machining bars; Class C bars contain nickel and are characterized by higher core strength. All classes shall be furnished in the hot-rolled, quenched, and tempered condition. The steel shall be made by the electric-furnace process only. The microstructure resulting from heat treatment shall not show free ferrite in amounts exceeding the prescribed values. The maximum depth of total and partial decarburization of hot-rolled bars and heat-treated bars shall not exceed the amounts prescribed. Heat or cast analysis shall be performed on four classes of steel, wherein the material shall conform to the required chemical composition for carbon, manganese, phosphorus, sulfur, silicon, chromium, aluminum, molybdenum, selenium, and nickel. After quenching and tempering, the steel shall conform to one of the specified hardness ranges.
SCOPE
1.1 This specification covers alloy steel bars, suitable for surface hardening by nitriding, designated as Classes A, B, C, and D. Class A and Class D bars are general-purpose bars; Class B bars are free-machining bars; Class C bars contain 3.50 % nickel and are characterized by higher core strength. All classes are normally furnished in the hot-rolled, quenched, and tempered condition. However, centerless-ground or turned bars, in any of the classes, may be specified by the purchaser. Also, as-rolled, annealed, or unannealed bars suitable for forging may be purchased to this specification. When as-rolled, annealed, or unannealed bars are furnished, Sections 6, 10, and 11 are not applicable.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers flanged U-channel carbon steel posts having a nominal weight ranging from 0.75 to 6.0 lb/ft and a nominal width ranging from 1.25 to 4.0 in. These posts are furnished in the as-wrought condition intended for applications requiring high tensile strength or crashworthiness and with a lower carbon (LC) designation for use where higher ductility or improved weldability are required. This specification indicates that tension tests and tensile tests are conducted on the flanged steel U-channel posts, and notes that retesting for failed mechanical properties may be permitted.
SCOPE
1.1 This specification covers flanged U-channel carbon steel posts having a nominal weight ranging from 0.75 to 6.0 lb/ft and a nominal width ranging from 1.25 to 4.0 in. These posts are furnished in the as-wrought condition intended for applications requiring high tensile strength or crashworthiness and with a lower carbon (LC) designation for use where higher ductility or improved weldability are required. These materials are available in multiple yield strength levels of 50, 60, 70, and 80 ksi (345, 420, 485, and 550 MPa). The 50- and 60-ksi (345- and 420-MPa) yield strength grades are available as lower carbon posts, designated as Grades 50LC or 60LC.
Note 1: This specification does not cover high-strength low-alloy (HSLA) post. Refer to Specification A572/A572M for HSLA. For structural Grade 36, refer to Specification A36/A36M.  
1.2 Units—The values stated in inch-pound units are to be regarded as the standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers hot-wrought and cold-finished quenched and tempered alloy steel bars. The steel materials shall be melt processed by using open-heart, basic oxygen, or electric furnace and shall conform to the austenitic grain size requirement. Tension tests shall be performed wherein the steel specimens shall conform to the required values of yield strength, tensile strength, and elongation.
SCOPE
1.1 This specification covers hot-wrought and cold-finished quenched and tempered alloy steel bars.  
1.2 Hot-wrought bars are available in three strength level classes designated BB, BC, and BD, and cold-finished bars in two strength level classes designated BB and BC. The bars are available in the conditions specified in 4.4 subject to the size limitations shown.  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.

ABSTRACT
This specification covers hot-worked alloy and carbon-boron steels designed to attain restricted depth of hardening in the end-quench test. These steel compositions are identified by the suffix letter “RH” added to the conventional grade number. The steel shall be made by one or more of the following primary processes: open-hearth, basic-oxygen, or electric furnace. The primary melting may incorporate separate degassing or ladle refining and may be followed by secondary melting using electroslag remelting or vacuum arc remelting. Where secondary melting is employed, the heat shall be defined as all the ingots remelted from a single primary heat. Immediately after hot working, the bars shall be allowed to cool when necessary to a temperature below the critical range under suitable conditions, to prevent injury by too rapid cooling. The steel shall have an austenitic grain size of five to eight. The grain structure shall be considered satisfactory when a minimum of 70% of the rated grains are within the specified size limits. Hardenability values specified are based on fine-grain steels and are not applicable to coarse-grain steel. All forged and rolled hardenability test specimens must be normalized prior to testing. Cast specimens need not be normalized.
SCOPE
1.1 This specification covers hot-worked alloy and carbon-boron steels designed to attain restricted depth of hardening in the end-quench test. These steel compositions are identified by the suffix letter “RH” added to the conventional grade number.  
1.2 In general, steels with restricted hardenability (RH steels) will exhibit a hardness range not greater than 5 HRC at the initial position on the end-quench hardenability bar and not greater than 65 % of the hardness range for standard H-band steels (Specification A304) in the inflection region. Generally the restricted hardenability band follows the middle of the corresponding standard H-band. An example of the RH band compared with the H band is given for Grade 4140 in Fig. 1.  
1.2.1 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.  
1.3 This specification is expressed in both inch-pound units and SI units. However, the material will be supplied to inch-pound units unless the purchase order specifies the “M” specification designation.

ABSTRACT
This specification covers carbon and alloy steel bars subject to end-quench hardenability requirements. The methods for estimating the hardness value of the material are presented. Method A is the minimum and maximum hardness values at any desired distance, Method B is the minimum and maximum distances at which any desired hardness value occurs, Method C is the two maximum hardness values at two desired distances, Method D is the two minimum hardness values at two desired distances, and Method E is any minimum hardness plus any maximum hardness. The heat analysis shall conform to the requirements as to chemical composition. The fine austenitic grain size requirements of the steel material are presented in details. The end-quench hardenability shall conform to the requirements specified on the purchase order. The test specimen requirements indicates that, the number and location of test specimens shall be in accordance with the manufacturers standard practice and shall adequately represent the hardenability of each heat, also, all forged or rolled hardenability test specimens must be normalized prior to testing. The grain size and end-quench hardenability test methods are presented in details.
SCOPE
1.1 This specification covers hot-worked alloy, carbon, and carbon-boron steels in a variety of compositions and sizes, which may attain specified depth of hardening in the end quench test. These steel compositions are identified by the suffix letter “H” added to the conventional grade number.  
1.2 This specification provides for analyses other than those listed under Tables 1 and 2. Special hardenability limits are also permissible when approved by the purchaser and manufacturer. (A) New designations established in accordance with Practice E527 and SAE J 1086, Recommended Practice for Numbering Metals and Alloys (UNS).(B) Sulfur content range is 0.035 to 0.050 %.(C) These steels can be expected to have a 0.0005 % min boron content.(D) Vanadium content range is 0.10 to 0.15 %.(E) Minimum vanadium content is 0.15 %.  (A) Standard H Steels can be produced with a lead range of 0.15–0.35 %. Such steels are identified by inserting the letter “L” between the second and third numerals of the grade designation, for example, 15L22 H. Lead is generally reported as a range of 0.15–0.35 %.(B) New designations established in accordance with Practice E527 and SAE J 1086, Recommended Practice for Numbering Metals and Alloys (UNS).(C) These steels can be expected to have 0.0005 % min boron content.  
1.3 The values stated in inch-pound units are to be regarded as standard. No other units of measurement are included in this standard.

ABSTRACT
This guide covers a group of requirements for carbon and alloy steel bars under each of the following specifications: hot-rolled carbon steel bars, cold-finished carbon steel bars, hot-rolled alloy steel bars, and cold-finished alloy steel bars. Heat and product analysis shall be performed on several grades of carbon steel bars, wherein the material shall conform to the required chemical composition for carbon, manganese, phosphorus, and sulfur. Several grades of alloy steel bars shall also undergo heat and product analysis and shall meet the required chemical composition for carbon, manganese, phosphorus, sulfur, silicon, nickel, chromium, and molybdenum. When compositions other than those indicated in the specified chemical components are required, the composition limits shall be prepared using the specified ranges and limits for carbon steel and alloy steel. The material shall undergo grain size test and shall conform to the specified grain size requirement. Mechanical tests shall also be performed on the steel test specimens.
SCOPE
1.1 This specification2 covers a group of common requirements which, unless otherwise specified in the purchase order or in an individual specification, shall apply to carbon and alloy steel bars under each of the following ASTM specifications (or under any other ASTM specification which invokes this specification or portions thereof):    
Title of Specification  
ASTM
DesignationA  
Hot-Rolled Carbon Steel Bars:  
Steel Bars, Carbon, Quenched and Tempered  
A321    
Steel Bars and Shapes, Carbon Rolled from “T'' Rails  
A499    
Steel Bars, Carbon, Merchant Quality, M-Grades  
A575    
Steel Bars, Carbon, Hot-Wrought, Special Quality  
A576    
Steel Bars, Carbon, Merchant Quality, Mechanical Properties  
A663/A663M    
Steel Bars, Carbon, Hot-Wrought, Special Quality, Mechanical Properties  
A675/A675M    
Steel Bars for Springs, Carbon and Alloy  
A689    
Cold-Finished Carbon Steel Bars:  
Steel Bars, Carbon and Alloy, Cold-Finished  
A108    
Cold-Drawn Stress-Relieved Carbon Steel Bars Subject to Mechanical Property Requirements  
A311/A311M  
Hot-Rolled Alloy Steel Bars:  
Steel Bars, Alloy, Standard Grades  
A322    
Carbon and Alloy Steel Bars Subject to End-Quench Hardenability Requirements  
A304    
Steel Bars, Alloy, Hot-Wrought or Cold-Finished, Quenched and Tempered  
A434/A434M    
Steel Bars, Alloy, Hot-Wrought, for Elevated Temperature or Pressure-Containing Parts, or Both  
A739    
Cold-Finished Alloy Steel Bars:  
Steel Bars, Alloy, Hot-Rolled or Cold-Finished, Quenched and Tempered  
A434/A434M    
Steel Bars, Carbon, Hot-Wrought or Cold-Finished, Special Quality, for Pressure Piping Components  
A696    
A These designations refer to the latest issue of the respective specifications, which appear either in the Annual Book of ASTM Standards, Vol 01.05, or as reprints obtainable from ASTM.  
1.2 In case of any conflict in requirements, the requirements of the purchase order, the individual material specification, and this general specification shall prevail in the sequence named.  
1.3 The values stated in inch-pound units or SI units are to be regarded as the standard. Within the text, the SI units are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system must be used independently of the other. Combining values from the two systems may result in nonconformance with the specification.  
1.4 For purposes of determining conformance to this specification and the various material specifications referenced in 1.1, dimensional values shall be rounded to the nearest unit in the right-hand place of figures used in expressing the limiting values in accordance with the rounding method of Practice E29.
Note 1: Specification A29/A29M previously listed dimensional tolerances for cold-finished bars;...

ABSTRACT
This specification covers hot-wrought, special quality microalloyed carbon steel bars intended for use as hot forging stock. The bars shall be hot-wrought, as-wrought, unless thermal treatment is necessary to ensure cold shearability. The steel specimens shall be killed and shall conform to the fine grain size requirement. Heat analysis and product analysis shall be performed wherein the specimens shall conform to the required chemical compositions of vanadium, columbium, and molybdenum.
SCOPE
1.1 This specification covers hot-wrought, special quality microalloyed carbon steel bars intended for use as hot forging stock. The bars shall be hot-wrought, as-wrought, unless thermal treatment is necessary to ensure cold shearability.  
1.2 The bars shall be furnished to chemical composition only. Chemical composition is based on standard carbon steel grades modified to include microalloying elements such as columbium (niobium), vanadium, or molybdenum. Desired mechanical properties are developed in the subsequent hot forging and controlled cooling operations.  
1.3 Sections and sizes of bar steel available are covered in Specification A29/A29M.  
1.4 Supplementary Requirements S1 to S6 are provided for use when additional controls or requirements are desired. These shall apply only when specified on the purchase order.  
1.5 The values stated in either inch-pound units or SI units are to be regarded separately as standard. Within the text and tables, SI units are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system must be used independently of the other. Combining values from the two systems may result in nonconformance with the specification.  
1.6 Unless the order specifies the applicable “M” specification designation, the material shall be furnished to the inch-pound units.

ABSTRACT
This specification covers hot-wrought, ferritic alloy steel bars for elevated temperature or pressure-containing parts suitable for fusion welding or both. The bars are furnished in two grades: Grade B 11 and Grade B 22. The steel shall be made by on or more of the following primary processes: open-hearth, basic-oxygen, or electric furnace. The bars shall be normalized and tempered. The heat analysis shall conform to the limits for chemical composition specified. The bars as represented by the test specimen shall conform to the tensile requirements specified.
SCOPE
1.1 This specification2 covers hot-wrought, ferritic alloy steel bars for elevated temperature or pressure-containing parts suitable for fusion welding or both.  
1.2 The bars are furnished in the following grades:    
Grade B 11: 1.25 % chromium, 0.55 % molybdenum  
Grade B 22: 2.25 % chromium, 1.00 % molybdenum  
1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.

ABSTRACT
This guide covers a group of requirements for carbon and alloy steel bars under each of the following specifications: hot-rolled carbon steel bars, cold-finished carbon steel bars, hot-rolled alloy steel bars, and cold-finished alloy steel bars. Heat and product analysis shall be performed on several grades of carbon steel bars, wherein the material shall conform to the required chemical composition for carbon, manganese, phosphorus, and sulfur. Several grades of alloy steel bars shall also undergo heat and product analysis and shall meet the required chemical composition for carbon, manganese, phosphorus, sulfur, silicon, nickel, chromium, and molybdenum. When compositions other than those indicated in the specified chemical components are required, the composition limits shall be prepared using the specified ranges and limits for carbon steel and alloy steel. The material shall undergo grain size test and shall conform to the specified grain size requirement. Mechanical tests shall also be performed on the steel test specimens.
SCOPE
1.1 This specification2 covers a group of common requirements which, unless otherwise specified in the purchase order or in an individual specification, shall apply to carbon and alloy steel bars under each of the following ASTM specifications (or under any other ASTM specification which invokes this specification or portions thereof):    
Title of Specification  
ASTM
DesignationA  
Hot-Rolled Carbon Steel Bars:  
Steel Bars, Carbon, Quenched and Tempered  
A321    
Steel Bars and Shapes, Carbon Rolled from “T'' Rails  
A499    
Steel Bars, Carbon, Merchant Quality, M-Grades  
A575    
Steel Bars, Carbon, Hot-Wrought, Special Quality  
A576    
Steel Bars, Carbon, Merchant Quality, Mechanical Properties  
A663/A663M    
Steel Bars, Carbon, Hot-Wrought, Special Quality, Mechanical Properties  
A675/A675M    
Steel Bars for Springs, Carbon and Alloy  
A689    
Cold-Finished Carbon Steel Bars:  
Steel Bars, Carbon and Alloy, Cold-Finished  
A108    
Cold-Drawn Stress-Relieved Carbon Steel Bars Subject to Mechanical Property Requirements  
A311/A311M  
Hot-Rolled Alloy Steel Bars:  
Steel Bars, Alloy, Standard Grades  
A322    
Carbon and Alloy Steel Bars Subject to End-Quench Hardenability Requirements  
A304    
Steel Bars, Alloy, Hot-Wrought or Cold-Finished, Quenched and Tempered  
A434/A434M    
Steel Bars, Alloy, Hot-Wrought, for Elevated Temperature or Pressure-Containing Parts, or Both  
A739    
Cold-Finished Alloy Steel Bars:  
Steel Bars, Alloy, Hot-Rolled or Cold-Finished, Quenched and Tempered  
A434/A434M    
Steel Bars, Carbon, Hot-Wrought or Cold-Finished, Special Quality, for Pressure Piping Components  
A696    
A These designations refer to the latest issue of the respective specifications, which appear either in the Annual Book of ASTM Standards, Vol 01.05, or as reprints obtainable from ASTM.  
1.2 In case of any conflict in requirements, the requirements of the purchase order, the individual material specification, and this general specification shall prevail in the sequence named.  
1.3 The values stated in inch-pound units or SI units are to be regarded as the standard. Within the text, the SI units are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system must be used independently of the other. Combining values from the two systems may result in nonconformance with the specification.  
1.4 For purposes of determining conformance to this specification and the various material specifications referenced in 1.1, dimensional values shall be rounded to the nearest unit in the right-hand place of figures used in expressing the limiting values in accordance with the rounding method of Practice E29.
Note 1: Specification A29/A29M previously listed dimensional tolerances for cold-finished bars;...

ABSTRACT
This specification covers hot-wrought and cold-finished quenched and tempered alloy steel bars. The steel materials shall be melt processed by using open-heart, basic oxygen, or electric furnace and shall conform to the austenitic grain size requirement. Tension tests shall be performed wherein the steel specimens shall conform to the required values of yield strength, tensile strength, and elongation.
SCOPE
1.1 This specification covers hot-wrought and cold-finished quenched and tempered alloy steel bars.  
1.2 Hot-wrought bars are available in three strength level classes designated BB, BC, and BD, and cold-finished bars in two strength level classes designated BB and BC. The bars are available in the conditions specified in 4.4 subject to the size limitations shown.  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.

SIGNIFICANCE AND USE
4.1 It is anticipated that the ASTM Subcommittees A01.02, A01.03, A01.06, A01.09, A01.11, A01.15, A01.19, A01.22, and A01.28 will use the standard composition limits listed in this guide for the grades identified in their product specifications unless there is a specific technical justification for doing otherwise.  
4.2 The composition limits given in this guide are to be used as guides in determining limits for each of the elements included in the total composition of each grade. The composition limits have been established with the intent that each ASTM subcommittee will find it necessary to require only a minimum number of changes to reflect specific technical effects. Section 5 lists the general guidelines followed for determining the limits for each element; the limits established in this guide are based upon these guidelines.
SCOPE
1.1 This guide covers ASTM Subcommittees A01.02, A01.03, A01.06, A01.09, A01.11, A01.15, A01.19, A01.22, and A01.28 for specifying chemical composition limits of wrought carbon, low-alloy, and alloy steels. It is intended that these recommended grade composition limits be suitable for adoption by other standardization bodies that prepare standards for carbon, low-alloy, and alloy steel products, including discontinued steels.  
1.2 Included in this guide are the recommendations for determining the number of significant figures for specifying chemical composition.  
1.3 The carbon and alloy steel grades in all standards overseen by the aforementioned ASTM subcommittees have been included, except those grades applicable to restricted special end uses.  
1.4 Not addressed are minor composition modifications that a specific ASTM subcommittee may find necessary to accommodate effects of normal processing or to enhance fabricability by the producer or user, or both.  
1.5 Also not generally addressed (except where established by ASTM subcommittees) is a complete rationalization of all limits, especially where such would conflict with long-standing practices and is not justified by special technical effect.  
1.6 This guide does not address discontinued or formerly standard steel grades. A listing of such steel grades can be found in SAE J1249. Also excluded from this guide are cast materials and welding filler metals.  
1.7 In 1995, the AISI made the decision to transfer the responsibility of maintaining its numbering system to the Society of Automotive Engineers (SAE) for carbon and alloy steels (SAE J403 and SAE J404) and to ASTM International for stainless steels (Guide A959 and others). To inform users of this important event, historical information is included in the appendix of this standard.  
1.8 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.

ABSTRACT
This specification covers the standard for carbon steel bars and shapes rolled from standard rail steel. The material shall be hot wrought from section “T” rails and shall be produced by hot forming slit railroad rail parts to yield straight lengths. One tension test and one hardness test shall be performed from each lot to determine the mechanical properties and shall conform to the requirement in tensile strength, elongation, Brinell hardness, and Rockwell B hardness.
SCOPE
1.1 This specification covers carbon steel bars and shapes produced from standard rail steel. These bars are furnished in the as-wrought condition intended for structural use, or bar and shape uses, where high tensile properties are applicable. These materials are available in four strength levels as Grade 50, Grade 60, Grade 70, and Grade 80.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.

ABSTRACT
This specification covers cold-drawn, stress-relieved carbon steel bars subject to mechanical property requirements. The bars are furnished in two classes, A and B. Class A are normal-draft cold-drawn and stress-relieved rounds, squares, hexagons, and flats. Class B are heavy-draft cold-drawn and stress-relieved rounds and hexagons. The steel shall be made by one or more of the following primary processes: open-hearth, basic-oxygen, or electric-furnace. The cast or heat analysis shall conform to the chemical composition requirements specified. Tension test shall be made to conform to the requirements specified.
SCOPE
1.1 This specification covers two classes, nine grades, and four conditions of stress-relieved cold-drawn carbon steel bars produced to mechanical property requirements. One class, B, is cold drawn with higher than normal (heavy) drafts to provide higher strength levels, and four grades provide improved machinability.  
1.2 Supplementary Requirements, S1 through S6, of an optional nature are provided.  
1.3 The values stated in inch-pound units or SI units are to be regarded as the standard. Within the text, the SI units are shown in brackets. The values stated in each system are not exact equivalents, therefore, each system must be used independently of the other. Combining values from the two systems may result in nonconformance with the specification.

ABSTRACT
This specification covers standards for hot-wrought, special quality microalloyed carbon steel bars intended for use in applications where as-rolled mechanical properties are desired. A typical end use includes hydraulic cylinder shafts. The typical chemical composition of microalloyed carbon steel shall contain carbon, manganese, phosphorus, sulfur, and vanadium. Heat and product analyses shall be conducted wherein the material shall conform to the required chemical composition for vanadium, columbium (niobium), and molybdenum. The elements and specified chemical ranges shall not exceed the required limits. The steel bars shall undergo tension test and conform to the mechanical property requirements such as yield strength, tensile strength, and elongation.
SCOPE
1.1 This specification covers hot-wrought, special quality microalloyed carbon steel bars intended for use in applications where as-rolled mechanical properties are desired. A typical end use is hydraulic cylinder shafts.  
1.2 The bars shall be furnished to chemical composition and mechanical properties as provided herein. Chemical composition is based on standard carbon steel grades modified to include microalloying elements such as columbium (niobium), vanadium, or molybdenum. Three strength classes are available, designated 75 [520], 80 [550], and 100 [690], corresponding to the minimum yield strength in ksi.  
1.3 Sections and sizes of bar steels available are covered in Specification A29/A29M.  
1.4 Supplementary Requirements S1 to S5 are provided for use when additional controls or requirements are desired. These shall apply only when specified on the purchase order.  
1.5 The values stated in either SI units or inch-pound units are to be regarded separately as standard. Within the text and tables, SI units are shown in brackets. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.  
1.6 Unless the order specifies the applicable “M” specification designation, the material shall be furnished to the inch-pound units.