SIST EN ISO 7539-10:2020

SLOVENSKI STANDARD
SIST EN ISO 7539-10:2020
01-julij-2020
Nadomešča:
SIST EN ISO 7539-10:2015
Korozija kovin in zlitin - Ugotavljanje pokanja zaradi napetostne korozije - 10. del:
Reverzna metoda "U-upognjenci" (ISO 7539-10:2020)
Corrosion of metals and alloys - Stress corrosion testing - Part 10: Reverse U-bend
method (ISO 7539-10:2020)
Korrosion der Metalle und Legierungen - Prüfung der Spannungsrisskorrosion - Teil 10:
Vorbereitung und Anwendung von reversierten Bügelproben (ISO 7539-10:2020)
Corrosion des métaux et alliages - Essais de corrosion sous contrainte - Partie 10:
Méthode d'essai par cintrage en U inversé (ISO 7539-10:2020)
Ta slovenski standard je istoveten z: EN ISO 7539-10:2020
ICS:
77.060 Korozija kovin Corrosion of metals
SIST EN ISO 7539-10:2020 en
2003-01.Slovenski inštitut za standardizacijo. Razmnoževanje celote ali delov tega standarda ni dovoljeno.

---------------------- Page: 1 ----------------------
SIST EN ISO 7539-10:2020

---------------------- Page: 2 ----------------------
SIST EN ISO 7539-10:2020


EN ISO 7539-10
EUROPEAN STANDARD

NORME EUROPÉENNE

May 2020
EUROPÄISCHE NORM
ICS 77.060 Supersedes EN ISO 7539-10:2014
English Version

Corrosion of metals and alloys - Stress corrosion testing -
Part 10: Reverse U-bend method (ISO 7539-10:2020)
Corrosion des métaux et alliages - Essais de corrosion Korrosion der Metalle und Legierungen - Prüfung der
sous contrainte - Partie 10: Méthode d'essai par Spannungsrisskorrosion - Teil 10: Vorbereitung und
cintrage en U inversé (ISO 7539-10:2020) Anwendung von reversierten Bügelproben (ISO 7539-
10:2020)
This European Standard was approved by CEN on 10 May 2020.

CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this
European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references
concerning such national standards may be obtained on application to the CEN-CENELEC Management Centre or to any CEN
member.

This European Standard exists in three official versions (English, French, German). A version in any other language made by
translation under the responsibility of a CEN member into its own language and notified to the CEN-CENELEC Management
Centre has the same status as the official versions.

CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia,
Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway,
Poland, Portugal, Republic of North Macedonia, Romania, Serbia, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and
United Kingdom.





EUROPEAN COMMITTEE FOR STANDARDIZATION
COMITÉ EUROPÉEN DE NORMALISATION

EUROPÄISCHES KOMITEE FÜR NORMUNG

CEN-CENELEC Management Centre: Rue de la Science 23, B-1040 Brussels
© 2020 CEN All rights of exploitation in any form and by any means reserved Ref. No. EN ISO 7539-10:2020 E
worldwide for CEN national Members.

---------------------- Page: 3 ----------------------
SIST EN ISO 7539-10:2020
EN ISO 7539-10:2020 (E)
Contents Page
European foreword . 3

2

---------------------- Page: 4 ----------------------
SIST EN ISO 7539-10:2020
EN ISO 7539-10:2020 (E)
European foreword
This document (EN ISO 7539-10:2020) has been prepared by Technical Committee ISO/TC 156
"Corrosion of metals and alloys" in collaboration with Technical Committee CEN/TC 262 “Metallic and
other inorganic coatings, including for corrosion protection and corrosion testing of metals and alloys”
the secretariat of which is held by BSI.
This European Standard shall be given the status of a national standard, either by publication of an
identical text or by endorsement, at the latest by November 2020, and conflicting national standards
shall be withdrawn at the latest by November 2020.
Attention is drawn to the possibility that some of the elements of this document may be the subject of
patent rights. CEN shall not be held responsible for identifying any or all such patent rights.
This document supersedes EN ISO 7539-10:2014.
According to the CEN-CENELEC Internal Regulations, the national standards organizations of the
following countries are bound to implement this European Standard: Austria, Belgium, Bulgaria,
Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland,
Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Republic of
North Macedonia, Romania, Serbia, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and the
United Kingdom.
Endorsement notice
The text of ISO 7539-10:2020 has been approved by CEN as EN ISO 7539-10:2020 without any
modification.


3

---------------------- Page: 5 ----------------------
SIST EN ISO 7539-10:2020

---------------------- Page: 6 ----------------------
SIST EN ISO 7539-10:2020
INTERNATIONAL ISO
STANDARD 7539-10
Second edition
2020-05
Corrosion of metals and alloys —
Stress corrosion testing —
Part 10:
Reverse U-bend method
Corrosion des métaux et alliages — Essais de corrosion sous
contrainte —
Partie 10: Méthode d'essai par cintrage en U inversé
Reference number
ISO 7539-10:2020(E)
©
ISO 2020

---------------------- Page: 7 ----------------------
SIST EN ISO 7539-10:2020
ISO 7539-10:2020(E)

COPYRIGHT PROTECTED DOCUMENT
© ISO 2020
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication may
be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting
on the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address
below or ISO’s member body in the country of the requester.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: +41 22 749 01 11
Fax: +41 22 749 09 47
Email: copyright@iso.org
Website: www.iso.org
Published in Switzerland
ii © ISO 2020 – All rights reserved

---------------------- Page: 8 ----------------------
SIST EN ISO 7539-10:2020
ISO 7539-10:2020(E)

Contents Page
Foreword .iv
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 1
4 Principle . 1
5 Specimens . 2
5.1 General . 2
5.2 Preparation of RUB specimens . 2
5.2.1 Tubing and piping . 2
5.2.2 Other products . 2
5.2.3 Reverse U-bending process . 3
5.3 Fastening RUB specimens with a loading bolt . 3
6 Experimental procedure . 3
7 Post-exposure evaluation . 4
8 Test report . 5
Annex A (informative) Preparation of non-pre-strained half tube RUB specimens .6
Annex B (informative) Preparation of RUB specimens with a gauge section .9
Bibliography .15
© ISO 2020 – All rights reserved iii

---------------------- Page: 9 ----------------------
SIST EN ISO 7539-10:2020
ISO 7539-10:2020(E)

Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out
through ISO technical committees. Each member body interested in a subject for which a technical
committee has been established has the right to be represented on that committee. International
organizations, governmental and non-governmental, in liaison with ISO, also take part in the work.
ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of
electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are
described in the ISO/IEC Directives, Part 1. In particular, the different approval criteria needed for the
different types of ISO documents should be noted. This document was drafted in accordance with the
editorial rules of the ISO/IEC Directives, Part 2 (see www .iso .org/ directives).
Attention is drawn to the possibility that some of the elements of this document may be the subject of
patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of
any patent rights identified during the development of the document will be in the Introduction and/or
on the ISO list of patent declarations received (see www .iso .org/ patents).
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation of the voluntary nature of standards, the meaning of ISO specific terms and
expressions related to conformity assessment, as well as information about ISO’s adherence to the
World Trade Organization (WTO) principles in the Technical Barriers to Trade (TBT) see www .iso .org/
iso/ foreword .html.
This document was prepared by Technical Committee ISO/TC 156, Corrosion of metals and alloys, in
collaboration with the European Committee for Standardization (CEN) Technical Committee CEN/
TC 262 Metallic and other inorganic coatings, including for corrosion protection and corrosion testing of
metals and alloys, in accordance with the Agreement on technical cooperation between ISO and CEN
(Vienna Agreement).
This second edition cancels and replaces the first edition (ISO 7539-10:2013), which has been technically
revised. The main changes compared with the previous edition are as follows:
— the specimen preparation, i.e. how RUB specimens are machined, bent and fastened, has been
revised in Clause 5 and Annexes A and B;
— the experimental procedure of how specimens are tested in a multiple immersion test with different
periods or in a serial immersion test has been revised in Clause 6;
— the post-exposure evaluation of how specimens are observed has been revised in Clause 7;
— information has been added for the test report in Clause 8;
— Figures A.1, A.2 and B.3 and Table B.1 have been revised;
— new Figures A.3 and B.4 have been added to illustrate the RUB specimen before and after fastening.
A list of all parts in the ISO 7539 series can be found on the ISO website.
Any feedback or questions on this document should be directed to the user’s national standards body. A
complete listing of these bodies can be found at www .iso .org/ members .html.
iv © ISO 2020 – All rights reserved

---------------------- Page: 10 ----------------------
SIST EN ISO 7539-10:2020
INTERNATIONAL STANDARD ISO 7539-10:2020(E)
Corrosion of metals and alloys — Stress corrosion
testing —
Part 10:
Reverse U-bend method
WARNING — This document can involve hazardous materials, operations and equipment. It is
the responsibility of the user of this document to consult and establish appropriate safety and
health practices and to determine the applicability of regulatory limitations prior to use.
1 Scope
This document specifies procedures for designing, preparing and using reversed U-bend (RUB) test
specimens for investigating the susceptibility of the metal to stress corrosion cracking. The term
“metal” as used in this document includes alloys.
2 Normative references
The following documents are referred to in the text in such a way that some or all of their content
constitutes requirements of this document. For dated references, only the edition cited applies. For
undated references, the latest edition of the referenced document (including any amendments) applies.
ISO 7539-1, Corrosion of metals and alloys — Stress corrosion testing — Part 1: General guidance on testing
procedures
ISO 8407, Corrosion of metals and alloys — Removal of corrosion products from corrosion test specimens
3 Terms and definitions
For the purposes of this document, the terms and definitions given in ISO 7539-1 apply.
ISO and IEC maintain terminological databases for use in standardization at the following addresses:
— ISO Online browsing platform: available at https:// www .iso .org/ obp
— IEC Electropedia: available at http:// www .electropedia .org/
4 Principle
The RUB test is a particularly severe test for assessing susceptibility to stress corrosion cracking.
The test is intended primarily for application to metals with high corrosion resistance, such as Ni-
based alloys, with the advantage, compared to methods such as the conventional U-bend test, of
having significantly less stress relaxation. It is used primarily as a screening test for tubing, piping,
plate, bar and other products including welded materials. It may also be used as an acceptance test for
performance in service subject to agreement between the parties.
The principle of the test is to introduce very severe stresses in a high corrosion resistance metal, with
minimum relaxation, in order to enhance the likelihood of inducing stress corrosion cracking.
The test involves exposing a piece of metal of a semi-circular section bent back on itself (i.e. reversed
bent) into a U-shape to the corroding medium and holding it in a manner that ensures that there are
initial tensile stresses in excess of the yield strength over a large proportion of the inner surface. The
© ISO 2020 – All rights reserved 1

---------------------- Page: 11 ----------------------
SIST EN ISO 7539-10:2020
ISO 7539-10:2020(E)

test is accelerated by the presence of complex bi-axial stresses that may or may not exist in service. In
the act of forming specimens, varying amounts of cold work may be introduced, and this deformation
can influence the stress corrosion cracking tendency as compared to that of the material in the original
condition.
The test is normally performed in a laboratory by exposing the specimens to simulated service
conditions.
A further objective of the test is to compare and evaluate the influence of different material parameters.
The principal advantages of the test are its simplicity and its ability to provide a rapid screening. If
conventional U-bend or C-ring specimens are used for screening tests in a high temperature solution of
573 K or higher, marked stress relaxation occurs and a long testing time is needed for the evaluation.
However, the stress relaxation in RUB specimens is smaller than that in conventional U-bend and C-ring
specimens, due to the bi-axial stresses in RUB specimens. Therefore, screening tests can be done within
a relatively short time through the use of RUB specimens.
A disadvantage is that the stress state is complicated and is difficult to quantify with accuracy. If an
accurate stress state is desired, an alternative method should be used.
Wide variations in test results can be obtained for a given metal and environment even when testing
nominally identical specimens and the replication of tests is frequently necessary.
If specimens are prepared from tubing of different dimensions or are subjected to different stressing
procedures, test results can be even more variable.
5 Specimens
5.1 General
RUB specimens are prepared from pieces of production tubing, piping and other hollow cylindrical
products cut into half longitudinally or from a plate, bar or other products formed into a semi-circular
shape along the axial direction. The specimens should be cut by sawing or other such methods that do
not affect the material properties. Then they should be shaped into their dimensions by machining. The
side face of the specimens should be deburred and then finished by sequentially coarse-to-fine grinding
using abrasive papers or cloths to a su
...