Standard Practice for Determining the Separation Tendency of Polymer from Polymer-Modified Asphalt

SIGNIFICANCE AND USE
4.1 Purchasers of polymer-modified asphalt need guidelines on proper storage and handling procedures to maintain the integrity of material they have purchased. This practice provides a significant tool for understanding the characteristics of these materials as well as comparing various sources of supply.
Note 1: The quality of the results produced by this standard are dependent on the competence of the personnel performing the procedure and the capability, calibration, and maintenance of the equipment used. Agencies that meet the criteria of Specification D3666 are generally considered capable of competent and objective testing, sampling, inspection, etc. Users of this standard are cautioned that compliance with Specification D3666 alone does not completely ensure reliable results. Reliable results depend on many factors; following the suggestions of Specification D3666 or some similar acceptable guideline provides a means of evaluating and controlling some of those factors.
SCOPE
1.1 This practice describes a laboratory procedure for determining the tendency of polymer to separate from polymer-modified asphalt under static heated storage conditions. The results of testing on material prepared according to this practice may be used as a guideline when formulating products or to establish field handling procedures. Large differences in test results between top and bottom specimens indicate that there is a degree of incompatibility between the polymer and the base asphalt.  
1.2 The values stated in SI units are to be regarded as the standard. No other units of measurement are included in this standard.  
1.3 The text of this standard references notes and footnotes which provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

General Information

Status
Published
Publication Date
30-Apr-2020
Current Stage
Ref Project

Relations

Buy Standard

Standard
ASTM D7173-20 - Standard Practice for Determining the Separation Tendency of Polymer from Polymer-Modified Asphalt
English language
2 pages
sale 15% off
Preview
sale 15% off
Preview
Standard
REDLINE ASTM D7173-20 - Standard Practice for Determining the Separation Tendency of Polymer from Polymer-Modified Asphalt
English language
2 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (Sample)

This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the
Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
Designation: D7173 −20
Standard Practice for
Determining the Separation Tendency of Polymer from
1
Polymer-Modified Asphalt
This standard is issued under the fixed designation D7173; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope D36/D36M Test Method for Softening Point of Bitumen
(Ring-and-Ball Apparatus)
1.1 This practice describes a laboratory procedure for de-
D3666 Specification for Minimum Requirements for Agen-
termining the tendency of polymer to separate from polymer-
cies Testing and Inspecting Road and Paving Materials
modified asphalt under static heated storage conditions. The
D7175 Test Method for Determining the Rheological Prop-
resultsoftestingonmaterialpreparedaccordingtothispractice
erties of Asphalt Binder Using a Dynamic Shear Rheom-
may be used as a guideline when formulating products or to
eter
establish field handling procedures. Large differences in test
results between top and bottom specimens indicate that there is D7405 Test Method for Multiple Stress Creep and Recovery
a degree of incompatibility between the polymer and the base (MSCR) of Asphalt Binder Using a Dynamic Shear
asphalt.
Rheometer
1.2 The values stated in SI units are to be regarded as the
3. Summary of Practice
standard. No other units of measurement are included in this
standard.
3.1 A measured quantity of polymer-modified asphalt in a
1.3 The text of this standard references notes and footnotes
sealed aluminum tube is conditioned in a vertical position for
which provide explanatory material. These notes and footnotes
48 h at a temperature of 163 6 5 °C. At the end of the
(excluding those in tables and figures) shall not be considered
conditioning period, top and bottom portions are separated and
as requirements of the standard.
subjected to further testing to determine the degree of separa-
tion. Tests chosen for this purpose depend on the polymer
1.4 This standard does not purport to address all of the
safety concerns, if any, associated with its use. It is the modification system being evaluated and the type of informa-
responsibility of the user of this standard to establish appro- tion desired by the user. Softening point (Test Method D36/
priate safety, health, and environmental practices and deter-
D36M) and DSR (Test Method D7175) are the most common
mine the applicability of regulatory limitations prior to use.
tests used for this purpose. MSCR (Test Method D7405)isan
1.5 This international standard was developed in accor-
alternate test.
dance with internationally recognized principles on standard-
ization established in the Decision on Principles for the
4. Significance and Use
Development of International Standards, Guides and Recom-
4.1 Purchasers of polymer-modified asphalt need guidelines
mendations issued by the World Trade Organization Technical
on proper storage and handling procedures to maintain the
Barriers to Trade (TBT) Committee.
integrity of material they have purchased. This practice pro-
2. Referenced Documents
vides a significant tool for understanding the characteristics of
2
these materials as well as comparing various sources of supply.
2.1 ASTM Standards:
NOTE 1—The quality of the results produced by this standard are
1
This practice is under the jurisdiction of ASTM Committee D04 on Road and
dependent on the competence of the personnel performing the procedure
Paving Materials and is the direct responsibility of Subcommittee D04.47 on
and the capability, calibration, and maintenance of the equipment used.
Miscellaneous Asphalt Tests.
Agencies that meet the criteria of Specification D3666 are generally
Current edition approved May 1, 2020. Published May 2020. Originally
considered capable of competent and objective testing, sampling,
approved in 2005. Last previous edition approved in 2014 as D7173 – 14. DOI:
inspection, etc. Users of this standard are cautioned that compliance with
10.1520/D7173-20.
2 Specification D3666 alone does not completely ensure reliable results.
For referenced ASTM standards, visit the ASTM website, www.astm.org, or
Reliable results depend on many factors; following the suggestions of
contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
Specification D3666 or some similar acceptable guideline provides a
Standards volume information, refer to the standard’s Document Summary page on
the ASTM website. means of evaluating and controlling some of those factors.
Copyright © ASTM I
...

This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Because
it may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current version
of the standard as published by ASTM is to be considered the official document.
Designation: D7173 − 14 D7173 − 20
Standard Practice for
Determining the Separation Tendency of Polymer from
1
Polymer Modified Polymer-Modified Asphalt
This standard is issued under the fixed designation D7173; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope
1.1 This practice describes a laboratory procedure for determining the tendency of polymer to separate from polymer modified
polymer-modified asphalt under static heated storage conditions. The results of testing on material prepared according to this
practice may be used as a guideline when formulating products or to establish field handling procedures. Large differences in test
results between top and bottom specimens indicate that there is a degree of incompatibility between the polymer and the base
asphalt.
1.2 The values stated in SI units are to be regarded as the standard. No other units of measurement are included in this standard.
1.3 The text of this standard references notes and footnotes which provide explanatory material. These notes and footnotes
(excluding those in tables and figures) shall not be considered as requirements of the standard.
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility
of the user of this standard to establish appropriate safety safety, health, and healthenvironmental practices and to determine the
applicability of regulatory limitations prior to use.
1.5 This international standard was developed in accordance with internationally recognized principles on standardization
established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued
by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
2. Referenced Documents
2
2.1 ASTM Standards:
D36D36/D36M Test Method for Softening Point of Bitumen (Ring-and-Ball Apparatus)
D3666 Specification for Minimum Requirements for Agencies Testing and Inspecting Road and Paving Materials
D7175 Test Method for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer
D7405 Test Method for Multiple Stress Creep and Recovery (MSCR) of Asphalt Binder Using a Dynamic Shear Rheometer
3. Summary of Practice
3.1 A measured quantity of polymer modified polymer-modified asphalt in a sealed aluminum tube is conditioned in a vertical
position for 48 h at a temperature of 163 6 5°C.5 °C. At the end of the conditioning period, top and bottom portions are separated
and subjected to further testing to determine the degree of separation. Tests chosen for this purpose depend on the polymer
modification system being evaluated and the type of information desired by the user. Softening Pointpoint (Test Method
D36D36/D36M) and DSR (Test Method D7175) are the most common tests used for this purpose. MSCR (Test Method D7405)
is an alternate test.
4. Significance and Use
4.1 Purchasers of polymer modified polymer-modified asphalt need to be given guidelines on proper storage and handling
procedures to maintain the integrity of material they have purchased. This practice provides a significant tool for understanding
the characteristics of these materials as well as comparing various sources of supply.
1
This practice is under the jurisdiction of ASTM Committee D04 on Road and Paving Materials and is the direct responsibility of Subcommittee D04.47 on Miscellaneous
Asphalt Tests.
Current edition approved June 1, 2014May 1, 2020. Published July 2014May 2020. Originally approved in 2005. Last previous edition approved in 20112014 as
D7173 – 11.D7173 – 14. DOI: 10.1520/D7173-14.10.1520/D7173-20.
2
For referenced ASTM standards, visit the ASTM website, www.astm.org, or contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM Standards
volume information, refer to the standard’s Document Summary page on the ASTM website.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1

---------------------- Page: 1 ----------------------
D7173 − 20
NOTE 1—The quality of the results produced by this standard are dependent on the competence of the personnel performing the procedure and the
capability, calibration, and maintenance of the equipment used. Agencies that meet the cri
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.