IEC 61249-2-5:2003
(Main)Materials for printed boards and other interconnecting structures - Part 2-5: Reinforced base materials, clad and unclad - Brominated epoxide cellulose paper reinforced core/woven E-glass reinforced surfaces laminated sheets of defined flammability (vertical burning test), copper-clad
Materials for printed boards and other interconnecting structures - Part 2-5: Reinforced base materials, clad and unclad - Brominated epoxide cellulose paper reinforced core/woven E-glass reinforced surfaces laminated sheets of defined flammability (vertical burning test), copper-clad
Gives requirements for properties of brominated epoxide cellulose paper reinforced core/woven E-glass reinforced surfaces-laminated sheets of defined flammability, copper-clad in thicknesses of 0,80 mm up to 1,70 mm. The flammability rating is achieved through the use of brominated fire retardants reacted as part of the epoxide polymeric structure.
Matériaux pour circuits imprimés et autres structures d'interconnexion - Partie 2-5: Matériaux de base renforcés, plaqués et non-plaqués - Feuilles stratifiées avec couches centrales renforcées en papier cellulose époxyde bromé et couches superficielles renforcées en tissu de verre de type E époxyde, d'inflammabilité définie (essai de combustion verticale), plaquées cuivre
Indique les exigences concernant les propriétés des feuilles stratifiées avec couches centrales en papier cellulose époxyde bromé et couches superficielles en tissu de verre de type E époxyde renforcé, plaquées cuivre, d'inflammabilité définie et ayant une épaisseur comprise entre 0,80 mm et 1,70 mm. Les caractéristiques d'inflammabilité sont obtenues en utilisant des ignifuges bromés issus de la structure polymère époxyde.
General Information
Relations
Standards Content (Sample)
NORME ����
INTERNATIONALE ���
����������
INTERNATIONAL
Première édition
STANDARD
First edition
2003-11
���������������������������������
����������������������������������������
������������
������������� �������!�����"��#�$�����������
�#�$������%���##���������!������&�������’���
������#������!�������������������##�#��������(���
������������’��������!����##������!����������
���������&���������(���������(��"�����!#���� �#����
��!�����)������������ �������&������#�*"��
�#�$��������&���
�
�������#��!����������� ������������’���
��������������+��������������
����������
,���!������ �����������#�"��#����������#�����
-��������������������##�#��������������!������
�����.�/�&�����+#��������!���������!�����
#����������’������!���!�����!#���� �#��(��
)&������#� �����+�����*"���������#���
Numéro de référence
Reference number
CEI/IEC 61249-2-5:2003
Numérotation des publications Publication numbering
Depuis le 1er janvier 1997, les publications de la CEI As from 1 January 1997 all IEC publications are
sont numérotées à partir de 60000. Ainsi, la CEI 34-1 issued with a designation in the 60000 series. For
devient la CEI 60034-1. example, IEC 34-1 is now referred to as IEC 60034-1.
Editions consolidées Consolidated editions
Les versions consolidées de certaines publications de la The IEC is now publishing consolidated versions of its
CEI incorporant les amendements sont disponibles. Par publications. For example, edition numbers 1.0, 1.1
exemple, les numéros d’édition 1.0, 1.1 et 1.2 indiquent and 1.2 refer, respectively, to the base publication,
respectivement la publication de base, la publication de the base publication incorporating amendment 1 and
base incorporant l’amendement 1, et la publication de the base publication incorporating amendments 1
base incorporant les amendements 1 et 2. and 2.
Informations supplémentaires Further information on IEC publications
sur les publications de la CEI
Le contenu technique des publications de la CEI est The technical content of IEC publications is kept
constamment revu par la CEI afin qu'il reflète l'état under constant review by the IEC, thus ensuring that
actuel de la technique. Des renseignements relatifs à the content reflects current technology. Information
cette publication, y compris sa validité, sont dispo- relating to this publication, including its validity, is
nibles dans le Catalogue des publications de la CEI available in the IEC Catalogue of publications
(voir ci-dessous) en plus des nouvelles éditions, (see below) in addition to new editions, amendments
amendements et corrigenda. Des informations sur les and corrigenda. Information on the subjects under
sujets à l’étude et l’avancement des travaux entrepris consideration and work in progress undertaken by the
par le comité d’études qui a élaboré cette publication, technical committee which has prepared this
ainsi que la liste des publications parues, sont publication, as well as the list of publications issued,
également disponibles par l’intermédiaire de: is also available from the following:
• Site web de la CEI (www.iec.ch) • IEC Web Site (www.iec.ch)
• Catalogue des publications de la CEI • Catalogue of IEC publications
Le catalogue en ligne sur le site web de la CEI The on-line catalogue on the IEC web site
(www.iec.ch/searchpub) vous permet de faire des (www.iec.ch/searchpub) enables you to search by a
recherches en utilisant de nombreux critères, variety of criteria including text searches,
comprenant des recherches textuelles, par comité technical committees and date of publication. On-
d’études ou date de publication. Des informations en line information is also available on recently
ligne sont également disponibles sur les nouvelles issued publications, withdrawn and replaced
publications, les publications remplacées ou retirées, publications, as well as corrigenda.
ainsi que sur les corrigenda.
• IEC Just Published • IEC Just Published
Ce résumé des dernières publications parues This summary of recently issued publications
(www.iec.ch/online_news/justpub) est aussi dispo- (www.iec.ch/online_news/justpub) is also available
nible par courrier électronique. Veuillez prendre by email. Please contact the Customer Service
contact avec le Service client (voir ci-dessous) Centre (see below) for further information.
pour plus d’informations.
• Service clients • Customer Service Centre
Si vous avez des questions au sujet de cette If you have any questions regarding this
publication ou avez besoin de renseignements publication or need further assistance, please
supplémentaires, prenez contact avec le Service contact the Customer Service Centre:
clients:
Email: custserv@iec.ch Email: custserv@iec.ch
Tél: +41 22 919 02 11 Tel: +41 22 919 02 11
Fax: +41 22 919 03 00 Fax: +41 22 919 03 00
.
NORME ����
INTERNATIONALE ���
����������
INTERNATIONAL
Première édition
STANDARD
First edition
2003-11
���������������������������������
����������������������������������������
������������
������������� �������!�����"��#�$�����������
�#�$������%���##���������!������&�������’���
������#������!�������������������##�#��������(���
������������’��������!����##������!����������
���������&���������(���������(��"�����!#���� �#����
��!�����)������������ �������&������#�*"��
�#�$��������&���
�
�������#��!����������� ������������’���
��������������+��������������
����������
,���!������ �����������#�"��#����������#�����
-��������������������##�#��������������!������
�����.�/�&�����+#��������!���������!�����
#����������’������!���!�����!#���� �#��(��
)&������#� �����+�����*"���������#���
� IEC 2003 Droits de reproduction réservés � Copyright - all rights reserved
Aucune partie de cette publication ne peut être reproduite ni No part of this publication may be reproduced or utilized in any
utilisée sous quelque forme que ce soit et par aucun procédé, form or by any means, electronic or mechanical, including
électronique ou mécanique, y compris la photocopie et les photocopying and microfilm, without permission in writing from
microfilms, sans l'accord écrit de l'éditeur. the publisher.
International Electrotechnical Commission, 3, rue de Varembé, PO Box 131, CH-1211 Geneva 20, Switzerland
Telephone: +41 22 919 02 11 Telefax: +41 22 919 03 00 E-mail: inmail@iec.ch Web: www.iec.ch
CODE PRIX
PRICE CODE S
Commission Electrotechnique Internationale
International Electrotechnical Commission
3RXUUL[YSRLUFDWDORXJHQHYLJXHUX
SQH
XH RJ DWDO WF FXUU HH ULFHV )RU
– 2 – 61249-2-5 � CEI:2003
SOMMAIRE
AVANT-PROPOS .6
1 Domaine d’application.12
2 Références normatives.12
3 Matériaux et construction .14
3.1 Résine isolante.14
3.2 Renforcement.14
3.3 Feuille de métal .14
4 Marquage interne.14
5 Propriétés électriques.14
6 Propriétés non électriques du stratifié plaqué cuivre .16
6.1 Aspect de la feuille plaquée cuivre .16
6.2 Aspect de la face non plaquée .18
6.3 Epaisseur du stratifié .18
6.4 Courbure et vrillage .18
6.5 Propriétés concernant l’adhérence de la feuille de cuivre.20
6.6 Poinçonnage et usinage.22
6.7 Stabilité dimensionnelle.22
6.8 Dimensions des feuilles .22
6.9 Panneaux découpés.24
7 Propriétés non électriques du matériau de base après retrait complet de la feuille
de cuivre.24
7.1 Aspect du matériau de base diélectrique .24
7.2 Résistance aux flexions .26
7.3 Inflammabilité.26
7.4 Absorption d’eau.28
7.5 Blanchiment au croisement des fibres .28
7.6 Température de transition vitreuse et degré de polymérisation .30
8 Assurance de la qualité.30
8.1 Système de qualité .30
8.2 Responsabilité pour le contrôle .30
8.3 Contrôle de qualification .30
8.4 Contrôle de conformité de la qualité .30
8.5 Certificat de conformité.32
8.6 Fiche technique pour la sécurité.32
9 Emballage et marquage .32
10 Informations relatives aux commandes.32
Annexe A (informative) Informations d’ingénierie .34
Annexe B (informative) Constructions courantes de stratifiés .38
Annexe C (informative) Lignes directrices pour le contrôle de qualification
et de conformité .40
Bibliographie .42
�
61249-2-5 � IEC:2003 – 3 –
CONTENTS
FOREWORD.7
1 Scope.13
2 Normative references.13
3 Materials and construction .15
3.1 Resin system.15
3.2 Reinforcement.15
3.3 Metal foil.15
4 Internal marking.15
5 Electrical properties.15
6 Non-electrical properties of the copper-clad laminate .17
6.1 Appearance of the copper-clad sheet .17
6.2 Appearance of the unclad face.19
6.3 Laminate thickness.19
6.4 Bow and twist .19
6.5 Properties related to the copper foil bond .21
6.6 Punching and machining .23
6.7 Dimensional stability.23
6.8 Sheet sizes.23
6.9 Cut panels.25
7 Non-electrical properties of the base material after complete removal of the copper foil .25
7.1 Appearance of the dielectric base material .25
7.2 Flexural strength.27
7.3 Flammability.27
7.4 Water absorption.29
7.5 Measling.29
7.6 Glass transition temperature and cure factor .31
8 Quality assurance.31
8.1 Quality system.31
8.2 Responsibility for inspection.31
8.3 Qualification inspection.31
8.4 Quality conformance inspection.31
8.5 Certificate of conformance .33
8.6 Safety data sheet.33
9 Packaging and marking.33
10 Ordering information.33
Annex A (informative) Engineering information .35
Annex B (informative) Common laminate construction .39
Annex C (informative) Guideline for qualification and conformance inspection.41
Bibliography .43
– 4 – 61249-2-5 � CEI:2003
Tableau 1 – Propriétés électriques .14
Tableau 2 – Epaisseur nominale et tolérance des stratifiés plaqués métal.18
Tableau 3 – Courbure et vrillage.20
Tableau 4 – Forces d’arrachement et d’adhérence.20
Tableau 5 – Stabilité dimensionnelle.22
Tableau 6 – Tolérances de dimensions pour panneaux découpés .24
Tableau 7 – Rectangularité des panneaux découpés .24
Tableau 8 – Résistance aux flexions.26
Tableau 9 – Inflammabilité .28
Tableau 10 – Absorption d’eau .28
Tableau 11 – Blanchiment au croisement des fibres .28
Tableau 12 – Température de transition vitreuse et degré de polymérisation.30
Tableau C.1 – Lignes directrices pour le contrôle de qualification et de conformité.40
61249-2-5 � IEC:2003 – 5 –
Table 1 – Electrical properties .15
Table 2 – Nominal thickness and tolerance of metal-clad laminate .19
Table 3 – Bow and twist.21
Table 4 – Pull-off and peel strength .21
Table 5 – Dimensional stability .23
Table 6 – Size tolerance for cut panels .25
Table 7 – Rectangularity of cut panels .25
Table 8 – Flexural strength.27
Table 9 – Flammability .29
Table 10 – Water absorption .29
Table 11 – Measling .29
Table 12 – Glass transition temperature and cure factor .31
Table C.1 – Guideline for qualification and conformance inspection .41
– 6 – 61249-2-5 � CEI:2003
COMMISSION ÉLECTROTECHNIQUE INTERNATIONALE
____________
�
���������������������������������
����������������������������������������
�
������������������������� �!����"#$�%�!&�’(�)��!����"$"�’(�)��!����
*���((�!�!�����#���!��+�%�%$�%,�!�%�"���(�!���"#$�%��!��"�’�’�����
%�((�($!���’$�-��� �$.�����%$�%,�!�!�’��#�%��((�!���"#$�%��!�
�"���!!�����+���������-’�����’$�-��&����"#(�.� �(������#�"����
/�!!������%$. �!��$"�+����%�(�0&�’(�)���!�%��+���
�
�
AVANT-PROPOS
1) La Commission Electrotechnique Internationale (CEI) est une organisation mondiale de normalisation composée
de l'ensemble des comités électrotechniques nationaux (Comités nationaux de la CEI). La CEI a pour objet de
favoriser la coopération internationale pour toutes les questions de normalisation dans les domaines de
l'électricité et de l'électronique. A cet effet, la CEI – entre autres activités – publie des Normes internationales,
des Spécifications techniques, des Rapports techniques, des Spécifications accessibles au public (PAS) et des
Guides (ci-après dénommés "Publication(s) de la CEI"). Leur élaboration est confiée à des comités d'études,
aux travaux desquels tout Comité national intéressé par le sujet traité peut participer. Les organisations
internationales, gouvernementales et non gouvernementales, en liaison avec la CEI, participent également aux
travaux. La CEI collabore étroitement avec l'Organisation Internationale de Normalisation (ISO), selon des
conditions fixées par accord entre les deux organisations.
2) Les décisions ou accords officiels de la CEI concernant les questions techniques représentent, dans la mesure
du possible, un accord international sur les sujets étudiés, étant donné que les Comités nationaux de la CEI
intéressés sont représentés dans chaque comité d’études.
3) Les Publications de la CEI se présentent sous la forme de recommandations internationales et sont agréées
comme telles par les Comités nationaux de la CEI. Tous les efforts raisonnables sont entrepris afin que la CEI
s'assure de l'exactitude du contenu technique de ses publications; la CEI ne peut pas être tenue responsable de
l'éventuelle mauvaise utilisation ou interprétation qui en est faite par un quelconque utilisateur final.
4) Dans le but d'encourager l'uniformité internationale, les Comités nationaux de la CEI s'engagent, dans toute la
mesure possible, à appliquer de façon transparente les Publications de la CEI dans leurs publications
nationales et régionales. Toutes divergences entre toutes Publications de la CEI et toutes publications
nationales ou régionales correspondantes doivent être indiquées en termes clairs dans ces dernières.
5) La CEI n’a prévu aucune procédure de marquage valant indication d’approbation et n'engage pas sa
responsabilité pour les équipements déclarés conformes à une de ses Publications.
6) Tous les utilisateurs doivent s'assurer qu'ils sont en possession de la dernière édition de cette publication.
7) Aucune responsabilité ne doit être imputée à la CEI, à ses administrateurs, employés, auxiliaires ou
mandataires, y compris ses experts particuliers et les membres de ses comités d'études et des Comités
nationaux de la CEI, pour tout préjudice causé en cas de dommages corporels et matériels, ou de tout autre
dommage de quelque nature que ce soit, directe ou indirecte, ou pour supporter les coûts (y compris les frais
de justice) et les dépenses découlant de la publication ou de l'utilisation de cette Publication de la CEI ou de
toute autre Publication de la CEI, ou au crédit qui lui est accordé.
8) L'attention est attirée sur les références normatives citées dans cette publication. L'utilisation de publications
référencées est obligatoire pour une application correcte de la présente publication.
9) L’attention est attirée sur le fait que certains des éléments de la présente Publication de la CEI peuvent faire
l’objet de droits de propriété intellectuelle ou de droits analogues. La CEI ne saurait être tenue pour
responsable de ne pas avoir identifié de tels droits de propriété et de ne pas avoir signalé leur existence.
La Norme internationale CEI 61249-2-5 a été établie par le comité d'études 91 de la CEI:
Techniques d’assemblage des composants électroniques.
Le texte de cette norme est issu des documents suivants:
FDIS Rapport de vote
91/410/FDIS 91/426/RVD
Le rapport de vote indiqué dans le tableau ci-dessus donne toute information sur le vote ayant
abouti à l'approbation de cette norme.
61249-2-5 � IEC:2003 – 7 –
INTERNATIONAL ELECTROTECHNICAL COMMISSION
____________
�
�����������������������������
���������������������������������������
�
��������������� �!�"�#�$��%������&$’�!&�"���"�(�!&�"���
�� %�����"��) *�"��!�&&(& $��)�)�������� �!�"�! ���+��
, -�����.&�$$������ �!�"�$(���!�$�&�%�����"�$/���$��
��"�����"��&�%%�#�&��0�1-����!�&�#(����.���$�2’�! ))���!&�"�
�
�
FOREWORD
1) The International Electrotechnical Commission (IEC) is a worldwide organization for standardization comprising
all national electrotechnical committees (IEC National Committees). The object of IEC is to promote
international co-operation on all questions concerning standardization in the electrical and electronic fields. To
this end and in addition to other activities, IEC publishes International Standards, Technical Specifications,
Technical Reports, Publicly Available Specifications (PAS) and Guides (hereafter referred to as “IEC
Publication(s)”). Their preparation is entrusted to technical committees; any IEC National Committee interested
in the subject dealt with may participate in this preparatory work. International, governmental and non-
governmental organizations liaising with the IEC also participate in this preparation. IEC collaborates closely
with the International Organization for Standardization (ISO) in accordance with conditions determined by
agreement between the two organizations.
2) The formal decisions or agreements of IEC on technical matters express, as nearly as possible, an international
consensus of opinion on the relevant subjects since each technical committee has representation from all
interested IEC National Committees.
3) IEC Publications have the form of recommendations for international use and are accepted by IEC National
Committees in that sense. While all reasonable efforts are made to ensure that the technical content of IEC
Publications is accurate, IEC cannot be held responsible for the way in which they are used or for any
misinterpretation by any end user.
4) In order to promote international uniformity, IEC National Committees undertake to apply IEC Publications
transparently to the maximum extent possible in their national and regional publications. Any divergence
between any IEC Publication and the corresponding national or regional publication shall be clearly indicated in
the latter.
5) IEC provides no marking procedure to indicate its approval and cannot be rendered responsible for any
equipment declared to be in conformity with an IEC Publication.
6) All users should ensure that they have the latest edition of this publication.
7) No liability shall attach to IEC or its directors, employees, servants or agents including individual experts and
members of its technical committees and IEC National Committees for any personal injury, property damage or
other damage of any nature whatsoever, whether direct or indirect, or for costs (including legal fees) and
expenses arising out of the publication, use of, or reliance upon, this IEC Publication or any other IEC
Publications.
8) Attention is drawn to the Normative references cited in this publication. Use of the referenced publications is
indispensable for the correct application of this publication.
9) Attention is drawn to the possibility that some of the elements of this IEC Publication may be the subject of
patent rights. IEC shall not be held responsible for identifying any or all such patent rights.
International Standard IEC 61249-2-5 has been prepared by IEC technical committee 91:
Electronics assembly technology.
The text of this standard is based on the following documents:
FDIS Report on voting
91/410/FDIS 91/426/RVD
Full information on the voting for the approval of this standard can be found in the report on
voting indicated in the above table.
– 8 – 61249-2-5 � CEI:2003
Cette publication a été rédigée selon les Directives ISO/CEI, Partie 2.
La CEI 61249-2 comprend les parties suivantes, sous le titre général ������������������������
��������� ��� ������� ����������� ����������������� �� ������� ��� ���������� ��� ����� �����������
������������������������
Partie 2-1: Feuille de papier cellulose phénolique, de qualité économique
Partie 2-2: Feuilles stratifiées renforcées en feuille de papier cellulose phénolique, de qualité
électrique élevée, plaquées cuivre
Partie 2-4: Feuille stratifiée en fibre de verre non tissées/tissées polyester, d’inflammabilité
définie (essai de combustion verticale), plaquée cuivre
Partie 2-5: Feuilles stratifiées avec couches centrales renforcées en papier cellulose
époxyde bromé et couches superficielles renforcées en tissu de verre de type E
époxyde, d’inflammabilité définie (essai de combustion verticale), plaquées cuivre
Partie 2-6: Feuilles stratifiées renforcées en verre de type E époxyde bromé tissé/non tissé,
d’inflammabilité définie (essai de combustion verticale), plaquées cuivre
Partie 2-7: Feuille stratifiée tissée de verre E avec de la résine époxyde, d’inflammabilité
définie (essai de combustion verticale), plaquée cuivre
Partie 2-8: Feuilles stratifiées renforcées en tissu de fibres de verre époxyde bromé modifié,
d’inflammabilité définie (essai de combustion verticale), plaquées cuivre
Partie 2-9: Feuilles stratifiées renforcées en tissu de verre de type E époxyde, modifié ou
non, en bismaléimide/triazine, d’inflammabilité définie (essai de combustion
verticale), plaquées cuivre
Partie 2-10: Feuilles stratifiées renforcées en tissu de verre de type E ester de cyanate,
époxyde bromé, modifié ou non, d’inflammabilité définie (essai de combustion
verticale), plaquées cuivre
Partie 2-11: Feuilles stratifiées renforcées en polyimide et tissu de verre de type E époxyde
bromé modifié ou non modifié, d’inflammabilité définie (essai de combustion
verticale), plaquées cuivre
Partie 2-12: Stratifié à base d'aramide non tissé collé avec de la résine époxyde, recouvert de
cuivre, d'inflammabilité définie
Partie 2-13: Stratifié à base d'aramide non tissé collé avec de la résine cyanate ester, recou-
vert de cuivre, d'inflammabilité définie
Partie 2-18: Feuille stratifiée renforcées en fibres de verre non tissées polyester d'inflam-
mabilité définie (essai de combustion verticale), plaquée cuivre
Partie 2-19: Feuilles multicouches de fibre de verre linéaire cohérente avec résine époxyde
pour hautes températures, d’inflammabilité définie (essai d’inflammabilité
verticale), plaquées cuivre
Partie 2-21: Feuilles stratifiées renforcées en tissu de verre de type E époxyde non halogéné,
d’inflammabilité définie (essai de combustion verticale), plaquées cuivre
Part 2-22: Modified non-halogenated epoxide woven E-glass laminated sheets of defined
flammablity (vertical burning test), copper-clad
___________
A l’étude. Actuellement, les titres n'ont pas été traduits en français.
61249-2-5 � IEC:2003 – 9 –
This publication has been drafted in accordance with the ISO/IEC Directives, Part 2.
IEC 61249-2 consists of the following parts, under the general title �����������������������������
�������������������������������������������������������������������������������������������
Part 2-1: Phenolic cellulose paper laminate, economic grade
Part 2-2: Phenolic cellulose paper reinforced laminated sheets, high electrical grade,
copper-clad
Part 2-4: Polyester non-woven/woven fibreglass laminated sheet of defined flammability
(vertical burning test), copper-clad
Part 2-5: Brominated epoxide cellulose paper reinforced core/woven E-glass reinforced
surfaces laminated sheets of defined flammability (vertical burning test), copper-
clad
Part 2-6: Brominated epoxide non-woven/woven, E-glass reinforced laminated sheets of
defined flammability (vertical burning test), copper-clad
Part 2-7: Epoxide woven E-glass laminated sheet of defined flammability (vertical burning
test), copper-clad
Part 2-8: Modified brominated epoxide woven fibreglass reinforced laminated sheets of
defined flammability (vertical burning test), copper clad
Part 2-9: Bismaleimide/triazine, modified epoxide or unmodified, woven E-glass reinforced
laminated sheets of defined flammability (vertical burning test), copper-clad
Part 2-10: Cyanate ester, brominated epoxide, modified or unmodified, woven E-glass
reinforced laminated sheets of defined flammability (vertical burning test),
copper-clad
Part 2-11: Polyimide, brominated epoxide modified or unmodified, woven E-glass reinforced
laminated sheets of defined flammability (vertical burning test), copper-clad
Part 2-12: Epoxide non-woven aramid laminate of defined flammability, copper-clad
Part 2-13: Cyanate ester non-woven aramid laminate of defined flammability, copper-clad
Part 2-18: Polyester non-woven fibreglass reinforced laminated sheet of defined flammability
(vertical burning test), copper-clad
Part 2-19: Epoxide cross-plied linear fibreglass-reinforced laminated sheets of defined flam-
mability (vertical burning test), copper-clad
Part 2-21: Non-halogenated epoxide woven E-glass reinforced laminated sheets of defined
flammability (vertical burning test), copper-clad
Part 2-22: Modified non-halogenated epoxide woven E-glass laminated sheets of defined
flammablity (vertical burning test), copper-clad
___________
Under consideration.
– 10 – 61249-2-5 � CEI:2003
Part 2-23: Non-brominated phenolic, cellulose paper laminated sheets of defined
flammability, economic grade, copper clad
Part 2-26: Non-brominated epoxide, non-woven/woven glass fabric sheet of defined flam-
mability, copper-clad
Le comité a décidé que le contenu de cette publication ne sera pas modifié avant 2007. A cette
date, la publication sera
reconduite;
supprimée;
remplacée par une édition révisée, ou
amendée.
___________
A l’étude. Actuellement, les titres n'ont pas été traduits en français.
61249-2-5 � IEC:2003 – 11 –
Part 2-23: Non-brominated phenolic, cellulose paper laminated sheets of defined flammability,
economic grade, copper clad
Part 2-26: Non-brominated epoxide, non-woven/woven glass fabric sheet of defined flam-
mability, copper-clad
The committee has decided that the contents of this publication will remain unchanged until
2007. At this date, the publication will be
reconfirmed;
withdrawn;
replaced by a revised edition, or
amended.
___________
Under consideration.
– 12 – 61249-2-5 � CEI:2003
����������������������������������
����������������������������������������
�
������������������������� �!����"#$�%�!&�’(�)��!����"$"�’(�)��!����
*���((�!�!�����#���!��+�%�%$�%,�!�%�"���(�!���"#$�%��!��"�’�’�����
%�((�($!���’$�-��� �$.�����%$�%,�!�!�’��#�%��((�!���"#$�%��!�
�"���!!�����+���������-’�����’$�-��&����"#(�.� �(������#�"����
/�!!������%$. �!��$"�+����%�(�0&�’(�)���!�%��+���
�
�
�
1� �$.��"�����’’(�%���$"�
La présente partie de la CEI 61249 indique les exigences concernant les propriétés des feuilles
stratifiées avec couches centrales en papier cellulose époxyde bromé et couches superficielles
en tissu de verre de type E époxyde renforcé, plaquées cuivre, d’inflammabilité définie
(essai de combustion verticale) et ayant une épaisseur comprise entre 0,80 mm et 1,70 mm.
Les caractéristiques d’inflammabilité sont obtenues en utilisant des ignifuges bromés issus de
la structure polymère époxyde. La température de transition vitreuse est définie à 75 �C
minimum.
Certaines exigences de propriétés peuvent comprendre plusieurs classes de performance. Il
faut spécifier la classe désirée sur l'ordre d'achat faute de quoi c’est la classe par défaut du
matériau qui sera fournie.
�� ��#���"%�!�"$�.���+�!�
Les documents de référence suivants sont indispensables pour l'application du présent
document. Pour les références datées, seule l'édition citée s'applique. Pour les références non
datées, la dernière édition du document de référence s'applique (y compris les éventuels
amendements).
CEI 61189-2:1997, ��������������������������������������������������������������������������
�������������������������������������������������������������������������������������������
����������������������������������
CEI 61249-5-1:1995, �������������������������������������������������������������������������
��������������������������������������������������������������������������������� ���������
!�������"��#������������������$��������������������������������������������������������%�
ISO 9000:2000, !&��’�����������(���������������������������������������������������������
ISO 11014-1:1994, #������������������������������������������������������������������"��
�����������������&����
ISO 14001:1996, !&��’�����������(������������������������!������������������(���������)
����������������������������
61249-2-5 � IEC:2003 – 13 –
�����������������������������
����������������������������������������
�
��������������� �!�"�#�$��%������&$’�!&�"���"�(�!&�"���
�� %�����"��) *�"��!�&&(& $��)�)�������� �!�"�! ���+��
, -�����.&�$$������ �!�"�$(���!�$�&�%�����"�$/���$��
��"�����"��&�%%�#�&��0�1-����!�&�#(����.���$�2’�! ))���!&�"�
�
�
�
�
3� �! )��
This part of IEC 61249 gives requirements for properties of brominated epoxide cellulose paper
reinforced core/woven E-glass reinforced surfaces-laminated sheets of defined flammability
(vertical burning test), copper-clad in thicknesses of 0,80 mm up to 1,70 mm. The flammability
rating is achieved through the use of brominated fire retardants reacted as part of the epoxide
polymeric structure. The glass transition temperature is defined to be 75 °C minimum.
Some property requirements may have several classes of performance. The class desired
needs to be specified on the purchase order, otherwise the default class of material may be
supplied.
�� � �%���-���������!�$�
The following referenced documents are indispensable for the application of this document. For
dated references, only the edition cited applies. For undated references, the latest edition of
the referenced document (including any amendments) applies.
IEC 61189-2:1997, ����� �������� ���� ����������� ����������� ���������������� ����������� ����
���������������������������������������������������������������
IEC 61249-5-1:1995, ���������������������������������������������������������������������������
���������������������������������������������������������������������� ��!�����������"��������
���������������������#�������������������$
ISO 9000:2000, %�����&�������������&��������’�������������������������&
ISO 11014-1:1994, �����&����������������������������������������� ��!�����������������
�������������
ISO 14001:1996, (�������������������������&�������������������������������������������
– 14 – 61249-2-5 � CEI:2003
2� �������������%$"!���%��$"�
La feuille est constituée d’une base isolante sur laquelle est collée une feuille de métal sur une
face ou sur les deux.
231� ��!�"���!$(�"���
Epoxyde modifié ou non, résultant d'un stratifié avec une température de transition vitreuse de
75 �C minimum.
Il est permis d’ajouter des agents de contraste pour renforcer les traitements comme le
contrôle optique automatisé (AOI – automated optical inspection).
Sa résistance à la flamme est définie par rapport aux exigences d’inflammabilité de 7.3.
23�� ��"#$�%�.�"���
Renforcement en tissu de verre de type E comme spécifié dans la CEI 61249-6-3, tissu de
verre de type E (pour la fabrication de matériaux préimprégnés et plaqués cuivre).
Renforcement en papier cellulose non tissé.
232� *���((�����.���(�
Cuivre comme spécifié dans la CEI 61249-5-1, feuille de cuivre (pour la fabrication de
matériaux plaqués cuivre). Les feuilles préférentielles sont celles à cuivre déposé par
électrolyse et à ductilité définie.
4� ���)��5���"���"��
Non spécifié.
�� ��$’�����!��(�%���)��!�
Les exigences pour les propriétés électriques sont données au Tableau 1.
�� (����1�����$’�����!��(�%���)��!�
3URSULpWpV 0pWKRGHG¶HVVDL ([LJHQFHV
&(,
Résistance de la feuille 2E12 Comme spécifié dans la
CEI 61249-5-1
Résistance superficielle après chaleur humide dans la chambre 2E03 t3 000 M:
climatique (facultatif)
Résistance superficielle après chaleur humide et reprise 2E03 t30 000 M:
Résistivité transversale après chaleur humide dans la chambre 2E04 t1 000 M:m
climatique (facultatif)
Résistivité transversale après chaleur humide et reprise 2E04 t5 000 M:m
Permittivité relative après chaleur humide et reprise à 1 MHz 2E10 d5,4
Facteur de dissipation après chaleur humide et reprise à 1 MHz 2E10 d0,045
Résistance de l’arc 2E14 t60s
t1 000 M:
2E07
Résistance superficielle à 100 qC
Résistivité transversale 100 qC 2E07 t100 M:m
�
61249-2-5 � IEC:2003 – 15 –
4� �������&$���"�! �$��(!�� ��
The sheet consists of an insulating base with metal-foil bonded to one side or both.
453� ��$���$0$��%��
Epoxide, modified or unmodified, resulting in a laminate with a glass transition temperature of
75 °C minimum.
Contrast agents may be added to enhance processing such as automated optical inspection
(AOI).
Its flame resistance is defined in terms of the flammability requirements of 7.3.
45�� ����� �!�%����
Woven E-glass as specified in IEC 61249-6-3, woven E-glass fabric (for the manufacture of
prepreg and copper clad materials). Non-woven cellulose paper reinforcement.
454� ����&�� �&�
Copper as specified in IEC 61249-5-1, copper foil (for the manufacture of copper-clad
materials). The preferred foils are electro-deposited of defined ductility.
6� �������&�%��7��.�
Not specified.
�� �&�!���!�&�)� )�����$�
The requirements for the electrical property are shown in Table 1.
��#&��3����&�!���!�&�)� )�����$�
3URSHUW\ 7HVWPHWKRG 5HTXLUHPHQW
,(&
Resistance of foil 2E12 As specified in
IEC 61249-5-1
Surface resistance after damp heat while in the humidity 2E03
t3 000 M:
chamber (optional)
Surface resistance after damp heat and recovery 2E03 t30 000 M:
Volume resistivity after damp heat while in the humidity chamber 2E04 t1 000 M:m
(optional)
Volume resistivity after damp heat and recovery 2E04 t5 000 M:m
Relative permittivity after damp heat and recovery at 1 MHz 2E10 d5,4
Dissipation factor after damp heat and recovery at 1MHz 2E10 d0,045
Arc resistance 2E14 t60 s
2E07
Surface resistance at 100 qC t1 000 M:
Volume resistivity at 100 qC 2E07 t100 M:m
�
– 16 – 61249-2-5 � CEI:2003
6� ��$’�����!�"$"��(�%���)��!����!�����#���’(�)���%��+���
631� �!’�%�����(��#���((��’(�)����%��+���
La face plaquée cuivre doit être en grande partie exempte de défauts susceptibles d’affecter
l’aptitude du matériau lors de son utilisation dans le but prévu.
Pour les défauts spécifiques suivants, les exigences données doivent s’appliquer lorsque le
contrôle est effectué conformément à la CEI 61189-2, méthode 2M18.
63131� �.’���"��!�/’�)7��!����.��)��!����%$�’0�
La taille d’une empreinte, généralement sa longueur, doit être déterminée et une valeur en
points, à utiliser pour mesurer la qualité, doit lui être attribuée.
7DLOOH
9DOHXUHQSRLQWVSRXUFKDTXHHPSUHLQWH
mm
0,13 – 0,25 1
0,26 – 0,50 2
0,51 – 0,75 4
0,76 – 1,00 7
Supérieure à 1,00 30
Le décompte total de points doit être calculé pour toute surface de 300 mm x 300 mm pour
déterminer la classe d'empreinte du matériau.
Empreinte de classe A maximum de 29 points au total
Empreinte de classe B maximum de 17 points au total
Empreinte de classe C maximum de 5 points au total
Empreinte de classe D 0 point
Empreinte de classe X doit faire l’objet d’un accord entre l’utilisateur et le fournisseur.
La classe d'empreinte de matériau exigée doit être spécifiée dans l’ordre d’achat. Sauf
spécification contraire, c’est la classe d'empreinte A qui s’applique.
6313�� ����!��
La surface en cuivre ne doit pas présenter de rides.
63132� ���#(���!��
Les éraflures d’une profo
...








Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.
Loading comments...