EN 14428:2004+A1:2008

2003-01.Slovenski inštitut za standardizacijo. Razmnoževanje celote ali delov tega standarda ni dovoljeno.Shower enclosures - Functional requirements and test methodsZasloni za prhanje - Funkcionalne zahteve in preskusne metodeParois de douche - Prescriptions fonctionnelles et méthodes d'essaiDuschabtrennungen - Funktionsanforderungen und PrüfverfahrenTa slovenski standard je istoveten z:EN 14428:2004+A1:2008SIST EN 14428:2005+A1:2008en,fr,de91.140.70ICS:SLOVENSKI
STANDARDSIST EN 14428:2005+A1:200801-marec-2008

EUROPEAN STANDARD NORME EUROPÉENNE EUROPÄISCHE NORM
EN 14428:2004+A1
January 2008 ICS 91.140.70 Supersedes EN 14428:2004 English Version
Shower enclosures - Functional requirements and test methods Parois de douche - Prescriptions fonctionnelles et méthodes d'essai
Duschabtrennungen - Funktionsanforderungen und Prüfverfahren This European Standard was approved by CEN on 2 September 2004 and includes Amendment 1 approved by CEN on 24 November 2007.
CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the CEN Management Centre or to any CEN member.
This European Standard exists in three official versions (English, French, German). A version in any other language made by translation under the responsibility of a CEN member into its own language and notified to the CEN Management Centre has the same status as the official versions.
CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom.
EUROPEAN COMMITTEE FOR STANDARDIZATION
COMITÉ EUROPÉEN DE NORMALISATION EUROPÄISCHES KOMITEE FÜR NORMUNG
Management Centre: rue de Stassart, 36
B-1050 Brussels © 2008 CEN All rights of exploitation in any form and by any means reserved worldwide for CEN national Members. Ref. No. EN 14428:2004+A1:2008: E

!!!!Relationship between this European Standard and the essential Requirements of EU Directive 89/106/EEC, EU Construction Products Directive.32 ZA.1 Scope and relevant characteristics.32 ZA.2 Procedure for attestation of conformity of shower enclosures.33 ZA.2.1 System of attestation of conformity.33 ZA.2.2 Declaration of conformity.33 ZA.3 CE marking.34 !!!!Bibliography.36

4.3.1 General Shower enclosures may be glazed with various materials. Where glass is used, this shall meet the requirements of 4.3.2, and where plastics materials are used, they shall meet the requirements of 4.3.3. 4.3.2 Thermally toughened safety glass Thermally toughened safety glass shall meet the requirements of EN 12150-1:2000, except in respect of Clause 8 which is replaced by 5.1 of this document. When tested in accordance with 5.1, the minimum particle count shall be 40. 4.3.3 Plastics materials When tested in accordance with 5.2, sheets shall not break or they shall break safely. 4.4 Durability 4.4.1 General Products conforming with the requirements of 4.2 and 4.3 and the following are deemed to be durable. 4.4.2 Corrosion resistance All components shall consist of corrosion-proof materials or shall be corrosion-protected. All corrosion protection shall conform with the relevant requirements specified in European and International Standards. For example:  the minimum paint adhesion performance for powder-coated or wet-painted surfaces shall comply with a cross-cut value ≤ 2 when tested in accordance with EN ISO 2409;  the minimum average thickness of coating on aluminium shall be of grade AA 8 when tested in accordance with one of the methods given in ISO 7599. In no cases shall the minimum local thickness be less than 80 % of the minimum average thickness. 4.4.3 Resistance to chemicals and stains When tested in accordance with 5.3 the glazing materials shall not show permanent staining or deterioration. 4.4.4 Resistance to wet and dry cycling When tested in accordance with 5.4, the glazing materials shall not show any cracks, crazing or discoloration.

Key 1 Impact point Figure 1 — Position of impact point For thermally toughened soda lime silicate safety glass manufactured by vertical toughening, the impact point shall not be on the tong mark edge. 5.1.4 Assessment of fragmentation The particle count and measuring of the dimensions of the largest particle shall be made between 4 min to 5 min after fracture. An area of radius 100 mm, centred on the impact point, and a border of 25 mm, round the edge of the test specimen (see Figure 2), shall be excluded from the assessment.
Dimensions in millimetres
Key 1 Excluded area Figure 2 — Area to be excluded from the particle count determination and largest particle measurement The particle count shall be made in the region of coarsest fracture (the aim being to obtain the minimum value). The particle count shall be made by placing a mask of (50 ± 1) mm x (50 ± 1) mm on the test piece (see Figures 3,

Figure 3 — Select the area of coarsest fracture, place the template on the test specimen and draw round the template

NOTE Number of perimeter particles = 32/2 = 16 Figure 4 — Mark and count the perimeter fragments as 1/2 particle each

NOTE Number of central particles
= 53
Total number of particles = 16 + 53 = 69 Figure 5 — Mark and count the central fragments and add these to the perimeter count to obtain the particle count for the specimen
Figure 6 — Examples of crack-free particles and the assessment regarding their number

Figure 10 so that the test piece can make contact only with the strips of chloroprene or similar material. These strips shall be capable of being compressed by 10 % to 15 % of their original depth without a permanent set being introduced. The edge cover of the chloroprene on the test pieces shall be such that for the nominal
865 mm x 1 930 mm specimens the central area of (845 ± 3) mm x (1 910 ± 3) mm is unsupported. NOTE In order to limit the compression of the chloroprene strips to within approximately 15 %, spacers of appropriate thickness and material are recommended (see Figure 10). The components of the sub-frame shall be held together, and the sub-frame shall be held to the test frame, by bolts, toggle clamps or similar fixing devices as convenient, these being uniformly spaced no more than
450 mm apart and no fewer than two per side. c) impactor, consisting of a leather case of a punch bag type, modified with a central support rod and fitting system as shown in Figure 11, and filled with chilled lead shot. The leather case shall be made from six panels, as shown in Figure 12, which shall be securely stitched together leaving a slit approximately 175 mm long to allow for filling with the lead shot. Lace holes shall be inserted on each side of the slit which is closed by a leather thong. The neck shall be taped separately to cover the worm-drive hose clamp. The complete impactor shall weigh (45 ± 0,1) kg. The impactor shall be suppor
...