EN 485-2:2007

SLOVENSKI STANDARD
01-junij-2007
1DGRPHãþD
SIST EN 485-2:2004
$OXPLQLMLQDOXPLQLMHYH]OLWLQH3ORþHYLQHWUDNRYLLQSORãþHGHO0HKDQVNH
ODVWQRVWL
Aluminium and aluminium alloys - Sheet, strip and plate - Part 2: Mechanical properties
Aluminium und Aluminiumlegierungen - Bänder, Bleche und Platten - Teil 2:
Mechanische Eigenschaften
Aluminium et alliages d'aluminium - Tôles, bandes et tôles épaisses - Partie 2:
Caractéristiques mécaniques
Ta slovenski standard je istoveten z: EN 485-2:2007
ICS:
77.150.10 Aluminijski izdelki Aluminium products
2003-01.Slovenski inštitut za standardizacijo. Razmnoževanje celote ali delov tega standarda ni dovoljeno.

EUROPEAN STANDARD
EN 485-2
NORME EUROPÉENNE
EUROPÄISCHE NORM
April 2007
ICS 77.120.10 Supersedes EN 485-2:2004
English Version
Aluminium and aluminium alloys - Sheet, strip and plate - Part 2:
Mechanical properties
Aluminium et alliages d'aluminium - Tôles, bandes et tôles Aluminium und Aluminiumlegierungen - Bänder, Bleche
épaisses - Partie 2: Caractéristiques mécaniques und Platten - Teil 2: Mechanische Eigenschaften
This European Standard was approved by CEN on 28 February 2007.
CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European
Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national
standards may be obtained on application to the CEN Management Centre or to any CEN member.
This European Standard exists in three official versions (English, French, German). A version in any other language made by translation
under the responsibility of a CEN member into its own language and notified to the CEN Management Centre has the same status as the
official versions.
CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Cyprus, Czech Republic, Denmark, Estonia, Finland,
France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal,
Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom.
EUROPEAN COMMITTEE FOR STANDARDIZATION
COMITÉ EUROPÉEN DE NORMALISATION
EUROPÄISCHES KOMITEE FÜR NORMUNG
Management Centre: rue de Stassart, 36  B-1050 Brussels
© 2007 CEN All rights of exploitation in any form and by any means reserved Ref. No. EN 485-2:2007: E
worldwide for CEN national Members.

Contents Page
Foreword.3
1 Scope.4
2 Normative references.4
3 Requirements.4
4 List of alloys with mechanical property limits.4
4.1 General.4
4.2 Elongation.5
4.3 List of alloys and their mechanical properties .5
Annex A (normative) Rules for rounding.63
Annex B (informative) Explanation of temper designations used in Tables 1 to 46 based on
definitions of EN 515 .64
Bibliography .66

Foreword
This document (EN 485-2:2007) has been prepared by Technical Committee CEN/TC 132 “Aluminium and
aluminium alloys”, the secretariat of which is held by AFNOR.
This European Standard shall be given the status of a national standard, either by publication of an identical
text or by endorsement, at the latest by October 2007, and conflicting national standards shall be withdrawn at
the latest by October 2007.
This document supersedes EN 485-2:2004.
Within its programme of work, Technical Committee CEN/TC 132 entrusted CEN/TC 132/WG 7 "Sheet, strip
and plate" to revise EN 485-2:2004.
EN 485 comprises the following parts under the general tittle, "Aluminium and aluminium alloys — Sheet, strip
and plate".
 Part 1: Technical conditions for inspection and delivery
 Part 2: Mechanical properties
 Part 3: Tolerances on dimensions and form for hot-rolled products
 Part 4: Tolerances on shape and dimensions for cold-rolled products
Besides very slight editorial adjustments in the text and update of normative references, the following
technical changes have been made:
Clauses 3 to 9: Have been moved to prEN 485-1.
Tables 1 to 46: Due to the introduction of new alloys, the tables have been renumbered when
necessary.
New alloys: EN AW-2618A; EN AW-5010; EN AW-5026; EN AW-5059; EN AW-5070; EN AW-
5088; EN AW-6025; EN AW-7010 added.
Attention is drawn to the possibility that some of the elements of this document may be the subject of patent
rights. CEN shall not be held responsible for identifying any or all such patent rights.
CEN/TC 132 affirms it is its policy that in the case when a patentee refuses to grant licences on standardised
standard products under reasonable and not discriminatory conditions then this product shall be removed from
the corresponding standard.
According to the CEN/CENELEC Internal Regulations, the national standards organizations of the following
countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Cyprus, Czech
Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia,
Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain,
Sweden, Switzerland and United Kingdom.
1 Scope
This document specifies the mechanical properties of wrought aluminium and wrought aluminium alloy sheet,
strip and plate for general engineering applications.
It does not apply to semi-finished rolled products in coiled form to be subjected to further rolling (reroll stock)
or to special products such as corrugated, embossed, painted, sheets and strips or to special applications
such as aerospace, can stock, finstock, for which mechanical properties are specified in separate European
Standards.
The chemical composition limits of the alloys are specified in EN 573-3.
Temper designations are defined in Annex B, in compliance with the provisions of EN 515.
2 Normative references
The following referenced documents are indispensable for the application of this document. For dated
references, only the edition cited applies. For undated references, the latest edition of the referenced
document (including any amendments) applies.
prEN 485-1, Aluminium and aluminium alloys — Sheet, strip and plate — Part 1: Technical conditions for
inspection and delivery
EN 10002-1, Metallic materials — Tensile testing — Part 1: Method of test at ambient temperature
ASTM G66, Visual Assessment of Exfoliation Corrosion Susceptibility of 5xxx Series Aluminium Alloys
(ASSET test)
ASTM G67, Standard Test Method for Determining the Susceptibility to Intergranular Corrosion of 5xxx series
Aluminium Alloys by mass loss after exposure to nitric acid (NAMLT test)
3 Requirements
The mechanical properties shall be in conformity with those specified in Clause 4 or those agreed upon
between purchaser and manufacturer and stated on order document.
4 List of alloys with mechanical property limits
4.1 General
Tables 1 to 46 contain mechanical property limits values obtained by tensile testing according to EN 10002-1
after sampling and after sample preparation according to prEN 485-1.
They also contain values of bend radius and hardness following sampling and test methods as described in
prEN 485-1. These values are for information only.
For some alloys they contain provisions related to intergranular corrosion, exfoliation corrosion or stress
corrosion testing, see also prEN 485-1.
4.2 Elongation
The A value is the elongation measured over a gauge length of 50 mm and expressed in percent.
50mm
The A value for elongation is the elongation measured over a gauge length of 5,65 S (where S is the initial
o o
cross-sectional area of the test-piece), and expressed in percent.
4.3 List of alloys and their mechanical properties
Page
Table 1 — Aluminium EN AW-1050A [Al 99,5] 7
Table 2 — Aluminium EN AW-1070A [Al 99,7] 9
Table 3 — Aluminium EN AW-1080A [Al 99,8(A)] 10
Table 4 — Aluminium EN AW-1200 [Al 99,0] 11
Table 5 — Alloy EN AW-2014 [Al Cu4SiMg] 13
Table 6 — Alloy EN AW-2014A [Al Cu4SiMg(A)] 14
Table 7 — Alloy EN AW-2017A [Al Cu4MgSi(A)] 15
Table 8 — Alloy EN AW-2024 [Al Cu4Mg1] 16
Table 9 — Alloy EN AW-2618A [Al Cu2Mg1,5Ni] 17
Table 10 — Alloy EN AW-3003 [Al Mn1Cu] 18
Table 11 — Alloy EN AW-3004 [Al Mn1Mg1] 20
Table 12 — Alloy EN AW-3005 [Al Mn1Mg0,5] 21
Table 13 — Alloy EN AW-3103 [Al Mn1] 22
Table 14 — Alloy EN AW-3105 [Al Mn0,5Mg0,5] 24
Table 15 — Alloy EN AW-4006 [Al Si1Fe] 25
Table 16 — Alloy EN AW-4007 [Al Si1,5Mn] 26
Table 17 — Alloy EN AW-4015 [Al Si2Mn] 26
Table 18— Alloy EN AW-5005 [Al Mg1(B)], alloy EN AW-5005A [Al Mg1(C)] 27
Table 19 — Alloy EN AW-5010 [ AlMg 0,5Mn] 29
Table 20 — Alloy EN AW-5026 [AI Mg4,5 MnSiFe] 30
Table 21 — Alloy EN AW-5040 [Al Mg1,5Mn] 30
Table 22 — Alloy EN AW-5049 [Al Mg2Mn0,8] 31
Table 23 — Alloy EN AW-5050 [Al Mg1,5(C)] 33
Table 24 — Alloy EN AW-5052 [Al Mg2,5] 35
Table 25 — Alloy EN AW-5059 [Al Mg5,5MnZnZr] 36
Table 26 — Alloy EN AW-5070 [Al Mg4MnZn] 37
Table 27 — Alloy EN AW-5083 [Al Mg4,5Mn0,7] 38
Table 28 — Alloy EN AW-5086 [Al Mg4] 40
Table 29 — Alloy EN AW-5088 [AlMg5Mn0,4] 41
Table 30 — Alloy EN AW-5154A [Al Mg3,5(A)] 42
Table 31 — Alloy EN AW-5182 [Al Mg4,5Mn0,4] 44
Table 32 — Alloy EN AW-5251 [Al Mg2] 45
Table 33 — Alloy EN AW-5383 [Al Mg4,5Mn0,9] 47
Table 34 — Alloy EN AW-5449 [Al Mg2Mn0,8(B)] 48
Table 35 — Alloy EN AW-5454 [Al Mg3Mn] 49
Table 36 — Alloy EN AW-5754 [Al Mg3] 51
Table 37 — Alloy EN AW-6016 [Al Si1,2Mg0,4] 53
Table 38 — Alloy EN AW-6025 [Al Mg2,5SiMnCu] 53
Table 39 — Alloy EN AW-6061 [Al Mg1SiCu] 54
Table 40 — Alloy EN AW-6082 [Al Si1MgMn] 55
Table 41 — Alloy EN AW-7010 [Al Zn6MgCu] 56
Table 42 — Alloy EN AW-7020 [Al Zn4,5Mg1] 58
Table 43 — Alloy EN AW-7021 [Al Zn5,5Mg1,5] 59
Table 44 — Alloy EN AW-7022 [Al Zn5Mg3Cu] 59
Table 45 — Alloy EN AW-7075 [Al Zn5,5MgCu] 60
Table 46 — Alloy EN AW-8011A [Al FeSi(A)] 62

Table 1 — Aluminium EN AW-1050A [Al 99,5]
a
Temper Specified R R Elongation Hardness
Bend radius
m p0,2
thickness
min.
a
mm MPa MPa %
HBW
over up to min. max. min. max. A A 180° 90°
50 mm
a
150,0 60
F ≥ 2,5
O/H111 0,2 0,5 65 95 20 20 0 t 0 t 20
0,5 1,5 65 95 20 22 0 t 0 t 20
1,5 3,0 65 95 20 26 0 t 0 t 20
3,0 6,0 65 95 20 29 0,5 t 0,5 t 20
6,0 12,5 65 95 20 35 1,0 t 1,0 t 20
12,5 80,0 65 95 20  32  20
H112 12,5 75 30 20  23
≥ 6,0
12,5 80,0 70 25  20  22
H12 0,2 0,5 85 125 65 2 0,5 t 0 t 28
0,5 1,5 85 125 65 4 0,5 t 0 t 28
1,5 3,0 85 125 65 5 0,5 t 0,5 t 28
3,0 6,0 85 125 65 7 1,0 t 1,0 t 28
6,0 12,5 85 125 65 9  2,0 t 28
12,5 40,0 85 125 65  9  28
H14 0,2 0,5 105 145 85 2 1,0 t 0 t 34
1,0 t 0,5 t
0,5 1,5 105 145 85 2 34
1,5 3,0 105 145 85 4 1,0 t 1,0 t 34
1,5 t
3,0 6,0 105 145 85 5  34
6,0 12,5 105 145 85 6  2,5 t 34
12,5 25,0 105 145 85  6  34
H16 0,2 0,5 120 160 100 1  0,5 t 39
0,5 1,5 120 160 100 2  1,0 t 39
1,5 4,0 120 160 100 3  1,5 t 39
H18 0,2 0,5 135 120 1  1,0 t 42
2,0 t
0,5 1,5 140 120 2  42
1,5 3,0 140 120 2  3,0 t 42
H19 0,2 0,5 155 140 1  45
0,5 1,5 150 130 1  45
1,5 3,0 150 130 1  45
0,5 t 0 t
H22 0,2 0,5 85 125 55 4 27
0,5 1,5 85 125 55 5 0,5 t 0 t 27
1,5 3,0 85 125 55 6 0,5 t 0,5 t 27
3,0 6,0 85 125 55 11 1,0 t 1,0 t 27
2,0 t
6,0 12,5 85 125 55 12  27
Table 1 (continued)
a
Temper Specified R R Elongation Hardness
Bend radius
m p0,2
thickness
min.
a
mm MPa MPa % HBW
over up to min. max. min. max. A A 180° 90°
50 mm
H24 0,2 0,5 105 145 75 3 1,0 t 0 t 33
1,0 t 0,5 t
0,5 1,5 105 145 75 4 33
1,5 3,0 105 145 75 5 1,0 t 1,0 t 33
1,5 t 1,5 t
3,0 6,0 105 145 75 8 33
6,0 12,5 105 145 75 8  2,5 t 33
H26 0,2 0,5 120 160 90 2  0,5 t 38
0,5 1,5 120 160 90 3  1,0 t 38
1,5 4,0 120 160 90 4  1,5 t 38
1,0 t
H28 0,2 0,5 140 110 2  41
0,5 1,5 140 110 2  2,0 t 41
3,0 t
1,5 3,0 140 110 3  41
a
For information only.
Table 2 — Aluminium EN AW-1070A [Al 99,7]
a
Temper Specified R R Elongation Hardness
Bend radius
m p0,2
thickness
min.
a
mm MPa MPa %
HBW
over up to min. max. min. max. A A 180° 90°
50 mm
a
25,0 60
F ≥ 2,5
0 t 0 t
O/H111 0,2 0,5 60 90 15 23 18
0,5 1,5 60 90 15 25 0 t 0 t 18
0 t 0 t
1,5 3,0 60 90 15 29 18
3,0 6,0 60 90 15 32 0,5 t 0,5 t 18
0,5 t 0,5 t
6,0 12,5 60 90 15 35 18
12,5 25,0 60 90 15  32  18
H112 12,5 70 20 20
≥ 6,0
12,5 25,0 70   20
0,5 t 0 t
H12 0,2 0,5 80 120 55 5 26
0,5 1,5 80 120 55 6 0,5 t 0 t 26
1,5 3,0 80 120 55 7 0,5 t 0,5 t 26
3,0 6,0 80 120 55 9  1,0 t 26
2,0 t
6,0 12,5 80 120 55 12  26
H14 0,2 0,5 100 140 70 4 0,5 t 0 t 32
0,5 1,5 100 140 70 4 0,5 t 0,5 t 32
1,5 3,0 100 140 70 5 1,0 t 1,0 t 32
3,0 6,0 100 140 70 6  1,5 t 32
6,0 12,5 100 140 70 7  2,5 t 32
H16 0,2 0,5 110 150 90 2 1,0 t 0,5 t 36
0,5 1,5 110 150 90 2 1,0 t 1,0 t 36
1,5 4,0 110 150 90 3 1,0 t 1,0 t 36
H18 0,2 0,5 125 105 2  1,0 t 40
0,5 1,5 125 105 2  2,0 t 40
1,5 3,0 125 105 2  2,5 t 40
0,5 t 0 t
H22 0,2 0,5 80 120 50 7 26
0,5 1,5 80 120 50 8 0,5 t 0 t 26
0,5 t 0,5 t
1,5 3,0 80 120 50 10 26
3,0 6,0 80 120 50 12  1,0 t 26
6,0 12,5 80 120 50 15  2,0 t 26
H24 0,2 0,5 100 140 60 5 0,5 t 0 t 31
0,5 t 0,5 t
0,5 1,5 100 140 60 6 31
1,5 3,0 100 140 60 7 1,0 t 1,0 t 31
3,0 6,0 100 140 60 9  1,5 t 31
6,0 12,5 100 140 60 11  2,5 t 31
H26 0,2 0,5 110 150 80 3  0,5 t 35
1,0 t
0,5 1,5 110 150 80 3  35
1,5 4,0 110 150 80 4  1,0 t 35
a
For information only.
Table 3 — Aluminium EN AW-1080A [Al 99,8(A)]
a
Temper Specified R R Elongation Hardness
Bend radius
m p0,2
thickness
min.
a
mm MPa MPa %
HBW
over up to min. max. min. max. A A 180° 90°
50 mm
a
25,0 60
F ≥ 2,5
0 t 0 t
O/H111 0,2 0,5 60 90 15 26 18
0,5 1,5 60 90 15 28 0 t 0 t 18
0 t 0 t
1,5 3,0 60 90 15 31 18
3,0 6,0 60 90 15 35 0,5 t 0,5 t 18
0,5 t 0,5 t
6,0 12,5 60 90 15 35 18
H112 12,5 70  20
≥ 6,0
12,5 25,0 70   20
H12 0,2 0,5 80 120 55 5 0,5 t 0 t 26
0,5 t 0 t
0,5 1,5 80 120 55 6 26
1,5 3,0 80 120 55 7 0,5 t 0,5 t 26
3,0 6,0 80 120 55 9  1,0 t 26
6,0 12,5 80 120 55 12  2,0 t 26
H14 0,2 0,5 100 140 70 4 0,5 t 0 t 32
0,5 1,5 100 140 70 4 0,5 t 0,5 t 32
1,5 3,0 100 140 70 5 1,0 t 1,0 t 32
3,0 6,0 100 140 70 6  1,5 t 32
6,0 12,5 100 140 70 7  2,5 t 32
1,0 t 0,5 t
H16 0,2 0,5 110 150 90 2 36
0,5 1,5 110 150 90 2 1,0 t 1,0 t 36
1,5 4,0 110 150 90 3 1,0 t 1,0 t 36
H18 0,2 0,5 125 105 2  1,0 t 40
2,0 t
0,5 1,5 125 105 2  40
1,5 3,0 125 105 2  2,5 t 40
H22 0,2 0,5 80 120 50 8 0,5 t 0 t 26
0,5 t 0 t
0,5 1,5 80 120 50 9 26
1,5 3,0 80 120 50 11 0,5 t 0,5 t 26
1,0 t
3,0 6,0 80 120 50 13  26
6,0 12,5 80 120 50 15  2,0 t 26
H24 0,2 0,5 100 140 60 5 0,5 t 0 t 31
0,5 1,5 100 140 60 6 0,5 t 0,5 t 31
1,0 t 1,0 t
1,5 3,0 100 140 60 7 31
3,0 6,0 100 140 60 9  1,5 t 31
6,0 12,5 100 140 60 11  2,5 t 31
0,5 t
H26 0,2 0,5 110 150 80 3  35
0,5 1,5 110 150 80 3  1,0 t 35
1,0 t
1,5 4,0 110 150 80 4  35
a
For information only.
Table 4 — Aluminium EN AW-1200 [Al 99,0]
a
Temper Specified R R Elongation Hardness
Bend radius
m p0,2
thickness min.
a
mm MPa MPa %
HBW
over up to min. max. min. max. A A 180° 90°
50 mm
a
≥ 2,5 150,0 75
F
O/H111 0,2 0,5 75 105 25 19 0 t 0 t 23
0,5 1,5 75 105 25 21 0 t 0 t 23
1,5 3,0 75 105 25 24 0 t 0 t 23
3,0 6,0 75 105 25 28 0,5 t 0,5 t 23
6,0 12,5 75 105 25 33 1,0 t 1,0 t 23
12,5 80,0 75 105 25  30  23
H112 ≥ 6,0 12,5 85 35 16  26
12,5 80,0 80 30  16  24
0,5 t 0 t
H12 0,2 0,5 95 135 75 2 31
0,5 1,5 95 135 75 4 0,5 t 0 t 31
1,5 3,0 95 135 75 5 0,5 t 0,5 t 31
3,0 6,0 95 135 75 6 1,0 t 1,0 t 31
6,0 12,5 95 135 75 8  2,0 t 31
12,5 40,0 95 135 75  8  31
1,0 t 0 t
H14 0,2 0,5 105 155 95 1 37
0,5 1,5 115 155 95 3 1,0 t 0,5 t 37
1,0 t 1,0 t
1,5 3,0 115 155 95 4 37
3,0 6,0 115 155 95 5 1,5 t 1,5 t 37
2,5 t
6,0 12,5 115 155 90 6  37
12,5 25,0 115 155 90  6  37
H16 0,2 0,5 120 170 110 1  0,5 t 42
0,5 1,5 130 170 115 2  1,0 t 42
1,5 4,0 130 170 115 3  1,5 t 42
1,0 t
H18 0,2 0,5 150 130 1  45
0,5 1,5 150 130 2  2,0 t 45
3,0 t
1,5 3,0 150 130 2  45
H19 0,2 0,5 160 140 1  48
0,5 1,5 160 140 1  48
1,5 3,0 160 140 1  48
Table 4 (continued)
a
Temper Specified R R Elongation Hardness
Bend radius
m p0,2
thickness min.
mm MPa MPa %
a
over up to min. max. min. max. A A 180° 90°
HBW
50 mm
0,5 t 0 t
H22 0,2 0,5 95 135 65 4 30
0,5 1,5 95 135 65 5 0,5 t 0 t 30
0,5 t 0,5 t
1,5 3,0 95 135 65 6 30
3,0 6,0 95 135 65 10 1,0 t 1,0 t 30
2,0 t
6,0 12,5 95 135 65 10  30
H24 0,2 0,5 115 155 90 3 1,0 t 0 t 37
0,5 1,5 115 155 90 4 1,0 t 0,5 t 37
1,5 3,0 115 155 90 5 1,0 t 1,0 t 37
3,0 6,0 115 155 90 7  1,5 t 37
6,0 12,5 115 155 85 9  2,5 t 36
H26 0,2 0,5 130 170 105 2  0,5 t 41
1,0 t
0,5 1,5 130 170 105 3  41
1,5 4,0 130 170 105 4  1,5 t 41
a
For information only.
Table 5 — Alloy EN AW-2014 [Al Cu4SiMg]
a
Temper Specified R R Elongation Hardness
Bend radius
m p0,2
thickness min.
a
mm MPa MPa %
HBW
over up to min. max. min. max. A A 180° 90°
50 mm
O 1,5 220 140 12 0,5 t 0 t 55
≥ 0,4
1,5 3,0 220 140 13 1,0 t 1,0 t 55
3,0 6,0 220 140 16  1,5 t 55
6,0 9,0 220 140 16  2,5 t 55
9,0 12,5 220 140 16  4,0 t 55
12,5 25,0 220  10  55
T3 ≥ 0,4 1,5 395 245 14  111
1,5 6,0 400 245 14  112
b b
T4 ≥ 0,4 1,5 395 240 14 110
3,0 t 3,0 t
b b
T451 1,5 6,0 395 240 14 110
5,0 t 5,0 t
b
6,0 12,5 400 250 14  112
8,0 t
12,5 40,0 400 250  10  112
40,0 100,0 395 250  7  111
T42 6,0 395 230 14  110
≥ 0,4
6,0 12,5 400 235 14  111
12,5 25,0 400 235  12  111
b
T6 ≥ 0,4 1,5 440 390 6  133
5,0 t
b
T651 1,5 6,0 440 390 7  7,0 t 133
b
6,0 12,5 450 395 7  135
10 t
12,5 40,0 460 400  6  138
40,0 60,0 450 390  5  135
60,0 80,0 435 380  4  131
80,0 100,0 420 360  4  126
100,0 125,0 410 350  4  123
125,0 160,0 390 340  2
T62 12,5 440 390 7  133
≥ 0,4
12,5 25,0 450 395  6  135
Whenever a new application of this alloy is contemplated, and if this application involves special properties such as corrosion
resistance, toughness, fatigue strength, it is strongly recommended that the user consult the producer in order to make a precise and
appropriate selection of the material.
a
For information only.
b
Appreciably smaller cold bend radii can be achieved immediately after quenching.

Table 6 — Alloy EN AW-2014A [Al Cu4SiMg(A)]
a
Temper Specified R R Elongation Hardness
Bend radius
m p0,2
thickness min.
a
mm MPa MPa %
HBW
over up to min. max. min. max. A A 180° 90°
50 mm
1,0 t
O ≥ 0,2 0,5 235 110  55
2,0 t
0,5 1,5 235 110 14  55
1,5 3,0 235 110 16  2,0 t 55
2,0 t
3,0 6,0 235 110 16  55
b
T4 ≥ 0,2 0,5 400 225   3,0 t 110
b
T451 0,5 1,5 400 225 13  110
3,0 t
b
1,5 6,0 400 225 14  110
5,0 t
6,0 12,5 400 250 14
12,5 25,0 400 250  12
25,0 40,0 400 250  10
40,0 80,0 395 250  7
b
T6 0,5 440 380   150
≥ 0,2 5,0 t
b
T651 0,5 1,5 440 380 6  5,0 t 150
b
1,5 3,0 440 380 7  150
6,0 t
b
3,0 6,0 440 380 8  6,0 t 150
6,0 12,5 460 410 8
12,5 25,0 460 410  6
25,0 40,0 450 400  5
40,0 60,0 430 390  5
60,0 90,0 430 390  4
90,0 115,0 420 370  4
115,0 140,0 410 350  4
Whenever a new application of this alloy is contemplated, and if this application involves special properties such as corrosion
resistance, toughness, fatigue strength, it is strongly recommended that the user consult the producer in order to make a precise and
appropriate selection of the material.
a
For information only.
b
Appreciably smaller cold bend radii can be achieved immediately after quenching.

Table 7 — Alloy EN AW-2017A [Al Cu4MgSi(A)]
a
Temper Specified R R Elongation Hardness
Bend radius
m p0,2
thickness min.
a
mm MPa MPa %
HBW
over up to min. max. min. max. A A 180° 90°
50 mm
0,5 t 0 t
O ≥ 0,4 1,5 225 145 12 55
1,0 t 1,0 t
1,5 3,0 225 145 14 55
3,0 6,0 225 145 13  1,5 t 55
2,5 t
6,0 9,0 225 145 13  55
9,0 12,5 225 145 13  4,0 t 55
12,5 25,0 225 145 12  55
b b
T4 ≥ 0,4 1,5 390 245 14 3,0 t 3,0 t 110
b b
T451 1,5 6,0 390 245 15 110
5,0 t 5,0 t
b
6,0 12,5 390 260 13  111
8,0 t
12,5 40,0 390 250  12  110
40,0 60,0 385 245  12  108
60,0 80,0 370 240  7
80,0 120,0 360 240  6  105
120,0 150,0 350 240  4  101
150,0 180,0 330 220  2
180,0 200,0 300 200  2
T452 150,0 180,0 330 220  2
180,0 200,0 300 200  2
T42 3,0 390 235 14  109
≥ 0,4
3,0 12,5 390 235 15  109
12,5 25,0 390 235  12  109
Whenever a new application of this alloy is contemplated, and if this application involves special properties such as corrosion resistance,
toughness, fatigue strength, it is strongly recommended that the user consult the producer in order to make a precise and appropriate
selection of the material.
a
For information only.
b
Appreciably smaller cold bend radii can be achieved immediately after quenching.

Table 8 — Alloy EN AW-2024 [Al Cu4Mg1]
a
Temper Specified R R Elongation Hardness
Bend radius
m p0,2
thickness
min.
a
mm MPa MPa %
HBW
over up to min. max. min. max. A A 180° 90°
50 mm
0,5 t 0 t
O ≥ 0,4 1,5 220 140 12 55
2,0 t 1,0 t
1,5 3,0 220 140 13 55
3,0 6,0 220 140 13 3,0 t 1,5 t 55
2,5 t
6,0 9,0 220 140 13  55
9,0 12,5 220 140 13  4,0 t 55
12,5 25,0 220  11  55
T4 ≥ 0,4 1,5 425 275 12 4,0 t 120
1,5 6,0 425 275 14 5,0 t 120
b b
T3 1,5 435 290 12 123
≥ 0,4 4,0 t 4,0 t
b b
T351 1,5 3,0 435 290 14 4,0 t 4,0 t 123
b b
3,0 6,0 440 290 14 124
5,0 t 5,0 t
b
6,0 12,5 440 290 13  8,0 t 124
12,5 40,0 430 290  11  122
40,0 80,0 420 290  8  120
80,0 100,0 400 285  7  115
100,0 120,0 380 270  5  110
120,0 150,0 360 250  5  104
T42 6,0 425 260 15  119
≥ 0,4
6,0 12,5 425 260 12  119
12,5 25,0 420 260  8  118
T8 1,5 460 400 5  138
≥ 0,4
T851 1,5 6,0 460 400 6  138
6,0 12,5 460 400 5  138
12,5 25,0 455 400  4  137
25,0 40,0 455 395  4  136
T62 ≥ 0,4 12,5 440 345 5  129
12,5 25,0 435 345  4  128
Whenever a new application of this alloy is contemplated, and if this application involves special properties such as corrosion
resistance, toughness, fatigue strength, it is strongly recommended that the user consult the producer in order to make a precise and
appropriate selection of the material.
a
For information only.
b
Appreciably smaller cold bend radii can be achieved immediately after quenching.

Table 9 — Alloy EN AW-2618A [Al Cu2Mg1,5Ni]
a
Temper Specified R R Elongation Hardness
Bend radius
m p0,2
thickness
min.
a
mm MPa MPa %
HBW
over up to min. max. min. max. A A 180° 90°
50 mm
T851 > 6,0 12,5 420 375 5
12,5 40,0 420 375  5
40,0 80,0 410 370  5
80,0 100,0 405 365  4
100,0 140,0 395 360  4
a
No data available.
Table 10 — Alloy EN AW-3003 [Al Mn1Cu]
a
Temper Specified R R Elongation Hardness
Bend radius
m p0,2
thickness
min.
a
mm MPa MPa %
HBW
over up to min. max. min. max. A A 180° 90°
50 mm
a
F ≥ 2,5 80,0 95
O/H111 0,2 0,5 95 135 35 15 0 t 0 t 28
0,5 1,5 95 135 35 17 0 t 0 t 28
1,5 3,0 95 135 35 20 0 t 0 t 28
3,0 6,0 95 135 35 23 1,0 t 1,0 t 28
6,0 12,5 95 135 35 24  1,5 t 28
12,5 50,0 95 135 35  23  28
H112 ≥ 6,0 12,5 115 70 10  35
12,5 80,0 100 40  18  29
H12 0,2 0,5 120 160 90 3 1,5 t 0 t 38
0,5 1,5 120 160 90 4 1,5 t 0,5 t 38
1,5 3,0 120 160 90 5 1,5 t 1,0 t 38
3,0 6,0 120 160 90 6  1,0 t 38
6,0 12,5 120 160 90 7  2,0 t 38
12,5 40,0 120 160 90  8  38
2,0 t 0,5 t
H14 0,2 0,5 145 185 125 2 46
0,5 1,5 145 185 125 2 2,0 t 1,0 t 46
2,0 t 1,0 t
1,5 3,0 145 185 125 3 46
3,0 6,0 145 185 125 4  2,0 t 46
2,5 t
6,0 12,5 145 185 125 5  46
12,5 25,0 145 185 125  5  46
H16 0,2 0,5 170 210 150 1 2,5 t 1,0 t 54
0,5 1,5 170 210 150 2 2,5 t 1,5 t 54
1,5 4,0 170 210 150 2 2,5 t 2,0 t 54
1,5 t
H18 0,2 0,5 190 170 1  60
0,5 1,5 190 170 2  2,5 t 60
3,0 t
1,5 3,0 190 170 2  60
H19 0,2 0,5 210 180 1  65
0,5 1,5 210 180 2  65
1,5 3,0 210 180 2  65
H22 0,2 0,5 120 160 80 6 1,0 t 0 t 37
1,0 t 0,5 t
0,5 1,5 120 160 80 7 37
1,5 3,0 120 160 80 8 1,0 t 1,0 t 37
1,0 t
3,0 6,0 120 160 80 9  37
6,0 12,5 120 160 80 11  2,0 t 37

Table 10 (continued)
a
Temper Specified R R Elongation Hardness
Bend radius
m p0,2
thickness
min.
a
mm MPa MPa %
HBW
over up to min. max. min. max. A A 180° 90°
50 mm
1,5 t 0,5 t
H24 0,2 0,5 145 185 115 4 45
0,5 1,5 145 185 115 4 1,5 t 1,0 t 45
1,5 t 1,0 t
1,5 3,0 145 185 115 5 45
3,0 6,0 145 185 115 6  2,0 t 45
2,5 t
6,0 12,5 145 185 110 8  45
H26 0,2 0,5 170 210 140 2 2,0 t 1,0 t 53
0,5 1,5 170 210 140 3 2,0 t 1,5 t 53
1,5 4,0 170 210 140 3 2,0 t 2,0 t 53
H28 0,2 0,5 190 160 2  1,5 t 59
2,5 t
0,5 1,5 190 160 2  59
1,5 3,0 190 160 3  3,0 t 59
a
For information only.
Table 11 — Alloy EN AW-3004 [Al Mn1Mg1]
a
Temper Specified R R Elongation Hardness
Bend radius
m p0,2
thickness
min.
a
mm MPa MPa %
HBW
over up to min. max. min. max. A A 180° 90°
50 mm
a
≥ 2,5 80,0 155
F
0 t 0 t
O/H111 0,2 0,5 155 200 60 13 45
0,5 1,5 155 200 60 14 0 t 0 t 45
0,5 t 0 t
1,5 3,0 155 200 60 15 45
3,0 6,0 155 200 60 16 1,0 t 1,0 t 45
2,0 t
6,0 12,5 155 200 60 16  45
12,5 50,0 155 200 60  14  45
H12 0,2 0,5 190 240 155 2 1,5 t 0 t 59
0,5 1,5 190 240 155 3 1,5 t 0,5 t 59
1,5 3,0 190 240 155 4 2,0 t 1,0 t 59
3,0 6,0 190 240 155 5  1,5 t 59
H14 0,2 0,5 220 265 180 1 2,5 t 0,5 t 67
2,5 t 1,0 t
0,5 1,5 220 265 180 2 67
1,5 3,0 220 265 180 2 2,5 t 1,5 t 67
2,0 t
3,0 6,0 220 265 180 3  67
H16 0,2 0,5 240 285 200 1 3,5 t 1,0 t 73
0,5 1,5 240 285 200 1 3,5 t 1,5 t 73
1,5 4,0 240 285 200 2  2,5 t 73
H18 0,2 0,5 260 230 1  1,5 t 80
2,5 t
0,5 1,5 260 230 1  80
1,5 3,0 260 230 2  80
H19 0,2 0,5 270 240 1  83
0,5 1,5 270 240 1  83
H22/H32 0,2 0,5 190 240 145 4 1,0 t 0 t 58
1,0 t 0,5 t
0,5 1,5 190 240 145 5 58
1,5 3,0 190 240 145 6 1,5 t 1,0 t 58
1,5 t
3,0 6,0 190 240 145 7  58
H24/H34 0,2 0,5 220 265 170 3 2,0 t 0,5 t 66
0,5 1,5 220 265 170 4 2,0 t 1,0 t 66
1,5 3,0 220 265 170 4 2,0 t 1,5 t 66
H26/H36 0,2 0,5 240 285 190 3 3,0 t 1,0 t 72
3,0 t 1,5 t
0,5 1,5 240 285 190 3 72
1,5 3,0 240 285 190 3  2,5 t 72
H28/H38 0,2 0,5 260 220 2  1,5 t 79
0,5 1,5 260 220 3  2,5 t 79
a
For information only.
Table 12 — Alloy EN AW-3005 [Al Mn1Mg0,5]
a
Temper Specified R R Elongation Hardness
Bend radius
m p0,2
thickness
min.
a
mm MPa MPa %
HBW
over up to min. max. min. max. A A 180° 90°
50 mm
a
≥ 2,5 80,0 115
F
O/H111 0,2 0,5 115 165 45 12 0 t 0 t 33
0,5 1,5 115 165 45 14 0 t 0 t 33
1,5 3,0 115 165 45 16 1,0 t 0,5 t 33
3,0 6,0 115 165 45 19  1,0 t 33
1,5 t 0 t
H12 0,2 0,5 145 195 125 3 46
0,5 1,5 145 195 125 4 1,5 t 0,5 t 46
2,0 t 1,0 t
1,5 3,0 145 195 125 4 46
3,0 6,0 145 195 125 5  1,5 t 46
H14 0,2 0,5 170 215 150 1 2,5 t 0,5 t 54
0,5 1,5 170 215 150 2 2,5 t 1,0 t 54
1,5 3,0 170 215 150 2  1,5 t 54
3,0 6,0 170 215 150 3  2,0 t 54
H16 0,2 0,5 195 240 175 1  1,0 t 61
1,5 t
0,5 1,5 195 240 175 2  61
1,5 4,0 195 240 175 2  2,5 t 61
H18 0,2 0,5 220 200 1  1,5 t 69
0,5 1,5 220 200 2  2,5 t 69
1,5 3,0 220 200 2  69
H19 0,2 0,5 235 210 1  73
0,5 1,5 235 210 1  73
H22 0,2 0,5 145 195 110 5 1,0 t 0 t 45
0,5 1,5 145 195 110 5 1,0 t 0,5 t 45
1,5 3,0 145 195 110 6 1,5 t 1,0 t 45
3,0 6,0 145 195 110 7  1,5 t 45
H24 0,2 0,5 170 215 130 4 1,5 t 0,5 t 52
1,5 t 1,0 t
0,5 1,5 170 215 130 4 52
1,5 3,0 170 215 130 4  1,5 t 52
H26 0,2 0,5 195 240 160 3  1,0 t 60
0,5 1,5 195 240 160 3  1,5 t 60
1,5 3,0 195 240 160 3  2,5 t 60
1,5 t
H28 0,2 0,5 220 190 2  68
0,5 1,5 220 190 2  2,5 t 68
1,5 3,0 220 190 3  68
a
For information only.
Table 13 — Alloy EN AW-3103 [Al Mn1]
a
Temper Specified R R Elongation Hardness
Bend radius
m p0,2
thickness
min.
a
mm MPa MPa %
HBW
over up to min. max. min. max. A A 180° 90°
50 mm
a
80,0 90
F ≥ 2,5
O/H111 0,2 0,5 90 130 35 17 0 t 0 t 27
0 t 0 t
0,5 1,5 90 130 35 19 27
1,5 3,0 90 130 35 21 0 t 0 t 27
1,0 t 1,0 t
3,0 6,0 90 130 35 24 27
6,0 12,5 90 130 35 28  1,5 t 27
12,5 50,0 90 130 35  25  27
H112 12,5 110 70 10  34
≥ 6,0
12,5 80,0 95 40  18  28
H12 0,2 0,5 115 155 85 3 1,5 t 0 t 36
1,5 t 0,5 t
0,5 1,5 115 155 85 4 36
1,5 3,0 115 155 85 5 1,5 t 1,0 t 36
3,0 6,0 115 155 85 6  1,0 t 36
6,0 12,5 115 155 85 7  2,0 t 36
12,5 40,0 115 155 85  8  36
H14 0,2 0,5 140 180 120 2 2,0 t 0,5 t 45
0,5 1,5 140 180 120 2 2,0 t 1,0 t 45
1,5 3,0 140 180 120 3 2,0 t 1,0 t 45
3,0 6,0 140 180 120 4  2,0 t 45
6,0 12,5 140 180 120 5  2,5 t 45
12,5 25,0 140 180 120  5  45
2,5 t 1,0 t
H16 0,2 0,5 160 200 145 1 51
0,5 1,5 160 200 145 2 2,5 t 1,5 t 51
2,5 t 2,0 t
1,5 4,0 160 200 145 2 51
4,0 8,0 160 200 145 2 2,0 t 1,5 t 51
H18 0,2 0,5 185 165 1  1,5 t 58
0,5 1,5 185 165 2  2,5 t 58
1,5 3,0 185 165 2  3,0 t 58
H19 0,2 0,5 200 175 1  62
0,5 1,5 200 175 2  62
1,5 3,0 200 175 2  62
H22 0,2 0,5 115 155 75 6 1,0 t 0 t 36
1,0 t 0,5 t
0,5 1,5 115 155 75 7 36
1,5 3,0 115 155 75 8 1,0 t 1,0 t 36
3,0 6,0 115 155 75 9  1,0 t 36
6,0 12,5 115 155 75 11  2,0 t 36

Table 13 (continued)
a
Temper Specified R R Elongation Hardness
Bend radius
m p0,2
thickness
min.
a
mm MPa MPa %
HBW
over up to min. max. min. max. A A 180° 90°
50 mm
1,5 t 0,5 t
H24 0,2 0,5 140 180 110 4 44
0,5 1,5 140 180 110 4 1,5 t 1,0 t 44
1,5 t 1,0 t
1,5 3,0 140 180 110 5 44
3,0 6,0 140 180 110 6  2,0 t 44
2,5 t
6,0 12,5 140 180 110 8  44
H26 0,2 0,5 160 200 135 2 2,0 t 1,0 t 50
0,5 1,5 160 200 135 3 2,0 t 1,5 t 50
1,5 4,0 160 200 135 3 2,0 t 2,0 t 50
H28 0,2 0,5 185 155 2  1,5 t 58
2,5 t
0,5 1,5 185 155 2  58
1,5 3,0 185 155 3  3,0 t 58
a
For information only.
Table 14 — Alloy EN AW-3105 [Al Mn0,5Mg0,5]
a
Temper Specified R R Elongation Hardness
Bend radius
m p0,2
thickness
min.
a
mm MPa MPa %
HBW
over up to min. max. min. max. A A 180° 90°
50 mm
a
≥ 2,5 80,0 100
F
O/H111 0,2 0,5 100 155 40 14 0 t 29
0,5 1,5 100 155 40 15 0 t 29
1,5 3,0 100 155 40 17 0,5 t 29
H12 0,2 0,5 130 180 105 3 1,5 t 41
1,5 t
0,5 1,5 130 180 105 4  41
1,5 3,0 130 180 105 4 1,5 t 41
H14 0,2 0,5 150 200 130 2 2,5 t 48
0,5 1,5 150 200 130 2 2,5 t 48
1,5 3,0 150 200 130 2 2,5 t 48
H16 0,2 0,5 175 225 160 1  56
0,5 1,5 175 225 160 2  56
1,5 3,0 175 225 160 2  56
H18 0,2 0,5 195 180 1  62
0,5 1,5 195 180 1  62
1,5 3,0 195 180 1  62
H19 0,2 0,5 215 190 1  67
0,5 1,5 215 190 1  67
H22 0,2 0,5 130 180 105 6  41
0,5 1,5 130 180 105 6  41
1,5 3,0 130 180 105 7  41
H24 0,2 0,5 150 200 120 4 2,5 t 47
2,5 t
0,5 1,5 150 200 120 4  47
1,5 3,0 150 200 120 5 2,5 t 47
H26 0,2 0,5 175 225 150 3  55
0,5 1,5 175 225 150 3  55
1,5 3,0 175 225 150 3  55
H28 0,2 0,5 195 170 2  61
0,5 1,5 195 170 2  61
a
For information only.
Table 15 — Alloy EN AW-4006 [Al Si1Fe]
a
Temper Specified R R Elongation Hardness
Bend radius
m p0,2
thickness
min.
a
mm MPa MPa %
HBW
over up to min. max. min. max. A A 180° 90°
50 mm
a
≥ 2,5 6,0 95
F
O 0,2 0,5 95 130 40 17 0 t 28
0,5 1,5 95 130 40 19 0 t 28
1,5 3,0 95 130 40 22 0 t 28
3,0 6,0 95 130 40 25 1,0 t 28
1,5 t
H12 0,2 0,5 120 160 90 4  38
0,5 1,5 120 160 90 4 1,5 t 38
1,5 t
1,5 3,0 120 160 90 5  38
H14 0,2 0,5 140 180 120 3 2,0 t 45
0,5 1,5 140 180 120 3 2,0 t 45
1,5 3,0 140 180 120 3 2,0 t 45
b
0,2 0,5 120 160 55 14  35
T4
0,5 1,5 120 160 55 16  35
1,5 3,0 120 160 55 18  35
3,0 6,0 120 160 55 21  35
a
For information only.
b
The T4 temper is not normally supplied by the producers of wrought products such as circles, strips and sheets. It is obtained by
rapid cooling after heating at a relatively elevated temperature, above 500 °C. This thermal cycle is routinely achieved when enamelling
the finished products made out of this alloy, such as frying pans, pressure cookers, pans, etc.

Table 16 — Alloy EN AW-4007 [Al Si1,5Mn]
a
Temper Specified R R Elongation Hardness
Bend radius
m p0,2
thickness
min.
b
mm MPa MPa %
HBW
A A
over up to min. max. min. max. 180° 90°
50 mm
b
6,0 110
F ≥ 2,5
O/H111 0,2 0,5 110 150 45 15  32
0,5 1,5 110 150 45 16  32
1,5 3,0 110 150 45 19  32
3,0 6,0 110 150 45 21  32
6,0 12,5 110 150 45 25  32
H12 0,2 0,5 140 180 110 4  44
0,5 1,5 140 180 110 4  44
1,5 3,0 140 180 110 5  44
a
No data available.
b
For information only
Table 17 — Alloy EN AW-4015 [Al Si2Mn]
a
Temper Specified R R Elongation Hardness
Bend radius
m p0,2
thickness
min.
b
mm MPa MPa %
HBW
over up to min. max. min. max. A A 180° 90°
50 mm
O/H111 0,2 3,0 150 45 20  35
H12 0,2 0,5 120 175 90 4  45
0,5 3,0 120 175 90 4  45
H14 0,2 0,5 150 200 120 2  50
0,5 3,0 150 200 120 3  50
H16 0,2 0,5 170 220 150 1  60
0,5 3,0 170 220 150 2  60
H18 0,2 3,0 200 250 180 1  70
a
No data available.
b
For information only.
Table 18 — Alloy EN AW-5005 [Al Mg1(B)], alloy EN AW-5005A [Al Mg1(C)]
a
Temper Specified R R Elongation Hardness
Bend radius
m p0,2
thickness
min.
a
mm MPa MPa %
HBW
over up to min. max. min. max. A A 180° 90°
50 mm
a
≥ 2,5 80,0 100
F
O/H111 0,2 0,5 100 145 35 15 0 t 0 t 29
0,5 1,5 100 145 35 19 0 t 0 t 29
1,5 3,0 100 145 35 20 0,5 t 0 t 29
3,0 6,0 100 145 35 22 1,0 t 1,0 t 29
6,0 12,5 100 145 35 24  1,5 t 29
12,5 50,0 100 145 35  20  29
1,0 t 0 t
H12 0,2 0,5 125 165 95 2 39
0,5 1,5 125 165 95 2 1,0 t 0,5 t 39
1,5 t 1,0 t
1,5 3,0 125 165 95 4 39
3,0 6,0 125 165 95 5  1,0 t 39
2,0 t
6,0 12,5 125 165 95 7  39
H14 0,2 0,5 145 185 120 2 2,0 t 0,5 t 48
0,5 1,5 145 185 120 2 2,0 t 1,0 t 48
1,5 3,0 145 185 120 3 2,5 t 1,0 t 48
3,0 6,0 145 185 120 4  2,0 t 48
6,0 12,5 145 185 120 5  2,5 t 48
H16 0,2 0,5 165 205 145 1  1,0 t 52
1,5 t
0,5 1,5 165 205 145 2  52
1,5 3,0 165 205 145 3  2,0 t 52
2,5 t
3,0 4,0 165 205 145 3  52
H18 0,2 0,5 185 165 1  1,5 t 58
0,5 1,5 185 165 2  2,5 t 58
1,5 3,0 185 165 2  3,0 t 58
H19 0,2 0,5 205 185 1  64
0,5 1,5 205 185 2  64
1,5 3,0 205 185 2  64
H22/H32 0,2 0,5 125 165 80 4 1,0 t 0 t 38
0,5 1,5 125 165 80 5 1,0 t 0,5 t 38
1,5 3,0 125 165 80 6 1,5 t 1,0 t 38
3,0 6,0 125 165 80 8  1,0 t 38
6,0 12,5 125 165 80 10  2,0 t 38

Table 18 (continued)
a
Temper Specified R R Elongation Hardness
Bend radius
m p0,2
thickness
min.
a
mm MPa MPa %
HBW
over up to min. max. min. max. A A 180° 90°
50 mm
1,5 t 0,5 t
H24/H34 0,2 0,5 145 185 110 3 47
0,5 1,5 145 185 110 4 1,5 t 1,0 t 47
2,0 t 1,0 t
1,5 3,0 145 185 110 5 47
3,0 6,0 145 185 110 6  2,0 t 47
2,5 t
6,0 12,5 145 185 110 8  47
1,0 t
H26/H36 0,2 0,5 165 205 135 2  52
0,5 1,5 165 205 135 3  1,5 t 52
1,5 3,0 165 205 135 4  2,0 t 52
3,0 4,0 165 205 135 4  2,5 t 52
1,5 t
H28/H38 0,2 0,5 185 160 1  58
0,5 1,5 185 160 2  2,5 t 58
3,0 t
1,5 3,0 185 160 3  58
a
For information only.
Table 19 — Alloy EN AW-5010 [AlMg 0,5Mn]
a
Temper Specified R R Elongation Hardness
Bend radius
m p0,2
thickness
min.
a
mm MPa MPa %
HBW
over up to min. max. min. max. A A 180° 90°
50 mm
a
80,0 90
F ≥ 2,5
0 t 0 t
O/H111 0,2 0,5 90 130 35 17 27
0,5 1,5 90 130 35 19 0 t 0 t 27
0 t 0 t
1,5 3,0 90 130 35 21 27
3,0 6,0 90 130 35 24 1,0 t 1,0 t 27
H12 0,2 0,5 110 155 85 2 1,5 t 0 t 36
0,5 1,5 110 155 85 3 1,5 t 0,5 t 36
1,5 3,0 110 155 85 4 2,0 t 1,0 t 36
3,0 6,0 110 155 85 5  1,5 t 36
H14 0,2 0,5 140 175 115 2 2,0 t 0,5 t 45
2,0 t 1,0 t
0,5 1,5 140 175 115 2 45
1,5 3,0 140 175 115 3 2,5 t 1,5 t 45
2,0 t
3,0 6,0 140 175 115 4  45
H16 0,2 0,5 155 195 140 1 2,5 t 1,0 t 51
0,5 1,5 155 195 140 2 2,5 t 1,5 t 51
1,5 4,0 155 195 140 2 2,5 t 2,0 t 51
H18 0,2 0,5 175 160 1  1,5 t 58
2,5 t
0,5 1,5 175 160 2  58
1,5 3,0 175 160 2  3,0 t 58
H19 0,2 0,5 190 170 1  62
0,5 1,5 190 170 1  62
1,5 3,0 190 170 1  62
1,0 t 0 t
H22 0,2 0,5 110 155 75 4 36
0,5 1,5 110 155 75 5 1,0 t 0,5 t 36
1,0 t 1,0 t
1,5 3,0 110 155 75 6 36
3,0 6,0 110 155 75 7  1,5 t 36
H24 0,2 0,5 135 175 105 3 1,5 t 0,5 t 44
0,5 1,5 135 175 105 4 1,5 t 1,0 t 44
1,5 3,0 135 175 105 5 2,0 t 1,5 t 44
2,0 t 1,0 t
H26 0,2 0,5 155 195 130 2 50
0,5 1,5 155 195 130 3 2,0 t 1,5 t 50
2,5 t 2,0 t
1,5 4,0 155 195 130 3 50
H28 0,2 0,5 175 150 1  2,0 t 58
0,5 1,5 175 150 2  2,5 t 58
1,5 3,0 175 150 3  3,0 t 58
a
For information only.
Table 20 — Alloy EN AW-5026 [AI Mg4,5MnSiFe]
a
Temper Specified R R Elongation Hardness
Bend radius
m p0,2
thickness
min.
a
mm MPa MPa %
HBW
over up to min. max. min. max. A A 180° 90°
50 mm
O / H111 ≥ 4 10 12 245 300 120
245 300 120
10 50 11
50 100 245 300 120 10
100 200 230 285 120  9
200 350 210 270 90  6
H14 12,5 250 300 200 10
≥ 5
12,5 15 250 300 200  10
H24 ≥ 3 12,5 300 340 220 5
12,5 20 300 340 220  4
H34 ≥ 5 12,5 250 300 200 10
12,5 15 250 300 200  10
a
No data available.
Table 21 — Alloy EN AW-5040 [Al Mg1,5Mn]
Temper Specified R R Elongation Bend radius Hardness
m p0,2
thickness
min.
a
mm MPa MPa %
HBW
over up to min. max. min. max. A A 180° 90°
50 mm
H24/H34 ≥ 0,8 1,8 220 260 170 6  66
H26/H36 2,0 240 280 205 5  74
≥ 1,0
a
For information only.
Table 22 — Alloy EN AW-5049 [Al Mg2Mn0,8]
a
Temper Specified R R Elongation Hardness
Bend radius
m p0,2
thickness
min.
a
mm MPa MPa %
HBW
A A
over up to min. max. min. max. 180° 90°
50 mm
a
100,0 190
F ≥ 2,5
O/H111 0,2 0,5 190 240 80 12 0,5 t 0 t 52
0,5 1,5 190 240 80 14 0,5 t 0,5 t 52
1,5 3,0 190 240 80 16 1,0 t 1,0 t 52
3,0 6,0 190 240 80 18 1,0 t 1,0 t 52
6,0 12,5 190 240 80 18  2,0 t 52
12,5 100,0 190 240 80  17  52
H112 12,5 210 100 12  62
≥ 6,0
12,5 25,0 200 90  10  58
25,0 40,0 190 80  12  52
40,0 80,0 190 80  14  52
H12 0,2 0,5 220 270 170 4  66
0,5 1,5 220 270 170 5  66
1,5 3,0 220 270 170 6  66
3,0 6,0 220 270 170 7  66
6,0 12,5 220 270 170 9  66
12,5 40,0 220 270 170  9  66
H14 0,2 0,5 240 280 190 3  72
0,5 1,5 240 280 190 3  72
1,5 3,0 240 280 190 4  72
3,0 6,0 240 280 190 4  72
6,0 12,5 240 280 190 5  72
12,5 25,0 240 280 190  5  72
H16 0,2 0,5 265 305 220 2  80
0,5 1,5 265 305 220 3  80
1,5 3,0 265 305 220 3  80
3,0 6,0 265 305 220 3  80
H18 0,2 0,5 290 250 1  88
0,5 1,5 290 250 2  88
1,5 3,0 290 250 2  88
H22/H32 0,2 0,5 220 270 130 7 1,5 t 0,5 t 63
1,5 t 1,0 t
0,5 1,5 220 270 130 8 63
1,5 3,0 220 270 130 10 2,0 t 1,5 t 63
3,0 6,0 220 270 130 11  1,5 t 63
6,0 12,5 220 270 130 10  2,5 t 63
12,5 40,0 220 270 130  9  63
Table 22 (continued)
a
Temper Specified R R Elongation Hardness
Bend radius
m p0,2
thickness
min.
a
mm MPa MPa %
HBW
A A
over up to min. max. min. max. 180° 90°
50 mm
H24/H34 0,2 0,5 240 280 160 6 2,5 t 1,0 t 70
0,5 1,5 240 280 160 6 2,5 t 1,5 t 70
1,5 3,0 240 280 160 7 2,5 t 2,0 t 70
3,0 6,0 240 280 160 8  2,5 t 70
6,0 12,5 240 28
...