ISO 6133:2015
(Main)Rubber and plastics - Analysis of multi-peak traces obtained in determinations of tear strength and adhesion strength
Rubber and plastics - Analysis of multi-peak traces obtained in determinations of tear strength and adhesion strength
ISO 6133:2015 specifies five methods of calculating, after testing, the tear strength and the adhesion strength of vulcanized rubber or fabrics coated with or adhered to rubber or plastics. The results are calculated by determining the median and range of peak values from a graphical plot of force versus time recorded during the test. A trace for an adhesion strength test or tear strength test can show few or many force peaks, depending on the material under investigation. The choice of the method of calculation depends on the number of peaks in the trace. The purpose of this International Standard is to obtain more uniformity in the evaluation and presentation of test results. It is applicable only, however, when specified in another International Standard, i.e. a method of test or a specification. For other details, such as apparatus, test piece preparation, conditioning, procedure, etc., requirements given in the relevant International Standard shall apply. NOTE In certain cases, the methods of analysis given might not be adequate, for example, for peak values showing a trend with time. In cases where the minimum force values are of interest, it is possible to use the same methods of calculation as when determining from a range of peak values.
Caoutchouc et plastiques — Analyse des tracés multi-pics obtenus lors des déterminations de la résistance au déchirement et de la force d'adhérence
ISO 6133:2015 spécifie cinq méthodes de calcul, après essais, de la résistance au déchirement et de la force d'adhérence du caoutchouc vulcanisé ou des supports textiles revêtus ou adhérant sur le caoutchouc ou les plastiques. Les résultats sont calculés par détermination de la médiane et de l'étendue de la valeur des pics d'après un graphique, représentant la variation de la force en fonction du temps, enregistré pendant l'essai. Le tracé obtenu au cours d'un essai d'adhérence ou de résistance au déchirement peut présenter des pics de force peu nombreux ou nombreux, selon le matériau à l'étude. Le choix de la méthode de calcul dépend du nombre de pics du tracé. L'objectif de la présente Norme internationale est de donner plus d'homogénéité à l'évaluation et à la présentation des résultats des essais. Elle n'est toutefois applicable que lorsqu'elle est spécifiée dans une autre Norme internationale, c'est-à-dire une méthode d'essai ou une spécification. Pour les autres détails tels qu'appareillage, préparation des éprouvettes, conditionnement, mode opératoire, etc., les conditions spécifiées dans la Norme internationale appropriée doivent être appliquées. NOTE Dans certains cas, les méthodes d'analyse données peuvent ne pas convenir, par exemple, pour des valeurs de pic montrant une certaine tendance avec le temps. Dans les cas où l'on s'intéresse aux valeurs minimales de la force, il est possible d'utiliser les mêmes méthodes de calcul que lorsqu'on les détermine à partir d'une étendue de valeurs de pic.
General Information
- Status
- Published
- Publication Date
- 12-Aug-2015
- Technical Committee
- ISO/TC 45/SC 2 - Testing and analysis
- Drafting Committee
- ISO/TC 45/SC 2/WG 1 - Physical properties
- Current Stage
- 9093 - International Standard confirmed
- Start Date
- 10-Jun-2025
- Completion Date
- 13-Dec-2025
Relations
- Effective Date
- 04-Jan-2014
Overview
ISO 6133:2015 - "Rubber and plastics - Analysis of multi-peak traces obtained in determinations of tear strength and adhesion strength" - defines standardized methods for post-test analysis of force-versus-time traces produced during tear and adhesion tests on vulcanized rubber, rubber-coated fabrics or plastics. The standard specifies five calculation methods (A–E) to determine the median peak force and range of peak values from multi-peak traces, promoting uniform evaluation and presentation of test results.
Key topics and requirements
- Scope: Applies to the analysis step only and is to be used when referenced by another test method or specification (e.g., a method of test for tear or adhesion).
- Five analysis methods (A–E):
- Method A: For traces with fewer than five peaks - determine median, range, minimum and maximum.
- Method B: For 5–20 peaks - use central 80% of the trace and compute median and range.
- Method C: For >20 clearly defined peaks - sample 9 evenly spaced peak values and compute median and range.
- Method D: For undulating traces where peaks are not distinct - report the arithmetic mean (midpoint between max and min).
- Method E: For very dense peaks (too close for counting) - report arithmetic mean as midpoint of highest and lowest peaks.
- Peak definition and validity:
- A peak is a point where slope changes from positive to negative (instantaneous maximum).
- A peak is valid only if the drop to the following minimum exceeds 2% of the maximum force.
- Signal handling: When using computerized analysis, filter the signal (e.g., impose minimum drop percentage and minimum time between peaks) to avoid spurious small peaks.
- Limitations: Methods may be inadequate for traces showing a clear trend over time; same methods can be applied when minimum force values are of interest.
Applications
- Quality control and R&D in rubber and plastics manufacturing for evaluating tear strength and adhesion strength.
- Test laboratories reporting standardized, comparable results of force-time traces.
- Product specification verification where an internationally consistent method of analyzing multi-peak traces is required.
Who should use this standard
- Materials and test engineers, laboratory technicians, QA professionals, and standards bodies involved in mechanical testing of rubber and rubber-coated fabrics.
- Organizations that need consistent post-processing rules for force vs time traces to ensure comparability of tear and adhesion data.
Trace-analysis report (required items)
Reports should include: reference to ISO 6133, the relevant test, the chosen method (A–E), median peak (or mean for D/E), range of peak values, and date of calculation.
Related standards
- ISO 6133 is intended to be referenced by other ISO test methods and specifications for tear and adhesion testing. It was developed by ISO/TC 45 (Rubber and rubber products), SC 2 (Testing and analysis).
ISO 6133:2015 - Rubber and plastics -- Analysis of multi-peak traces obtained in determinations of tear strength and adhesion strength
ISO 6133:2015 - Caoutchouc et plastiques -- Analyse des tracés multi-pics obtenus lors des déterminations de la résistance au déchirement et de la force d'adhérence
Frequently Asked Questions
ISO 6133:2015 is a standard published by the International Organization for Standardization (ISO). Its full title is "Rubber and plastics - Analysis of multi-peak traces obtained in determinations of tear strength and adhesion strength". This standard covers: ISO 6133:2015 specifies five methods of calculating, after testing, the tear strength and the adhesion strength of vulcanized rubber or fabrics coated with or adhered to rubber or plastics. The results are calculated by determining the median and range of peak values from a graphical plot of force versus time recorded during the test. A trace for an adhesion strength test or tear strength test can show few or many force peaks, depending on the material under investigation. The choice of the method of calculation depends on the number of peaks in the trace. The purpose of this International Standard is to obtain more uniformity in the evaluation and presentation of test results. It is applicable only, however, when specified in another International Standard, i.e. a method of test or a specification. For other details, such as apparatus, test piece preparation, conditioning, procedure, etc., requirements given in the relevant International Standard shall apply. NOTE In certain cases, the methods of analysis given might not be adequate, for example, for peak values showing a trend with time. In cases where the minimum force values are of interest, it is possible to use the same methods of calculation as when determining from a range of peak values.
ISO 6133:2015 specifies five methods of calculating, after testing, the tear strength and the adhesion strength of vulcanized rubber or fabrics coated with or adhered to rubber or plastics. The results are calculated by determining the median and range of peak values from a graphical plot of force versus time recorded during the test. A trace for an adhesion strength test or tear strength test can show few or many force peaks, depending on the material under investigation. The choice of the method of calculation depends on the number of peaks in the trace. The purpose of this International Standard is to obtain more uniformity in the evaluation and presentation of test results. It is applicable only, however, when specified in another International Standard, i.e. a method of test or a specification. For other details, such as apparatus, test piece preparation, conditioning, procedure, etc., requirements given in the relevant International Standard shall apply. NOTE In certain cases, the methods of analysis given might not be adequate, for example, for peak values showing a trend with time. In cases where the minimum force values are of interest, it is possible to use the same methods of calculation as when determining from a range of peak values.
ISO 6133:2015 is classified under the following ICS (International Classification for Standards) categories: 83.060 - Rubber; 83.080.01 - Plastics in general. The ICS classification helps identify the subject area and facilitates finding related standards.
ISO 6133:2015 has the following relationships with other standards: It is inter standard links to ISO 6133:1998. Understanding these relationships helps ensure you are using the most current and applicable version of the standard.
ISO 6133:2015 is available in PDF format for immediate download after purchase. The document can be added to your cart and obtained through the secure checkout process. Digital delivery ensures instant access to the complete standard document.
Standards Content (Sample)
INTERNATIONAL ISO
STANDARD 6133
Third edition
2015-08-15
Rubber and plastics — Analysis
of multi-peak traces obtained in
determinations of tear strength and
adhesion strength
Caoutchouc et plastiques — Analyse des tracés multi-pics obtenus
lors des déterminations de la résistance au déchirement et de la
force d’adhérence
Reference number
©
ISO 2015
© ISO 2015, Published in Switzerland
All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized otherwise in any form
or by any means, electronic or mechanical, including photocopying, or posting on the internet or an intranet, without prior
written permission. Permission can be requested from either ISO at the address below or ISO’s member body in the country of
the requester.
ISO copyright office
Ch. de Blandonnet 8 • CP 401
CH-1214 Vernier, Geneva, Switzerland
Tel. +41 22 749 01 11
Fax +41 22 749 09 47
copyright@iso.org
www.iso.org
ii © ISO 2015 – All rights reserved
Contents Page
Foreword .iv
1 Scope . 1
2 Terms and definitions . 1
3 Procedure. 1
3.1 General . 1
3.2 Method A . 2
3.3 Method B . 2
3.4 Method C . 3
3.5 Method D . 3
3.6 Method E . 4
4 Trace-analysis report . 5
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out
through ISO technical committees. Each member body interested in a subject for which a technical
committee has been established has the right to be represented on that committee. International
organizations, governmental and non-governmental, in liaison with ISO, also take part in the work.
ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of
electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are
described in the ISO/IEC Directives, Part 1. In particular the different approval criteria needed for the
different types of ISO documents should be noted. This document was drafted in accordance with the
editorial rules of the ISO/IEC Directives, Part 2 (see www.iso.org/directives).
Attention is drawn to the possibility that some of the elements of this document may be the subject of
patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of
any patent rights identified during the development of the document will be in the Introduction and/or
on the ISO list of patent declarations received (see www.iso.org/patents).
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation on the meaning of ISO specific terms and expressions related to conformity
assessment, as well as information about ISO’s adherence to the WTO principles in the Technical
Barriers to Trade (TBT) see the following URL: Foreword - Supplementary information.
The committee responsible for this document is ISO/TC 45, Rubber and rubber products, Subcommittee
SC 2, Testing and analysis.
This third edition cancels and replaces the second edition (ISO 6133:1998), which has been technically
revised to define the force difference for recognizing a peak.
iv © ISO 2015 – All rights reserved
INTERNATIONAL STANDARD ISO 6133:2015(E)
Rubber and plastics — Analysis of multi-peak traces
obtained in determinations of tear strength and
adhesion strength
1 Scope
This International Standard specifies five methods of calculating, after testing,
...
NORME ISO
INTERNATIONALE 6133
Troisième édition
2015-08-15
Caoutchouc et plastiques — Analyse
des tracés multi-pics obtenus lors
des déterminations de la résistance
au déchirement et de la force
d’adhérence
Rubber and plastics — Analysis of multi-peak traces obtained in
determinations of tear strength and adhesion strength
Numéro de référence
©
ISO 2015
DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2015, Publié en Suisse
Droits de reproduction réservés. Sauf indication contraire, aucune partie de cette publication ne peut être reproduite ni utilisée
sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique, y compris la photocopie, l’affichage sur
l’internet ou sur un Intranet, sans autorisation écrite préalable. Les demandes d’autorisation peuvent être adressées à l’ISO à
l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.
ISO copyright office
Ch. de Blandonnet 8 • CP 401
CH-1214 Vernier, Geneva, Switzerland
Tel. +41 22 749 01 11
Fax +41 22 749 09 47
copyright@iso.org
www.iso.org
ii © ISO 2015 – Tous droits réservés
Sommaire Page
Avant-propos .v
1 Domaine d’application . 1
2 Termes et définitions . 1
3 Mode opératoire. 2
3.1 Généralités . 2
3.2 Méthode A . 2
3.3 Méthode B . 2
3.4 Méthode C . 3
3.5 Méthode D . 4
3.6 Méthode E. 5
4 Rapport d’analyse du tracé . 6
Avant-propos
L’ISO (Organisation internationale de normalisation) est une fédération mondiale d’organismes
nationaux de normalisation (comités membres de l’ISO). L’élaboration des Normes internationales est
en général confiée aux comités techniques de l’ISO. Chaque comité membre intéressé par une étude
a le droit de faire partie du comité technique créé à cet effet. Les organisations internationales,
gouvernementales et non gouvernementales, en liaison avec l’ISO participent également aux travaux.
L’ISO collabore étroitement avec la Commission électrotechnique internationale (CEI) en ce qui
concerne la normalisation électrotechnique.
Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont
décrites dans les Directives ISO/CEI, Partie 1. Il convient, en particulier de prendre note des différents
critères d’approbation requis pour les différents types de documents ISO. Le présent document a été
rédigé conformément aux règles de rédaction données dans les Directives ISO/CEI, Partie 2 (voir www.
iso.org/directives).
L’attention est appelée sur le fait que certains des éléments du présent document peuvent faire l’objet de
droits de propriété intellectuelle ou de droits analogues. L’ISO ne saurait être tenue pour responsable
de ne pas avoir identifié de tels droits de propriété et averti de leur existence. Les détails concernant
les références aux droits de propriété intellectuelle ou autres droits analogues identifiés lors de
l’élaboration du document sont indiqués dans l’Introduction et/ou dans la liste des déclarations de
brevets reçues par l’ISO (voir www.iso.org/brevets).
Les appellations commerciales éventuellement mentionnées dans le présent document sont données
pour information, par souci de commodité, à l’intention des utilisateurs et ne sauraient constituer un
engagement.
Pour une explication de la signification des termes et expressions spécifiques de l’ISO liés à
l’évaluation de la conformité, ou pour toute information au sujet de l’adhésion de l’ISO aux principes
de l’OMC concernant les obstacles techniques au commerce (OTC), voir le lien suivant: Avant-propos —
Informations supplémentaires.
Le comité chargé de l’élaboration du présent document est l’ISO/TC 45, Élastomères et produits à base
d’élastomères, sous-comité SC 2, Essais et analyses.
Cette troisième édition annule et remplace la deuxième édition (ISO 6133:1998), qui a fait l’objet d’une
révision afin de définir la différence de forces pour la reconnaissance d’un pic.
iv © ISO 2015 – Tous droits réservés
NORME INTERNATIONALE ISO 6133:2015(F)
Caoutchouc et plastiques — Analyse des tracés multi-
pics obtenus lors des déterminations de la résistance au
déchirement et de la force d’adhérence
1 Domaine d’application
La présente Norme internationale spécifie cinq méthodes de calcul, après essais, de la résistance
au déchirement et de la force d’adhérence du caoutchouc vulcanisé ou des supports textiles revêtus
ou adhérant sur le caoutchouc ou les plastiques. Les résultats sont calculés par déter
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.
Loading comments...