EN ISO 14373:2015
(Main)Resistance welding - Procedure for spot welding of uncoated and coated low carbon steels (ISO 14373:2015)
Resistance welding - Procedure for spot welding of uncoated and coated low carbon steels (ISO 14373:2015)
ISO 14373:2015 specifies requirements for resistance spot welding in the fabrication of assemblies of uncoated and metallic coated low carbon steel, comprising two or three sheets of metal, where the maximum single sheet thickness of components to be welded is within the range 0,4 mm to 3 mm, for the following materials: uncoated steels; hot-dip zinc or iron-zinc alloy (galvannealed) coated steel; electrolytic zinc, zinc-iron, or zinc-nickel coated steel; aluminium coated steel; zinc-aluminium coated steel. It is applicable to welding of sheets of the same or dissimilar thickness, where the thickness ratio is less than or equal to 3:1. It applies to the welding of three thicknesses, where the total thickness is less than or equal to 9 mm.
Welding with the following types of equipment is within its scope: pedestal welding equipment; gun welders; automatic welding equipment where the components are fed by robots or automatic feeding equipment; multi welders; robotic welders. It also gives information, for guidance only, on appropriate welding equipment on spot welding conditions.
The welding of organic coated or primer coated steels is not within its scope.
Widerstandsschweißen - Verfahren zum Punktschweißen von niedriglegierten Stählen mit oder ohne metallischem Überzug (ISO 14373:2015)
Diese Internationale Norm legt die Anforderungen an das Widerstandspunktschweißen an Bauteilen aus niedriglegiertem Stahl mit oder ohne metallischem Überzug fest, die aus zwei oder drei verschiedenen Blechdicken bestehen können, wobei die maximale Dicke eines Einzelbleches der zu schweißenden Bauteile im Bereich von 0,4 mm bis 3 mm aus folgenden Werkstoffen liegt:
- Stahl ohne Überzug;
- Stahl mit Feuerverzinkung oder Fe Zn Legierung (Galvannealed);
- Stahl mit elektrolytisch aufgebrachtem Zn oder Zn Ni Überzug;
- Stahl mit Aluminiumüberzug;
- Stahl mit Zn Al Legierungsüberzug.
Diese Internationale Norm gilt für das Schweißen von Blechen oder Platten gleicher oder unterschiedlicher Dicke mit einem Dickenverhältnis von nicht mehr als 3:1. Sie gilt auch für die Dreiblechschweißung mit einer Gesamtdicke von bis zu 9 mm.
Die folgenden Schweißeinrichtungen liegen im Anwendungsbereich dieser Internationalen Norm:
a) Ständerschweißmaschinen;
b) Schweißpistolen;
c) automatische Schweißeinrichtungen, bei denen die Bauteile durch Roboter oder automatische Zuführungen zugeführt werden;
d) Vielpunktschweißanlagen;
e) Roboterschweißanlagen.
Anhang A enthält Angaben über geeignete Schweißeinrichtungen und Anhang B informiert über die Punktschweißbedingungen. Diese Informationen dienen jedoch nur als Anhalt. In Abhängigkeit von den Fertigungsbedingungen, der Schweißeinrichtung, den Eigenschaften des Sekundärkreises, dem Elektrodenwerkstoff und der Elektrodengeometrie sind gegebenenfalls Anpassungen erforderlich. Falls eine entsprechende Anwendungsnorm hierzu existiert, können weiterführende Informationen daraus entnommen werden.
Das Schweißen von organisch oder mit Primern beschichteten Stählen liegt nicht im Anwendungsbereich dieser Internationalen Norm.
Soudage par résistance - Mode opératoire pour le soudage par points des aciers à bas carbone revêtus et non revêtus (ISO 14373:2015)
L'ISO 14373:2015 spécifie les exigences relatives au soudage par résistance par points pour la fabrication d'assemblages en acier à bas carbone revêtu ou non revêtu avec deux ou trois épaisseurs de métal, l'épaisseur maximale d'une tôle simple constituant les pièces à souder étant comprise entre 0,4 mm et 3 mm pour les matériaux suivants: aciers non revêtus; acier galvanisé à chaud ou revêtu d'un alliage de fer-zinc (recuit par galvanisation); acier avec revêtement électrolytique de zinc, zinc-fer ou zinc-nickel; acier revêtu d'aluminium; acier revêtu de zinc-aluminium. Elle s'applique au soudage de tôles présentant une épaisseur similaire ou différente, et dont le rapport entre les épaisseurs est inférieur ou égal à 3:1. Elle s'applique au soudage de trois épaisseurs, dont l'épaisseur totale est inférieure ou égale à 9 mm.
Elle concerne le soudage réalisé avec les types de matériels suivants: machine de soudage avec commande au pied; machines à souder mobiles (au pistolet); matériel de soudage automatique avec lequel les composants sont mis en place par des robots ou des appareils d'alimentation automatique; machines à souder multi-points; robots de soudage. Elle donne des informations sur le matériel de soudage approprié et sur les conditions de soudage par points. Ces renseignements ne sont fournis qu'à titre informatif.
Elle ne couvre pas le soudage d'aciers revêtus de produit organique ou d'apprêt (primaire).
Uporovno varjenje - Postopek točkovnega varjenja neprevlečenih in prevlečenih maloogljičnih jekel (ISO 14373:2015)
General Information
Relations
Standards Content (Sample)
SLOVENSKI STANDARD
01-junij-2015
1DGRPHãþD
SIST EN ISO 14373:2007
8SRURYQRYDUMHQMH3RVWRSHNWRþNRYQHJDYDUMHQMDQHSUHYOHþHQLKLQSUHYOHþHQLK
PDORRJOMLþQLKMHNHO ,62
Resistance welding - Procedure for spot welding of uncoated and coated low carbon
steels (ISO 14373:2015)
Widerstandsschweißen - Verfahren zum Punktschweißen von niedriglegierten Stählen
mit oder ohne metallischem Überzug (ISO 14373:2015)
Soudage par résistance - Mode opératoire pour le soudage par points des aciers à bas
carbone revêtus et non revêtus (ISO 14373:2015)
Ta slovenski standard je istoveten z: EN ISO 14373:2015
ICS:
25.160.10 Varilni postopki in varjenje Welding processes
2003-01.Slovenski inštitut za standardizacijo. Razmnoževanje celote ali delov tega standarda ni dovoljeno.
EUROPEAN STANDARD
EN ISO 14373
NORME EUROPÉENNE
EUROPÄISCHE NORM
March 2015
ICS 25.160.10 Supersedes EN ISO 14373:2007
English Version
Resistance welding - Procedure for spot welding of uncoated
and coated low carbon steels (ISO 14373:2015)
Soudage par résistance - Mode opératoire pour le soudage Widerstandsschweißen - Verfahren zum Punktschweißen
par points des aciers à bas carbone revêtus et non revêtus von niedriglegierten Stählen mit oder ohne metallischem
(ISO 14373:2015) Überzug (ISO 14373:2015)
This European Standard was approved by CEN on 3 January 2015.
CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European
Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national
standards may be obtained on application to the CEN-CENELEC Management Centre or to any CEN member.
This European Standard exists in three official versions (English, French, German). A version in any other language made by translation
under the responsibility of a CEN member into its own language and notified to the CEN-CENELEC Management Centre has the same
status as the official versions.
CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia,
Finland, Former Yugoslav Republic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania,
Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and United
Kingdom.
EUROPEAN COMMITTEE FOR STANDARDIZATION
COMITÉ EUROPÉEN DE NORMALISATION
EUROPÄISCHES KOMITEE FÜR NORMUNG
CEN-CENELEC Management Centre: Avenue Marnix 17, B-1000 Brussels
© 2015 CEN All rights of exploitation in any form and by any means reserved Ref. No. EN ISO 14373:2015 E
worldwide for CEN national Members.
Contents Page
Foreword .3
Foreword
This document (EN ISO 14373:2015) has been prepared by IIW “International Institute of Welding“ in
collaboration with Technical Committee CEN/TC 121 “Welding” the secretariat of which is held by DIN.
This European Standard shall be given the status of a national standard, either by publication of an identical
text or by endorsement, at the latest by September 2015, and conflicting national standards shall be
withdrawn at the latest by September 2015.
Attention is drawn to the possibility that some of the elements of this document may be the subject of patent
rights. CEN [and/or CENELEC] shall not be held responsible for identifying any or all such patent rights.
This document supersedes EN ISO 14373:2007.
According to the CEN-CENELEC Internal Regulations, the national standards organizations of the following
countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech
Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Macedonia, France, Germany, Greece,
Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal,
Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and the United Kingdom.
Endorsement notice
The text of ISO 14373:2015 has been approved by CEN as EN ISO 14373:2015 without any modification.
INTERNATIONAL ISO
STANDARD 14373
Second edition
2015-03-15
Resistance welding — Procedure for
spot welding of uncoated and coated
low carbon steels
Soudage par résistance — Mode opératoire pour le soudage par
points des aciers à bas carbone revêtus et non revêtus
Reference number
ISO 14373:2015(E)
©
ISO 2015
ISO 14373:2015(E)
© ISO 2015
All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized otherwise in any form
or by any means, electronic or mechanical, including photocopying, or posting on the internet or an intranet, without prior
written permission. Permission can be requested from either ISO at the address below or ISO’s member body in the country of
the requester.
ISO copyright office
Case postale 56 • CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax + 41 22 749 09 47
E-mail copyright@iso.org
Web www.iso.org
Published in Switzerland
ii © ISO 2015 – All rights reserved
ISO 14373:2015(E)
Contents Page
Foreword .iv
Introduction .v
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 2
4 Symbols and abbreviated terms . 2
5 Materials . 3
5.1 Form . 3
5.2 Steel grades . 3
6 Surface conditions . 3
7 Edge conditions, form of component, and weld spacing . 3
8 Electrodes . 3
8.1 Materials . 3
8.2 Dimensions . 3
8.3 Cooling of electrodes . 5
9 Weld assessment . 6
9.1 General . 6
9.2 Weldability tests . 6
9.3 Production tests . 6
9.4 Frequency of testing . 6
10 Weld quality requirements . 7
10.1 Weld diameter . 7
10.2 Weld penetration and indentation . 7
10.3 Failure description of welds . 7
10.4 Tensile shear strength . 7
10.5 Weld appearance . 8
10.5.1 Surface condition . 8
10.5.2 Distortion . 8
11 Multi-weld arrays . 9
Annex A (informative) Recommendations for spot welding equipment .11
Annex B (informative) Typical spot welding conditions .12
Annex C (informative) Partial list of steel types applicable to this International Standard .14
Bibliography .15
ISO 14373:2015(E)
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out
through ISO technical committees. Each member body interested in a subject for which a technical
committee has been established has the right to be represented on that committee. International
organizations, governmental and non-governmental, in liaison with ISO, also take part in the work.
ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of
electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are
described in the ISO/IEC Directives, Part 1. In particular the different approval criteria needed for the
different types of ISO documents should be noted. This document was drafted in accordance with the
editorial rules of the ISO/IEC Directives, Part 2 (see www.iso.org/directives).
Attention is drawn to the possibility that some of the elements of this document may be the subject of
patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of
any patent rights identified during the development of the document will be in the Introduction and/or
on the ISO list of patent declarations received (see www.iso.org/patents).
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation on the meaning of ISO specific terms and expressions related to conformity
assessment, as well as information about ISO’s adherence to the WTO principles in the Technical Barriers
to Trade (TBT) see the following URL: Foreword - Supplementary information
ISO 14373 was prepared by IIW, International Institute of Welding, Commission III. Requests for official
interpretations of any aspect of this International Standard should be directed to the ISO Central
Secretariat, who will for
...
2003-01.Slovenski inštitut za standardizacijo. Razmnoževanje celote ali delov tega standarda ni dovoljeno.Widerstandsschweißen - Verfahren zum Punktschweißen von niedriglegierten Stählen mit oder ohne metallischem Überzug (ISO/FDIS 14373:2014)Soudage par résistance - Mode opératoire pour le soudage par points des aciers à bas carbone revêtus et non revêtus (ISO/FDIS 14373:2014)Resistance welding - Procedure for spot welding of uncoated and coated low carbon steels (ISO/FDIS 14373:2014)25.160.10Varilni postopki in varjenjeWelding processesICS:Ta slovenski standard je istoveten z:FprEN ISO 14373kSIST FprEN ISO 14373:2014de01-december-2014kSIST FprEN ISO 14373:2014SLOVENSKI
STANDARD
kSIST FprEN ISO 14373:2014
EUROPÄISCHE NORM EUROPEAN STANDARD NORME EUROPÉENNE
SCHLUSS-ENTWURF
FprEN ISO 14373
Oktober 2014 ICS 25.160.10 Vorgesehen als Ersatz für EN ISO 14373:2007Deutsche Fassung
Widerstandsschweißen - Verfahren zum Punktschweißen von niedriglegierten Stählen mit oder ohne metallischem Überzug (ISO/FDIS 14373:2014)
Resistance welding - Procedure for spot welding of uncoated and coated low carbon steels (ISO/FDIS 14373:2014)
Soudage par résistance - Mode opératoire pour le soudage par points des aciers à bas carbone revêtus et non revêtus (ISO/FDIS 14373:2014) Dieser Europäische Norm-Entwurf wird den CEN-Mitgliedern zur parallelen formellen Abstimmung vorgelegt. Er wurde vom Technischen Komitee CEN/TC 121 erstellt.
Wenn aus diesem Norm-Entwurf eine Europäische Norm wird, sind die CEN-Mitglieder gehalten, die CEN-Geschäftsordnung zu erfüllen, in der die Bedingungen festgelegt sind, unter denen dieser Europäischen Norm ohne jede Änderung der Status einer nationalen Norm zu geben ist.
Dieser Europäische Norm-Entwurf wurde vom CEN in drei offiziellen Fassungen (Deutsch, Englisch, Französisch) erstellt. Eine Fassung in einer anderen Sprache, die von einem CEN-Mitglied in eigener Verantwortung durch Übersetzung in seine Landessprache gemacht und dem Management-Zentrum des CEN-CENELEC mitgeteilt worden ist, hat den gleichen Status wie die offiziellen Fassungen.
CEN-Mitglieder sind die nationalen Normungsinstitute von Belgien, Bulgarien, Dänemark, Deutschland, der ehemaligen jugoslawischen Republik Mazedonien, Estland, Finnland, Frankreich, Griechenland, Irland, Island, Italien, Kroatien, Lettland, Litauen, Luxemburg, Malta, den Niederlanden, Norwegen, Österreich, Polen, Portugal, Rumänien, Schweden, der Schweiz, der Slowakei, Slowenien, Spanien, der Tschechischen Republik, der Türkei, Ungarn, dem Vereinigten Königreich und Zypern.
Die Empfänger dieses Norm-Entwurfs werden gebeten, mit ihren Kommentaren jegliche relevante Patentrechte, die sie kennen, mitzuteilen und unterstützende Dokumentationen zur Verfügung zu stellen.
Warnvermerk : Dieses Schriftstück hat noch nicht den Status einer Europäischen Norm. Es wird zur Prüfung und Stellungnahme vorgelegt. Es kann sich noch ohne Ankündigung ändern und darf nicht als Europäischen Norm in Bezug genommen werden.
EUROPÄISCHES KOMITEE FÜR NORMUNG EUROPEAN COMMITTEE FOR STANDARDIZATION
COMITÉ EUROPÉEN DE NORMALISATION
CEN-CENELEC Management-Zentrum:
Avenue Marnix 17,
B-1000 Brüssel © 2014 CEN Alle Rechte der Verwertung, gleich in welcher Form und in welchem Verfahren, sind weltweit den nationalen Mitgliedern von CEN vorbehalten.Ref. Nr. FprEN ISO 14373:2014 DkSIST FprEN ISO 14373:2014
FprEN ISO 14373:2014 (D) 2 Inhalt Seite Vorwort .3 Einleitung .4 1 Anwendungsbereich .5 2 Normative Verweisungen .5 3 Begriffe .6 4 Symbole und Abkürzungen .7 5 Werkstoff .7 5.1 Form .7 5.2 Stahlsorten .7 6 Oberflächenbeschaffenheit .7 7 Randabstand, Form der zu schweißenden Bauteile und Schweißpunktabstand .8 8 Elektroden .8 8.1 Werkstoffe .8 8.2 Abmessungen .8 8.3 Elektrodenkühlung . 11 9 Beurteilung der Schweißqualität . 11 9.1 Allgemeines . 11 9.2 Prüfverfahren zur Beurteilung der Schweißeignung . 12 9.3 Fertigungsprüfungen . 12 9.4 Prüfungshäufigkeit . 12 10 Anforderungen an die Schweißqualität . 13 10.1 Punktdurchmesser . 13 10.2 Einbrand und Elektrodeneindruck . 13 10.3 Fehlerbeschreibung der Schweißverbindung . 13 10.4 Scherzugfestigkeit . 13 10.5 Aussehen der Schweißverbindung . 14 10.5.1 Oberflächenbeschaffenheit . 14 10.5.2 Deformation . 14 11 Verbindungen mit mehreren Schweißpunkten . 15 Anhang A (informativ)
Empfehlungen für Punktschweißeinrichtungen . 17 Anhang B (informativ)
Typische Punktschweißbedingungen . 18 Anhang C (informativ)
Unvollständige Liste der Stahlsorten im Geltungsbereich dieser Internationalen Norm . 20 Anhang D (informativ)
Typische Brucharten und Definition der Punktdurchmesser . 21 Literaturhinweise . 23
kSIST FprEN ISO 14373:2014
FprEN ISO 14373:2014 (D) 3 Vorwort Dieses Dokument (FprEN ISO 14373:2014) wurde vom Technischen Komitee ISO/TC 44 „Welding and allied processes“ in Zusammenarbeit mit dem Technischen Komitee CEN/TC 121 „Schweißen“ erarbeitet, dessen Sekretariat vom DIN gehalten wird. Dieses Dokument ist derzeit zur parallelen formellen Abstimmung vorgelegt. Dieses Dokument wird EN ISO 14373:2007 ersetzen. Anerkennungsnotiz Der Text von ISO/FDIS 14373:2014 wurde vom CEN als FprEN ISO 14373:2014 ohne irgendeine Abänderung genehmigt.
kSIST FprEN ISO 14373:2014
FprEN ISO 14373:2014 (D) 4 Einleitung Diese Internationale Norm enthält keine Bilder mehr, in denen die Brucharten und die Verfahren für den Schlagscherzugversuch und den Schlagkopfzugversuch nach ISO 14329 dargestellt sind. Diese Internationale Norm wurde überarbeitet, um sie an ISO 17677-1 anzugleichen.
kSIST FprEN ISO 14373:2014
FprEN ISO 14373:2014 (D) 5 1 Anwendungsbereich Diese Internationale Norm legt die Anforderungen an das Widerstandspunktschweißen an Bauteilen aus niedriglegiertem Stahl mit oder ohne metallischem Überzug fest, die aus zwei oder drei verschiedenen Blechdicken bestehen können, wobei die maximale Dicke eines Einzelbleches der zu schweißenden Bauteile im Bereich von 0,4 mm bis 3 mm aus folgenden Werkstoffen liegt: Stahl ohne Überzug; Stahl mit Feuerverzinkung oder Fe-Zn-Legierung (Galvannealed); Stahl mit elektrolytisch aufgebrachtem Zn- oder Zn-Ni-Überzug; Stahl mit Aluminiumüberzug; Stahl mit Zn-Al-Legierungsüberzug. Diese Internationale Norm gilt für das Schweißen von Blechen oder Platten gleicher oder unterschiedlicher Dicke mit einem Dickenverhältnis von nicht mehr als 3:1. Sie gilt auch für die Dreiblechschweißung mit einer Gesamtdicke von bis zu 9 mm. Die folgenden Schweißeinrichtungen liegen im Anwendungsbereich dieser Internationalen Norm: a) Ständerschweißmaschinen; b) Schweißpistolen; c) automatische Schweißeinrichtungen, bei denen die Bauteile durch Roboter oder automatische Zuführungen zugeführt werden; d) Vielpunktschweißanlagen; e) Roboterschweißanlagen. Anhang A enthält Angaben über geeignete Schweißeinrichtungen und Anhang B informiert über die Punktschweißbedingungen. Diese Informationen dienen jedoch nur als Anhalt. In Abhängigkeit von den Fertigungsbedingungen, der Schweißeinrichtung, den Eigenschaften des Sekundärkreises, dem Elektrodenwerkstoff und der Elektrodengeometrie sind gegebenenfalls Anpassungen erforderlich. Falls eine entsprechende Anwendungsnorm hierzu existiert, können weiterführende Informationen daraus entnommen werden. Das Schweißen von organisch oder mit Primern beschichteten Stählen liegt nicht im Anwendungsbereich dieser Internationalen Norm. 2 Normative Verweisungen Die folgenden Dokumente, die in diesem Dokument teilweise oder als Ganzes zitiert werden, sind für die Anwendung dieses Dokuments erforderlich. Bei datierten Verweisungen gilt nur die in Bezug genommene Ausgabe. Bei undatierten Verweisungen gilt die letzte Ausgabe des in Bezug genommenen Dokuments (einschließlich aller Änderungen).
ISO 5182, Resistance welding — Materials for electrodes and ancillary equipment ISO 10447, Resistance welding — Peel and chisel testing of resistance spot and projection welds ISO 14270, Resistance welding — Specimen dimensions and procedure for mechanized peel testing resistance spot, seam and embossed projection welds kSIST FprEN ISO 14373:2014
FprEN ISO 14373:2014 (D) 6 ISO 15609-5, Specification and qualification of welding procedures for metallic materials — Welding procedure specification — Part 5: Resistance welding ISO 15614-12, Specification and qualification of welding procedures for metallic materials — Welding procedure test — Part 12: Spot, seam and projection welding ISO 17677-1, Resistance welding — Vocabulary — Part 1: Spot, projection and seam welding ISO 18278-1, Resistance welding — Weldability — Part 1: Assessment of weldability for resistance spot, seam and projection welding of metallic materials ISO 18272-2, Resistance welding — Weldability — Part 2: Alternative procedures for the assessment of sheet steels for spot welding 3 Begriffe Für die Anwendung dieses Dokuments gelten die Begriffe nach ISO 17677-1 und die folgenden Begriffe. 3.1 Kopfzugprüfung Prüfverfahren zur Bestimmung der von der Schweißverbindung unter Kopfzugbeanspruchung übertragbaren Kraft 3.2 Scherprüfung Scherzugprüfung Prüfverfahren zur Bestimmung der von der Schweißverbindung unter Scherbeanspruchung übertragbaren Kraft 3.3 Schweißlinse linsenförmige Zone einer Widerstandspunktschweißung, in der das Metall beider (aller) Bleche geschmolzen und wieder erstarrt ist 3.4 Punktabstand Mittenabstand zwischen zwei benachbarten Punktschweißungen 3.5 Randabstand Abstand vom Rand des Bauteils bis zur Mitte des Schweißpunktes kSIST FprEN ISO 14373:2014
FprEN ISO 14373:2014 (D) 7 4 Symbole und Abkürzungen Siehe Tabelle 1. Tabelle 1 — Symbole und Benennungen Symbol Benennung Einheit dw Punktdurchmesser (siehe ISO 17677-1) mm dc Haftzonendurchmesser mm de Durchmesser der Elektrodenarbeitsfläche mm dn Linsendurchmesser
mm t Blechdicke mm Ps Scherzugkraft der Schweißung kN Rm Zugfestigkeit des zu schweißenden Stahls MPa
5 Werkstoff 5.1 Form Der Stahl muss als flachgewalztes Material vorliegen, als Coil oder auf Maß geschnitten, und frei von schädlichen Fehlstellen sein. 5.2 Stahlsorten Anhang C enthält eine unvollständige Liste der Stahlsorten, die im Geltungsbereich dieser Internationalen Norm liegen. 6 Oberflächenbeschaffenheit Für das Schweißen müssen die Oberflächen der zu schweißenden Bauteile frei von Fett, Zunder, Rost, Farbe, Schmutz oder übermäßiger Rauheit sein. Warmgewalzter Stahl ohne Überzug muss gebeizt sein. Stähle mit Überzug können mit einer Passivierungsbehandlung durch Chromatierung bzw. Phosphatierung geliefert werden. Bei bestimmten Anwendungen können phosphatierte weiche Stähle zum Einsatz kommen. Diese Werkstoffe können punktgeschweißt werden, allerdings kann die Anpassung der in Anhang B genannten Richtwerte erforderlich sein. Allgemein kann gesagt werden, dass nur dünn phosphatierte Stähle für das Punktschweißen geeignet sind. ANMERKUNG Vor dem Schweißen darf der Stahl mit Primern, Rosthemmern und Ölen unter der Voraussetzung behandelt werden, dass die Schichtdicke gleichmäßig ist und erwiesenermaßen Schweißverbindungen mit gleich bleibender, der vorliegenden Internationalen Norm entsprechenden Qualität erzielt werden können. Der übermäßige Einsatz zusätzlich
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.