(Main)Measurement of the carbonation depth of hardened concrete
Measurement of the carbonation depth of hardened concrete
No scope available
Merjenje globine karbonatizacije strjenega betona
General Information
Standards Content (Sample)
SLOVENSKI STANDARD
01-februar-2001
Merjenje globine karbonatizacije strjenega betona
Measurement of the carbonation depth of hardened concrete
Ta slovenski standard je istoveten z: CR 12793:1997
ICS:
91.100.30 Beton in betonski izdelki Concrete and concrete
products
2003-01.Slovenski inštitut za standardizacijo. Razmnoževanje celote ali delov tega standarda ni dovoljeno.
SIST
...
This May Also Interest You
This Technical Specification describes the testing of the freeze-thaw scaling resistance of concrete both with water and with sodium chloride solution. It can be used either to compare new constituents or new concrete compositions against a constituent or a concrete composition that is known to give adequate performance in the local environment or to assess the test results against some absolute numerical values based on local experiences.
Extrapolation of test results to assess different concretes, i.e. new constituents or new concrete compositions, requires an expert evaluation.
NOTE In some cases the test methods may not be suitable for testing special concretes e.g. high strength concrete or permeable concrete. In these cases the result needs to be treated with caution. Also, the testing methods included in this document may not identify aggregates that are subject to occasional ‘pop-outs’.
There is no established correlation between the results obtained by the three test methods. All tests will clearly identify poor and good behaviour, but they differ in their assessment of marginal behaviour. The application of different acceptance limits for test results enables assessment for different degrees of exposure severity. Change of parameters of the testing procedure may have artefacts, some of which explained in Annex A.
- Technical specification32 pagesEnglish languagesale 10% offe-Library read for×1 day
This Technical Report describes a method for characterising the time-dependent leaching behaviour of components from hardened concrete, for use in the natural environment.
This method specifies the procedures for determining the controlling mechanism(s) for leaching of components, their effective diffusion coefficients, in the case of diffusion-control and their cumulative release behaviour over any period of time.
This characterisation method consists of two leaching test procedures. A potential or availability (pulverised specimen) test and a diffusion (tank) [monolithic specimen] test.
The test procedures produce leachates, the analytical procedures for which are not included in this Technical Report.
This Technical Report does not comprise a compliance method.
NOTE 1 The information obtained from the method is quantitative. In the absence, however, of similar information for other construction materials or compliance criteria for acceptable/unacceptable performance of hardened concrete, the data obtained with neither permit a relative nor an absolute assessment of the environmental quality/compatibility of the concrete, unless, by default, in the case where leached concentrations of environmentally significant components are at, or below, their analytical limits of detection.
NOTE 2 In principle, this method could be used to characterise the leaching behaviour of hardened concrete, irrespective of the exposure conditions (e.g. natural environment, contact with drinking water etc.) which the concrete would experience in service. It should be noted, however, that a European standard test method for the extraction/migration of mineral micropollutants is also likely to be developed by CEN/TC 164 - Water supply.
NOTE 3 Analytical procedures for determining concentrations of components in leachates and which may be suitable for the purposes of this Technical Report are being developed by CEN/TC 292 - (...)
- Technical report55 pagesEnglish languagesale 10% offe-Library read for×1 day
This document outlines three test methods. The first is designed to test the constituents of concrete, not designated as WT products, using reference concrete matrices (control mixes and test mixes) wherein the release of (regulated) dangerous substances from the constituent under test, into soil, groundwater or surface water, can be determined. The types of constituent which can be tested using this method are as follows:
a) factory-made cements;
b) aggregates;
c) additions type I;
d) additions type II;
e) admixtures;
f) polymer modifiers;
g) fibres.
The second method, in normative Annex A, is designed to test factory made concrete products, not designated as WT products, as either test pieces sawn or cored from pre-hardened monoliths or as standard-sized moulded test pieces formed from proxy samples of fresh wet material taken from concrete used in the production of factory made items.
The third method, in informative Annex B, is designed to test concretes sampled in the fresh wet state or pre-packaged state, not officially classified as WT products, as standard-sized moulded test pieces.
All three methods produce eluates that may be used for the purposes of characterisation testing, initial type testing (ITT) or further testing (FT) of either the constituents of concrete identified in this Scope or of production concretes.
- Technical report35 pagesEnglish languagesale 10% offe-Library read for×1 day
This European Technical Report describes procedures for determining the contents of most of the constituents of the cements that fall within the scope of EN 197-1.
In principle, the method described in Clause 6 applies to all cements, whatever the number and nature of their constituents, but in practice is limited to the cements identified in Table 1.
The method in clause 6 should be considered to be the method of choice and is based on a sequential selective dissolution of the cement’s constituents, generally of an unknown number, where they are not available separately for analysis at the same time as the cement.
The method of choice enables the quantitative determination (by mass) of: Portland cement clinker, blastfurnace slag, siliceous fly ash, natural pozzolans, limestone, silica fume and set regulators in cements of the types identified in Table 1. Table 1 is derived from Table 1 of EN 197-1.
NOTE 1 Where cements contain calcareous fly ash, burnt shale and/or constituents that partly contain mineral phases, similar to those of clinker, further investigation into the characteristics of those constituents will be necessary before the method can be applied.
The method of choice has limitations, as indicated earlier, and cannot be considered to be a means by which clinker content can simply be determined in isolation from any other constituent. Clinker content is determined ‘by difference’ and other constituents contain, in part, mineral phases similar to those present in clinker and can cause interferences that lead to difficulties in interpretation of the results.
Where apparently anomalous results are obtained, it is recommended that further investigations are undertaken in accordance with the procedure given in Section 6.2.5.4.
Any other method with the same objectives, and intended for use where the constituents are unavailable for separate analysis, can be considered to be an alternative to the method of choice when it is shown that, with appropr
- Technical report34 pagesEnglish languagesale 10% offe-Library read for×1 day
- 18-Sep-2007
- 91.100.30
- 305/2011
- 89/106/EEC
- CEN/TC 51
This document specifies a method for identifying an admixture by infrared analysis (IR).
- Standard6 pagesEnglish languagesale 10% offe-Library read for×1 day
- 06-Aug-2024
- 91.100.10
- 91.100.30
- CEN/TC 104
This document specifies the method for the determination of the tensile splitting strength of test specimens of hardened concrete. The reference specimens are moulded cylindrical specimens.
Cores of at least 75 mm diameter complying with the requirements of EN 12504-1 can be tested using this method.
The use of cubic or prismatic specimens is included in Annex A.
- Standard15 pagesEnglish languagesale 10% offe-Library read for×1 day
- 21-Nov-2023
- 91.100.30
- 305/2011
- CEN/TC 104
This document provides the specifications, the basic performance criteria and the Assessment and Verification of Constancy of Performance (AVCP) for unreinforced, reinforced and prestressed precast concrete products made of compact light-, normal- and heavyweight concrete according to EN 206 with no appreciable amount of entrapped air other than entrained air. Concrete containing fibres for other than mechanical properties (steel, polymer or other fibres) is also covered. It does not cover precast reinforced components of lightweight aggregate concrete with open structure nor glass-fibre reinforced concrete.
It can also be used to specify products for which there is no standard. Not all of the specifications (Clause 4) of this document are relevant to all precast concrete products.
Some European product standards refer to this document. They can include specific provisions that take precedence over the provisions of this document.
- Standard77 pagesEnglish languagesale 10% offe-Library read for×1 day
- 14-Nov-2023
- 91.100.30
- CEN/TC 229
This document specifies methods (Methods A and B) for the determination of the first peak, ultimate and residual strength of specimens of hardened sprayed concrete.
- Standard22 pagesEnglish languagesale 10% offe-Library read for×1 day
- Standard22 pagesEnglish languagesale 10% offe-Library read for×1 day
- 31-Oct-2023
- 91.100.30
- CEN/TC 104
This document specifies the constituent materials, the composition and the mixing method to produce reference concrete and reference mortar for testing the efficacy and the compatibility of admixtures in accordance with the EN 934 series.
- Standard10 pagesEnglish languagesale 10% offe-Library read for×1 day
- 04-Jul-2023
- 91.100.10
- 91.100.30
- CEN/TC 104
This document specifies the constituent materials, the composition and the mix procedure to produce a reference concrete with a prescribed consistency and segregated portion for testing viscosity modifying admixtures as defined in EN 934-2. It also describes how to determine the requirements for the test mix in comparison with the control mix.
- Standard9 pagesEnglish languagesale 10% offe-Library read for×1 day
- 04-Jul-2023
- 91.100.30
- CEN/TC 104
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.