IEC 61249-2-22:2005

NORME CEI
INTERNATIONALE IEC
61249-2-22
INTERNATIONAL
Première édition
STANDARD
First edition
2005-01
Matériaux pour circuits imprimés
et autres structures d'interconnexion –
Partie 2-22:
Matériaux de base renforcés, plaqués et
non plaqués – Feuilles stratifiées en tissu
de verre de type E époxyde non halogéné
modifié, d'inflammabilité définie (essai de
combustion verticale), plaquées cuivre
Materials for printed boards
and other interconnecting structures –
Part 2-22:
Reinforced base materials clad and unclad –
Modified non-halogenated epoxide woven
E-glass laminated sheets of defined flammability
(vertical burning test), copper-clad
Numéro de référence
Reference number
CEI/IEC 61249-2-22:2005
Numérotation des publications Publication numbering
Depuis le 1er janvier 1997, les publications de la CEI As from 1 January 1997 all IEC publications are
sont numérotées à partir de 60000. Ainsi, la CEI 34-1 issued with a designation in the 60000 series. For
devient la CEI 60034-1. example, IEC 34-1 is now referred to as IEC 60034-1.
Editions consolidées Consolidated editions
Les versions consolidées de certaines publications de la The IEC is now publishing consolidated versions of its
CEI incorporant les amendements sont disponibles. Par publications. For example, edition numbers 1.0, 1.1
exemple, les numéros d’édition 1.0, 1.1 et 1.2 indiquent and 1.2 refer, respectively, to the base publication,
respectivement la publication de base, la publication de the base publication incorporating amendment 1 and
base incorporant l’amendement 1, et la publication de the base publication incorporating amendments 1
base incorporant les amendements 1 et 2. and 2.
Informations supplémentaires Further information on IEC publications
sur les publications de la CEI
Le contenu technique des publications de la CEI est The technical content of IEC publications is kept
constamment revu par la CEI afin qu'il reflète l'état under constant review by the IEC, thus ensuring that
actuel de la technique. Des renseignements relatifs à the content reflects current technology. Information
cette publication, y compris sa validité, sont dispo- relating to this publication, including its validity, is
nibles dans le Catalogue des publications de la CEI available in the IEC Catalogue of publications
(voir ci-dessous) en plus des nouvelles éditions, (see below) in addition to new editions, amendments
amendements et corrigenda. Des informations sur les and corrigenda. Information on the subjects under
sujets à l’étude et l’avancement des travaux entrepris consideration and work in progress undertaken by the
par le comité d’études qui a élaboré cette publication, technical committee which has prepared this
ainsi que la liste des publications parues, sont publication, as well as the list of publications issued,
également disponibles par l’intermédiaire de: is also available from the following:
x Site web de la CEI (www.iec.ch) x IEC Web Site (www.iec.ch)
x Catalogue des publications de la CEI x Catalogue of IEC publications
Le catalogue en ligne sur le site web de la CEI The on-line catalogue on the IEC web site
(www.iec.ch/searchpub) vous permet de faire des (www.iec.ch/searchpub) enables you to search by a
recherches en utilisant de nombreux critères, variety of criteria including text searches,
comprenant des recherches textuelles, par comité technical committees and date of publication. On-
d’études ou date de publication. Des informations en line information is also available on recently
ligne sont également disponibles sur les nouvelles issued publications, withdrawn and replaced
publications, les publications remplacées ou retirées, publications, as well as corrigenda.
ainsi que sur les corrigenda.
x IEC Just Published x IEC Just Published
Ce résumé des dernières publications parues This summary of recently issued publications
(www.iec.ch/online_news/justpub) est aussi dispo- (www.iec.ch/online_news/justpub) is also available
nible par courrier électronique. Veuillez prendre by email. Please contact the Customer Service
contact avec le Service client (voir ci-dessous) Centre (see below) for further information.
pour plus d’informations.
x Service clients x Customer Service Centre
Si vous avez des questions au sujet de cette If you have any questions regarding this
publication ou avez besoin de renseignements publication or need further assistance, please
supplémentaires, prenez contact avec le Service contact the Customer Service Centre:
clients:
Email: custserv@iec.ch Email: custserv@iec.ch
Tél: +41 22 919 02 11 Tel: +41 22 919 02 11
Fax: +41 22 919 03 00 Fax: +41 22 919 03 00
.
NORME CEI
INTERNATIONALE IEC
61249-2-22
INTERNATIONAL
Première édition
STANDARD
First edition
2005-01
Matériaux pour circuits imprimés
et autres structures d'interconnexion –
Partie 2-22:
Matériaux de base renforcés, plaqués et
non plaqués – Feuilles stratifiées en tissu
de verre de type E époxyde non halogéné
modifié, d'inflammabilité définie (essai de
combustion verticale), plaquées cuivre
Materials for printed boards
and other interconnecting structures –
Part 2-22:
Reinforced base materials clad and unclad –
Modified non-halogenated epoxide woven
E-glass laminated sheets of defined flammability
(vertical burning test), copper-clad
 IEC 2005 Droits de reproduction réservés  Copyright - all rights reserved
Aucune partie de cette publication ne peut être reproduite ni No part of this publication may be reproduced or utilized in any
utilisée sous quelque forme que ce soit et par aucun procédé, form or by any means, electronic or mechanical, including
électronique ou mécanique, y compris la photocopie et les photocopying and microfilm, without permission in writing from
microfilms, sans l'accord écrit de l'éditeur. the publisher.
International Electrotechnical Commission, 3, rue de Varembé, PO Box 131, CH-1211 Geneva 20, Switzerland
Telephone: +41 22 919 02 11 Telefax: +41 22 919 03 00 E-mail: inmail@iec.ch Web: www.iec.ch
CODE PRIX
Commission Electrotechnique Internationale PRICE CODE T
International Electrotechnical Commission
ɆɟɠɞɭɧɚɪɨɞɧɚɹɗɥɟɤɬɪɨɬɟɯɧɢɱɟɫɤɚɹɄɨɦɢɫɫɢɹ
Pour prix, voir catalogue en vigueur
For price, see current catalogue

– 2 – 61249-2-22 ¤ CEI:2005
SOMMAIRE
AVANT-PROPOS.6
1 Domaine d'application .12
2 Références normatives.12
3 Matériaux et construction .14
3.1 Résine isolante.14
3.2 Feuille de métal.14
3.3 Renforcement.14
4 Marquage interne .14
5 Propriétés électriques.14
6 Propriétés non électriques de la feuille stratifiée plaquée cuivre.16
6.1 Aspect de la feuille plaquée cuivre.16
6.2 Aspect de la face non plaquée.20
6.3 Épaisseur du stratifié.20
6.4 Courbure et vrillage .20
6.5 Propriétés concernant l’adhérence de la feuille de cuivre .22
6.6 Poinçonnage et usinage .24
6.7 Stabilité dimensionnelle.24
6.8 Dimensions des feuilles .26
6.9 Panneaux découpés .26
7 Propriétés non électriques du matériau de base après retrait total de la feuille de
cuivre.28
7.1 Aspect du matériau de base diélectrique.28
7.2 Résistance aux flexions .28
7.3 Inflammabilité.30
7.4 Absorption d’eau .30
7.5 Blanchiment au croisement des fibres.32
7.6 Température de transition vitreuse et degré de polymérisation .32
8 Assurance de la qualité .34
8.1 Système de qualité .34
8.2 Responsabilité pour le contrôle.34
8.3 Contrôle de qualification .34
8.4 Contrôle de conformité de la qualité.34
8.5 Certificat de conformité .34
8.6 Fiche technique pour la sécurité .34
9 Emballage et marquage.36
10 Informations relatives aux commandes .36
Annexe A (informative) Informations d'ingénierie.38
Annexe B (informative) Constructions courantes de stratifiés .42
Annexe C (informative) Lignes directrices pour le contrôle de qualification et de
conformité .46
Bibliographie .48

61249-2-22¤ IEC:2005 – 3 –
CONTENTS
FOREWORD .7
1 Scope .13
2 Normative references .13
3 Materials and construction.15
3.1 Resin system.15
3.2 Metal foil .15
3.3 Reinforcement.15
4 Internal marking .15
5 Electrical properties.15
6 Non-electrical properties of the copper-clad laminate .17
6.1 Appearance of the copper-clad sheet.17
6.2 Appearance of the unclad face .21
6.3 Laminate thickness.21
6.4 Bow and twist .21
6.5 Properties related to the copper foil bond.23
6.6 Punching and machining.25
6.7 Dimensional stability.25
6.8 Sheet sizes .27
6.9 Cut panels.27
7 Non-electrical properties of the base material after complete removal of the
copper foil. .29
7.1 Appearance of the dielectric base material.29
7.2 Flexural strength .29
7.3 Flammability.31
7.4 Water absorption .31
7.5 Measling. .33
7.6 Glass transition temperature and cure factor.33
8 Quality assurance.35
8.1 Quality system.35
8.2 Responsibility for inspection .35
8.3 Qualification inspection .35
8.4 Quality conformance inspection .35
8.5 Certificate of conformance.35
8.6 Safety data sheet .35
9 Packaging and marking .37
10 Ordering information.37
Annex A (informative) Engineering information.39
Annex B (informative) Common laminate constructions .43
Annex C (informative) Guideline for qualification and conformance inspection .47
Bibliography .25

– 4 – 61249-2-22 ¤ CEI:2005
Tableau 1 – Propriétés électriques.16
Tableau 2 – Épaisseur nominale et tolérance des stratifiés plaqués métal .20
Tableau 3 – Exigences de courbure et de vrillage .22
Tableau 4 – Exigences pour les forces d’arrachement et d’adhérence .24
Tableau 5 – Stabilité dimensionnelle.26
Tableau 6 – Tolérances de tailles pour panneaux découpés .26
Tableau 7 – Rectangularité des panneaux découpés.28
Tableau 8 – Exigences de résistance aux flexions.30
Tableau 9 – Exigences d’inflammabilité.30
Tableau 10 – Exigences d’absorption d’eau .32
Tableau 11 – Exigences de blanchiment au croisement des fibres.32
Tableau 12 – Exigences de température de transition vitreuse et de facteur de
traitement .32

61249-2-22¤ IEC:2005 – 5 –
Table 1 – Electrical properties .17
Table 2 – Nominal thickness and tolerance of metal-clad laminate .21
Table 3 – Bow and twist requirements.23
Table 4 – Pull-off and peel strength requirements .25
Table 5 – Dimensional stability .27
Table 6 – Size tolerances for cut panels.27
Table 7 – Rectangularity of cut panels .29
Table 8 – Flexural strength requirements .31
Table 9 – Flammability requirements.31
Table 10– Water absorption requirements.33
Table 11 – Measling requirements .33
Table 12 – Glass transition temperature and cure factor requirements.33

– 6 – 61249-2-22 ¤ CEI:2005
COMMISSION ÉLECTROTECHNIQUE INTERNATIONALE
___________
MATÉRIAUX POUR CIRCUITS IMPRIMÉS
ET AUTRES STRUCTURES D’INTERCONNEXION –
Partie 2-22: Matériaux de base renforcés, plaqués et non plaqués –
Feuilles stratifiées en tissu de verre de type E époxyde
non halogéné modifié, d’inflammabilité définie
(essai de combustion verticale), plaquées cuivre
AVANT-PROPOS
1) La Commission Electrotechnique Internationale (CEI) est une organisation mondiale de normalisation
composée de l'ensemble des comités électrotechniques nationaux (Comités nationaux de la CEI). La CEI a
pour objet de favoriser la coopération internationale pour toutes les questions de normalisation dans les
domaines de l'électricité et de l'électronique. A cet effet, la CEI – entre autres activités – publie des Normes
internationales, des Spécifications techniques, des Rapports techniques, des Spécifications accessibles au
public (PAS) et des Guides (ci-après dénommés "Publication(s) de la CEI"). Leur élaboration est confiée à des
comités d'études, aux travaux desquels tout Comité national intéressé par le sujet traité peut participer. Les
organisations internationales, gouvernementales et non gouvernementales, en liaison avec la CEI, participent
également aux travaux. La CEI collabore étroitement avec l'Organisation Internationale de Normalisation (ISO),
selon des conditions fixées par accord entre les deux organisations.
2) Les décisions ou accords officiels de la CEI concernant les questions techniques représentent, dans la mesure
du possible, un accord international sur les sujets étudiés, étant donné que les Comités nationaux de la CEI
intéressés sont représentés dans chaque comité d’études.
3) Les Publications de la CEI se présentent sous la forme de recommandations internationales et sont agréées
comme telles par les Comités nationaux de la CEI. Tous les efforts raisonnables sont entrepris afin que la CEI
s'assure de l'exactitude du contenu technique de ses publications; la CEI ne peut pas être tenue responsable
de l'éventuelle mauvaise utilisation ou interprétation qui en est faite par un quelconque utilisateur final.
4) Dans le but d'encourager l'uniformité internationale, les Comités nationaux de la CEI s'engagent, dans toute la
mesure possible, à appliquer de façon transparente les Publications de la CEI dans leurs publications
nationales et régionales. Toutes divergences entre toutes Publications de la CEI et toutes publications
nationales ou régionales correspondantes doivent être indiquées en termes clairs dans ces dernières.
5) La CEI n’a prévu aucune procédure de marquage valant indication d’approbation et n'engage pas sa
responsabilité pour les équipements déclarés conformes à une de ses Publications.
6) Tous les utilisateurs doivent s'assurer qu'ils sont en possession de la dernière édition de cette publication.
7) Aucune responsabilité ne doit être imputée à la CEI, à ses administrateurs, employés, auxiliaires ou
mandataires, y compris ses experts particuliers et les membres de ses comités d'études et des Comités
nationaux de la CEI, pour tout préjudice causé en cas de dommages corporels et matériels, ou de tout autre
dommage de quelque nature que ce soit, directe ou indirecte, ou pour supporter les coûts (y compris les frais
de justice) et les dépenses découlant de la publication ou de l'utilisation de cette Publication de la CEI ou de
toute autre Publication de la CEI, ou au crédit qui lui est accordé.
8) L'attention est attirée sur les références normatives citées dans cette publication. L'utilisation de publications
référencées est obligatoire pour une application correcte de la présente publication.
9) L’attention est attirée sur le fait que certains des éléments de la présente Publication de la CEI peuvent faire
l’objet de droits de propriété intellectuelle ou de droits analogues. La CEI ne saurait être tenue pour
responsable de ne pas avoir identifié de tels droits de propriété et de ne pas avoir signalé leur existence.
La Norme internationale CEI 61249-2-22 a été établie par le comité d'études 91 de la CEI:
Techniques d'assemblage des composants électroniques.
Le texte de cette norme est issu des documents suivants:
FDIS Rapport de vote
91/494/FDIS 91/504/RVD
Le rapport de vote indiqué dans le tableau ci-dessus donne toute information sur le vote
ayant abouti à l'approbation de cette norme.
Cette publication a été rédigée selon les Directives ISO/CEI, Partie 2.

61249-2-22¤ IEC:2005 – 7 –
INTERNATIONAL ELECTROTECHNICAL COMMISSION
___________
MATERIALS FOR PRINTED BOARDS
AND OTHER INTERCONNECTING STRUCTURES –
Part 2-22: Reinforced base materials clad and unclad –
Modified non-halogenated epoxide woven E-glass laminated sheets
of defined flammability (vertical burning test), copper-clad
FOREWORD
1) The International Electrotechnical Commission (IEC) is a worldwide organization for standardization comprising
all national electrotechnical committees (IEC National Committees). The object of IEC is to promote
international co-operation on all questions concerning standardization in the electrical and electronic fields. To
this end and in addition to other activities, IEC publishes International Standards, Technical Specifications,
Technical Reports, Publicly Available Specifications (PAS) and Guides (hereafter referred to as “IEC
Publication(s)”). Their preparation is entrusted to technical committees; any IEC National Committee interested
in the subject dealt with may participate in this preparatory work. International, governmental and non-
governmental organizations liaising with the IEC also participate in this preparation. IEC collaborates closely
with the International Organization for Standardization (ISO) in accordance with conditions determined by
agreement between the two organizations.
2) The formal decisions or agreements of IEC on technical matters express, as nearly as possible, an
international consensus of opinion on the relevant subjects since each technical committee has representation
from all interested IEC National Committees.
3) IEC Publications have the form of recommendations for international use and are accepted by IEC National
Committees in that sense. While all reasonable efforts are made to ensure that the technical content of IEC
Publications is accurate, IEC cannot be held responsible for the way in which they are used or for any
misinterpretation by any end user.
4) In order to promote international uniformity, IEC National Committees undertake to apply IEC Publications
transparently to the maximum extent possible in their national and regional publications. Any divergence
between any IEC Publication and the corresponding national or regional publication shall be clearly indicated in
the latter.
5) IEC provides no marking procedure to indicate its approval and cannot be rendered responsible for any
equipment declared to be in conformity with an IEC Publication.
6) All users should ensure that they have the latest edition of this publication.
7) No liability shall attach to IEC or its directors, employees, servants or agents including individual experts and
members of its technical committees and IEC National Committees for any personal injury, property damage or
other damage of any nature whatsoever, whether direct or indirect, or for costs (including legal fees) and
expenses arising out of the publication, use of, or reliance upon, this IEC Publication or any other IEC
Publications.
8) Attention is drawn to the Normative references cited in this publication. Use of the referenced publications is
indispensable for the correct application of this publication.
9) Attention is drawn to the possibility that some of the elements of this IEC Publication may be the subject of
patent rights. IEC shall not be held responsible for identifying any or all such patent rights.
International Standard IEC 61249-2-22 has been prepared by IEC technical committee 91:
Electronics assembly technology.
The text of this standard is based on the following documents:
FDIS Report on voting
91/494/FDIS 91/504/RVD
Full information on the voting for the approval of this standard can be found in the report on
voting indicated in the above table.
This publication has been drafted in accordance with the ISO/IEC Directives, Part 2.

– 8 – 61249-2-22 ¤ CEI:2005
La CEI 61249-2 comprend les parties suivantes, sous le titre général Matériaux pour circuits
imprimés et autres structures d’interconnexion – Partie 2: Matériaux de base renforcés plaqués et
non plaqués:
Partie 2-1: Feuilles stratifiées renforcées de papier cellulose phénolique, de qualité
économique, plaquées cuivre
Partie 2-2: Feuilles stratifiées renforcées de papier cellulose phénolique, de haute qualité
électrique, plaquées cuivre
Partie 2-4: Feuilles stratifiées en fibres de verre non tissées/tissées polyester,
d'inflammabilité définie (essai de combustion verticale ), plaquées cuivre
Partie 2-5: Feuilles stratifiées avec couches centrales renforcées en papier cellulose
époxyde bromé et couches superficielles renforcées en tissu de verre de type
époxyde, d’inflammabilité définie (essai de combustion verticale) plaquées
cuivre
Partie 2-6: Feuilles stratifiées renforcées en verre de type E époxyde bromé tissé/non
tissé, d'inflammabilité définie (essai de combustion verticale), plaquées cuivre
Partie 2-7: Feuille stratifiée tissée de verre E avec la résine époxyde, d’inflammabilité
définie (essai de combustion verticale), plaquée cuivre
Partie 2-8: Feuilles stratifiées renforcées en tissu de fibres de verre époxyde bromé
modifié, d'inflammabilité définie (essai de combustion verticale), plaquées
cuivre
Partie 2-9: Feuilles stratifiées renforcées en tissu de verre de type E époxyde, modifié ou
non, et bismaléimide/triazine, d'inflammabilité définie (essai de combustion
verticale), plaquées cuivre
Partie 2-10: Feuilles stratifiées renforcées en tissu de verre de type E ester de cyanate,
époxyde bromé, modifié ou non, d’inflammabilité définie (essai de combustion
verticale) plaquées cuivre,
Partie 2-11: Feuilles stratifiées renforcées en polyimide et tissu de verre de type E
époxyde bromé modifié ou non modifié, plaquée cuivre, d’inflammabilité
définie (essai de combustion verticale) plaquées cuivre
Partie 2-12: Stratifié à base d'aramide non tissé collé avec de la résine époxyde, recouvert
de cuivre, d'inflammabilité définie
Partie 2-13: Stratifié à base d'aramide non tissé collé avec de la résine cyanate ester,
recouvert de cuivre, d'inflammabilité définie
Partie 2-18: Feuille stratifiée renforcée de fibres de verre non tissées polyester,
d'inflammabilité définie (essai de combustion verticale ), plaquée cuivre
Partie 2-19: Feuilles multicouches de fibre de verre linéaire cohérente avec résine époxyde
pour hautes températures, d'inflammabilité définie (essai d'inflammabilité
verticale), plaquées cuivre
Partie 2-21: Feuilles stratifiées en tissu de verre de type E époxyde non halogéné,
d’inflammabilité définie (essai de combustion verticale), plaquées cuivre
Partie 2-22: Feuilles stratifiées en tissu de verre de type E époxyde non halogéné modifié,
d’inflammabilité définie (essai de combustion verticale), plaquées cuivre
Partie 2-23: Feuilles stratifiées renforcées de papier cellulose phénolique non halogéné, de
qualité économique, plaquées cuivre
Partie 2-26: Feuilles stratifiées renforcées en tissu de verre de type E époxyde
tissée/non tissée, non halogéné, d'inflammabilité définie, plaquées cuivre

61249-2-22¤ IEC:2005 – 9 –
IEC 61249-2 consists of the following parts, under the general title Materials for printed
boards and other interconnecting structures – Part 2: Reinforced base materials, clad and
unclad:
Part 2-1: Phenolic cellulose paper reinforced laminated sheets, economic grade, copper
clad
Part 2-2: Phenolic cellulose paper reinforced laminated sheets, high electrical grade,
copper-clad
Part 2-4: Polyester non-woven/woven fibreglass laminated sheets of defined flammability
(vertical burning test), copper-clad
Part 2-5: Brominated epoxide cellulose paper reinforced core/woven E-glass reinforced
surfaces laminate sheets of defined flammability (vertical burning test), copper-
clad
Part 2-6: Brominated epoxide non-woven/woven, E-glass reinforced laminated sheets of
defined flammability (vertical burning test), copper-clad
Part 2-7: Epoxide woven E-glass laminated sheet of defined flammability (vertical burning
test), copper-clad
Part 2-8: Modified brominated epoxide woven fibreglass reinforced laminated sheets of
defined flammability (vertical burning test), copper-clad
Part 2-9: Bismaleimide/triazine, modified epoxide or unmodified, woven E-glass reinforced
laminated sheets of defined flammability (vertical burning test), copper-clad
Part 2-10: Cyanate ester, brominated epoxide, modified or unmodified, woven E-glass
reinforced laminated sheets of defined flammability (vertical burning test), copper-
clad
Part 2-11: Polyimide, brominated epoxide modified or unmodified, woven E-glass reinforced
laminated sheets of defined flammability (vertical burning test), copper-clad
Part 2-12: Epoxide non-woven aramid laminate of defined flammability, copper-clad
Part 2-13: Cyanate ester non-woven aramid laminate of defined flammability, copper-clad
Part 2-18: Polyester non-woven fibreglass reinforced laminated sheet of defined flammability
(vertical burning test), copper-clad
Part 2-19: Epoxide cross-plied linear fibreglass-reinforced laminated sheets of defined flam-
mability (vertical burning test), copper-clad
Part 2-21: Non-halogenated epoxide woven E-glass reinforced laminated sheets of defined
flammability (vertical burning test), copper-clad
Part 2-22: Modified non-halogenated epoxide woven E-glass laminated sheets of defined
flammability (vertical burning test), copper-clad
Part 2-23: Non-halogenated phenolic, cellulose paper reinforced laminated sheets, economic
grade, copper-clad
Part 2-26: Non-halogenated epoxide, nonwoven/woven E-glass reinforced laminated sheets
of defined flammability (vertical burning test), copper-clad

– 10 – 61249-2-22 ¤ CEI:2005
Le comité a décidé que le contenu de cette publication ne sera pas modifié avant la date de
maintenance indiquée sur le site web de la CEI sous «http://webstore.iec.ch» dans les
données relatives à la publication recherchée. A cette date, la publication sera
• reconduite;
• supprimée;
• remplacée par une édition révisée, ou
• amendée.
61249-2-22¤ IEC:2005 – 11 –
The committee has decided that the contents of this publication will remain unchanged until
the maintenance result date indicated on the IEC web site under "http://webstore.iec.ch" in
the data related to the specific publication. At this date, the publication will be
• reconfirmed;
• withdrawn;
• replaced by a revised edition, or
• amended.
– 12 – 61249-2-22 ¤ CEI:2005
MATÉRIAUX POUR CIRCUITS IMPRIMÉS
ET AUTRES STRUCTURES D’INTERCONNEXION –
Partie 2-22: Matériaux de base renforcés, plaqués et non plaqués –
Feuilles stratifiées en tissu de verre de type E époxyde
non halogéné modifié, d’inflammabilité définie
(essai de combustion verticale) plaquée cuivre
1 Domaine d'application
La présente partie de la CEI 61249 donne les exigences concernant les propriétés des
feuilles stratifiées en tissu de verre de type E époxyde non halogéné modifié ayant une
épaisseur comprise entre 0,05 mm et 3,2 mm, d’inflammabilité définie (essai de combustion
verticale) plaquées cuivre. Les caractéristiques d’inflammabilité sont obtenues en utilisant
des mélanges à base de phosphore et/ou des ignifuges en hydroxyde d’aluminium contenus
dans la structure polymère. La température de transition vitreuse est définie entre 150 °C et
190 °C.
Certaines exigences de propriétés peuvent comprendre plusieurs classes de performance. Il
y a lieu de spécifier la classe désirée sur l'ordre d'achat, faute de quoi c’est la classe par
défaut du matériau qui sera fournie.
2 Références normatives
Les documents de référence suivants sont indispensables pour l'application du présent
document. Pour les références datées, seule l'édition citée s'applique. Pour les références
non datées, la dernière édition du document de référence s'applique (y compris les éventuels
amendements).
CEI 60194:1999, Conception, fabrication et assemblage des cartes imprimées - Termes et
définitions
CEI 61189-2:1997, Méthodes d’essai pour les matériaux électriques, les cartes imprimées et
autres structures d’interconnexion et ensembles – Partie 2: Méthodes d’essai pour structures
d’interconnexion
CEI 61249-5-1:1995, Matériaux pour structures d’interconnexion – Partie 5: Collection de
spécifications intermédiaires pour feuilles et films conducteurs avec ou sans revêtement –
Section 1: Feuilles de cuivre (pour la fabrication des matériaux de base plaqués cuivre)
ISO 9000:2000, Systèmes de management de la qualité – Principes essentiels et vocabulaire
ISO 11014-1:1994, Fiches de données de sécurité pour les produits chimiques – Partie 1:
Contenu et plan type
ISO 14001:1996, Systèmes de management environnemental – Spécification et lignes directrices
pour son utilisation
61249-2-22¤ IEC:2005 – 13 –
MATERIALS FOR PRINTED BOARDS
AND OTHER INTERCONNECTING STRUCTURES –
Part 2-22: Reinforced base materials clad and unclad –
Modified non-halogenated epoxide woven E-glass laminated sheets
of defined flammability (vertical burning test), copper-clad
1 Scope
This part of IEC 61249 gives requirements for properties of modified non-halogenated
epoxide woven E-glass laminated sheet 0,05 mm up to 3,2 mm, of defined flammability
(vertical burning test), copper-clad. The flammability rating is achieved through the use of
phosphorus compounds and/or aluminium hydroxide fire retardants contained as part of the
polymeric structure. The glass transition temperature is defined to be between 150 °C to
190 °C.
Some property requirements may have several classes of performance. The class desired
should be specified on the purchase order, otherwise the default class of material will be
supplied.
2 Normative references
The following referenced documents are indispensable for the application of this document.
For dated references, only the edition cited applies. For undated references, the latest edition
of the referenced document (including any amendments) applies.
IEC 60194:1999, Printed board design, manufacture and assembly – Terms and definitions
IEC 61189-2:1997,Test methods for electrical materials, printed boards and interconnection
structures and assemblies – Part 2: Test method for materials for interconnection structures
IEC 61249-5-1:1995, Materials for interconnection structures – Part 5: Sectional specification
set for conductive foils and films with and without coatings – Section 1: Copper foils (for the
manufacture of copper-clad base materials)
ISO 9000:2000, Quality management systems – Fundamentals and vocabulary
ISO 11014-1:1994, Safety data sheet for chemical products – Part 1: Content and order
of sections
ISO 14001:1996, Environmental management systems – Specification with guidance for use

– 14 – 61249-2-22 ¤ CEI:2005
3 Matériaux et construction
La feuille est composée d’une base isolante sur laquelle est collée une feuille de métal sur une
face ou sur les deux. Se réfèrer à la CEI 60194 pour les termes et définitions.
3.1 Résine isolante
Stratifié de verre tissée de type E époxyde non halogéné et époxyde modifié non halogéné
majoritairement bifonctionnel avec une température de transition vitreuse de 150 °C à
190 °C.
Au total, le maximum d'halogènes contenu dans la résine et la matrice de renforcement est
–6 –6 –6
de 1 500 × 10 avec un maximum de 900 × 10 de chlorine et un maximum de 900 × 10
de bromine.
Il est permis d’ajouter des agents de contraste pour renforcer les traitements tel que le
contrôle optique automatisé (AOI – automated optical inspection).
Sa résistance à la flamme est définie par rapport aux exigences d’inflammabilité du 7.3.
3.2 Feuille de métal
Cuivre comme spécifié dans la CEI 61249-5-1. Les feuilles préférentielles sont celles qui sont
déposées par électrolyse avec une ductilité définie.
3.3 Renforcement
Verre tissée de type E comme spécifié dans la CEI 61249-6-3.
4 Marquage interne
Non spécifié.
5 Propriétés électriques
Les exigences pour les propriétés électriques sont données dans le Tableau 1.

61249-2-22¤ IEC:2005 – 15 –
3 Materials and construction
The sheet consists of an insulating base with metal-foil bonded to one side or both. Refer to
IEC 60194 for terms and definitions.
3.1 Resin system
Majority di-functional non-halogenated epoxide, modified non-halogenated epoxide, woven E-
glass laminate with a glass transition temperature of 150 °C to 190 °C.
–6
The maximum total halogens contained in the resin plus reinforcement matrix is 1 500 × 10
–6 –6
with a maximum chlorine of 900 × 10 and a maximum bromine of 900 × 10 .
Contrast agents may be added to enhance processing such as automated optical inspection
(AOI).
Its flame resistance is defined in terms of the flammability requirements of 7.3.
3.2 Metal foil
Copper as specified in IEC 61249-5-1.The preferred foils are electro-deposited of defined
ductility.
3.3 Reinforcement
Woven E-glass as specified in IEC 61249-6-3.
4 Internal marking
Not specified.
5 Electrical properties
The electrical property requirements are shown in Table 1.

– 16 – 61249-2-22 ¤ CEI:2005
Tableau 1 – Propriétés électriques
Méthode d’essai
Propriété Exigence
(CEI 61189-2)
Résistance de la feuille 2E12 Comme spécifié dans la
CEI 61249-5-1
Résistance superficielle après chaleur humide dans la 2E03
≥10 000 MΩ
chambre climatique (facultatif)
Résistance superficielle après chaleur humide et reprise 2E03
≥50 000 MΩ
Résistivité transversale après chaleur humide dans la 2E04
≥5 000 MΩm
chambre climatique (facultatif)
Résistivité transversale après chaleur humide et reprise 2E04
≥10 000 MΩm
Permittivité relative après chaleur humide et reprise 2E10 ≤5,4
(1 MHz)
Facteur de dissipation après chaleur humide et reprise 2E10
≤0,035
(1 MHz)
Rigidité électrique (seulement pour les matériaux 2E11
≥30 kV/mm
d'épaisseur <0,5 mm)
Résistance de l’arc 2E14
≥60 s
Claquage diélectrique (seulement pour les matériaux 2E15
≥40 kV
d'épaisseur >0,5 mm)
Résistance superficielle à 125 °C 2E07
≥ 10 000 MΩ
Résistivité transversale à 125 °C 2E07 ≥ 10 000 MΩm
6 Propriétés non électriques de la feuille stratifiée plaquée cuivre
6.1 Aspect de la feuille plaquée cuivre
La face plaquée cuivre doit être en grande partie exempte de défauts pouvant affecter
l’aptitude du matériau à son utilisation dans le but prévu.
Pour les défauts spécifiques suivants, les exigences données doivent s’appliquer lorsque le
contrôle est effectué conformément à la méthode 2M18 de la CEI 61189-2.
6.1.1 Empreintes (piqûres et marques de coup)
La taille d’une empreinte, généralement sa longueur, doit être déterminée et on doit lui
attribuer une valeur en points à utiliser pour mesurer la qualité.
Taille Valeur en points pour
mm chaque empreinte
0,13 – 0,25 1
0,26 – 0,50 2
0,51 – 0,75 4
0,76 – 1,00 7
Supérieure à 1,00 30
61249-2-22¤ IEC:2005 – 17 –
Table 1 – Electrical properties
Test method
Property Requirement
(IEC 61189-2)
Resistance of foil 2E12 As specified in IEC 61249-5-1
Surface resistance after damp heat while in the humidity 2E03
≥10 000 MΩ
chamber (optional)
Surface resistance after damp heat and recovery 2E03
≥50 000 MΩ
Volume resistivity after damp heat while in the humidity 2E04
≥5 000 MΩm
chamber (optional)
Volume resistivity after damp heat and recovery 2E04
≥10 000 MΩm
Relative permittivity after damp heat and recovery 2E10
≤5,4
(1 MHz)
Dissipation factor after damp heat and recovery 2E10
≤0,035
(1 MHz)
Electric strength (only for material thickness less than 2E11
≥30 kV/mm
0,5 mm )
Arc resistance 2E14
≥60 s
Dielectric breakdown (only for material thicknesses 2E15
≥40 kV
≥ 0,5 mm)
Surface resistance at 125 °C 2E07 ≥10 000 MΩ
Volume resistivity at 125 °C 2E07
≥10 000 MΩm
6 Non-electrical properties of the copper-clad laminate
6.1 Appearance of the copper-clad sheet
The copper-clad face shall be substantially free from defects that may have an impact on the
material´s fitness for use for the intended purpose.
For the following specific defects the requirements given shall apply when inspection is made
in accordance with IEC 61189-2 method 2M18.
6.1.1 Indentations (pits and dents)
The size of an indentation, usually the length, shall be determined and given a point value to
be used as measure of the quality.
Size Point value for
mm each indentation
0,13 – 0,25 1
0,26 – 0,50 2
0,51 – 0,75 4
0,76 – 1,00 7
Over 1,00 30
– 18 – 61249-2-22 ¤ CEI:2005
Le nombre total de points pour toute zone de 300 m
...