ASTM B805-23
(Specification)Standard Specification for Precipitation Hardening Nickel Alloys Bar and Wire
Standard Specification for Precipitation Hardening Nickel Alloys Bar and Wire
ABSTRACT
This specification covers UNS N07716, N07725, N07773, N07776, N09777, and N09925 nickel alloy hot or cold finished rounds, squares, hexagons, rectangles, and cold finished wires. Bars should be supplied in solution treated conditions while wires should be in both solution-treated and cold-finished conditions. The recommended solution treatment should consist of heating the material to a certain temperature followed by rapid cooling. Solution-treated materials should at least conform to the minimum room temperature mechanical properties and should be suitable for subsequent age hardening.
SCOPE
1.1 This specification covers nickel alloys UNS N07716, N07725, N07773, N07776, N09777, and N09925 in the form of hot or cold finished rounds, squares, hexagons, rectangles, and cold finished wire.
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.
1.3 The following precautionary caveat pertains only to the test methods, portion, Section 13, of this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to become familiar with all hazards including those identified in the appropriate Safety Data Sheet (SDS) for this product/material as provided by the manufacturer, to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
General Information
Buy Standard
Standards Content (Sample)
This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the
Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
Designation: B805 − 23
Standard Specification for
1
Precipitation Hardening Nickel Alloys Bar and Wire
This standard is issued under the fixed designation B805; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope* E8/E8M Test Methods for Tension Testing of Metallic Ma-
terials
1.1 This specification covers nickel alloys UNS N07716,
E29 Practice for Using Significant Digits in Test Data to
N07725, N07773, N07776, N09777, and N09925 in the form
Determine Conformance with Specifications
of hot or cold finished rounds, squares, hexagons, rectangles,
E1473 Test Methods for Chemical Analysis of Nickel,
and cold finished wire.
Cobalt, and High-Temperature Alloys
1.2 The values stated in inch-pound units are to be regarded
as standard. The values given in parentheses are mathematical
3. Terminology
conversions to SI units that are provided for information only
3.1 Definitions—Definitions for terms defined in Terminol-
and are not considered standard.
ogy B899 shall apply unless otherwise defined by the require-
1.3 The following precautionary caveat pertains only to the
ments of this document.
test methods, portion, Section 13, of this specification: This
3.2 Definitions of Terms Specific to This Standard:
standard does not purport to address all of the safety concerns,
3.2.1 bar, n—material of round, rectangular (flats),
if any, associated with its use. It is the responsibility of the user
hexagonal, square, or other solid section up to and including
of this standard to become familiar with all hazards including
1
10 in. (254 mm) in width and ⁄8 in. (3.2 mm) or over in
those identified in the appropriate Safety Data Sheet (SDS) for
thickness in straight lengths.
this product/material as provided by the manufacturer, to
establish appropriate safety, health, and environmental prac- 3.2.2 wire, n—a cold-worked solid product of uniform cross
tices and determine the applicability of regulatory limitations
section along its whole length, usually supplied in coil form.
prior to use.
1.4 This international standard was developed in accor-
4. Ordering Information
dance with internationally recognized principles on standard-
4.1 It is the responsibility of the purchaser to specify all
ization established in the Decision on Principles for the
requirements that are necessary for material ordered under this
Development of International Standards, Guides and Recom-
specification. Examples of such requirements include, but are
mendations issued by the World Trade Organization Technical
not limited to the following:
Barriers to Trade (TBT) Committee.
4.1.1 Alloy name or UNS number,
4.1.2 ASTM designation and date of issue,
2. Referenced Documents
4.1.3 Quantity,
2
2.1 ASTM Standards:
4.1.4 Form (bar or wire),
B880 Specification for General Requirements for Chemical
4.1.5 Dimensions,
Check Analysis Limits for Nickel, Nickel Alloys and
4.1.6 Condition,
Cobalt Alloys
4.1.7 Finish,
B899 Terminology Relating to Non-ferrous Metals and Al-
4.1.8 Certification—State if certification is required,
loys
4.1.9 Samples for Product Analysis—State if samples for
product analysis are to be furnished, and
4.1.10 Purchaser Inspection—State if purchaser inspection
1
This specification is under the jurisdiction of ASTM Committee B02 on
is required and which tests or inspections are to be witnessed.
Nonferrous Metals and Alloys and is the direct responsibility of Subcommittee
B02.07 on Refined Nickel and Cobalt and Their Alloys.
Current edition approved April 1, 2023. Published May 2023. Originally 5. Chemical Composition
ɛ1
approved in 1990. Last previous edition approved in 2017 as B805 – 06 (2017) .
5.1 The material shall conform to the composition limits
DOI: 10.1520/B0805-23.
2
For referenced ASTM standards, visit the ASTM website, www.astm.org, or specified in Table 1.
contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
5.2 If a product (check) analysis is performed, the material
Standards volume information, refer to the standard’s Document Summary page on
the ASTM website. shall conform to the tolerances provided in Specification B880.
*A Summary of Changes section appears at the end of this standard
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1
---------------------- Page: 1 ----------------------
B805 − 23
A
TABLE 1 Chemical Requirements
Composition, Weight %
Element
Alloy N07716 Alloy N07725 Alloy
...
This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Because
it may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current version
of the standard as published by ASTM is to be considered the official document.
´1
Designation: B805 − 06 (Reapproved 2017) B805 − 23
Standard Specification for
1
Precipitation Hardening Nickel Alloys Bar and Wire
This standard is issued under the fixed designation B805; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1
ε NOTE—Editorial changes were made throughout in April 2017.
1. Scope*
1.1 This specification covers nickel alloys UNS N07716, N07725, N07773, N07776, N09777, and N09925 in the form of hot or
cold finished rounds, squares, hexagons, rectangles, and cold finished wire.
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical
conversions to SI units that are provided for information only and are not considered standard.
1.3 The following precautionary caveat pertains only to the test methods, portion, Section 13, of this specification: This standard
does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this
standard to become familiar with all hazards including those identified in the appropriate Safety Data Sheet (SDS) for this
product/material as provided by the manufacturer, to establish appropriate safety and health practices,safety, health, and
environmental practices and determine the applicability of regulatory limitations prior to use.
1.4 This international standard was developed in accordance with internationally recognized principles on standardization
established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued
by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
2. Referenced Documents
2
2.1 ASTM Standards:
B880 Specification for General Requirements for Chemical Check Analysis Limits for Nickel, Nickel Alloys and Cobalt Alloys
B899 Terminology Relating to Non-ferrous Metals and Alloys
E8/E8M Test Methods for Tension Testing of Metallic Materials
E29 Practice for Using Significant Digits in Test Data to Determine Conformance with Specifications
E1473 Test Methods for Chemical Analysis of Nickel, Cobalt, and High-Temperature Alloys
3. Terminology
3.1 Definitions—Definitions for terms defined in Terminology B899 shall apply unless otherwise defined by the requirements of
this document.
3.2 Definitions of Terms Specific to This Standard:
1
This specification is under the jurisdiction of ASTM Committee B02 on Nonferrous Metals and Alloys and is the direct responsibility of Subcommittee B02.07 on Refined
Nickel and Cobalt and Their Alloys.
Current edition approved April 1, 2017April 1, 2023. Published April 2017May 2023. Originally approved in 1990. Last previous edition approved in 20112017 as
ɛ1
B805 – 06 (2011).(2017) . DOI: 10.1520/B0805-06R17E01.10.1520/B0805-23.
2
For referenced ASTM standards, visit the ASTM website, www.astm.org, or contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM Standards
volume information, refer to the standard’s Document Summary page on the ASTM website.
*A Summary of Changes section appears at the end of this standard
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1
---------------------- Page: 1 ----------------------
B805 − 23
3.2.1 bar, n—material of round, rectangular (flats), hexagonal, square, or other solid section up to and including 10 in. (254 mm)
1
10 in. (254 mm) in width and ⁄8 in. (3.2 mm) or over in thickness in straight lengths.
3.2.2 wire, n—a cold-worked solid product of uniform cross section along its whole length, usually supplied in coil form.
4. Ordering Information
4.1 It is the responsibility of the purchaser to specify all requirements that are necessary for material ordered under this
specification. Examples of such requirements include, but are not limited to the following:
4.1.1 Alloy name or UNS number,
4.1.2 ASTM designation and date of issue,
4.1.3 Quantity,
4.1.4 Form (bar or wire),
4.1.5 Dimensions,
4.1.6 Condition,
4.1.7 Finish,
4.1.8 Certification—State if certification is required,
4.1.9 Samples for Product Analysis—State if samples for product analysis are to be furnished, and
4.1.10 Purchaser Inspection—State if purchaser inspection is required and which tests or inspections are to be witnessed.
5. Chemical Compos
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.