General methods of test for pigments and extenders — Part 15: Comparison of resistance to light of coloured pigments of similar types

This document describes a general method of test for comparing the resistance to light of samples of similar types of coloured pigments (agreed reference pigment and test sample). Two methods of exposure are described in this document. In method A, the material is exposed under glass to natural light. In method B, the material is exposed to direct artificial light.

Méthodes générales d'essai des pigments et matières de charge — Partie 15: Comparaison de la résistance à la lumière des pigments colorés de types semblables

Le présent document décrit une méthode générale d'essai pour la comparaison de la résistance à la lumière de deux échantillons de pigments colorés de types semblables (pigment de référence agréé et échantillon pour essai). Deux méthodes d'exposition sont décrites dans le présent document. Dans la méthode A, le matériau est exposé sous verre à la lumière naturelle. Dans la méthode B, le matériau est exposé directement à une lumière artificielle.

General Information

Status
Published
Publication Date
29-Jul-2019
Current Stage
9020 - International Standard under periodical review
Start Date
15-Jul-2024
Completion Date
15-Jul-2024
Ref Project

Relations

Buy Standard

Standard
ISO 787-15:2019 - General methods of test for pigments and extenders
English language
7 pages
sale 15% off
Preview
sale 15% off
Preview
Standard
ISO 787-15:2019 - General methods of test for pigments and extenders — Part 15: Comparison of resistance to light of coloured pigments of similar types Released:7/30/2019
English language
7 pages
sale 15% off
Preview
sale 15% off
Preview
Standard
ISO 787-15:2019 - Méthodes générales d'essai des pigments et matieres de charge
French language
7 pages
sale 15% off
Preview
sale 15% off
Preview
Standard
ISO 787-15:2019 - Méthodes générales d'essai des pigments et matières de charge — Partie 15: Comparaison de la résistance à la lumière des pigments colorés de types semblables Released:7/30/2019
French language
7 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (Sample)


INTERNATIONAL ISO
STANDARD 787-15
Second edition
2019-08
General methods of test for pigments
and extenders —
Part 15:
Comparison of resistance to light of
coloured pigments of similar types
Méthodes générales d'essai des pigments et matières de charge —
Partie 15: Comparaison de la résistance à la lumière des pigments
colorés de types semblables
Reference number
©
ISO 2019
© ISO 2019
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication may
be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting
on the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address
below or ISO’s member body in the country of the requester.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: +41 22 749 01 11
Fax: +41 22 749 09 47
Email: copyright@iso.org
Website: www.iso.org
Published in Switzerland
ii © ISO 2019 – All rights reserved

Contents Page
Foreword .iv
Introduction .v
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 1
4 Principle . 1
5 Apparatus and materials. 2
6 Sampling . 4
7 Procedure. 5
7.1 Preparation of the test specimens . 5
7.2 Exposure of the test specimens . 5
8 Test report . 5
Bibliography . 7
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out
through ISO technical committees. Each member body interested in a subject for which a technical
committee has been established has the right to be represented on that committee. International
organizations, governmental and non-governmental, in liaison with ISO, also take part in the work.
ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of
electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are
described in the ISO/IEC Directives, Part 1. In particular the different approval criteria needed for the
different types of ISO documents should be noted. This document was drafted in accordance with the
editorial rules of the ISO/IEC Directives, Part 2 (see www .iso .org/directives).
Attention is drawn to the possibility that some of the elements of this document may be the subject of
patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of
any patent rights identified during the development of the document will be in the Introduction and/or
on the ISO list of patent declarations received (see www .iso .org/patents).
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation on the voluntary nature of standards, the meaning of ISO specific terms and
expressions related to conformity assessment, as well as information about ISO's adherence to the
World Trade Organization (WTO) principles in the Technical Barriers to Trade (TBT) see the following
URL: www .iso .org/iso/foreword .html.
This document was prepared by Technical Committee ISO/TC 256, Pigments, dyestuffs and extenders.
This second edition cancels and replaces the first edition (ISO 787-15:1986), of which it constitutes a
minor revision. The changes compared to the previous edition are as follows:
— Clause 3 on “Terms and definitions”, with a general reference to ISO 18451-1, has been added;
— a bibliography has been added;
— the text has been editorially revised.
A list of all parts in the ISO 787 series can be found on the ISO website.
Any feedback or questions on this document should be directed to the user’s national standards body. A
complete listing of these bodies can be found at www .iso .org/members .html.
iv © ISO 2019 – All rights reserved

Introduction
The terms “resistance to light” and “light fastness (or colour fastness)” describe the resistance of a
material to change in its appearance as a result of exposure to light. The magnitude of the change, if any,
is influenced by the quantity and quality of the light to which the material is exposed, and by the nature
and composition of the material itself. Two compositions, each consisting of identical components but in
different proportions, may not have the same resistance to light. Also, two compositions each consisting of
the same proportions of similar, but not identical, components may not have the same resistance to light.
When exposed to natural light, the conditions of the test vary continuously because of the large number
of variables (for example intensity and spectral distribution of the light, temperature, relative humidity,
and the amount and nature of atmospheric contaminants) and therefore results cannot be related to
similar tests carried out on other occasions. Consequently, expressing the results as a function of time
alone is not recommended.
These considerations form the basis for the comparison of light fastness of two different samples
of a coloured pigment. Each sample is incorporated in the same proportion in otherwise identical
compositions and these compositions, in a suitable form, are examined for any difference in their
change of appearance after exposure to the same quantity and quality of light. In order to comply with
these exposure conditions, it is necessary for the compositions to be exposed side by side at the same
time to the same light source for the same period of time.
In addition, the light fastness of a pigment may be affected by the presence of other pigments such as
titanium dioxide. This important aspect may be accommodated in document by allowing the agreed
binder (medium) to consist of a dispersion of such a pigment. The test procedure is then followed as
described.
The extent, to which the change on exposure is allowed to proceed before the comparison is made, may
be of importance. It is unrealistic to assess the exposures when the change is only equivalent to the
first perceptible change, but it is also inadvisable to wait until the amount of change is large. Thus, it is
recommended that comparisons of change of appearance be made when the amount of change of the
pigment with known resistance to light (agreed reference pigment) is equal to fastness grade 4 and 3 of
the grey scale in accordance with ISO 105-A02.
For any particular application, the method of test described in this document should be completed
by the following supplementary information. This information should be derived, in part or totally,
from a national or an international standard or other document related to the product under test or, if
appropriate, should be agreed between the interested parties.
a) Type and identification of the agreed reference pigment.
b) The binder (medium) for dispersion of the test sample and the agreed reference pigment and details
of the composition of the dispersion.
c) The method of dispersion to be used.
d) Whether the test is to be carried out under natural exposure (method A) or artificial light
(method B).
e) If method A is to be used, the exposure angle of the test specimens and glass cover.
f) If method B is to be used, the details of the apparatus and of the light source.
INTERNATIONAL STANDARD ISO 787-15:2019(E)
General methods of test for pigments and extenders —
Part 15:
Comparison of resistance to light of coloured pigments of
similar types
1 Scope
This document describes a general method of test for comparing the resistance to light of samples of
similar types of coloured pigments (agreed reference pigment and test sample).
Two methods of exposure are described in this document. In method A, the material is exposed under
glass to natural light. In method B, the material is exposed to direct artificial light.
2 Normative references
The following documents are referred to in the text in such a way that some or all of their content
constitutes requirements of this document. For dated references, only the edition cited applies. For
undated references, the latest edition of the referenced document (including any amendments) applies.
ISO 105-A02, Textiles — Tests for colour fastness — Part A02: Grey scale for assessing change in colour
ISO 15528, Paints, varnishes and raw materials for paints and varnishes — Sampling
ISO 18451-1, Pigments, dyestuffs and extenders — Terminology — Part 1: General terms
CIE Publication No 20 (TC-2.2), Recommendations for the integrated irradiance and the spectral
distribution of simulated solar radiation for testing purposes
3 Terms and definitions
For the purposes of this document, the terms and definitions given in ISO 18451-1 apply.
ISO and IEC maintain terminological databases for use in standardization at the following addresses:
— ISO Online browsing platform: available at https: //www .iso .org/obp
— IEC Electropedia: available at http: //www .electropedia .org/
4 Principle
The test sample and the agreed reference pigment are each dispersed in the same agreed binder
(medium). The dispersions are applied to a substrate and dried. They are then exposed to natural
daylight with protection from rain (method A) or to artificial light (method B) under specified
conditions.
The resistance to light is assessed by comparing the change in colour of the test sample to that of the
agreed reference pigment.
5 Apparatus and materials
5.1 Substrate
a) aluminium or rigid cardboard panels of suitable size for the applicator used, and with a white high
gloss, light fast, coated and non-absorbent surface for the application of paint or
b) paper used as substrate for mass tone prints.
5.2 Film applicator or other device, suitable for applying, side by side, two films of wet thickness
50 µm to 100 µm, or a suitable apparatus for preparing mass tone prints with a thickness of about 1,5 µm.
5.3 Cover sheet, of aluminium foil or other suitable opaque material.
5.4 Grey scale for assessing change in colour, complying with ISO 105-A02.
5.5 Agreed reference pigment, for comparison with the test sample. It shall be agreed between the
parties and shall be similar in composition to that of the test sample.
5.6 Binder (medium), to be agreed between the interested parties. Its choice should be made with
regard to the field of application of the pigments being tested.
5.7 Cabinet for exposure under glass to natural light (for method A).
The exposure cabinet shall have a glass cover and shall be of a sufficient size to carry out the expected
number of tests.
The cabinet shall be constructed of metal, wood or other material capable of protecting the coated test
substrates (specimens) from rain and similar climatic effects, and there shall be adequate ventilation to
allow free flow of air over the test specimens.
The glass cover shall be a single piece of clear sheet glass, of thickness 2 mm to 3 mm, and free from
bubbles or other imperfections. The transmittance of the glass shall be approximately 90 % at 360 nm
and throughout the visible region of the spectrum, falling to a transmittance of less than 1 % at 300 nm
and shorter wavelengths. To maintain these characteristics, it is usually necessary to clean the glass
periodically and to replace the glass at intervals of not more than 2 years.
The cabinet shall be fitted with a means of support that allows the specimens to be placed not less than
50 mm below, and in a plane parallel to, the glass cover. The cabinet shall be placed so as to receive direct
sunlight throughout the day without shadows of neighbouring objects falling upon it. If the cabinet is
placed over ground, the distance between the bott
...


INTERNATIONAL ISO
STANDARD 787-15
Second edition
2019-08
General methods of test for pigments
and extenders —
Part 15:
Comparison of resistance to light of
coloured pigments of similar types
Méthodes générales d'essai des pigments et matières de charge —
Partie 15: Comparaison de la résistance à la lumière des pigments
colorés de types semblables
Reference number
©
ISO 2019
© ISO 2019
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication may
be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting
on the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address
below or ISO’s member body in the country of the requester.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: +41 22 749 01 11
Fax: +41 22 749 09 47
Email: copyright@iso.org
Website: www.iso.org
Published in Switzerland
ii © ISO 2019 – All rights reserved

Contents Page
Foreword .iv
Introduction .v
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 1
4 Principle . 1
5 Apparatus and materials. 2
6 Sampling . 4
7 Procedure. 5
7.1 Preparation of the test specimens . 5
7.2 Exposure of the test specimens . 5
8 Test report . 5
Bibliography . 7
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out
through ISO technical committees. Each member body interested in a subject for which a technical
committee has been established has the right to be represented on that committee. International
organizations, governmental and non-governmental, in liaison with ISO, also take part in the work.
ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of
electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are
described in the ISO/IEC Directives, Part 1. In particular the different approval criteria needed for the
different types of ISO documents should be noted. This document was drafted in accordance with the
editorial rules of the ISO/IEC Directives, Part 2 (see www .iso .org/directives).
Attention is drawn to the possibility that some of the elements of this document may be the subject of
patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of
any patent rights identified during the development of the document will be in the Introduction and/or
on the ISO list of patent declarations received (see www .iso .org/patents).
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation on the voluntary nature of standards, the meaning of ISO specific terms and
expressions related to conformity assessment, as well as information about ISO's adherence to the
World Trade Organization (WTO) principles in the Technical Barriers to Trade (TBT) see the following
URL: www .iso .org/iso/foreword .html.
This document was prepared by Technical Committee ISO/TC 256, Pigments, dyestuffs and extenders.
This second edition cancels and replaces the first edition (ISO 787-15:1986), of which it constitutes a
minor revision. The changes compared to the previous edition are as follows:
— Clause 3 on “Terms and definitions”, with a general reference to ISO 18451-1, has been added;
— a bibliography has been added;
— the text has been editorially revised.
A list of all parts in the ISO 787 series can be found on the ISO website.
Any feedback or questions on this document should be directed to the user’s national standards body. A
complete listing of these bodies can be found at www .iso .org/members .html.
iv © ISO 2019 – All rights reserved

Introduction
The terms “resistance to light” and “light fastness (or colour fastness)” describe the resistance of a
material to change in its appearance as a result of exposure to light. The magnitude of the change, if any,
is influenced by the quantity and quality of the light to which the material is exposed, and by the nature
and composition of the material itself. Two compositions, each consisting of identical components but in
different proportions, may not have the same resistance to light. Also, two compositions each consisting of
the same proportions of similar, but not identical, components may not have the same resistance to light.
When exposed to natural light, the conditions of the test vary continuously because of the large number
of variables (for example intensity and spectral distribution of the light, temperature, relative humidity,
and the amount and nature of atmospheric contaminants) and therefore results cannot be related to
similar tests carried out on other occasions. Consequently, expressing the results as a function of time
alone is not recommended.
These considerations form the basis for the comparison of light fastness of two different samples
of a coloured pigment. Each sample is incorporated in the same proportion in otherwise identical
compositions and these compositions, in a suitable form, are examined for any difference in their
change of appearance after exposure to the same quantity and quality of light. In order to comply with
these exposure conditions, it is necessary for the compositions to be exposed side by side at the same
time to the same light source for the same period of time.
In addition, the light fastness of a pigment may be affected by the presence of other pigments such as
titanium dioxide. This important aspect may be accommodated in document by allowing the agreed
binder (medium) to consist of a dispersion of such a pigment. The test procedure is then followed as
described.
The extent, to which the change on exposure is allowed to proceed before the comparison is made, may
be of importance. It is unrealistic to assess the exposures when the change is only equivalent to the
first perceptible change, but it is also inadvisable to wait until the amount of change is large. Thus, it is
recommended that comparisons of change of appearance be made when the amount of change of the
pigment with known resistance to light (agreed reference pigment) is equal to fastness grade 4 and 3 of
the grey scale in accordance with ISO 105-A02.
For any particular application, the method of test described in this document should be completed
by the following supplementary information. This information should be derived, in part or totally,
from a national or an international standard or other document related to the product under test or, if
appropriate, should be agreed between the interested parties.
a) Type and identification of the agreed reference pigment.
b) The binder (medium) for dispersion of the test sample and the agreed reference pigment and details
of the composition of the dispersion.
c) The method of dispersion to be used.
d) Whether the test is to be carried out under natural exposure (method A) or artificial light
(method B).
e) If method A is to be used, the exposure angle of the test specimens and glass cover.
f) If method B is to be used, the details of the apparatus and of the light source.
INTERNATIONAL STANDARD ISO 787-15:2019(E)
General methods of test for pigments and extenders —
Part 15:
Comparison of resistance to light of coloured pigments of
similar types
1 Scope
This document describes a general method of test for comparing the resistance to light of samples of
similar types of coloured pigments (agreed reference pigment and test sample).
Two methods of exposure are described in this document. In method A, the material is exposed under
glass to natural light. In method B, the material is exposed to direct artificial light.
2 Normative references
The following documents are referred to in the text in such a way that some or all of their content
constitutes requirements of this document. For dated references, only the edition cited applies. For
undated references, the latest edition of the referenced document (including any amendments) applies.
ISO 105-A02, Textiles — Tests for colour fastness — Part A02: Grey scale for assessing change in colour
ISO 15528, Paints, varnishes and raw materials for paints and varnishes — Sampling
ISO 18451-1, Pigments, dyestuffs and extenders — Terminology — Part 1: General terms
CIE Publication No 20 (TC-2.2), Recommendations for the integrated irradiance and the spectral
distribution of simulated solar radiation for testing purposes
3 Terms and definitions
For the purposes of this document, the terms and definitions given in ISO 18451-1 apply.
ISO and IEC maintain terminological databases for use in standardization at the following addresses:
— ISO Online browsing platform: available at https: //www .iso .org/obp
— IEC Electropedia: available at http: //www .electropedia .org/
4 Principle
The test sample and the agreed reference pigment are each dispersed in the same agreed binder
(medium). The dispersions are applied to a substrate and dried. They are then exposed to natural
daylight with protection from rain (method A) or to artificial light (method B) under specified
conditions.
The resistance to light is assessed by comparing the change in colour of the test sample to that of the
agreed reference pigment.
5 Apparatus and materials
5.1 Substrate
a) aluminium or rigid cardboard panels of suitable size for the applicator used, and with a white high
gloss, light fast, coated and non-absorbent surface for the application of paint or
b) paper used as substrate for mass tone prints.
5.2 Film applicator or other device, suitable for applying, side by side, two films of wet thickness
50 µm to 100 µm, or a suitable apparatus for preparing mass tone prints with a thickness of about 1,5 µm.
5.3 Cover sheet, of aluminium foil or other suitable opaque material.
5.4 Grey scale for assessing change in colour, complying with ISO 105-A02.
5.5 Agreed reference pigment, for comparison with the test sample. It shall be agreed between the
parties and shall be similar in composition to that of the test sample.
5.6 Binder (medium), to be agreed between the interested parties. Its choice should be made with
regard to the field of application of the pigments being tested.
5.7 Cabinet for exposure under glass to natural light (for method A).
The exposure cabinet shall have a glass cover and shall be of a sufficient size to carry out the expected
number of tests.
The cabinet shall be constructed of metal, wood or other material capable of protecting the coated test
substrates (specimens) from rain and similar climatic effects, and there shall be adequate ventilation to
allow free flow of air over the test specimens.
The glass cover shall be a single piece of clear sheet glass, of thickness 2 mm to 3 mm, and free from
bubbles or other imperfections. The transmittance of the glass shall be approximately 90 % at 360 nm
and throughout the visible region of the spectrum, falling to a transmittance of less than 1 % at 300 nm
and shorter wavelengths. To maintain these characteristics, it is usually necessary to clean the glass
periodically and to replace the glass at intervals of not more than 2 years.
The cabinet shall be fitted with a means of support that allows the specimens to be placed not less than
50 mm below, and in a plane parallel to, the glass cover. The cabinet shall be placed so as to receive direct
sunlight throughout the day without shadows of neighbouring objects falling upon it. If the cabinet is
placed over ground, the distance between the bott
...


NORME ISO
INTERNATIONALE 787-15
Deuxième édition
2019-08
Méthodes générales d'essai des
pigments et matières de charge —
Partie 15:
Comparaison de la résistance à la
lumière des pigments colorés de types
semblables
General methods of test for pigments and extenders —
Part 15: Comparison of resistance to light of coloured pigments of
similar types
Numéro de référence
©
ISO 2019
DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2019
Tous droits réservés. Sauf prescription différente ou nécessité dans le contexte de sa mise en œuvre, aucune partie de cette
publication ne peut être reproduite ni utilisée sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique,
y compris la photocopie, ou la diffusion sur l’internet ou sur un intranet, sans autorisation écrite préalable. Une autorisation peut
être demandée à l’ISO à l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.
ISO copyright office
Case postale 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Genève
Tél.: +41 22 749 01 11
Fax: +41 22 749 09 47
E-mail: copyright@iso.org
Web: www.iso.org
Publié en Suisse
ii © ISO 2019 – Tous droits réservés

Sommaire Page
Avant-propos .iv
Introduction .v
1 Domaine d'application . 1
2 Références normatives . 1
3 Termes et définitions . 1
4 Principe . 1
5 Appareillage et matériaux . 2
6 Échantillonnage . 5
7 Mode opératoire. 5
7.1 Préparation des éprouvettes . 5
7.2 Exposition des éprouvettes . 6
8 Rapport d'essai . 6
Bibliographie . 7
Avant-propos
L'ISO (Organisation internationale de normalisation) est une fédération mondiale d'organismes
nationaux de normalisation (comités membres de l'ISO). L'élaboration des Normes internationales est
confiée aux comités techniques de l’ISO. Chaque comité membre intéressé par une étude a le droit de
faire partie du comité technique créé à cet effet. Les organisations internationales, gouvernementales
et non gouvernementales, en liaison avec l'ISO participent également aux travaux. L'ISO collabore
étroitement avec la Commission électrotechnique internationale (IEC) en ce qui concerne la
normalisation électrotechnique.
Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont
décrites dans les Directives ISO/IEC, Partie 1. Il convient en particulier de prendre note des différents
critères d'approbation requis pour les différents types de documents ISO. Le présent document a été
rédigé conformément aux règles de rédaction données dans les Directives ISO/IEC, Partie 2 (voir www
.iso .org/directives).
L'attention est attirée sur le fait que certains des éléments du présent document peuvent faire l'objet de
droits de propriété intellectuelle ou de droits analogues. L'ISO ne saurait être tenue pour responsable
de ne pas avoir identifié de tels droits de propriété et averti de leur existence. Les détails concernant
les références aux droits de propriété intellectuelle ou autres droits analogues identifiés lors de
l'élaboration du document sont indiqués dans l'Introduction et/ou dans la liste des déclarations de
brevets reçues par l'ISO (voir www .iso .org/patents).
Les appellations commerciales éventuellement mentionnées dans le présent document sont données
pour information, par souci de commodité, à l'intention des utilisateurs et ne sauraient constituer un
engagement.
Pour une explication de la nature volontaire des normes, la signification des termes et expressions
spécifiques de l'ISO liés à l'évaluation de la conformité, ou pour toute information au sujet de l'adhésion
de l'ISO aux principes de l'Organisation mondiale du commerce (OMC) concernant les obstacles
techniques au commerce (OTC), voir le lien suivant: www .iso .org/iso/fr/avant -propos .html.
Le présent document a été élaboré par le comité technique ISO/TC 256, Pigments, colorants et matières
de charge.
Cette deuxième édition annule et remplace la première édition (ISO 787-15:1986), dont elle constitue
une révision mineure. Les modifications par rapport à l'édition précédente sont les suivantes:
— l'Article 3 relatif aux «Termes et définitions», comportant une référence générale à l'ISO 18451-1, a
été ajouté;
— une Bibliographie a été ajoutée;
— le texte a fait l'objet d'une révision éditoriale.
Une liste de toutes les parties de la série ISO 787 est disponible sur le site de l'ISO.
Il convient que l'utilisateur adresse tout retour d'information ou toute question concernant le présent
document à l'organisme national de normalisation de son pays. Une liste exhaustive desdits organismes
se trouve à l'adresse www .iso .org/fr/members .html.
iv © ISO 2019 – Tous droits réservés

Introduction
Les termes «résistance à la lumière» et «solidité à la lumière (ou solidité des couleurs)» décrivent
la résistance d'un produit à changer d'apparence, après exposition à la lumière. L'importance du
changement éventuel est influencée par la quantité et la qualité de la lumière à laquelle le produit est
exposé, et par la nature et la composition du produit lui-même. Deux compositions constituées chacune
de composants identiques, mais en proportions différentes, peuvent ne pas avoir la même résistance à
la lumière. De même, deux compositions constituées chacune des mêmes proportions de composants
semblables mais non identiques, peuvent ne pas avoir la même résistance à la lumière.
En exposition à la lumière naturelle, les conditions de l'essai évolueront de façon continue en raison
du nombre important des facteurs (par exemple: intensité et distribution spectrale de la lumière,
température, humidité relative, importance et nature des agents atmosphériques contaminants) et
c'est pourquoi les résultats ne peuvent pas être comparés à des essais similaires effectués dans d'autres
occasions. En conséquence, il n'est pas recommandé d'exprimer ces résultats uniquement en fonction
du temps.
Ces considérations sont les idées de base pour la comparaison de la solidité à la lumière de deux
échantillons différents d'un pigment coloré. Chaque échantillon est incorporé dans les mêmes
proportions dans des compositions par ailleurs identiques, et ces dernières, de forme convenable,
sont examinées pour déceler toute différence du changement d'apparence après exposition à la même
quantité et à la même qualité de lumière. Pour satisfaire à ces conditions d'exposition, il est nécessaire
que les compositions soient exposées côte à côte en même temps à la même source de lumière, et
pendant la même durée.
Enfin, la solidité à la lumière peut être affectée par la présence d'autres pigments comme le dioxyde de
titane. Cet aspect important peut être pris en compte dans le présent document en prenant pour liant
(milieu) agréé une dispersion de ce pigment. Le mode opératoire est alors celui décrit.
Le degré de changement produit au cours de l'exposition avant d'effectuer la comparaison peut avoir
de l'importance. Il n'est pas réaliste d'évaluer les expositions lorsque le changement est seulement
équivalent au premier changement perceptible, mais il est également peu sage d'attendre jusqu'à ce que
le changement soit important. Il est recommandé de faire la comparaison du changement d'apparence
lorsque l'importance du changement d'un pigment de résistance connue (pigment de référence agréé)
est égale au degré 4 ou 3 de l'échelle de gris suivant l'ISO 105-A02.
Pour toute application particulière, il convient de compléter la méthode décrite dans le présent document
par les informations supplémentaires suivantes. Il convient que ces informations proviennent, en partie
ou en totalité, d'une norme nationale ou internationale ou de tout autre document concernant le produit
à soumettre à essai ou bien, si nécessaire, il convient qu'elles fassent l'objet d'un accord entre les parties
intéressées.
a) Le type et l'identification du liant de référence agréé.
b) Le liant (milieu) pour la dispersion de l'échantillon soumis à essai et du pigment de référence agréé
et les détails relatifs à la composition de la dispersion.
c) La méthode de dispersion utilisée.
d) L'exposition à la lumière naturelle (méthode A) ou à la lumière artificielle (méthode B).
e) Dans le cas de la méthode A, l'angle d'exposition des éprouvettes et de la plaque de verre.
f) Dans le cas de la méthode B, des détails sur l'appareillage et la source lumineuse.
NORME INTERNATIONALE ISO 787-15:2019(F)
Méthodes générales d'essai des pigments et matières de
charge —
Partie 15:
Comparaison de la résistance à la lumière des pigments
colorés de types semblables
1 Domaine d'application
Le présent document décrit une méthode générale d'essai pour la comparaison de la résistance à la
lumière de deux échantillons de pigments colorés de types semblables (pigment de référence agréé et
échantillon pour essai).
Deux méthodes d'exposition sont décrites dans le présent document. Dans la méthode A, le matériau est
exposé sous verre à la lumière naturelle. Dans la méthode B, le matériau est exposé directement à une
lumière artificielle.
2 Références normatives
Les documents suivants cités dans le texte constituent, pour tout ou partie de leur contenu, des
exigences du présent document. Pour les références datées, seule l'édition citée s'applique. Pour les
références non datées, la dernière édition du document de référence s'applique (y compris les éventuels
amendements).
ISO 105-A02, Textiles — Essais de solidité des teintures — Partie A02: Échelle de gris pour l'évaluation des
dégradations
ISO 15528, Peintures, vernis et matières premières pour peintures et vernis — Échantillonnage
ISO 18451-1, Pigments, colorants et matières de charge — Terminologie — Partie 1: Termes généraux
Publication CIE N° 20 (TC-2.2), Recommandations concernant l'éclairement énergétique et la répartition
spectrale du rayonnement solaire en vue de sa reproduction artificielle pour les essais
3 Termes et définitions
Pour les besoins du présent document, les termes et définitions de l'ISO 18451-1 s'appliquent.
L'ISO et l'IEC tiennent à jour des bases de données terminologiques destinées à être utilisées en
normalisation, consultables aux adresses suivantes:
— ISO Online browsing platform: disponible à l'adresse https: //www .iso .org/obp
— IEC Electropedia: disponible à l'adresse http: //www .electropedia .org/
4 Principe
L'échantillon pour essai et le pigment de référence agréé sont dispersés dans le même liant (milieu)
agréé. Les dispersions sont appliquées sur un subjectile et séchées; elles sont ensuite exposées à
la lumière du jour naturelle avec protection contre la pluie (méthode A) ou à une lumière artificielle
(méthode B) dans des conditions spécifiées.
La résistance à la lumière est évaluée par comparaison du changement de couleur de l'échantillon pour
essai par rapport au pigment de référence agréé.
5 Appareillage et matériaux
5.1 Subjectile
a) plaques d'aluminium ou de carton rigide, de dimensions appropriées à l'applicateur utilisé, ayant
une surface blanche de brillant élevé, solide à la lumière, enduite et non absorbante, convenable
pour l'application de la peinture, ou
b) papier convenable comme subjectile pour empreintes d'une épaisseur.
5.2 Applicateur de feuil ou autre dispositif, permettant l'application de deux feuils côte à côte,
d'épaisseur humide comprise entre 50 µm et 100 µm, ou appareillage convenant à la préparation
d'empreintes d'une épaisseur d'environ 1,5 µm.
5.3 Cache, en feuilles d'aluminium ou en matière opaque convenable.
5.4 Échelle de gris pour l'évaluation des dégradations, conforme à l'ISO 105-A02.
5.5 Pigment de référence agréé, pour comparaison avec l'échantillon pour essai. Il doit faire l'objet
d'un accord entre les parties intéressées et doit être de composition semblable à celle de l'échantillon
pour essai.
5.6 Liant (milieu), doit faire l'objet d'un accord entre les parties intéressées. Il convient de choisir le
liant en fonction de l'application des pigments à sou
...


NORME ISO
INTERNATIONALE 787-15
Deuxième édition
2019-08
Méthodes générales d'essai des
pigments et matières de charge —
Partie 15:
Comparaison de la résistance à la
lumière des pigments colorés de types
semblables
General methods of test for pigments and extenders —
Part 15: Comparison of resistance to light of coloured pigments of
similar types
Numéro de référence
©
ISO 2019
DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2019
Tous droits réservés. Sauf prescription différente ou nécessité dans le contexte de sa mise en œuvre, aucune partie de cette
publication ne peut être reproduite ni utilisée sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique,
y compris la photocopie, ou la diffusion sur l’internet ou sur un intranet, sans autorisation écrite préalable. Une autorisation peut
être demandée à l’ISO à l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.
ISO copyright office
Case postale 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Genève
Tél.: +41 22 749 01 11
Fax: +41 22 749 09 47
E-mail: copyright@iso.org
Web: www.iso.org
Publié en Suisse
ii © ISO 2019 – Tous droits réservés

Sommaire Page
Avant-propos .iv
Introduction .v
1 Domaine d'application . 1
2 Références normatives . 1
3 Termes et définitions . 1
4 Principe . 1
5 Appareillage et matériaux . 2
6 Échantillonnage . 5
7 Mode opératoire. 5
7.1 Préparation des éprouvettes . 5
7.2 Exposition des éprouvettes . 6
8 Rapport d'essai . 6
Bibliographie . 7
Avant-propos
L'ISO (Organisation internationale de normalisation) est une fédération mondiale d'organismes
nationaux de normalisation (comités membres de l'ISO). L'élaboration des Normes internationales est
confiée aux comités techniques de l’ISO. Chaque comité membre intéressé par une étude a le droit de
faire partie du comité technique créé à cet effet. Les organisations internationales, gouvernementales
et non gouvernementales, en liaison avec l'ISO participent également aux travaux. L'ISO collabore
étroitement avec la Commission électrotechnique internationale (IEC) en ce qui concerne la
normalisation électrotechnique.
Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont
décrites dans les Directives ISO/IEC, Partie 1. Il convient en particulier de prendre note des différents
critères d'approbation requis pour les différents types de documents ISO. Le présent document a été
rédigé conformément aux règles de rédaction données dans les Directives ISO/IEC, Partie 2 (voir www
.iso .org/directives).
L'attention est attirée sur le fait que certains des éléments du présent document peuvent faire l'objet de
droits de propriété intellectuelle ou de droits analogues. L'ISO ne saurait être tenue pour responsable
de ne pas avoir identifié de tels droits de propriété et averti de leur existence. Les détails concernant
les références aux droits de propriété intellectuelle ou autres droits analogues identifiés lors de
l'élaboration du document sont indiqués dans l'Introduction et/ou dans la liste des déclarations de
brevets reçues par l'ISO (voir www .iso .org/patents).
Les appellations commerciales éventuellement mentionnées dans le présent document sont données
pour information, par souci de commodité, à l'intention des utilisateurs et ne sauraient constituer un
engagement.
Pour une explication de la nature volontaire des normes, la signification des termes et expressions
spécifiques de l'ISO liés à l'évaluation de la conformité, ou pour toute information au sujet de l'adhésion
de l'ISO aux principes de l'Organisation mondiale du commerce (OMC) concernant les obstacles
techniques au commerce (OTC), voir le lien suivant: www .iso .org/iso/fr/avant -propos .html.
Le présent document a été élaboré par le comité technique ISO/TC 256, Pigments, colorants et matières
de charge.
Cette deuxième édition annule et remplace la première édition (ISO 787-15:1986), dont elle constitue
une révision mineure. Les modifications par rapport à l'édition précédente sont les suivantes:
— l'Article 3 relatif aux «Termes et définitions», comportant une référence générale à l'ISO 18451-1, a
été ajouté;
— une Bibliographie a été ajoutée;
— le texte a fait l'objet d'une révision éditoriale.
Une liste de toutes les parties de la série ISO 787 est disponible sur le site de l'ISO.
Il convient que l'utilisateur adresse tout retour d'information ou toute question concernant le présent
document à l'organisme national de normalisation de son pays. Une liste exhaustive desdits organismes
se trouve à l'adresse www .iso .org/fr/members .html.
iv © ISO 2019 – Tous droits réservés

Introduction
Les termes «résistance à la lumière» et «solidité à la lumière (ou solidité des couleurs)» décrivent
la résistance d'un produit à changer d'apparence, après exposition à la lumière. L'importance du
changement éventuel est influencée par la quantité et la qualité de la lumière à laquelle le produit est
exposé, et par la nature et la composition du produit lui-même. Deux compositions constituées chacune
de composants identiques, mais en proportions différentes, peuvent ne pas avoir la même résistance à
la lumière. De même, deux compositions constituées chacune des mêmes proportions de composants
semblables mais non identiques, peuvent ne pas avoir la même résistance à la lumière.
En exposition à la lumière naturelle, les conditions de l'essai évolueront de façon continue en raison
du nombre important des facteurs (par exemple: intensité et distribution spectrale de la lumière,
température, humidité relative, importance et nature des agents atmosphériques contaminants) et
c'est pourquoi les résultats ne peuvent pas être comparés à des essais similaires effectués dans d'autres
occasions. En conséquence, il n'est pas recommandé d'exprimer ces résultats uniquement en fonction
du temps.
Ces considérations sont les idées de base pour la comparaison de la solidité à la lumière de deux
échantillons différents d'un pigment coloré. Chaque échantillon est incorporé dans les mêmes
proportions dans des compositions par ailleurs identiques, et ces dernières, de forme convenable,
sont examinées pour déceler toute différence du changement d'apparence après exposition à la même
quantité et à la même qualité de lumière. Pour satisfaire à ces conditions d'exposition, il est nécessaire
que les compositions soient exposées côte à côte en même temps à la même source de lumière, et
pendant la même durée.
Enfin, la solidité à la lumière peut être affectée par la présence d'autres pigments comme le dioxyde de
titane. Cet aspect important peut être pris en compte dans le présent document en prenant pour liant
(milieu) agréé une dispersion de ce pigment. Le mode opératoire est alors celui décrit.
Le degré de changement produit au cours de l'exposition avant d'effectuer la comparaison peut avoir
de l'importance. Il n'est pas réaliste d'évaluer les expositions lorsque le changement est seulement
équivalent au premier changement perceptible, mais il est également peu sage d'attendre jusqu'à ce que
le changement soit important. Il est recommandé de faire la comparaison du changement d'apparence
lorsque l'importance du changement d'un pigment de résistance connue (pigment de référence agréé)
est égale au degré 4 ou 3 de l'échelle de gris suivant l'ISO 105-A02.
Pour toute application particulière, il convient de compléter la méthode décrite dans le présent document
par les informations supplémentaires suivantes. Il convient que ces informations proviennent, en partie
ou en totalité, d'une norme nationale ou internationale ou de tout autre document concernant le produit
à soumettre à essai ou bien, si nécessaire, il convient qu'elles fassent l'objet d'un accord entre les parties
intéressées.
a) Le type et l'identification du liant de référence agréé.
b) Le liant (milieu) pour la dispersion de l'échantillon soumis à essai et du pigment de référence agréé
et les détails relatifs à la composition de la dispersion.
c) La méthode de dispersion utilisée.
d) L'exposition à la lumière naturelle (méthode A) ou à la lumière artificielle (méthode B).
e) Dans le cas de la méthode A, l'angle d'exposition des éprouvettes et de la plaque de verre.
f) Dans le cas de la méthode B, des détails sur l'appareillage et la source lumineuse.
NORME INTERNATIONALE ISO 787-15:2019(F)
Méthodes générales d'essai des pigments et matières de
charge —
Partie 15:
Comparaison de la résistance à la lumière des pigments
colorés de types semblables
1 Domaine d'application
Le présent document décrit une méthode générale d'essai pour la comparaison de la résistance à la
lumière de deux échantillons de pigments colorés de types semblables (pigment de référence agréé et
échantillon pour essai).
Deux méthodes d'exposition sont décrites dans le présent document. Dans la méthode A, le matériau est
exposé sous verre à la lumière naturelle. Dans la méthode B, le matériau est exposé directement à une
lumière artificielle.
2 Références normatives
Les documents suivants cités dans le texte constituent, pour tout ou partie de leur contenu, des
exigences du présent document. Pour les références datées, seule l'édition citée s'applique. Pour les
références non datées, la dernière édition du document de référence s'applique (y compris les éventuels
amendements).
ISO 105-A02, Textiles — Essais de solidité des teintures — Partie A02: Échelle de gris pour l'évaluation des
dégradations
ISO 15528, Peintures, vernis et matières premières pour peintures et vernis — Échantillonnage
ISO 18451-1, Pigments, colorants et matières de charge — Terminologie — Partie 1: Termes généraux
Publication CIE N° 20 (TC-2.2), Recommandations concernant l'éclairement énergétique et la répartition
spectrale du rayonnement solaire en vue de sa reproduction artificielle pour les essais
3 Termes et définitions
Pour les besoins du présent document, les termes et définitions de l'ISO 18451-1 s'appliquent.
L'ISO et l'IEC tiennent à jour des bases de données terminologiques destinées à être utilisées en
normalisation, consultables aux adresses suivantes:
— ISO Online browsing platform: disponible à l'adresse https: //www .iso .org/obp
— IEC Electropedia: disponible à l'adresse http: //www .electropedia .org/
4 Principe
L'échantillon pour essai et le pigment de référence agréé sont dispersés dans le même liant (milieu)
agréé. Les dispersions sont appliquées sur un subjectile et séchées; elles sont ensuite exposées à
la lumière du jour naturelle avec protection contre la pluie (méthode A) ou à une lumière artificielle
(méthode B) dans des conditions spécifiées.
La résistance à la lumière est évaluée par comparaison du changement de couleur de l'échantillon pour
essai par rapport au pigment de référence agréé.
5 Appareillage et matériaux
5.1 Subjectile
a) plaques d'aluminium ou de carton rigide, de dimensions appropriées à l'applicateur utilisé, ayant
une surface blanche de brillant élevé, solide à la lumière, enduite et non absorbante, convenable
pour l'application de la peinture, ou
b) papier convenable comme subjectile pour empreintes d'une épaisseur.
5.2 Applicateur de feuil ou autre dispositif, permettant l'application de deux feuils côte à côte,
d'épaisseur humide comprise entre 50 µm et 100 µm, ou appareillage convenant à la préparation
d'empreintes d'une épaisseur d'environ 1,5 µm.
5.3 Cache, en feuilles d'aluminium ou en matière opaque convenable.
5.4 Échelle de gris pour l'évaluation des dégradations, conforme à l'ISO 105-A02.
5.5 Pigment de référence agréé, pour comparaison avec l'échantillon pour essai. Il doit faire l'objet
d'un accord entre les parties intéressées et doit être de composition semblable à celle de l'échantillon
pour essai.
5.6 Liant (milieu), doit faire l'objet d'un accord entre les parties intéressées. Il convient de choisir le
liant en fonction de l'application des pigments à sou
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.