D08.09 - Liquid Applied Coatings for Roofing and Asphaltic Concrete Pavement

ABSTRACT
This specification establishes the manufacture, testing, and performance requirements of two types of asphalt-based emulsions for use in a relatively thick film as a protective coating for metal surfaces. Type I are quick-setting emulsified asphalt suitable for continuous exposure to water within a few days after application and drying. Type II, on the other hand, are emulsified asphalt suitable for continuous exposure to the weather, only after application and drying. Upon being sampled appropriately, the materials shall conform to composition requirements as to density, residue by evaporation, nonvolatile matter soluble in trichloroethylene, and ash and water content. They shall also adhere to performance requirements as to uniformity, consistency, stability, wet flow, firm set, heat test, flexibility, resistance to water, and loss of adhesion.
SCOPE
1.1 This specification covers emulsified asphalt suitable for application in a relatively thick film as a protective coating for metal surfaces.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.3 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers emulsified asphalt suitable for use as a protective coating for built-up roofs and other exposed surfaces with specified inclines. The emulsified asphalts are grouped into three types, as follows: Type I, which contains fillers or fibers including asbestos; Type II, which contains fillers or fibers other than asbestos; and Type III, which do not contain any form of fibrous reinforcement. These types are further subdivided into two classes, as follows: Class 1, which is prepared with mineral colloid emulsifying agents; and Class 2, which is prepared with chemical emulsifying agents. Other than consistency and homogeneity of the final products, they shall also conform to specified physical property requirements such as weight, residue by evaporation, ash content of residue, water content flammability, firm set, flexibility, resistance to water, and behavior during heat and direct flame tests.
SCOPE
1.1 This specification covers emulsified asphalt suitable for use as a protective coating for built-up roofs and other exposed surfaces with inclines of not less than 4 % or 42 mm/m [1/2 in./ft].  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
4.1 This procedure measures the amount of hydrogen gas generation potential of aluminized emulsion roof coating. There is the possibility of water reacting with aluminum pigment to generate hydrogen gas. This situation is to be avoided, so this test was designed to evaluate coating formulations and assess the propensity to gassing.
SCOPE
1.1 This test method covers a hydrogen gas and stability test for aluminum emulsified asphalt coatings.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SCOPE
1.1 This specification covers liquid-applied water-dispersed acrylic latex elastomeric protective roof coatings.  
1.2 This specification does not provide guidance for application.  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This practice covers the application of mineral-colloid-stabilized, emulsified coal-tar pitch, as a weather protection and aliphatic-solvent-resistant sealer for use on bituminous pavements of airports, parking lots, and driveways. The procedure for preparation of (1) old asphalt surfaces, (2) new asphalt surfaces, and (3) emulsion, and the procedure for application of emulsion for the first coat and second coat are detailed. When sand addition to the top coat of the emulsion is necessary, the sand shall meet the prescribed sieve size requirements. Application precautions including weather conditions, pavement and air temperatures, drying time, and emulsion freezing are also provided.
SCOPE
1.1 This practice covers the application of mineral-colloid-stabilized, emulsified coal-tar pitch meeting the requirements of Specification D5727/D5727M, as a weather protection and aliphatic-solvent-resistant sealer for use on bituminous pavements of airports, parking lots, and driveways.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
5.1 The results of this practice may be used to distinguish tar-based emulsion from an asphalt-based emulsion for specification compliance purposes.
SCOPE
1.1 This practice uses infrared analytical techniques to qualitatively determine in the laboratory a ratio of aromatic absorbance to aliphatic absorbance. This practice may be used to determine if the bitumen in the emulsion is predominantly aromatic or aliphatic in nature.  
1.2 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers a single component protective roof coating composed of solvent-borne moisture curing urethane elastomeric polymer, to which various pigments or other additives have been added to give the required physical properties. The product, as manufactured, shall be in liquid form for application to spray polyurethane foam (SPF) surfaces by brushing, rolling, or spraying. However, guidance for its application is not addressed here. Coatings shall be tested and conform accordingly to specified liquid property requirements as to viscosity, and volume and weight of solids. Dry films shall also adhere to the following physical property requirements, when tested as appropriate: initial percent elongation at break; initial tensile strength at maximum stress; final percent elongation at break after accelerated weathering; permeance; water absorption; adhesion; fungi resistance; tear resistance; and low temperature flexibility.
SCOPE
1.1 This specification covers a single component, moisture cured, elastomeric urethane polymer coating used as a protective coating for spray polyurethane foam roofing systems.  
1.2 This specification does not provide guidance for application.  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.4 The following precautionary caveat pertains only to the test method portions, Sections 5 and 6.  
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers mineral-colloid-stabilized, concentrated, emulsified, and refined coal tar suitable for use as weather-protective and aliphatic-solvent resistant coatings over bituminous pavements, such as those found at airports, parking areas, and driveways. The emulsion shall be homogeneous and exhibit no separation or coagulation of components that cannot be overcome by moderate stirring. Specimens shall be sampled and shall undergo tests to examine their conformance with physical properties such as uniformity, wet film continuity, resistance to freezing, density, residue by evaporation, water content, resistance to volatilization and residue weight loss, solubility of residue in CS2, ash of residue, drying time, flexibility, and resistance to heat, kerosene, and water.
SCOPE
1.1 This specification covers mineral-colloid-stabilized, concentrated, emulsified, refined coal tar suitable for use as weather-protective and aliphatic-solvent resistant coatings over bituminous pavements, such as those found at airports, parking areas, and driveways. The specification for this material was previously covered by Federal Specification RP355.  
Note 1: Dilute the concentrated emulsion after testing and prior to application to meet the application specification requirements. Application shall be made in accordance with Practice D3423/D3423M.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.3 The following precautionary caveat pertains only to the test methods portion, Section 6, of this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification establishes the material and manufacturing requirements for water-based asphalt emulsion (mineral colloid or chemically stabilized type) pavement sealers suitable for use as a weather-protective coating over bituminous pavements, such as roadways, driveways, and parking areas. The base asphalt emulsion shall be made using binders prepared from crude petroleum; the mineral filler (when used), shall consist of finely ground clay, silica, limestone, slate, basalt, slag, or other inert inorganic filler materials; and the aggregate shall be either a natural or manufactured angular aggregate composed of clean, hard, durable particles free of clay or other objectionable material. The aggregate to be used shall follow the manufacturer's recommendations; however, 100% of the aggregate shall pass a 2.38 mm [No. 8] mesh-sieve at all times. Aggregate may either be added at the point of manufacture, post-added at the job site, or both. The use of an additive is optional and shall be approved by the asphalt emulsion pavement sealer manufacturer.
This specification also covers the physical requirements, sampling, inspection, and packaging and package marking for asphalt emulsion pavement sealers (mineral colloid or chemically stabilized type).
SCOPE
1.1 This specification covers water-based asphalt emulsion (mineral colloid or chemically stabilized type) pavement sealer suitable for use as a weather-protective coating over bituminous pavements, such as roadways, parking areas, and driveways.
Note 1: Application shall be made in accordance with a forthcoming ASTM standard on the application of asphalt emulsion pavement sealer.  
1.2 The values stated in SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers a liquid-applied solvent dispersed elastomeric coating used as a roofing membrane for spray polyurethane foam (SPF) insulation whose principal polymer in the dispersion contains more than 95 % silicone. The product, as manufactured, shall be in liquid form for application to SPF surfaces by brushing, squeegeeing, rolling, or spraying. The product shall be composed of dispersion containing as the principal polymer more than 95 % silicone polymers to which various pigments and other additives have been added to give the required physical properties. Liquid properties like viscosity, volume solids, and weight solids shall be determined after conducting different tests. Physical properties of cured silicone coating like elongation, tensile strength, permeance, accelerated weathering, adhesion, tear resistance, and low-temperature flexibility shall be determined after a series of tests.
SCOPE
1.1 This specification covers a liquid-applied solvent dispersed elastomeric coating used as a roofing membrane for spray polyurethane foam (SPF) insulation whose principal polymer in the dispersion contains more than 95 % silicone.  
1.2 This specification does not provide guidance for application.  
1.3 The following precautionary caveat pertains only to the test method portions, Sections 5 and 6.  
1.4 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
4.1 This practice is designed as a guide for architects, engineers, property owners or their representatives, or combination thereof. Its use helps ensure the satisfactory performance of the protective coating system when applied over bituminous concrete pavements.
SCOPE
1.1 This practice covers the application of emulsified refined coal tar slurry meeting the requirements of Specification D6945/D6945M Types I and II, by mechanized equipment as a weather protection and petroleum (aliphatic) solvent resistant sealer for use on bituminous concrete pavements. In order to clarify the differences between Types I and II, see 3.3 for standard definition of terms.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers mineral-colloid-stabilized, emulsified refined coal tar suitable for use as a weather-protective and petroleum (aliphatic) solvent resistant coating. This product is typically applied to commercial lots and other low speed bituminous concrete pavements suitable for protection. The material shall be classified as: Type I and Type II. The refined coal tar emulsion seal coat shall consist of a mixture of refined coal tar emulsion, water, and aggregate and be proportioned within the ranges specified. Mixture and aggregate verification tests shall be performed to conform with the specified requirements.
SCOPE
1.1 This specification covers mineral-colloid-stabilized, emulsified refined coal tar suitable for use as a weather-protective and petroleum (aliphatic) solvent resistant coating. This product is typically applied to commercial lots and other low-speed bituminous concrete pavements suitable for protection.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SCOPE
1.1 This performance specification covers mixtures of emulsified coal-tar pitch (mineral colloid type), mineral aggregates, and optional polymeric admixtures that are used as a weather-protective and straight aliphatic hydrocarbon resistant coatings over bituminous pavements of airports, parking areas, and driveways.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.3 The following safety hazards statement applies only to the test method portion, Section 6, of this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SCOPE
1.1 This specification covers liquid-applied neoprene and chlorosulfonated polyethylene synthetic rubber solutions suitable for use in roofing and waterproofing.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.3 The following precautionary caveat pertains only to the Test Methods portion, Section 9, of this specification:  This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification describes the test methods for and physical requirements of mineral-colloid-stabilized, emulsified coal-tar pitch suitable for use as a weather-protective and aliphatic-solvent resistant coating over bituminous pavements of airports, parking areas, and driveways. The emulsion shall be made using tars having viscosities of RT-11 or higher, and the mineral filler (mineral colloids) shall consist of finely ground clay, silica, or other inert inorganic materials. And when specified, the emulsion shall be fortified with antifreeze. The properties for which coal-tar pitches shall be appropriately tested on and accordingly adhere to are: wet film continuity; freezing resistance; density; volatile matter content; residue by evaporation; volatilization resistance and residue weight loss; solubility of residue in CS2; ash content of residue; flammability; drying time and firm set; heat resistance; resistance to kerosene and water; and impact resistance before and after accelerated weathering.
SCOPE
1.1 This specification covers mineral-colloid-stabilized, emulsified coal-tar pitch suitable for use as a weather-protective and aliphatic-solvent resistant coating over bituminous pavements of airports, parking areas, and driveways.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.  
1.3 The following precautionary caveat pertains only to the test method portion, Section 6, of this specification:  This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SCOPE
1.1 This specification covers liquid-applied water-dispersed acrylic latex elastomeric protective roof coatings.  
1.2 This specification does not provide guidance for application.  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers emulsified asphalt suitable for use as a protective coating for built-up roofs and other exposed surfaces with specified inclines. The emulsified asphalts are grouped into three types, as follows: Type I, which contains fillers or fibers including asbestos; Type II, which contains fillers or fibers other than asbestos; and Type III, which do not contain any form of fibrous reinforcement. These types are further subdivided into two classes, as follows: Class 1, which is prepared with mineral colloid emulsifying agents; and Class 2, which is prepared with chemical emulsifying agents. Other than consistency and homogeneity of the final products, they shall also conform to specified physical property requirements such as weight, residue by evaporation, ash content of residue, water content flammability, firm set, flexibility, resistance to water, and behavior during heat and direct flame tests.
SCOPE
1.1 This specification covers emulsified asphalt suitable for use as a protective coating for built-up roofs and other exposed surfaces with inclines of not less than 4 % or 42 mm/m [1/2 in./ft].  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers testing and material properties of water-dispersed protective roof coatings composed of a water-based acrylic latex elastomeric emulsion polymer, to which various pigments and other additives have been added to give the required physical properties. The product, as manufactured, shall be in liquid form for application to the roof surface by brushing, squeegeeing, rolling, or spraying. Guidance for its application is not addressed here. Coatings shall be tested and adhere to liquid property requirements as to viscosity, and volume and weight of solids. Conversely, films shall also conform to dry physical properties, as follows: initial percent elongation at break; initial tensile strength at maximum stress; final percent elongation at break after accelerated weathering; permeance; water swelling; adhesion; fungi resistance; tear resistance; and low temperature flexibility after accelerated weathering.
SCOPE
1.1 This specification covers liquid-applied water-dispersed acrylic latex elastomeric protective roof coatings.  
1.2 This specification does not provide guidance for application.  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification establishes the manufacture, testing, and performance requirements of two types of asphalt-based emulsions for use in a relatively thick film as a protective coating for metal surfaces. Type I are quick-setting emulsified asphalt suitable for continuous exposure to water within a few days after application and drying. Type II, on the other hand, are emulsified asphalt suitable for continuous exposure to the weather, only after application and drying. Upon being sampled appropriately, the materials shall conform to composition requirements as to density, residue by evaporation, nonvolatile matter soluble in trichloroethylene, and ash and water content. They shall also adhere to performance requirements as to uniformity, consistency, stability, wet flow, firm set, heat test, flexibility, resistance to water, and loss of adhesion.
SCOPE
1.1 This specification covers emulsified asphalt suitable for application in a relatively thick film as a protective coating for metal surfaces.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.  
1.3 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
4.1 This procedure measures the amount of hydrogen gas generation potential of aluminized emulsion roof coating. There is the possibility of water reacting with aluminum pigment to generate hydrogen gas. This situation is to be avoided, so this test was designed to evaluate coating formulations and assess the propensity to gassing.
SCOPE
1.1 This test method covers a hydrogen gas and stability test for aluminum emulsified asphalt coatings.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SCOPE
1.1 This performance specification covers mixtures of emulsified coal-tar pitch (mineral colloid type), mineral aggregates, and optional polymeric admixtures that are used as a weather-protective and straight aliphatic hydrocarbon resistant coatings over bituminous pavements of airports, parking areas, and driveways.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.  
1.3 The following safety hazards statement applies only to the test method portion, Section 6, of this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
4.1 This practice is designed as a guide for architects, engineers, property owners or their representatives, or combination thereof. Its use helps ensure the satisfactory performance of the protective coating system when applied over bituminous concrete pavements.
SCOPE
1.1 This practice covers the application of emulsified refined coal tar slurry meeting the requirements of Specification D6945/D6945M Types I and II, by mechanized equipment as a weather protection and petroleum (aliphatic) solvent resistant sealer for use on bituminous concrete pavements. In order to clarify the differences between Types I and II, see 3.3 for standard definition of terms.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers mineral-colloid-stabilized, concentrated, emulsified, and refined coal tar suitable for use as weather-protective and aliphatic-solvent resistant coatings over bituminous pavements, such as those found at airports, parking areas, and driveways. The emulsion shall be homogeneous and exhibit no separation or coagulation of components that cannot be overcome by moderate stirring. Specimens shall be sampled and shall undergo tests to examine their conformance with physical properties such as uniformity, wet film continuity, resistance to freezing, density, residue by evaporation, water content, resistance to volatilization and residue weight loss, solubility of residue in CS2, ash of residue, drying time, flexibility, and resistance to heat, kerosene, and water.
SCOPE
1.1 This specification covers mineral-colloid-stabilized, concentrated, emulsified, refined coal tar suitable for use as weather-protective and aliphatic-solvent resistant coatings over bituminous pavements, such as those found at airports, parking areas, and driveways. The specification for this material was previously covered by Federal Specification RP355.  
Note 1: Dilute the concentrated emulsion after testing and prior to application to meet the application specification requirements. Application shall be made in accordance with Practice D3423/D3423M.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.  
1.3 The following precautionary caveat pertains only to the test methods portion, Section 6, of this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers mineral-colloid-stabilized, emulsified refined coal tar suitable for use as a weather-protective and petroleum (aliphatic) solvent resistant coating. This product is typically applied to commercial lots and other low speed bituminous concrete pavements suitable for protection. The material shall be classified as: Type I and Type II. The refined coal tar emulsion seal coat shall consist of a mixture of refined coal tar emulsion, water, and aggregate and be proportioned within the ranges specified. Mixture and aggregate verification tests shall be performed to conform with the specified requirements.
SCOPE
1.1 This specification covers mineral-colloid-stabilized, emulsified refined coal tar suitable for use as a weather-protective and petroleum (aliphatic) solvent resistant coating. This product is typically applied to commercial lots and other low speed bituminous concrete pavements suitable for protection.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory requirements prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SCOPE
1.1 This specification covers water based asphalt emulsion (mineral colloid or chemically stabilized type) pavement sealer suitable for use as a weather-protective coating over bituminous pavements, such as roadways, parking areas, and driveways.
Note 1: Application shall be made in accordance with a forthcoming ASTM standard on the application of asphalt emulsion pavement sealer.  
1.2 The values stated in SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
5.1 The results of this practice may be used to distinguish tar-based emulsion from an asphalt-based emulsion for specification compliance purposes.
SCOPE
1.1 This practice uses infrared analytical techniques to qualitatively determine in the laboratory a ratio of aromatic absorbance to aliphatic absorbance. This practice may be used to determine if the bitumen in the emulsion is predominantly aromatic or aliphatic in nature.  
1.2 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

ABSTRACT
This specification covers a single component protective roof coating composed of solvent-borne moisture curing urethane elastomeric polymer, to which various pigments or other additives have been added to give the required physical properties. The product, as manufactured, shall be in liquid form for application to spray polyurethane foam (SPF) surfaces by brushing, rolling, or spraying. However, guidance for its application is not addressed here. Coatings shall be tested and conform accordingly to specified liquid property requirements as to viscosity, and volume and weight of solids. Dry films shall also adhere to the following physical property requirements, when tested as appropriate: initial percent elongation at break; initial tensile strength at maximum stress; final percent elongation at break after accelerated weathering; permeance; water absorption; adhesion; fungi resistance; tear resistance; and low temperature flexibility.
SCOPE
1.1 This specification covers a single component, moisture cured, elastomeric urethane polymer coating used as a protective coating for spray polyurethane foam roofing systems.  
1.2 This specification does not provide guidance for application.  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.  
1.4 The following precautionary caveat pertains only to the test method portions, Sections 5 and 6.  
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory requirements prior to use.

ABSTRACT
This specification covers a liquid-applied solvent dispersed elastomeric coating used as a roofing membrane for spray polyurethane foam (SPF) insulation whose principal polymer in the dispersion contains more than 95 % silicone. The product, as manufactured, shall be in liquid form for application to SPF surfaces by brushing, squeegeeing, rolling, or spraying. The product shall be composed of dispersion containing as the principal polymer more than 95 % silicone polymers to which various pigments and other additives have been added to give the required physical properties. Liquid properties like viscosity, volume solids, and weight solids shall be determined after conducting different tests. Physical properties of cured silicone coating like elongation, tensile strength, permeance, accelerated weathering, adhesion, tear resistance, and low-temperature flexibility shall be determined after a series of tests.
SCOPE
1.1 This specification covers a liquid-applied solvent dispersed elastomeric coating used as a roofing membrane for spray polyurethane foam (SPF) insulation whose principal polymer in the dispersion contains more than 95 % silicone.  
1.2 This specification does not provide guidance for application.  
1.3 The following precautionary caveat pertains only to the test method portions, Sections 5 and 6.  
1.4 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.  
1.5 This standard may involve hazardous materials, operations, and equipment. This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory requirements prior to use.

ABSTRACT
This practice covers the application of mineral-colloid-stabilized, emulsified coal-tar pitch, as a weather protection and aliphatic-solvent-resistant sealer for use on bituminous pavements of airports, parking lots, and driveways. The procedure for preparation of (1) old asphalt surfaces, (2) new asphalt surfaces, and (3) emulsion, and the procedure for application of emulsion for the first coat and second coat are detailed. When sand addition to the top coat of the emulsion is necessary, the sand shall meet the prescribed sieve size requirements. Application precautions including weather conditions, pavement and air temperatures, drying time, and emulsion freezing are also provided.
SCOPE
1.1 This practice covers the application of mineral-colloid-stabilized, emulsified coal-tar pitch meeting the requirements of Specification D5727/D5727M, as a weather protection and aliphatic-solvent-resistant sealer for use on bituminous pavements of airports, parking lots, and driveways.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

ABSTRACT
This specification covers emulsified asphalt suitable for use as a protective coating for built-up roofs and other exposed surfaces with specified inclines. The emulsified asphalts are grouped into three types, as follows: Type I, which contains fillers or fibers including asbestos; Type II, which contains fillers or fibers other than asbestos; and Type III, which do not contain any form of fibrous reinforcement. These types are further subdivided into two classes, as follows: Class 1, which is prepared with mineral colloid emulsifying agents; and Class 2, which is prepared with chemical emulsifying agents. Other than consistency and homogeneity of the final products, they shall also conform to specified physical property requirements such as weight, residue by evaporation, ash content of residue, water content flammability, firm set, flexibility, resistance to water, and behavior during heat and direct flame tests.
SCOPE
1.1 This specification covers emulsified asphalt suitable for use as a protective coating for built-up roofs and other exposed surfaces with inclines of not less than 4 % or 42 mm/m (1/2 in./ft).  
1.2 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

ABSTRACT
This specification establishes the manufacture, testing, and performance requirements of two types of asphalt-based emulsions for use in a relatively thick film as a protective coating for metal surfaces. Type I are quick-setting emulsified asphalt suitable for continuous exposure to water within a few days after application and drying. Type II, on the other hand, are emulsified asphalt suitable for continuous exposure to the weather, only after application and drying. Upon being sampled appropriately, the materials shall conform to composition requirements as to density, residue by evaporation, nonvolatile matter soluble in trichloroethylene, and ash and water content. They shall also adhere to performance requirements as to uniformity, consistency, stability, wet flow, firm set, heat test, flexibility, resistance to water, and loss of adhesion.
SCOPE
1.1 This specification covers emulsified asphalt suitable for application in a relatively thick film as a protective coating for metal surfaces.
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.

ABSTRACT
This specification covers mineral-colloid-stabilized, emulsified refined coal tar suitable for use as a weather-protective and petroleum (aliphatic) solvent resistant coating. This product is typically applied to commercial lots and other low speed bituminous concrete pavements suitable for protection. The material shall be classified as: Type I and Type II. The refined coal tar emulsion seal coat shall consist of a mixture of refined coal tar emulsion, water, and aggregate and be proportioned within the ranges specified. Mixture and aggregate verification tests shall be performed to conform with the specified requirements.
SCOPE
1.1 This specification covers mineral-colloid-stabilized, emulsified refined coal tar suitable for use as a weather-protective and petroleum (aliphatic) solvent resistant coating. This product is typically applied to commercial lots and other low speed bituminous concrete pavements suitable for protection.
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory requirements prior to use.

SIGNIFICANCE AND USE
This procedure measures the amount of hydrogen gas generation potential of aluminized emulsion roof coating. There is the possibility of water reacting with aluminum pigment to generate hydrogen gas. This situation is to be avoided, so this test was designed to evaluate coating formulations and assess the propensity to gassing.
SCOPE
1.1 This test method covers a hydrogen gas and stability test for aluminum emulsified asphalt coatings.
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

SIGNIFICANCE AND USE
This practice is designed as a guide for architects, engineers, property owners or their representatives, or combination thereof. Its use helps ensure the satisfactory performance of the protective coating system when applied over bituminous concrete pavements.
SCOPE
1.1 This practice covers the application of emulsified refined coal tar slurry meeting the requirements of Specification D6945 Types I and II, by mechanized equipment as a weather protection and petroleum (aliphatic) solvent resistant sealer for use on bituminous concrete pavements. In order to clarify the differences between Types I and II, see 3.3 for standard definition of terms.
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

ABSTRACT
This practice covers the application of mineral-colloid-stabilized, emulsified coal-tar pitch, as a weather protection and aliphatic-solvent-resistant sealer for use on bituminous pavements of airports, parking lots, and driveways. The procedure for preparation of (1) old asphalt surfaces, (2) new asphalt surfaces, and (3) emulsion, and the procedure for application of emulsion for the first coat and second coat are detailed. When sand addition to the top coat of the emulsion is necessary, the sand shall meet the prescribed sieve size requirements. Application precautions including weather conditions, pavement and air temperatures, drying time, and emulsion freezing are also provided.
SCOPE
1.1 This practice covers the application of mineral-colloid-stabilized, emulsified coal-tar pitch meeting the requirements of Specification D3320, as a weather protection and aliphatic-solvent-resistant sealer for use on bituminous pavements of airports, parking lots, and driveways.
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

SCOPE
1.1 This performance specification covers mixtures of emulsified coal-tar pitch (mineral colloid type), mineral aggregates, and optional polymeric admixtures that are used as a weather-protective and straight aliphatic hydrocarbon resistant coatings over bituminous pavements of airports, parking areas, and driveways.
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.
1.3 The following safety hazards statement applies only to the test method portion, Section 6, of this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

ABSTRACT
This specification covers mineral-colloid-stabilized, concentrated, emulsified, and refined coal tar suitable for use as weather-protective and aliphatic-solvent resistant coatings over bituminous pavements, such as those found at airports, parking areas, and driveways. The emulsion shall be homogeneous and exhibit no separation or coagulation of components that cannot be overcome by moderate stirring. Specimens shall be sampled and shall undergo tests to examine their conformance with physical properties such as uniformity, wet film continuity, resistance to freezing, density, residue by evaporation, water content, resistance to volatilization and residue weight loss, solubility of residue in CS2, ash of residue, drying time, flexibility, and resistance to heat, kerosene, and water.
SCOPE
1.1 This specification covers mineral-colloid-stabilized, concentrated, emulsified, refined coal tar suitable for use as weather-protective and aliphatic-solvent resistant coatings over bituminous pavements, such as those found at airports, parking areas, and driveways. The specification for this material was previously covered by Federal Specification RP355.
Note 1—Dilute the concentrated emulsion after testing and prior to application to meet the application specification requirements. Application shall be made in accordance with Practice D3423.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.
1.3 The following precautionary caveat pertains only to the test methods portion, Section 6, of this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

SIGNIFICANCE AND USE
The results of this practice may be used to distinguish tar-based emulsion from an asphalt-based emulsion for specification compliance purposes.
SCOPE
1.1 This practice uses infrared analytical techniques to qualitatively determine in the laboratory a ratio of aromatic absorbance to aliphatic absorbance. This practice may be used to determine if the bitumen in the emulsion is predominantly aromatic or aliphatic in nature.
1.2 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

ABSTRACT
This specification covers emulsified asphalt suitable for use as a protective coating for built-up roofs and other exposed surfaces with specified inclines. The emulsified asphalts are grouped into three types, as follows: Type I, which contains fillers or fibers including asbestos; Type II, which contains fillers or fibers other than asbestos; and Type III, which do not contain any form of fibrous reinforcement. These types are further subdivided into two classes, as follows: Class 1, which is prepared with mineral colloid emulsifying agents; and Class 2, which is prepared with chemical emulsifying agents. Other than consistency and homogeneity of the final products, they shall also conform to specified physical property requirements such as weight, residue by evaporation, ash content of residue, water content flammability, firm set, flexibility, resistance to water, and behavior during heat and direct flame tests.
SCOPE
1.1 This specification covers emulsified asphalt suitable for use as a protective coating for built-up roofs and other exposed surfaces with inclines of not less than 4 % or 42 mm/m (1/2 in./ft).
1.2 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

SCOPE
1.1 This specification covers liquid-applied neoprene and chlorosulfonated polyethylene synthetic rubber solutions suitable for use in roofing and waterproofing.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.  
1.3 The following precautionary caveat pertains only to the test method portion, Section 9, of this specification: This standard does not purport to address the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

ABSTRACT
This specification covers mineral-colloid-stabilized, concentrated, emulsified, and refined coal tar suitable for use as weather-protective and aliphatic-solvent resistant coatings over bituminous pavements, such as those found at airports, parking areas, and driveways. The emulsion shall be homogeneous and exhibit no separation or coagulation of components that cannot be overcome by moderate stirring. Specimens shall be sampled and shall undergo tests to examine their conformance with physical properties such as uniformity, wet film continuity, resistance to freezing, density, residue by evaporation, water content, resistance to volatilization and residue weight loss, solubility of residue in CS2, ash of residue, drying time, flexibility, and resistance to heat, kerosene, and water.
SCOPE
1.1 This specification covers mineral-colloid-stabilized, concentrated, emulsified, refined coal tar suitable for use as weather-protective and aliphatic-solvent resistant coatings over bituminous pavements, such as those found at airports, parking areas, and driveways. The specification for this material was previously covered by Federal Specification RP355. Note 1Dilute the concentrated emulsion after testing and prior to application to meet the application specification requirements. Application shall be made in accordance with Practice D 3423.
1.2 The values stated in SI units are to be regarded as the standard. The inch-pound units shown in parentheses are for information only.
The following precautionary caveat pertains only to the test methods portion, Section , of this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

SIGNIFICANCE AND USE
This procedure measures the amount of hydrogen gas generation potential of aluminized emulsion roof coating. There is the possibility of water reacting with aluminum pigment to generate hydrogen gas. This situation is to be avoided, so this test was designed to evaluate coating formulations and assess the propensity to gassing.
SCOPE
1.1 This test method covers a hydrogen gas and stability test for aluminum emulsified asphalt coatings.
1.2 The values stated in inch-pound units are to be regarded as the standard. The SI units given in parentheses are for information only.
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

SCOPE
1.1 This performance specification covers mixtures of emulsified coal-tar pitch (mineral colloid type), mineral aggregates, and optional polymeric admixtures that are used as a weather-protective and straight aliphatic hydrocarbon resistant coatings over bituminous pavements of airports, parking areas, and driveways.
1.2 The following safety hazards statement applies only to the test method portion, Section 6, of this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

ABSTRACT
This practice covers the application of mineral-colloid-stabilized, emulsified coal-tar pitch, as a weather protection and aliphatic-solvent-resistant sealer for use on bituminous pavements of airports, parking lots, and driveways. The procedure for preparation of (1) old asphalt surfaces, (2) new asphalt surfaces, and (3) emulsion, and the procedure for application of emulsion for the first coat and second coat are detailed. When sand addition to the top coat of the emulsion is necessary, the sand shall meet the prescribed sieve size requirements. Application precautions including weather conditions, pavement and air temperatures, drying time, and emulsion freezing are also provided.
SCOPE
1.1 This practice covers the application of mineral-colloid-stabilized, emulsified coal-tar pitch meeting the requirements of Specification D 3320, as a weather protection and aliphatic-solvent-resistant sealer for use on bituminous pavements of airports, parking lots, and driveways.
1.2 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

SIGNIFICANCE AND USE
This practice is designed as a guide for architects, engineers, property owners or their representatives, or combination thereof. Its use helps ensure the satisfactory performance of the protective coating system when applied over bituminous concrete pavements.
SCOPE
1.1 This practice covers the application of emulsified refined coal tar slurry meeting the requirements of Specification D 6945 Types I and II, by mechanized equipment as a weather protection and petroleum (aliphatic) solvent resistant sealer for use on bituminous concrete pavements. In order to clarify the differences between Types I and II, see 3.3 for standard definition of terms.
1.2 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

ABSTRACT
This specification covers mineral-colloid-stabilized, emulsified refined coal tar suitable for use as a weather-protective and petroleum (aliphatic) solvent resistant coating. This product is typically applied to commercial lots and other low speed bituminous concrete pavements suitable for protection. The material shall be classified as: Type I and Type II. The refined coal tar emulsion seal coat shall consist of a mixture of refined coal tar emulsion, water, and aggregate and be proportioned within the ranges specified. Mixture and aggregate verification tests shall be performed to conform with the specified requirements.
SCOPE
1.1 This specification covers mineral-colloid-stabilized, emulsified refined coal tar suitable for use as a weather-protective and petroleum (aliphatic) solvent resistant coating. This product is typically applied to commercial lots and other low speed bituminous concrete pavements suitable for protection.
1.2 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory requirements prior to use.

SIGNIFICANCE AND USE
The results of this practice may be used to distinguish tar-based emulsion from an asphalt-based emulsion for specification compliance purposes.
SCOPE
1.1 This practice uses infrared analytical techniques to qualitatively determine in the laboratory a ratio of aromatic absorbance to aliphatic absorbance. This practice may be used to determine if the bitumen in the emulsion is predominantly aromatic or aliphatic in nature.
1.2 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

SCOPE
1.1 This practice uses infrared analytical techniques to qualitatively determine in the laboratory a ratio of aromatic absorbance to aliphatic absorbance. This practice may be used to determine if the bitumen in the emulsion is predominantly aromatic or aliphatic in nature.
1.2 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

SCOPE
1.1 This specification covers mineral-colloid-stabilized, emulsified coal-tar pitch suitable for use as a weather-protective and aliphatic-solvent resistant coating over bituminous pavements of airports, parking areas, and driveways.  
1.2 The values stated in SI (metric) units are to be regarded as the standard.  
1.3 The following precautionary caveat pertains only to the test method portion, Section 6, of this specification: This standard may involve hazardous materials, operations, and equipment. This standard does not purport to address all of the safety problems associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

SCOPE
1.1 This specification covers mineral-colloid-stabilized, concentrated, emulsified, refined coal tar suitable for use as weather-protective and aliphatic-solvent resistant coatings over bituminous pavements such as those found at airports, parking areas, and driveways. The specification for this material was previously covered by Federal Specification RP355.  Note 1-Dilute the concentrated emulsion after testing and prior to application to meet the application specification requirements. Application shall be made in accordance with Practice D3423.
1.2 The following precautionary caveat pertains only to the test methods portion, Section 6, of this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.