ISO 10111:2019
(Main)Metallic and other inorganic coatings — Measurement of mass per unit area — Review of gravimetric and chemical analysis methods
Metallic and other inorganic coatings — Measurement of mass per unit area — Review of gravimetric and chemical analysis methods
This document gives guidelines for determining the average surface density over a measured area of anodic oxide or of a coating deposited autocatalytically, mechanically, by chemical conversion, by electrodeposition, by hot dip galvanizing and by chemical or physical vapour deposition using gravimetric and other chemical analysis procedures that have attained some degree of national or international standardization. A variety of procedures are described and include: — gravimetric procedures for chemical or electrochemical dissolution of the coating or the substrate to determine the coating surface density; — gravimetric procedures for weighing the uncoated substrate and the coated (finished) specimen to determine the coating surface density; — analytical procedures that utilize dissolution of the coating for determination of the coating surface density by instrumental chemical analysis methods. With the exception of the gravimetric method as described in ISO 3892, this document does not give the measurement uncertainties of the methods cited.
Revêtements métalliques et autres revêtements inorganiques — Mesurage de la masse surfacique — Présentation des méthodes d'analyse gravimétrique et chimique
Le présent document donne des recommandations relatives aux méthodes générales d'analyse gravimétrique ou chimique de diverses sortes ayant atteint un degré de normalisation à l'échelon national ou international, utilisées pour la détermination de la masse surfacique moyenne de revêtements obtenus par dépôt électrolytique, dépôt par immersion, dépôt autocatalytique, matoplastie, déposition en phase gazeuse par procédé chimique ou physique, anodisation ou conversion chimique. Il décrit un certain nombre de ces procédés de détermination de la masse surfacique, parmi lesquels: — des méthodes gravimétriques pour la mise en solution chimique ou électrochimique du dépôt ou du métal de base permettant la détermination de la masse surfacique du dépôt; — des méthodes gravimétriques pour la pesée du métal de base nu et de l'éprouvette revêtue (finie) permettant la détermination de la masse surfacique du dépôt; — des méthodes analytiques qui utilisent la mise en solution du dépôt en vue d'une détermination de la masse surfacique du dépôt par des méthodes instrumentales d'analyse chimique. Sauf pour la méthode gravimétrique telle que décrite dans l'ISO 3892, le présent document n'indique pas les incertitudes de mesurage liées aux méthodes citées.
General Information
Relations
Buy Standard
Standards Content (Sample)
INTERNATIONAL ISO
STANDARD 10111
Second edition
2019-01
Metallic and other inorganic
coatings — Measurement of mass per
unit area — Review of gravimetric and
chemical analysis methods
Revêtements métalliques et autres revêtements inorganiques —
Mesurage de la masse surfacique — Présentation des méthodes
d'analyse gravimétrique et chimique
Reference number
©
ISO 2019
© ISO 2019
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication may
be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting
on the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address
below or ISO’s member body in the country of the requester.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: +41 22 749 01 11
Fax: +41 22 749 09 47
Email: copyright@iso.org
Website: www.iso.org
Published in Switzerland
ii © ISO 2019 – All rights reserved
Contents Page
Foreword .iv
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 1
4 Principle . 2
5 Special equipment . 2
6 Preparation of test specimen . 2
6.1 Size . 2
6.2 Shape . 2
6.3 Edge condition . 2
6.4 Heat treatment . 2
7 Measurement of coated area . 3
7.1 Measurement method . 3
7.2 Surface measuring equipment. 3
7.2.1 Geometrical (projected) surface area . 3
7.2.2 Surface area increase due to roughness (optional) . 3
7.3 Number of measurements . 3
8 Determination of mass of coating by chemical analysis . 4
8.1 General . 4
8.2 Restrictions . 4
9 Gravimetric determination of mass of coating . 4
9.1 Specimen size . 4
9.2 Limitations . 4
9.3 Restrictions . 4
9.4 Gravimetric analysis equipment . 4
9.5 Procedure . 5
9.5.1 General. 5
9.5.2 Difference method with dissolution of the coating . 5
9.5.3 Direct weighing method with dissolution of the substrate . 5
9.5.4 Difference method without dissolution . 5
10 Calculations. 6
10.1 Surface density . 6
10.2 Thickness . 6
Annex A (informative) Reagents for selective dissolution of metal layers . 7
Bibliography .11
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out
through ISO technical committees. Each member body interested in a subject for which a technical
committee has been established has the right to be represented on that committee. International
organizations, governmental and non-governmental, in liaison with ISO, also take part in the work.
ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of
electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are
described in the ISO/IEC Directives, Part 1. In particular, the different approval criteria needed for the
different types of ISO documents should be noted. This document was drafted in accordance with the
editorial rules of the ISO/IEC Directives, Part 2 (see www .iso .org/directives).
Attention is drawn to the possibility that some of the elements of this document may be the subject of
patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of
any patent rights identified during the development of the document will be in the Introduction and/or
on the ISO list of patent declarations received (see www .iso .org/patents).
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation of the voluntary nature of standards, the meaning of ISO specific terms and
expressions related to conformity assessment, as well as information about ISO's adherence to the
World Trade Organization (WTO) principles in the Technical Barriers to Trade (TBT) see www .iso
.org/iso/foreword .html.
This document was prepared by Technical Committee ISO/TC 107, Metallic and other inorganic coatings.
This second edition cancels and replaces the first edition (ISO 10111:2000), which has been technically
revised. The following changes have been made:
a) a gravimetric method has been added for weighing the uncoated substrate and the finished sample;
b) the surface area increase caused by surface roughness has been considered to obtain a more
realistic estimation of local geometric coating thickness (optional);
c) Annex A, which gives reagents for etching or stripping solutions, has been changed to informative
as other solutions can be applied;
d) reagents in Annex A that referred to no longer existing standards or which contain hazardous
chemicals have been removed;
e) outdated and uncited references in the Bibliography have been removed.
Any feedback or questions on this document should be directed to the user’s national standards body. A
complete listing of these bodies can be found at www .iso .org/members .html.
iv © ISO 2019 – All rights reserved
INTERNATIONAL STANDARD ISO 10111:2019(E)
Metallic and other inorganic coatings — Measurement of
mass per unit area — Review of gravimetric and chemical
analysis methods
WARNING — The use of this document can involve hazardous materials, operations and
equipment. It does not purport to address all of the safety or environmental problems associated
with its use. It is the responsibility of users of this document to take appropriate measures
to ensure the safety and health of personnel and the environment prior to application of this
document.
1 Scope
This document gives guidelines for determining the average surface density over a measured area
of anodic oxide or of a coating deposited autocatalytically, mechanically, by chemical conversion,
by electrodeposition, by hot dip galvanizing and by chemical or physical vapour deposition using
gravimetric and other chemical analysis procedures that have attained some degree of national or
international standardization.
A variety of procedures are described and include:
— gravimetric procedures for chemical or electrochemical dissolution of the coating or the substrate
to determine the coating surface density;
— gravimetric procedures for weighing the uncoated substrate and the coated (finished) specimen to
determine the coating surface density;
— analytical procedures that utilize dissolution of the coating for determination of the coating surface
density by instrumental chemical analysis methods.
With the exception of the gravimetric method as described in ISO 3892, this document does not give the
measurement uncertainties of the methods cited.
2 Normative references
The following documents are referred to in the text in such a way that some or all of their content
constitutes requirements of this document. For dated references, only the edition cited applies. For
undated references, the latest edition of the referenced document (including any amendments) applies.
ISO 2080, Metallic and other inorganic coatings — Surface treatment, metallic and other inorganic
coatings — Vocabulary
3 Terms and definitions
For the purposes of this document, the terms and definitions given in ISO 2080 apply.
ISO and IEC maintain terminological databases for use in standardization at the following addresses:
— ISO Online browsing platform: available at https: //www .iso .org/obp
— IEC Electropedia: available at http: //www .electropedia .org/
4 Principle
The mass of a coating over a measured area is determined by
a) weighing the test specimen before and after dissolving the coating in a reagent or electrolyte that
does not attack the substrate, or
b) weighing the coating after dissolving the substrate in a reagent that does not attack the coating, or
c) dissolving both the coating and the substrate, or the coating alone, and quantitatively analysing the
resulting solution, or
d) weighing the test specimen before and after the coating process, provided that the mass of the
substrate material removed during those pre-treatment steps, after which a weighing would
negatively affect the coating deposition steps, is negligible compared to the mass of the coating.
The surface density of the coating is calculated from the mass and area measurements. Its thickness is
based on the mass, area and density of the coating material.
5 Special equipment
Certain specialized chemical, electrochemical and chemical analysis equipment is required for some of
the specific methods referred to in Table A.1 (see Clauses 8 and 9).
6 Preparation of test specimen
6.1 Size
The specimen should be large enough to permit area and mass measurement of adequate
...
INTERNATIONAL ISO
STANDARD 10111
Second edition
2019-01
Metallic and other inorganic
coatings — Measurement of mass per
unit area — Review of gravimetric and
chemical analysis methods
Revêtements métalliques et autres revêtements inorganiques —
Mesurage de la masse surfacique — Présentation des méthodes
d'analyse gravimétrique et chimique
Reference number
©
ISO 2019
© ISO 2019
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication may
be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting
on the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address
below or ISO’s member body in the country of the requester.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: +41 22 749 01 11
Fax: +41 22 749 09 47
Email: copyright@iso.org
Website: www.iso.org
Published in Switzerland
ii © ISO 2019 – All rights reserved
Contents Page
Foreword .iv
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 1
4 Principle . 2
5 Special equipment . 2
6 Preparation of test specimen . 2
6.1 Size . 2
6.2 Shape . 2
6.3 Edge condition . 2
6.4 Heat treatment . 2
7 Measurement of coated area . 3
7.1 Measurement method . 3
7.2 Surface measuring equipment. 3
7.2.1 Geometrical (projected) surface area . 3
7.2.2 Surface area increase due to roughness (optional) . 3
7.3 Number of measurements . 3
8 Determination of mass of coating by chemical analysis . 4
8.1 General . 4
8.2 Restrictions . 4
9 Gravimetric determination of mass of coating . 4
9.1 Specimen size . 4
9.2 Limitations . 4
9.3 Restrictions . 4
9.4 Gravimetric analysis equipment . 4
9.5 Procedure . 5
9.5.1 General. 5
9.5.2 Difference method with dissolution of the coating . 5
9.5.3 Direct weighing method with dissolution of the substrate . 5
9.5.4 Difference method without dissolution . 5
10 Calculations. 6
10.1 Surface density . 6
10.2 Thickness . 6
Annex A (informative) Reagents for selective dissolution of metal layers . 7
Bibliography .11
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out
through ISO technical committees. Each member body interested in a subject for which a technical
committee has been established has the right to be represented on that committee. International
organizations, governmental and non-governmental, in liaison with ISO, also take part in the work.
ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of
electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are
described in the ISO/IEC Directives, Part 1. In particular, the different approval criteria needed for the
different types of ISO documents should be noted. This document was drafted in accordance with the
editorial rules of the ISO/IEC Directives, Part 2 (see www .iso .org/directives).
Attention is drawn to the possibility that some of the elements of this document may be the subject of
patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of
any patent rights identified during the development of the document will be in the Introduction and/or
on the ISO list of patent declarations received (see www .iso .org/patents).
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation of the voluntary nature of standards, the meaning of ISO specific terms and
expressions related to conformity assessment, as well as information about ISO's adherence to the
World Trade Organization (WTO) principles in the Technical Barriers to Trade (TBT) see www .iso
.org/iso/foreword .html.
This document was prepared by Technical Committee ISO/TC 107, Metallic and other inorganic coatings.
This second edition cancels and replaces the first edition (ISO 10111:2000), which has been technically
revised. The following changes have been made:
a) a gravimetric method has been added for weighing the uncoated substrate and the finished sample;
b) the surface area increase caused by surface roughness has been considered to obtain a more
realistic estimation of local geometric coating thickness (optional);
c) Annex A, which gives reagents for etching or stripping solutions, has been changed to informative
as other solutions can be applied;
d) reagents in Annex A that referred to no longer existing standards or which contain hazardous
chemicals have been removed;
e) outdated and uncited references in the Bibliography have been removed.
Any feedback or questions on this document should be directed to the user’s national standards body. A
complete listing of these bodies can be found at www .iso .org/members .html.
iv © ISO 2019 – All rights reserved
INTERNATIONAL STANDARD ISO 10111:2019(E)
Metallic and other inorganic coatings — Measurement of
mass per unit area — Review of gravimetric and chemical
analysis methods
WARNING — The use of this document can involve hazardous materials, operations and
equipment. It does not purport to address all of the safety or environmental problems associated
with its use. It is the responsibility of users of this document to take appropriate measures
to ensure the safety and health of personnel and the environment prior to application of this
document.
1 Scope
This document gives guidelines for determining the average surface density over a measured area
of anodic oxide or of a coating deposited autocatalytically, mechanically, by chemical conversion,
by electrodeposition, by hot dip galvanizing and by chemical or physical vapour deposition using
gravimetric and other chemical analysis procedures that have attained some degree of national or
international standardization.
A variety of procedures are described and include:
— gravimetric procedures for chemical or electrochemical dissolution of the coating or the substrate
to determine the coating surface density;
— gravimetric procedures for weighing the uncoated substrate and the coated (finished) specimen to
determine the coating surface density;
— analytical procedures that utilize dissolution of the coating for determination of the coating surface
density by instrumental chemical analysis methods.
With the exception of the gravimetric method as described in ISO 3892, this document does not give the
measurement uncertainties of the methods cited.
2 Normative references
The following documents are referred to in the text in such a way that some or all of their content
constitutes requirements of this document. For dated references, only the edition cited applies. For
undated references, the latest edition of the referenced document (including any amendments) applies.
ISO 2080, Metallic and other inorganic coatings — Surface treatment, metallic and other inorganic
coatings — Vocabulary
3 Terms and definitions
For the purposes of this document, the terms and definitions given in ISO 2080 apply.
ISO and IEC maintain terminological databases for use in standardization at the following addresses:
— ISO Online browsing platform: available at https: //www .iso .org/obp
— IEC Electropedia: available at http: //www .electropedia .org/
4 Principle
The mass of a coating over a measured area is determined by
a) weighing the test specimen before and after dissolving the coating in a reagent or electrolyte that
does not attack the substrate, or
b) weighing the coating after dissolving the substrate in a reagent that does not attack the coating, or
c) dissolving both the coating and the substrate, or the coating alone, and quantitatively analysing the
resulting solution, or
d) weighing the test specimen before and after the coating process, provided that the mass of the
substrate material removed during those pre-treatment steps, after which a weighing would
negatively affect the coating deposition steps, is negligible compared to the mass of the coating.
The surface density of the coating is calculated from the mass and area measurements. Its thickness is
based on the mass, area and density of the coating material.
5 Special equipment
Certain specialized chemical, electrochemical and chemical analysis equipment is required for some of
the specific methods referred to in Table A.1 (see Clauses 8 and 9).
6 Preparation of test specimen
6.1 Size
The specimen should be large enough to permit area and mass measurement of adequate
...
NORME ISO
INTERNATIONALE 10111
Deuxième édition
2019-01
Revêtements métalliques et autres
revêtements inorganiques —
Mesurage de la masse surfacique —
Présentation des méthodes d'analyse
gravimétrique et chimique
Metallic and other inorganic coatings — Measurement of mass per
unit area — Review of gravimetric and chemical analysis methods
Numéro de référence
©
ISO 2019
DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2019
Tous droits réservés. Sauf prescription différente ou nécessité dans le contexte de sa mise en œuvre, aucune partie de cette
publication ne peut être reproduite ni utilisée sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique,
y compris la photocopie, ou la diffusion sur l’internet ou sur un intranet, sans autorisation écrite préalable. Une autorisation peut
être demandée à l’ISO à l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.
ISO copyright office
Case postale 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Genève
Tél.: +41 22 749 01 11
Fax: +41 22 749 09 47
E-mail: copyright@iso.org
Web: www.iso.org
Publié en Suisse
ii © ISO 2019 – Tous droits réservés
Sommaire Page
Avant-propos .iv
1 Domaine d'application . 1
2 Références normatives . 1
3 Termes et définitions . 1
4 Principe . 2
5 Équipement spécial . 2
6 Préparation des éprouvettes . 2
6.1 Taille . 2
6.2 Forme . 2
6.3 État des rives . 2
6.4 Traitement thermique . 2
7 Mesurage de la surface revêtue . 3
7.1 Méthode de mesure . 3
7.2 Appareillage de mesure de la surface . 3
7.2.1 Surface géométrique (projetée). 3
7.2.2 Augmentation de la surface due à la rugosité (facultatif) . 3
7.3 Nombre de mesurages . 3
8 Détermination de la masse de revêtement par analyse chimique .4
8.1 Généralités . 4
8.2 Restrictions . 4
9 Détermination gravimétrique de la masse de revêtement . 4
9.1 Dimensions de l'éprouvette . 4
9.2 Limites . 4
9.3 Restrictions . 4
9.4 Appareillage pour analyse gravimétrique . 5
9.5 Mode opératoire . 5
9.5.1 Généralités . 5
9.5.2 Pesée différentielle avec mise en solution du revêtement . 5
9.5.3 Pesée directe avec mise en solution du substrat . 5
9.5.4 Pesée différentielle sans mise en solution . 6
10 Calculs . 6
10.1 Masse surfacique . 6
10.2 Épaisseur . 6
Annexe A (informative) Réactifs pour mise en solution sélective des couches métalliques .7
Bibliographie .11
Avant-propos
L'ISO (Organisation internationale de normalisation) est une fédération mondiale d'organismes
nationaux de normalisation (comités membres de l'ISO). L'élaboration des Normes internationales est
en général confiée aux comités techniques de l'ISO. Chaque comité membre intéressé par une étude
a le droit de faire partie du comité technique créé à cet effet. Les organisations internationales,
gouvernementales et non gouvernementales, en liaison avec l'ISO participent également aux travaux.
L'ISO collabore étroitement avec la Commission électrotechnique internationale (IEC) en ce qui
concerne la normalisation électrotechnique.
Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont
décrites dans les Directives ISO/IEC, Partie 1. Il convient, en particulier, de prendre note des différents
critères d'approbation requis pour les différents types de documents ISO. Le présent document a été
rédigé conformément aux règles de rédaction données dans les Directives ISO/IEC, Partie 2 (voir www
.iso .org/directives).
L'attention est attirée sur le fait que certains des éléments du présent document peuvent faire l'objet de
droits de propriété intellectuelle ou de droits analogues. L'ISO ne saurait être tenue pour responsable
de ne pas avoir identifié de tels droits de propriété et averti de leur existence. Les détails concernant
les références aux droits de propriété intellectuelle ou autres droits analogues identifiés lors de
l'élaboration du document sont indiqués dans l'Introduction et/ou dans la liste des déclarations de
brevets reçues par l'ISO (voir www .iso .org/brevets).
Les appellations commerciales éventuellement mentionnées dans le présent document sont données
pour information, par souci de commodité, à l’intention des utilisateurs et ne sauraient constituer un
engagement.
Pour une explication de la nature volontaire des normes, la signification des termes et expressions
spécifiques de l'ISO liés à l'évaluation de la conformité, ou pour toute information au sujet de l'adhésion
de l'ISO aux principes de l’Organisation mondiale du commerce (OMC) concernant les obstacles
techniques au commerce (OTC), voir www .iso .org/avant -propos.
Le présent document a été élaboré par le comité technique ISO/TC 107, Revêtements métalliques et
autres revêtements inorganiques.
Cette deuxième édition annule et remplace la première édition (ISO 10111:2000) qui a fait l'objet d'une
révision technique. Les modifications suivantes ont été apportées:
a) une méthode gravimétrique a été ajoutée pour la pesée du métal de base nu et de l'échantillon fini;
b) on a considéré que l'augmentation de la surface due à la rugosité de surface conduisait à une
estimation plus réaliste de l'épaisseur du revêtement liée à la géométrie locale (facultatif);
c) l'Annexe A, qui indique les réactifs pour les solutions d'attaque ou de décapage, est devenue
informative puisque d'autres solutions peuvent être appliquées;
d) certains réactifs dans l'Annexe A, qui faisaient référence à des normes qui n'existent plus ou
contenant des produits chimiques dangereux, ont été supprimés;
e) les références bibliographiques obsolètes et non citées ont été supprimées.
Il convient que l’utilisateur adresse tout retour d’information ou toute question concernant le présent
document à l’organisme national de normalisation de son pays. Une liste exhaustive desdits organismes
se trouve à l’adresse www .iso .org/fr/members .html.
iv © ISO 2019 – Tous droits réservés
NORME INTERNATIONALE ISO 10111:2019(F)
Revêtements métalliques et autres revêtements
inorganiques — Mesurage de la masse surfacique —
Présentation des méthodes d'analyse gravimétrique et
chimique
AVERTISSEMENT — Le présent document peut impliquer l'utilisation de produits et la mise
en œuvre de modes opératoires et d'appareillages à caractère dangereux. Il n'est pas censé
aborder tous les problèmes de sécurité ou environnementaux liés à sa mise en œuvre. Il est de
la responsabilité de ceux qui utilisent le présent document de prendre les mesures appropriées
pour garantir la sécurité et la santé du personnel ainsi que la protection environnementale
avant de l'appliquer.
1 Domaine d'application
Le présent document donne des recommandations relatives aux méthodes générales d'analyse
gravimétrique ou chimique de diverses sortes ayant atteint un degré de normalisation à l'échelon
national ou international, utilisées pour la détermination de la masse surfacique moyenne de
revêtements obtenus par dépôt électrolytique, dépôt par immersion, dépôt autocatalytique, matoplastie,
déposition en phase gazeuse par procédé chimique ou physique, anodisation ou conversion chimique.
Il décrit un certain nombre de ces procédés de détermination de la masse surfacique, parmi lesquels:
— des méthodes gravimétriques pour la mise en solution chimique ou électrochimique du dépôt ou du
métal de base permettant la détermination de la masse surfacique du dépôt;
— des méthodes gravimétriques pour la pesée du métal de base nu et de l'éprouvette revêtue (finie)
permettant la détermination de la masse surfacique du dépôt;
— des méthodes analytiques qui utilisent la mise en solution du dépôt en vue d'une détermination de
la masse surfacique du dépôt par des méthodes instrumentales d'analyse chimique.
Sauf pour la méthode gravimétrique telle que décrite dans l'ISO 3892, le présent document n'indique
pas les incertitudes de mesurage liées aux méthodes citées.
2 Références normatives
Les documents suivants sont cités dans le texte de sorte qu’ils constituent, pour tout ou partie de leur
contenu, des exigences du présent document. Pour les références datées, seule l’édition citée s’applique.
Pour les références non datées, la dernière édition du document de référence s'applique (y compris les
éventuels amendements).
ISO 2080, Revêtements métalliques et autres revêtements inorganiques — Traitement de surface,
revêtements métalliques et autres revêtements inorganiques — Vocabulaire
3 Termes et définitions
Pour les besoins du présent document, les termes et les définitions de l'ISO 2080 s’appliquent.
L’ISO et l’IEC tiennent à jour des bases de données terminologiques destinées à être utilisées en
normalisation, consultables aux adresses suivantes:
— ISO Online browsing platform: disponible à l’adresse https: //www .iso .org/obp
— IEC Electropedia: disponible à l’adresse http: //www .electropedia .org/
4 Principe
La masse de revêtement déposée sur une surface mesurée est déterminée par:
a) pesée d'une éprouvette avant et après mise en solution du revêtement dans un réactif ou un
électrolyte qui n'attaque pas le
...
NORME ISO
INTERNATIONALE 10111
Deuxième édition
2019-01
Revêtements métalliques et autres
revêtements inorganiques —
Mesurage de la masse surfacique —
Présentation des méthodes d'analyse
gravimétrique et chimique
Metallic and other inorganic coatings — Measurement of mass per
unit area — Review of gravimetric and chemical analysis methods
Numéro de référence
©
ISO 2019
DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2019
Tous droits réservés. Sauf prescription différente ou nécessité dans le contexte de sa mise en œuvre, aucune partie de cette
publication ne peut être reproduite ni utilisée sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique,
y compris la photocopie, ou la diffusion sur l’internet ou sur un intranet, sans autorisation écrite préalable. Une autorisation peut
être demandée à l’ISO à l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.
ISO copyright office
Case postale 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Genève
Tél.: +41 22 749 01 11
Fax: +41 22 749 09 47
E-mail: copyright@iso.org
Web: www.iso.org
Publié en Suisse
ii © ISO 2019 – Tous droits réservés
Sommaire Page
Avant-propos .iv
1 Domaine d'application . 1
2 Références normatives . 1
3 Termes et définitions . 1
4 Principe . 2
5 Équipement spécial . 2
6 Préparation des éprouvettes . 2
6.1 Taille . 2
6.2 Forme . 2
6.3 État des rives . 2
6.4 Traitement thermique . 2
7 Mesurage de la surface revêtue . 3
7.1 Méthode de mesure . 3
7.2 Appareillage de mesure de la surface . 3
7.2.1 Surface géométrique (projetée). 3
7.2.2 Augmentation de la surface due à la rugosité (facultatif) . 3
7.3 Nombre de mesurages . 3
8 Détermination de la masse de revêtement par analyse chimique .4
8.1 Généralités . 4
8.2 Restrictions . 4
9 Détermination gravimétrique de la masse de revêtement . 4
9.1 Dimensions de l'éprouvette . 4
9.2 Limites . 4
9.3 Restrictions . 4
9.4 Appareillage pour analyse gravimétrique . 5
9.5 Mode opératoire . 5
9.5.1 Généralités . 5
9.5.2 Pesée différentielle avec mise en solution du revêtement . 5
9.5.3 Pesée directe avec mise en solution du substrat . 5
9.5.4 Pesée différentielle sans mise en solution . 6
10 Calculs . 6
10.1 Masse surfacique . 6
10.2 Épaisseur . 6
Annexe A (informative) Réactifs pour mise en solution sélective des couches métalliques .7
Bibliographie .11
Avant-propos
L'ISO (Organisation internationale de normalisation) est une fédération mondiale d'organismes
nationaux de normalisation (comités membres de l'ISO). L'élaboration des Normes internationales est
en général confiée aux comités techniques de l'ISO. Chaque comité membre intéressé par une étude
a le droit de faire partie du comité technique créé à cet effet. Les organisations internationales,
gouvernementales et non gouvernementales, en liaison avec l'ISO participent également aux travaux.
L'ISO collabore étroitement avec la Commission électrotechnique internationale (IEC) en ce qui
concerne la normalisation électrotechnique.
Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont
décrites dans les Directives ISO/IEC, Partie 1. Il convient, en particulier, de prendre note des différents
critères d'approbation requis pour les différents types de documents ISO. Le présent document a été
rédigé conformément aux règles de rédaction données dans les Directives ISO/IEC, Partie 2 (voir www
.iso .org/directives).
L'attention est attirée sur le fait que certains des éléments du présent document peuvent faire l'objet de
droits de propriété intellectuelle ou de droits analogues. L'ISO ne saurait être tenue pour responsable
de ne pas avoir identifié de tels droits de propriété et averti de leur existence. Les détails concernant
les références aux droits de propriété intellectuelle ou autres droits analogues identifiés lors de
l'élaboration du document sont indiqués dans l'Introduction et/ou dans la liste des déclarations de
brevets reçues par l'ISO (voir www .iso .org/brevets).
Les appellations commerciales éventuellement mentionnées dans le présent document sont données
pour information, par souci de commodité, à l’intention des utilisateurs et ne sauraient constituer un
engagement.
Pour une explication de la nature volontaire des normes, la signification des termes et expressions
spécifiques de l'ISO liés à l'évaluation de la conformité, ou pour toute information au sujet de l'adhésion
de l'ISO aux principes de l’Organisation mondiale du commerce (OMC) concernant les obstacles
techniques au commerce (OTC), voir www .iso .org/avant -propos.
Le présent document a été élaboré par le comité technique ISO/TC 107, Revêtements métalliques et
autres revêtements inorganiques.
Cette deuxième édition annule et remplace la première édition (ISO 10111:2000) qui a fait l'objet d'une
révision technique. Les modifications suivantes ont été apportées:
a) une méthode gravimétrique a été ajoutée pour la pesée du métal de base nu et de l'échantillon fini;
b) on a considéré que l'augmentation de la surface due à la rugosité de surface conduisait à une
estimation plus réaliste de l'épaisseur du revêtement liée à la géométrie locale (facultatif);
c) l'Annexe A, qui indique les réactifs pour les solutions d'attaque ou de décapage, est devenue
informative puisque d'autres solutions peuvent être appliquées;
d) certains réactifs dans l'Annexe A, qui faisaient référence à des normes qui n'existent plus ou
contenant des produits chimiques dangereux, ont été supprimés;
e) les références bibliographiques obsolètes et non citées ont été supprimées.
Il convient que l’utilisateur adresse tout retour d’information ou toute question concernant le présent
document à l’organisme national de normalisation de son pays. Une liste exhaustive desdits organismes
se trouve à l’adresse www .iso .org/fr/members .html.
iv © ISO 2019 – Tous droits réservés
NORME INTERNATIONALE ISO 10111:2019(F)
Revêtements métalliques et autres revêtements
inorganiques — Mesurage de la masse surfacique —
Présentation des méthodes d'analyse gravimétrique et
chimique
AVERTISSEMENT — Le présent document peut impliquer l'utilisation de produits et la mise
en œuvre de modes opératoires et d'appareillages à caractère dangereux. Il n'est pas censé
aborder tous les problèmes de sécurité ou environnementaux liés à sa mise en œuvre. Il est de
la responsabilité de ceux qui utilisent le présent document de prendre les mesures appropriées
pour garantir la sécurité et la santé du personnel ainsi que la protection environnementale
avant de l'appliquer.
1 Domaine d'application
Le présent document donne des recommandations relatives aux méthodes générales d'analyse
gravimétrique ou chimique de diverses sortes ayant atteint un degré de normalisation à l'échelon
national ou international, utilisées pour la détermination de la masse surfacique moyenne de
revêtements obtenus par dépôt électrolytique, dépôt par immersion, dépôt autocatalytique, matoplastie,
déposition en phase gazeuse par procédé chimique ou physique, anodisation ou conversion chimique.
Il décrit un certain nombre de ces procédés de détermination de la masse surfacique, parmi lesquels:
— des méthodes gravimétriques pour la mise en solution chimique ou électrochimique du dépôt ou du
métal de base permettant la détermination de la masse surfacique du dépôt;
— des méthodes gravimétriques pour la pesée du métal de base nu et de l'éprouvette revêtue (finie)
permettant la détermination de la masse surfacique du dépôt;
— des méthodes analytiques qui utilisent la mise en solution du dépôt en vue d'une détermination de
la masse surfacique du dépôt par des méthodes instrumentales d'analyse chimique.
Sauf pour la méthode gravimétrique telle que décrite dans l'ISO 3892, le présent document n'indique
pas les incertitudes de mesurage liées aux méthodes citées.
2 Références normatives
Les documents suivants sont cités dans le texte de sorte qu’ils constituent, pour tout ou partie de leur
contenu, des exigences du présent document. Pour les références datées, seule l’édition citée s’applique.
Pour les références non datées, la dernière édition du document de référence s'applique (y compris les
éventuels amendements).
ISO 2080, Revêtements métalliques et autres revêtements inorganiques — Traitement de surface,
revêtements métalliques et autres revêtements inorganiques — Vocabulaire
3 Termes et définitions
Pour les besoins du présent document, les termes et les définitions de l'ISO 2080 s’appliquent.
L’ISO et l’IEC tiennent à jour des bases de données terminologiques destinées à être utilisées en
normalisation, consultables aux adresses suivantes:
— ISO Online browsing platform: disponible à l’adresse https: //www .iso .org/obp
— IEC Electropedia: disponible à l’adresse http: //www .electropedia .org/
4 Principe
La masse de revêtement déposée sur une surface mesurée est déterminée par:
a) pesée d'une éprouvette avant et après mise en solution du revêtement dans un réactif ou un
électrolyte qui n'attaque pas le
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.