Recycled carbon fibre —
2025-01
Determination of tensile strength
distribution and interfacial
shear strength of single filament
embedded in matrix polymer
Fibre de carbone recyclée — Détermination de la distribution
de la résistance à la traction et de la résistance au cisaillement
interfacial d'un filament unique noyé dans une matrice polymère
Reference number
© ISO 2025
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication may
be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting on
the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address below
or ISO’s member body in the country of the requester.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: +41 22 749 01 11
Email: copyright@iso.org
Website: www.iso.org
Published in Switzerland
ii
Contents Page
Foreword .iv
Introduction .v
1 Scope . 1
2 Normative references . 1
3 Terms, definitions and symbols. 1
3.1 Terms and definitions .1
3.2 Symbols .1
4 Principle . 2
5 Tensile test machine and specimen . 2
5.1 Tensile test machine .2
5.2 Grip.2
5.3 Microscope .2
5.4 Test specimens.2
5.5 Number of tests .4
6 Testing technique. 4
6.1 Test procedure .4
6.2 Validity of the test .6
7 Calculation of results . 6
7.1 Summary of measurement data .6
7.2 Calculation of tensile strength distribution .7
7.3 Calculation of interfacial shear strength .8
7.4 Validity of the test result .8
8 Reporting of test results . 9
Bibliography .10

iii
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out through
ISO technical committees. Each member body interested in a subject for which a technical committee
has been established has the right to be represented on that committee. International organizations,
governmental and non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely
with the International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are described
in the ISO/IEC Directives, Part 1. In particular, the different approval criteria needed for the different types
of ISO document should be noted. This document was drafted in accordance with the editorial rules of the
ISO/IEC Directives, Part 2 (see www.iso.org/directives).
ISO draws attention to the possibility that the implementation of this document may involve the use of (a)
patent(s). ISO takes no position concerning the evidence, validity or applicability of any claimed patent
rights in respect thereof. As of the date of publication of this document, ISO had not received notice of (a)
patent(s) which may be required to implement this document. However, implementers are cautioned that
this may not represent the latest information, which may be obtained from the patent database available at
www.iso.org/patents. ISO shall not be held responsible for identifying any or all such patent rights.
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation of the voluntary nature of standards, the meaning of ISO specific terms and expressions
related to conformity assessment, as well as information about ISO's adherence to the World Trade
Organization (WTO) principles in the Technical Barriers to Trade (TBT), see www.iso.org/iso/foreword.html.
This document was prepared by Technical Committee ISO/TC 61, Plastic, Subcommittee SC 13, Composite
and reinforced fibre.
Any feedback or questions on this document should be directed to the user’s national standards body. A
complete listing of these bodies can be found at www.iso.org/members.html.

iv
Introduction
The properties of recycled carbon fibres are potentially different from those of the original virgin carbon fibres.
Therefore, it is very important to evaluate the properties of recycled carbon fibres in order to reuse them as
reinforcing fibres. The tensile strength distribution and interfacial shear strength of recycled carbon fibres are
essential for the production of composite materials using recycled carbon fibres. This document describes how
to measure the tensile strength distribution and interfacial shear strength of recycled carbon fibres.

v
International Standard ISO 19350:2025(en)
Recycled carbon fibre — Determination of tensile strength
distribution and interfacial shear strength of single filament
embedded in matrix polymer
1 Scope
This document specifies methods for the simultaneous measurement of the fibre tensile strength
distribution, and the fibre resin interfacial shear strength of recycled carbon fibres using the modified
[1]
fragmentation test .
2 Normative references
The following documents are referred to in the text in such a way that some or all of their content constitutes
requirements of this document. For dated references, only the edition cited applies. For undated references,
the latest edition of the referenced document (including any amendments) applies.
ISO 10618, Carbon fibre — Determination of tensile properties of resin-impregnated yarn
ISO 11566, Carbon fibre — Determination of the tensile properties of single-filament specimens
ISO 11567, Carbon fibre — Determination of filament diameter and cross-sectional area
3 Terms, definitions and symbols
3.1 Terms and definitions
No terms and definitions are listed in this document.
ISO and IEC maintain terminology databases for use in standardization at the following addresses:
— ISO Online browsing platform: available at https:// www .iso .org/ obp
— IEC Electropedia: available at https:// www .electropedia .org/
3.2 Symbols
Symbol Definition
E
fibre tensile modulus, GPa Tensile modulus of the recycled carbon fibres
D
average fibre diameter, μm Average fibre diameter of the recycled carbon fibres
L Gauge length, mm Initial distance between grips
Total fibre length, mm Total length of a fibre within the observed area of all speci-
l
mens
Length of a fibre within the observed area of each specimen i
l Fibre length, mm
i
m
Weibull shape parameter Shape parameter of the 2-parameters’ Weibull distribution
Total number of break points
N()ε Total number of fibre break points in all specimens at ε
fibre fibre
Δ Displacement, mm Displacement given between gauges
Incremental film strain The magnitude of the strain on the film in each step
Δε
film
Symbol Definition
Δn ε Incremental number of fibre break Incremental n
...