ISO 9327-4:1999
(Main)Steel forgings and rolled or forged bars for pressure purposes - Technical delivery conditions - Part 4: Weldable fine grain steels with high proof strength
Steel forgings and rolled or forged bars for pressure purposes - Technical delivery conditions - Part 4: Weldable fine grain steels with high proof strength
1.1 This part of ISO 9327 applies to forgings and rolled or forged bars in thicknesses up to 250 mm manufactured from fine grain steels (see NOTE) given in Table 1 and to be delivered according to the specifications given in ISO 9327-1. The steels are classified into room temperature grades (P...), elevated temperature grades (PH...), low temperature grades (PL...), low and elevated temperature grades (PLH...). NOTE Fine grain steels are here understood as steels with grain size 6 or finer according to the grain size charts in ISO 643. 1.2 This part of ISO 9327 covers the following data: a) In Table 1 the limits for the chemical composition according to the cast analysis; the tensile properties at room temperature; the indications on the usual heat treatment condition at the time of delivery; b) in Table 2 the permissible product analysis tolerances on the limiting values given for the cast analysis; c) in Table 3 the minimum impact energy values; d) in Table 4 the minimum elevated temperature proof strength values.
Pièces forgées et barres laminées ou forgées en acier pour appareils à pression — Conditions techniques de livraison — Partie 4: Aciers soudables à grain fin à limite conventionnelle d'élasticité élevée
1.1 La présente partie de l'ISO 9327 traite des pièces forgées et des barres forgées ou laminées, dont l'épaisseur est inférieure ou égale à 250 mm, fabriquées dans les aciers à grain fin (voir note) figurant dans le Tableau 1 et devant être livrées conformément aux spécifications données dans l'ISO 9327-1. Les aciers sont classés en: nuances pour utilisation à température ambiante (P?); nuances pour utilisation à température élevée (PH?); nuances pour utilisation à basse température (PL?); nuances pour utilisation à basse température et à température élevée (PLH?). NOTE 1 Par aciers à grain fin, on entend ici les aciers dont la grosseur du grain est inférieure ou égale à 6, conformément aux tableaux de l'ISO 643. 1.2 La présente partie de l'ISO 9327 couvre les points suivants: a) dans le Tableau 1, les limites relatives: à la composition chimique, selon l'analyse de coulée; aux caractéristiques de traction à température ambiante; aux indications concernant l'état de traitement thermique habituel à la livraison; b) dans le Tableau 2, les écarts admissibles de l'analyse sur produit par rapport aux valeurs limites spécifiées pour l'analyse de coulée; c) dans le Tableau 3, les valeurs minimales d'énergie de rupture par flexion par choc; d) dans le Tableau 4, les valeurs minimales de limite conventionnelle d'élasticité à température élevée.
General Information
- Status
- Published
- Publication Date
- 07-Jul-1999
- Technical Committee
- ISO/TC 17/SC 10 - Steel for pressure purposes
- Drafting Committee
- ISO/TC 17/SC 10 - Steel for pressure purposes
- Current Stage
- 9092 - International Standard to be revised
- Start Date
- 25-Apr-2024
- Completion Date
- 13-Dec-2025
Relations
- Revises
ISO 2604-1:1975 - Steel products for pressure purposes - Quality requirements - Part 1: Forgings - Effective Date
- 15-Apr-2008
ISO 9327-4:1999 - Overview
ISO 9327-4:1999 specifies technical delivery conditions for weldable fine grain steels with high proof strength used for steel forgings and rolled or forged bars for pressure purposes. It applies to products up to 250 mm thickness and is intended to be used together with ISO 9327-1 (General requirements). The standard classifies steels into room‑temperature (P...), elevated‑temperature (PH...), low‑temperature (PL...) and combined low/elevated‑temperature (PLH...) grades. “Fine grain” is defined as grain size 6 or finer per ISO 643.
Key topics and requirements
- Chemical composition and product analysis: Limits for cast analysis and permissible product analysis tolerances are given (see Table 1 and Table 2).
- Mechanical properties: Tensile properties at room temperature and minimum 0.2% proof strength at elevated temperatures are defined (Table 4).
- Toughness / impact energy: Minimum Charpy V‑notch impact energy requirements are specified (Table 3). Tests use standard 10 mm × 10 mm specimens per ISO 148; the average of three tests is required, with one value allowed down to 70% of the specified average.
- Heat treatment and delivery condition: Typical delivery conditions (e.g., normalized, quenched & tempered) are indicated for each grade.
- Inspection, testing and conformity: Conformity assessment, sampling and testing frequency reference ISO 9327-1 and ISO/TR 15461. Marking and ordering follow ISO 9327-1.
Practical applications
ISO 9327-4 is tailored for components where a combination of high proof strength, good weldability, and fine‑grain toughness is critical. Typical applications include:
- Pressure vessels and boilers
- Piping flanges, forged fittings and connectors for high‑pressure systems
- Valve and pump components subjected to elevated or low temperatures
- Critical structural forgings in petrochemical and power industries
Using this standard helps ensure material traceability, consistent mechanical performance (strength and toughness), and suitability for welding in pressure‑rated applications.
Who should use this standard
- Material and metallurgical engineers specifying steel grades for pressure equipment
- Forging houses, steel mills and foundries producing forgings and bars
- Quality and inspection teams performing chemical, tensile and impact testing
- Design engineers, procurement and compliance personnel working to pressure‑equipment regulations
Related standards
- ISO 9327-1 - General requirements (ordering, inspection, marking)
- ISO 148 - Charpy impact test (V‑notch)
- ISO 643 - Grain‑size determination
- ISO/TR 15461 - Testing frequency and sampling for forgings
Keywords: ISO 9327-4:1999, weldable fine grain steels, steel forgings, rolled bars, pressure purposes, technical delivery conditions, proof strength, Charpy V‑notch, chemical composition, heat treatment.
ISO 9327-4:1999 - Steel forgings and rolled or forged bars for pressure purposes — Technical delivery conditions — Part 4: Weldable fine grain steels with high proof strength Released:7/8/1999
ISO 9327-4:1999 - Pièces forgées et barres laminées ou forgées en acier pour appareils à pression — Conditions techniques de livraison — Partie 4: Aciers soudables à grain fin à limite conventionnelle d'élasticité élevée Released:7/8/1999
Frequently Asked Questions
ISO 9327-4:1999 is a standard published by the International Organization for Standardization (ISO). Its full title is "Steel forgings and rolled or forged bars for pressure purposes - Technical delivery conditions - Part 4: Weldable fine grain steels with high proof strength". This standard covers: 1.1 This part of ISO 9327 applies to forgings and rolled or forged bars in thicknesses up to 250 mm manufactured from fine grain steels (see NOTE) given in Table 1 and to be delivered according to the specifications given in ISO 9327-1. The steels are classified into room temperature grades (P...), elevated temperature grades (PH...), low temperature grades (PL...), low and elevated temperature grades (PLH...). NOTE Fine grain steels are here understood as steels with grain size 6 or finer according to the grain size charts in ISO 643. 1.2 This part of ISO 9327 covers the following data: a) In Table 1 the limits for the chemical composition according to the cast analysis; the tensile properties at room temperature; the indications on the usual heat treatment condition at the time of delivery; b) in Table 2 the permissible product analysis tolerances on the limiting values given for the cast analysis; c) in Table 3 the minimum impact energy values; d) in Table 4 the minimum elevated temperature proof strength values.
1.1 This part of ISO 9327 applies to forgings and rolled or forged bars in thicknesses up to 250 mm manufactured from fine grain steels (see NOTE) given in Table 1 and to be delivered according to the specifications given in ISO 9327-1. The steels are classified into room temperature grades (P...), elevated temperature grades (PH...), low temperature grades (PL...), low and elevated temperature grades (PLH...). NOTE Fine grain steels are here understood as steels with grain size 6 or finer according to the grain size charts in ISO 643. 1.2 This part of ISO 9327 covers the following data: a) In Table 1 the limits for the chemical composition according to the cast analysis; the tensile properties at room temperature; the indications on the usual heat treatment condition at the time of delivery; b) in Table 2 the permissible product analysis tolerances on the limiting values given for the cast analysis; c) in Table 3 the minimum impact energy values; d) in Table 4 the minimum elevated temperature proof strength values.
ISO 9327-4:1999 is classified under the following ICS (International Classification for Standards) categories: 77.140.30 - Steels for pressure purposes; 77.140.85 - Iron and steel forgings. The ICS classification helps identify the subject area and facilitates finding related standards.
ISO 9327-4:1999 has the following relationships with other standards: It is inter standard links to ISO 2604-1:1975. Understanding these relationships helps ensure you are using the most current and applicable version of the standard.
ISO 9327-4:1999 is available in PDF format for immediate download after purchase. The document can be added to your cart and obtained through the secure checkout process. Digital delivery ensures instant access to the complete standard document.
Standards Content (Sample)
INTERNATIONAL ISO
STANDARD 9327-4
First edition
1999-06-15
Steel forgings and rolled or forged bars for
pressure purposes — Technical delivery
conditions —
Part 4:
Weldable fine grain steels with high proof
strength
Pièces forgées et barres laminées ou forgées en acier pour appareils
à pression — Conditions techniques de livraison —
Partie 4: Aciers soudables à grain fin à limite conventionnelle d'élasticité
élevée
A Reference number
Contents
Page
1 Scope .1
2 Normative references .2
3 Terms and definitions .2
4 Ordering.2
5 Requirements.2
6 Inspection, testing and conformity of products .2
7 Marking .2
Bibliography.8
© ISO 1999
All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized in any form or by any means, electronic
or mechanical, including photocopying and microfilm, without permission in writing from the publisher.
International Organization for Standardization
Case postale 56 • CH-1211 Genève 20 • Switzerland
Internet iso@iso.ch
Printed in Switzerland
ii
©
ISO
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies (ISO
member bodies). The work of preparing International Standards is normally carried out through ISO technical
committees. Each member body interested in a subject for which a technical committee has been established has
the right to be represented on that committee. International organizations, governmental and non-governmental, in
liaison with ISO, also take part in the work. ISO collaborates closely with the International Electrotechnical
Commission (IEC) on all matters of electrotechnical standardization.
International Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part 3.
Draft International Standards adopted by the technical committees are circulated to the member bodies for voting.
Publication as an International Standard requires approval by at least 75 % of the member bodies casting a vote.
International Standard ISO 9327-4 was prepared by Technical Committee ISO/TC 17, Steel, Subcommittee SC 10,
Steel for pressure purposes.
This first edition, together with parts 1 to 3 and 5 of ISO 9327, cancels and replaces ISO 2604-1:1975.
ISO 9327 consists of the following parts, under the general title Steel forgings and rolled or forged bars for pressure
purposes — Technical delivery conditions:
Part 1: General requirements
Part 2: Non-alloy and alloy (Mo, Cr and CrMo) steels with specified elevated temperature properties
Part 3: Nickel steels with specified low temperature properties
Part 4: Weldable fine grain steels with high proof strength
Part 5: Stainless steels
iii
©
INTERNATIONAL STANDARD ISO ISO 9327-4:1999(E)
Steel forgings and rolled or forged bars for pressure purposes —
Technical delivery conditions —
Part 4:
Weldable fine grain steels with high proof strength
1 Scope
1.1 This part of ISO 9327 applies to forgings and rolled or forged bars in thicknesses up to 250 mm manufactured
from fine grain steels (see NOTE) given in Table 1 and to be delivered according to the specifications given in
ISO 9327-1.
The steels are classified into
room temperature grades (P.),
elevated temperature grades (PH.),
low temperature grades (PL.),
low and elevated temperature grades (PLH.).
NOTE Fine grain steels are here understood as steels with grain size 6 or finer according to the grain size charts in
ISO 643.
This part of ISO 9327 covers the following data:
1.2
a) In Table 1 the limits for
the chemical composition according to the cast analysis;
the tensile properties at room temperature;
the indications on the usual heat treatment condition at the time of delivery;
b) in Table 2 the permissible product analysis tolerances on the limiting values given for the cast analysis;
c) in Table 3 the minimum impact energy values;
d) in Table 4 the minimum el
...
NORME ISO
INTERNATIONALE 9327-4
Première édition
1999-06-15
Pièces forgées et barres laminées
ou forgées en acier pour appareils
à pression — Conditions techniques
de livraison —
Partie 4:
Aciers soudables à grain fin à limite
conventionnelle d'élasticité élevée
Steel forgings and rolled or forged bars for pressure purposes —
Technical delivery conditions —
Part 4: Weldable fine grain steels with high proof strength
A
Numéro de référence
Sommaire
Page
1 Domaine d’application .1
2 Références normatives .2
3 Termes et définitions.2
4 Commande et désignation.2
5 Exigences .2
6 Contrôles, essais et conformité des produits.2
7 Marquage.2
Bibliographie.8
© ISO 1999
Droits de reproduction réservés. Sauf prescription différente, aucune partie de cette publication ne peut être reproduite ni utilisée sous quelque
forme que ce soit et par aucun procédé, électronique ou mécanique, y compris la photocopie et les microfilms, sans l'accord écrit de l'éditeur.
Organisation internationale de normalisation
Case postale 56 • CH-1211 Genève 20 • Suisse
Internet iso@iso.ch
Imprimé en Suisse
ii
©
ISO ISO 9327-4:1999(F)
Avant-propos
L'ISO (Organisation internationale de normalisation) est une fédération mondiale d'organismes nationaux de
normalisation (comités membres de l'ISO). L'élaboration des Normes internationales est en général confiée aux
comités techniques de l'ISO. Chaque comité membre intéressé par une étude a le droit de faire partie du comité
technique créé à cet effet. Les organisations internationales, gouvernementales et non gouvernementales, en
liaison avec l'ISO participent également aux travaux. L'ISO collabore étroitement avec la Commission
électrotechnique internationale (CEI) en ce qui concerne la normalisation électrotechnique.
Les Normes internationales sont rédigées conformément aux règles données dans les Directives ISO/CEI, Partie 3.
Les projets de Normes internationales adoptés par les comités techniques sont soumis aux comités membres pour
vote. Leur publication comme Normes internationales requiert l'approbation de 75 % au moins des comités
membres votants.
La Norme internationale ISO 9327-4 a été élaborée par le comité technique ISO/TC 17, Acier, sous-comité SC 10,
Aciers pour service sous pression.
Cette première édition, conjointement avec les autres parties de l'ISO 9327, remplace l'ISO 2604-1:1975.
L'ISO 9327 comprend les parties suivantes, présentées sous le titre général Pièces forgées et barres laminées ou
forgées en acier pour appareils à pression — Conditions techniques de livraison:
Partie 1: Exigences générales
Partie 2: Aciers non alliés et alliés (Mo, Cr, CrMo) avec caractéristiques spécifiées à température élevée
Partie 3: Aciers alliés au nickel avec caractéristiques spécifiées à basse température
Partie 4: Aciers soudables à grain fin à limite d'élasticité élevée
Partie 5: Aciers inoxydables
iii
©
NORME INTERNATIONALE ISO ISO 9327-4:1999(F)
Pièces forgées et barres laminées ou forgées en acier pour
appareils à pression — Conditions techniques de livraison —
Partie 4:
Aciers soudables à grain fin à limite conventionnelle d'élasticité élevée
1 Domaine d’application
1.1 La présente partie de l’ISO 9327 traite des pièces forgées et des barres forgées ou laminées, dont l'épaisseur
est inférieure ou égale à 250 mm, fabriquées dans les aciers à grain fin (voir note) figurant dans le Tableau 1 et
devant être livrées conformément aux spécifications données dans l'ISO 9327-1.
Les aciers sont classés en:
nuances pour utilisation à température ambiante (P…);
nuances pour utilisation à température élevée (PH…);
nuances pour utilisation à basse température (PL…);
nuances pour utilisation à basse température et à température élevée (PLH…).
NOTE 1 Par aciers à grain fin, on entend ici les aciers dont la grosseur du grain est inférieure ou égale à 6, conformément aux
tableaux de l'ISO 643.
1.2 La présente partie de l’ISO 9327 couvre les points suivants:
a) dans le Tableau 1, les limites relatives:
à la composition chimique, selon l'analyse de coulée;
aux caractéristiques de traction à température ambiante;
aux indications concernant l'état de traitement thermique habituel à la livraison;
b) dans le Tableau 2, les écarts admissibles de l'analyse sur produit par rapport aux valeurs limites spécifiées
pour l'analyse de coulée;
c) dans le Tableau 3, les valeurs minimales d'énergie de rupture par flexion par choc;
d) dans le Tableau 4, les valeurs minimales de limite conventionnelle d'élasticité à température élevée.
©
ISO
2 Références normatives
Les documents normatifs suivants contiennent des dis
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.
Loading comments...