ISO/ASTM 52908:2023
(Main)Additive manufacturing of metals — Finished part properties — Post-processing, inspection and testing of parts produced by powder bed fusion
Additive manufacturing of metals — Finished part properties — Post-processing, inspection and testing of parts produced by powder bed fusion
This document specifies requirements for the qualification, quality assurance and post processing for metal parts made by powder bed fusion. This document specifies methods and procedures for testing and qualification of various characteristics of metallic parts made by additive manufacturing powder bed fusion processes, in accordance with ISO/ASTM 52927, categories H and M. This document is intended to be used by part providers and/or customers of parts. This document specifies qualification procedures where appropriate to meet defined quality levels.
Fabrication additive de métaux — Propriétés des pièces finies — Post-traitement, inspection et essais des pièces produites par fusion sur lit de poudre
Le présent document spécifie les exigences pour la qualification, l’assurance qualité et le post-traitement pour les pièces métalliques fabriquées par fusion sur lit de poudre. Le présent document spécifie des méthodes et des modes opératoires pour les essais et la qualification de différentes caractéristiques de pièces métalliques fabriquées de manière additive par fusion sur lit de poudre, conformément à l’ISO/ASTM 52927, catégories H et M. Le présent document est destiné à être utilisé par des fournisseurs de pièces et/ou par des clients de pièces. Le présent document spécifie des procédures de qualification permettant le cas échéant d’atteindre les niveaux de qualité définis.
General Information
Standards Content (Sample)
INTERNATIONAL ISO/ASTM
STANDARD 52908
First edition
2023-11
Additive manufacturing of metals —
Finished part properties — Post-
processing, inspection and testing of
parts produced by powder bed fusion
Fabrication additive de métaux — Propriétés des pièces finies — Post-
traitement, inspection et essais des pièces produites par fusion sur lit
de poudre
Reference number
© ISO/ASTM International 2023
© ISO/ASTM International 2023
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication may
be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting on
the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address below
or ISO’s member body in the country of the requester. In the United States, such requests should be sent to ASTM International.
ISO copyright office ASTM International
CP 401 • Ch. de Blandonnet 8 100 Barr Harbor Drive, PO Box C700
CH-1214 Vernier, Geneva West Conshohocken, PA 19428-2959, USA
Phone: +41 22 749 01 11 Phone: +610 832 9634
Fax: +610 832 9635
Email: copyright@iso.org Email: khooper@astm.org
Website: www.iso.org Website: www.astm.org
Published in Switzerland
ii
© ISO/ASTM International 2023 – All rights reserved
Contents Page
Foreword .v
Introduction . vi
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 2
4 Abbreviations . 2
5 Qualification . 2
5.1 General . 2
5.2 Part validation . 3
5.3 Technical documentation relating to part(s) produced . 3
5.4 Facility documentation . 3
5.4.1 Additive manufacturer documentation requirements . 3
5.4.2 Subcontractor documentation requirements . 3
5.5 Quality assurance documentation . 4
6 Post processing . 4
6.1 General . 4
6.2 Post-build activities . 4
6.3 Thermal treatment . 5
6.3.1 General . 5
6.3.2 Reducing residual stresses . 5
6.3.3 Reducing anisotropy . 5
6.3.4 Prepare material for mechanical post-processing . 5
6.3.5 Densification . 5
6.3.6 Annealing and aging . 5
6.4 Separation from the built platform and support structures . 6
6.5 Surface finishing . 6
6.5.1 Surface finishing operations . 6
6.5.2 Machining allowances . 6
7 Inspection and testing .6
7.1 General . 6
7.2 Metallurgical testing . 7
7.2.1 Objective . 7
7.2.2 Test specimen selection, design, and preparation for part characterization. 7
7.2.3 Test methods, parameters, and test specimens. 8
7.2.4 Chemical analysis . 9
7.2.5 Metallurgical properties . 9
7.2.6 Determining the non-metallic inclusion content . 9
7.2.7 Analysis and test report . 9
7.3 Material testing . 9
7.3.1 General . 9
7.3.2 Orientation in the build space . 10
7.3.3 Test specimen geometry and surface quality . 10
7.3.4 Density (part) . . 10
7.3.5 Archimedean method.12
7.3.6 Image analysis of metallographic specimens .13
7.4 Mechanical testing . 15
7.4.1 Static testing .15
7.4.2 Dynamic testing . 20
7.5 Surface quality inspection . 21
7.6 Geometrical inspection (form, dimension, and tolerances) . 21
7.7 Non-destructive testing . 21
iii
© ISO/ASTM International 2023 – All rights reserved
Bibliography .23
iv
© ISO/ASTM International 2023 – All rights reserved
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out
through ISO technical committees. Each member body interested in a subject for which a technical
committee has been established has the right to be represented on that committee. International
organizations, governmental and non-governmental, in liaison with ISO, also take part in the work.
ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of
electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are
described in the ISO/IEC Directives, Part 1. In particular, the different approval criteria needed for the
different types of ISO document should be noted. This document was drafted in accordance with the
editorial rules of the ISO/IEC Directives, Part 2 (see www.iso.org/directives).
ISO draws attention to the possibility that the implementation of this document may involve the use
of (a) patent(s). ISO takes no position concerning the evidence, validity or applicability of any claimed
patent rights in respect thereof. As of the date of publication of this document, ISO had not received
notice of (a) patent(s) which may be required to implement this document. However, implementers are
cautioned that this may not represent the latest information, which may be obtained from the patent
database available at www.iso.org/patents. ISO shall not be held responsible for identifying any or all
such patent rights.
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation of the voluntary nature of standards, the meaning of ISO specific terms and
expressions related to conformity assessment, as well as information about ISO's adherence to
the World Trade Organization (WTO) principles in the Technical Barriers to Trade (TBT), see
www.iso.org/iso/foreword.html.
This document was prepared by Technical Committee ISO/TC 261, Additive manufacturing, in
cooperation with ASTM Committee F42, Additive Manufacturing Technologies, on the basis of a
partnership agreement between ISO and ASTM International with the Objective to create a common set
of ISO/ASTM standards on Additive Manufacturing, and in collaboration with the European Committee
for Standardization (CEN) Technical Committee CEN/TC 438, Additive manufacturing, in accordance
with the Agreement on technical cooperation between ISO and CEN (Vienna Agreement).
Any feedback or questions on this document should be directed to the user’s national standards body. A
complete listing of these bodies can be found at www.iso.org/members.html.
v
© ISO/ASTM International 2023 – All rights reserved
Introduction
As with conventional manufacturing processes (e.g. casting and milling), metallic parts produced by
additive manufacturing technologies have critical-to-quality characteristics. These characteristics
include density, strength, hardness, surface quality, dimensional accuracy, residual stresses, absence
of cracks, voids, and structural homogeneity, which are typically tested in additively manufactured
components. The quality of additively manufactured components is essent
...
NORME ISO/ASTM
INTERNATIONALE 52908
Première édition
2023-11
Fabrication additive de métaux —
Propriétés des pièces finies — Post-
traitement, inspection et essais des
pièces produites par fusion sur lit de
poudre
Additive manufacturing of metals — Finished part properties — Post-
processing, inspection and testing of parts produced by powder bed
fusion
Numéro de référence
© ISO/ASTM International 2023
DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO/ASTM International 2023
Tous droits réservés. Sauf prescription différente ou nécessité dans le contexte de sa mise en œuvre, aucune partie de cette
publication ne peut être reproduite ni utilisée sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique,
y compris la photocopie, ou la diffusion sur l’internet ou un intranet, sans autorisation écrite soit de l’ISO à l’adresse ci-après,
soit d’un organisme membre de l’ISO dans le pays du demandeur. Aux États-Unis, les demandes doivent être adressées à ASTM
International.
ISO copyright office ASTM International
Case postale 401 • Ch. de Blandonnet 8 100 Barr Harbor Drive, PO Box C700
CH-1214 Vernier, Genève West Conshohocken, PA 19428-2959, USA
Tél.: +41 22 749 01 11 Tél.: +610 832 9634
Fax: +610 832 9635
E-mail: copyright@iso.org E-mail: khooper@astm.org
Web: www.iso.org Web: www.astm.org
Publié en Suisse
ii
© ISO/ASTM International 2023 – Tous droits réservés
Sommaire Page
Avant-propos .v
Introduction . vi
1 Domaine d’application . 1
2 Références normatives .1
3 Termes et définitions . 2
4 Abréviations . 2
5 Qualification . 3
5.1 Généralités . 3
5.2 Validation de la pièce . 3
5.3 Documentation technique relative à la ou aux pièce(s) produite(s). 3
5.4 Documentation de l’installation . 3
5.4.1 Exigences de documentation des fabricants additifs . 3
5.4.2 Exigences de documentation des sous-traitants . 4
5.5 Documentation d’assurance qualité . 4
6 Post-traitement . 4
6.1 Généralités . 4
6.2 Activités de post-traitement . 5
6.3 Traitement thermique . 5
6.3.1 Généralités . 5
6.3.2 Réduction du stress résiduel . 5
6.3.3 Réduction de l’anisotropie . 5
6.3.4 Préparation du matériau pour le post-traitement mécanique . 6
6.3.5 Densification . 6
6.3.6 Recuit et vieillissement . 6
6.4 Séparation de la plateforme de fabrication et des structures support . 6
6.5 Finition de surface . 6
6.5.1 Opérations de finition de surface . 6
6.5.2 Tolérances d’usinage . 7
7 Inspection et essais . 7
7.1 Généralités . 7
7.2 Essais métallurgiques . 7
7.2.1 Objectif . 7
7.2.2 Sélection, conception, et préparation de l'éprouvette pour la caractérisation
de la pièce . 8
7.2.3 Méthodes d’essai, paramètres et éprouvettes. 9
7.2.4 Analyse chimique . 9
7.2.5 Propriétés métallurgiques . 9
7.2.6 Détermination de la teneur en inclusions non métalliques. 9
7.2.7 Analyse et rapport d’essai . 10
7.3 Essais de matériau. 10
7.3.1 Généralités . 10
7.3.2 Orientation dans l’espace de fabrication . 10
7.3.3 Géométrie et qualité de surface de l'éprouvette d'essai . 10
7.3.4 Densité (pièce) . 11
7.3.5 Méthode archimédienne .12
7.3.6 Analyse d’images d’éprouvettes métallographiques .13
7.4 Essai mécanique . 15
7.4.1 Essais statiques . 15
7.4.2 Essais dynamiques . 20
7.5 Inspection de la qualité de surface . 22
7.6 Inspection géométrique (forme, dimensions et tolérances) .22
7.7 Essais non destructifs .22
iii
© ISO/ASTM International 2023 – Tous droits réservés
Bibliographie .23
iv
© ISO/ASTM International 2023 – Tous droits réservés
Avant-propos
L’ISO (Organisation internationale de normalisation) est une fédération mondiale d’organismes
nationaux de normalisation (comités membres de l’ISO). L’élaboration des Normes internationales est
en général confiée aux comités techniques de l’ISO. Chaque comité membre intéressé par une étude
a le droit de faire partie du comité technique créé à cet effet. Les organisations internationales,
gouvernementales et non gouvernementales, en liaison avec l’ISO participent également aux travaux.
L’ISO collabore étroitement avec la Commission électrotechnique internationale (IEC) en ce qui
concerne la normalisation électrotechnique.
Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont
décrites dans les Directives ISO/IEC, Partie 1. Il convient, en particulier de prendre note des différents
critères d’approbation requis pour les différents types de document ISO. Le présent document a été
rédigé conformément aux règles de rédaction données dans les Directives ISO/IEC, Partie 2 (voir
www.iso.org/directives).
L’ISO attire l’attention sur le fait que la mise en application du présent document peut entraîner
l’utilisation d’un ou de plusieurs brevets. L’ISO ne prend pas position quant à la preuve, à la validité
et à l’applicabilité de tout droit de brevet revendiqué à cet égard. À la date de publication du présent
document, l’ISO n'avait pas reçu notification qu’un ou plusieurs brevets pouvaient être nécessaires à sa
mise en application. Toutefois, il y a lieu d’avertir les responsables de la mise en application du présent
document que des informations plus récentes sont susceptibles de figurer dans la base de données de
brevets, disponible à l'adresse www.iso.org/brevets. L’ISO ne saurait être tenue pour responsable de ne
pas avoir identifié tout ou partie de tels droits de propriété.
Les appellations commerciales éventuellement mentionnées dans le présent document sont données
pour information, par souci de commodité, à l’intention des utilisateurs et ne sauraient constituer un
engagement.
Pour une explication de la nature volontaire des normes, la signification des termes et expressions
spécifiques de l’ISO liés à l’évaluation de la conformité, ou pour toute information au sujet de l’adhésion
de l’ISO aux principes de l’Organisation mondiale du commerce (OMC) concernant les obstacles
techniques au commerce (OTC), voir le lien suivant: www.iso.org/iso/foreword.html.
Le présent document a été élaboré par le Comité technique ISO/TC 261, Fabrication additive, en
coopération avec le Comité ASTM F42, Technologies de fabrication additive, dans le cadre d’un accord de
partenariat entre l’ISO et ASTM International dans l’objectif de créer un ensemble de normes ISO/ASTM
sur la fabrication additive, et en collaboration avec le Comité technique CEN/TC 438 Fabrication additive
du Comité Européen de Normalisation (CEN), conformément à l'Accord de coopération technique entre
l'ISO et le CEN (Accord de Vienne).
Il convient que l’utilisateur adresse tout retour d’information ou toute question concernant le présent
document à l’organisme national de normalisation de son pays. Une liste exhaustive desdits organismes
se trouve à l’adresse www.iso.org/members.html.
v
© ISO/ASTM International 2023 – Tous droits réservés
Introduction
Comme avec les procédés de fabrication conventionnels (par exemple moulage et fraisage), les pièces
métalliques produite
...
FINAL
INTERNATIONAL ISO/ASTM
DRAFT
STANDARD FDIS
ISO/TC 261
Additive manufacturing of metals —
Secretariat: DIN
Finished Part properties — Post-
Voting begins on:
2023-08-23 processing, inspection and testing of
parts produced by powder bed fusion
Voting terminates on:
2023-10-18
Fabrication additive de métaux — Propriétés des pièces finies — Post-
traitement, inspection et essais des pièces produites par fusion sur lit
de poudre
ISO/CEN PARALLEL PROCESSING
RECIPIENTS OF THIS DRAFT ARE INVITED TO
SUBMIT, WITH THEIR COMMENTS, NOTIFICATION
OF ANY RELEVANT PATENT RIGHTS OF WHICH
THEY ARE AWARE AND TO PROVIDE SUPPOR TING
DOCUMENTATION.
IN ADDITION TO THEIR EVALUATION AS
Reference number
BEING ACCEPTABLE FOR INDUSTRIAL, TECHNO-
ISO/ASTM FDIS 52908:2023(E)
LOGICAL, COMMERCIAL AND USER PURPOSES,
DRAFT INTERNATIONAL STANDARDS MAY ON
OCCASION HAVE TO BE CONSIDERED IN THE
LIGHT OF THEIR POTENTIAL TO BECOME STAN-
DARDS TO WHICH REFERENCE MAY BE MADE IN
NATIONAL REGULATIONS. © ISO/ASTM International 2023
ISO/ASTM FDIS 52908:2023(E)
FINAL
INTERNATIONAL ISO/ASTM
DRAFT
STANDARD FDIS
ISO/TC 261
Additive manufacturing of metals —
Secretariat: DIN
Finished Part properties — Post-
Voting begins on:
processing, inspection and testing of
parts produced by powder bed fusion
Voting terminates on:
Fabrication additive de métaux — Propriétés des pièces finies — Post-
traitement, inspection et essais des pièces produites par fusion sur lit
de poudre
© ISO/ASTM International 2023
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication may
ISO/CEN PARALLEL PROCESSING
be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting on
the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address below
or ISO’s member body in the country of the requester. In the United States, such requests should be sent to ASTM International.
ISO copyright office ASTM International
RECIPIENTS OF THIS DRAFT ARE INVITED TO
CP 401 • Ch. de Blandonnet 8 100 Barr Harbor Drive, PO Box C700
SUBMIT, WITH THEIR COMMENTS, NOTIFICATION
OF ANY RELEVANT PATENT RIGHTS OF WHICH
CH-1214 Vernier, Geneva West Conshohocken, PA 19428-2959, USA
THEY ARE AWARE AND TO PROVIDE SUPPOR TING
Phone: +41 22 749 01 11 Phone: +610 832 9634
DOCUMENTATION.
Fax: +610 832 9635
IN ADDITION TO THEIR EVALUATION AS
Reference number
Email: copyright@iso.org Email: khooper@astm.org
BEING ACCEPTABLE FOR INDUSTRIAL, TECHNO
ISO/ASTM FDIS 52908:2023(E)
Website: www.iso.org Website: www.astm.org
LOGICAL, COMMERCIAL AND USER PURPOSES,
DRAFT INTERNATIONAL STANDARDS MAY ON
Published in Switzerland
OCCASION HAVE TO BE CONSIDERED IN THE
LIGHT OF THEIR POTENTIAL TO BECOME STAN
DARDS TO WHICH REFERENCE MAY BE MADE IN
ii
© ISO/ASTM International 2023 – All rights reserved
NATIONAL REGULATIONS. © ISO/ASTM International 2023
ISO/ASTM FDIS 52908:2023(E)
Contents Page
Foreword .v
Introduction . vi
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 2
4 Abbreviations . 2
5 Qualification . 2
5.1 General . 2
5.2 Part validation . 2
5.3 Technical documentation relating to part(s) produced . 3
5.4 Facility documentation . 3
5.4.1 Additive manufacturer documentation requirements . 3
5.4.2 Subcontractor documentation requirements . 3
5.5 Quality assurance documentation . 4
6 Post processing . 4
6.1 General . 4
6.2 Post‑build activities . 4
6.3 Thermal treatment . 5
6.3.1 General . 5
6.3.2 Reducing residual stresses . 5
6.3.3 Reducing anisotropy . 5
6.3.4 Prepare material for mechanical post‑processing . 5
6.3.5 Densification . 5
6.3.6 Annealing and aging . 5
6.4 Separation from the built platform and support structures . 6
6.5 Surface finishing . 6
6.5.1 Surface finishing operations . 6
6.5.2 Machining allowances . 6
7 Inspection and testing .6
7.1 General . 6
7.2 Metallurgical testing . 7
7.2.1 Objective . 7
7.2.2 Test specimen selection, design, and preparation for part characterization. 7
7.2.3 Test methods, parameters, and test specimens. 8
7.2.4 Chemical analysis . 9
7.2.5 Metallurgical properties . 9
7.2.6 Determining the non‑metallic inclusion content . 9
7.2.7 Analysis and test report . 9
7.3 Material testing . 9
7.3.1 General . 9
7.3.2 Orientation in the build space . 10
7.3.3 Test specimen geometry and surface quality . 10
7.3.4 Density (part) . . 10
7.3.5 Archimedean method.12
7.3.6 Image analysis of metallographic specimens .13
7.4 Mechanical testing . 15
7.4.1 Static testing .15
7.4.2 Dynamic testing . 20
7.5 Surface quality inspection . 21
7.6 Geometrical inspection (form, dimension, and tolerances) . 21
7.7 Non‑destructive testing . 21
iii
© ISO/ASTM International 2023 – All rights reserved
ISO/ASTM FDIS 52908:2023(E)
Bibliography .23
iv
© ISO/ASTM International 2023 – All rights reserved
ISO/ASTM FDIS 52908:2023(E)
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out
through ISO technical committees. Each member body interested in a subject for which a technical
committee has been established has the right to be represented on that committee. International
organizations, governmental and nongovernmental, in liaison with ISO, also take part in the work.
ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of
electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are
described in the ISO/IEC Directives, Part 1. In particular, the different approval criteria needed for the
different types of ISO document should be noted. This document was drafted in accordance with the
editorial rules of the ISO/IEC Directives, Part 2 (see www.iso.org/directives).
ISO draws attention to the possibility that the implementation of this document may involve the use
of (a) patent(s). ISO takes no position concerning the evidence, validity or applicability of any claimed
patent rights in respect thereof. As of the date of publication of this document, ISO had not received
notice of (a) patent(s) which may be required to implement this document. However, implementers are
cautioned that this may not represent the latest information, which may be obtained from the patent
database available at www.iso.org/patents. ISO shall not be held responsible for identifying any or all
such patent rights.
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation of the voluntary nature of
...
ISO/ASTM FDIS 52908:2023(E)
Style Definition: List Bullet: Indent: Left: 0 pt, Hanging:
18 pt, No bullets or numbering, Tab stops: 18 pt, List
ISO/TC 261 & ASTM F 42
tab
Secretariat: DIN
Style Definition: List Bullet 2: Indent: Left: 14.15 pt,
Hanging: 18 pt, No bullets or numbering, Tab stops:
Date: 2023-06-14xx
32.15 pt, List tab
Additive manufacturing of metals — Finished part properties — Post processing, inspection and
Style Definition: List Bullet 3: Indent: Left: 28.3 pt,
testing of parts produced by powder bed fusion
Hanging: 18 pt, No bullets or numbering, Tab stops:
Fabrication additive de métaux — Propriétés des pièces finies — Post-traitement, inspection et essais des 46.3 pt, List tab
pièces produites par fusion sur lit de poudre
Style Definition: List Bullet 4: Indent: Left: 42.45 pt,
Hanging: 18 pt, No bullets or numbering, Tab stops:
60.45 pt, List tab
Style Definition: List Bullet 5: Indent: Left: 56.6 pt,
Hanging: 18 pt, No bullets or numbering, Tab stops:
74.6 pt, List tab
Style Definition: List Number: Indent: Left: 0 pt,
Hanging: 18 pt, No bullets or numbering, Tab stops:
18 pt, List tab
Style Definition: List Number 5: Indent: Left: 56.6 pt,
Hanging: 18 pt, No bullets or numbering, Tab stops:
74.6 pt, List tab
ISO/ASTM FDIS 52908:2023(E)
© ISO/ASTM 2023
Formatted: Pattern: Clear
Formatted: Pattern: Clear
All rights reserved. Unless otherwise specified, or required in the context of its implementation,
no part of this publication may be reproduced or utilized otherwise in any form or by any means,
electronic or mechanical, including photocopying, or posting on the internet or an intranet,
without prior written permission. Permission can be requested from either ISO at the address
below or ISO’s member body in the country of the requester. In the United States, such requests
should be sent to ASTM International.
ISO copyright office ASTM International
CP 401 • Ch. de Blandonnet 8 100 Barr Harbor Drive, PO Box C700
CH-1214 Vernier, Geneva West Conshohocken, PA 19428-2959, USA
Phone: +41 22 749 01 11 Phone: +610 832 9634
Fax: +41 22 749 09 47 Fax: +610 832 9635
Email: copyright@iso.orgcopyright@iso.org Email: khooper@astm.org
Website: www.iso.orgwww.iso.org Website: www.astm.orgwww.astm.org
ii © ISO/ASTM International 2023 – All rights reserved
ISO/ASTM FDIS 52908:2023(E)
Contents
Foreword . Error! Bookmark not defined.
Introduction. Error! Bookmark not defined.
1 Scope . Error! Bookmark not defined.
2 Normative references . Error! Bookmark not defined.
3 Terms and definitions . Error! Bookmark not defined.
4 Abbreviations . Error! Bookmark not defined.
5 Qualification . Error! Bookmark not defined.
5.1 General . Error! Bookmark not defined.
5.2 Part validation . Error! Bookmark not defined.
5.3 Technical documentation relating to part(s) produced . Error! Bookmark not defined.
5.4 Facility documentation. Error! Bookmark not defined.
5.4.1 Additive manufacturer documentation requirements . Error! Bookmark not defined.
5.4.2 Subcontractor documentation requirements . Error! Bookmark not defined.
5.5 Quality assurance documentation . Error! Bookmark not defined.
6 Post processing . Error! Bookmark not defined.
6.1 General . Error! Bookmark not defined.
6.2 Post-build activities . Error! Bookmark not defined.
6.3 Thermal treatment . Error! Bookmark not defined.
6.3.1 General . Error! Bookmark not defined.
6.3.2 Reducing residual stresses . Error! Bookmark not defined.
6.3.3 Reducing anisotropy . Error! Bookmark not defined.
6.3.4 Prepare material for mechanical post-processing . Error! Bookmark not defined.
6.3.5 Densification . Error! Bookmark not defined.
6.3.6 Annealing and aging . Error! Bookmark not defined.
6.4 Separation from the built platform and support structures . Error! Bookmark not defined.
6.5 Surface finishing . Error! Bookmark not defined.
6.5.1 Surface finishing operations . Error! Bookmark not defined.
6.5.2 Machining allowances . Error! Bookmark not defined.
7 Inspection and testing . Error! Bookmark not defined.
7.1 General . Error! Bookmark not defined.
7.2 Metallurgical testing . Error! Bookmark not defined.
7.2.1 Objective . Error! Bookmark not defined.
7.2.2 Test specimen selection, design, and preparation for part characterizationError! Bookmark not defined.
7.2.3 Test methods, parameters, and test specimens . Error! Bookmark not defined.
7.2.4 Chemical analysis . Error! Bookmark not defined.
7.2.5 Metallurgical properties . Error! Bookmark not defined.
7.2.6 Determining the non-metallic inclusion content . Error! Bookmark not defined.
7.2.7 Analysis and test report . Error! Bookmark not defined.
7.3 Material testing . Error! Bookmark not defined.
7.3.1 General . Error! Bookmark not defined.
7.3.2 Orientation in the build space . Error! Bookmark not defined.
7.3.3 Test specimen geometry and surface quality . Error! Bookmark not defined.
© ISO/ASTM International 2023 – All rights reserved iii
ISO/ASTM FDIS 52908:2023(E)
7.3.4 Density (part) . Error! Bookmark not defined.
7.3.5 Archimedean method . Error! Bookmark not defined.
7.3.6 Image analysis of metallographic specimens . Error! Bookmark not defined.
7.4 Mechanical testing . Error! Bookmark not defined.
7.4.1 Static testing . Error! Bookmark not defined.
7.4.2 Dynamic testing . Error! Bookmark not defined.
7.5 Surface quality inspection . Error! Bookmark not defined.
7.6 Geometrical inspection (form, dimension, and tolerances) . Error! Bookmark not defined.
7.7 Non-destructive testing . Error! Bookmark not defined.
Bibliography . Error! Bookmark not defined.
Foreword . vi
Introduction. vii
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 2
4 Abbreviations . 3
5 Qualification . 3
5.1 General . 3
5.2 Part validation . 3
5.3 Technical documentation relating to part(s) produced . 4
5.4 Facility documentation. 4
5.4.1 Additive manufacturer documentation requirements . 4
5.4.2 Subcontractor documentation requirements . 4
5.5 Quality assurance documentation . 5
6 Post processing . 5
6.1 General . 5
6.2 Post-build activities . 5
6.3 Thermal treatment . 6
6.3.1 General . 6
6.3.2 Reducing residual stresses . 6
6.3.3 Reducing anisotropy . 6
6.3.4 Prepare material for mechanical post-processing . 6
6.3.5 Densification . 6
6.3.6 Annealing and aging . 6
6.4 Separation from the built platform and support structures . 7
6.5 Surface finishing . 7
6.5.1 Surface finishing operations . 7
6.5.2 Machining allowances . 7
7 Inspection and testing . 7
7.1 General . 7
7.2 Metallurgical testing . 8
7.2.1 Objective . 8
7.2.2 Test specimen selection, design, and preparation for part characterization . 8
7.2.3 Test methods, parameters, and test specimens . 10
7.2.4 Chemical analysis .
...
PROJET
NORME ISO/ASTM
FINAL
INTERNATIONALE FDIS
ISO/TC 261
Fabrication additive de métaux —
Secrétariat: DIN
Propriétés des pièces finies — Post-
Début de vote:
2023-08-23 traitement, inspection et essais des
pièces produites par fusion sur lit de
Vote clos le:
2023-10-18
poudre
Additive manufacturing of metals — Finished Part properties — Post-
processing, inspection and testing of parts produced by powder bed
fusion
TRAITEMENT PARALLÈLE ISO/CEN
LES DESTINATAIRES DU PRÉSENT PROJET SONT
INVITÉS À PRÉSENTER, AVEC LEURS OBSER-
VATIONS, NOTIFICATION DES DROITS DE PRO-
PRIÉTÉ DONT ILS AURAIENT ÉVENTUELLEMENT
CONNAISSANCE ET À FOURNIR UNE DOCUMEN-
TATION EXPLICATIVE.
OUTRE LE FAIT D’ÊTRE EXAMINÉS POUR
ÉTABLIR S’ILS SONT ACCEPTABLES À DES FINS
INDUSTRIELLES, TECHNOLOGIQUES ET COM-
Numéro de référence
MERCIALES, AINSI QUE DU POINT DE VUE
ISO/ASTM FDIS 52908:2023(F)
DES UTILISATEURS, LES PROJETS DE NORMES
INTERNATIONALES DOIVENT PARFOIS ÊTRE
CONSIDÉRÉS DU POINT DE VUE DE LEUR POSSI-
BILITÉ DE DEVENIR DES NORMES POUVANT
SERVIR DE RÉFÉRENCE DANS LA RÉGLEMENTA-
TION NATIONALE. © ISO/ASTM International 2023
ISO/ASTM FDIS 52908:2023(F)
PROJET
NORME ISO/ASTM
FINAL
INTERNATIONALE FDIS
ISO/TC 261
Fabrication additive de métaux —
Secrétariat: DIN
Propriétés des pièces finies — Post-
Début de vote:
2023-08-23 traitement, inspection et essais des
pièces produites par fusion sur lit de
Vote clos le:
2023-10-18
poudre
Additive manufacturing of metals — Finished Part properties — Post-
processing, inspection and testing of parts produced by powder bed
fusion
DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO/ASTM International 2023
Tous droits réservés. Sauf prescription différente ou nécessité dans le contexte de sa mise en œuvre, aucune partie de cette
publication ne peut être reproduite ni utilisée sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique,
TRAITEMENT PARALLÈLE ISO/CEN
y compris la photocopie, ou la diffusion sur l’internet ou un intranet, sans autorisation écrite soit de l’ISO à l’adresse ci-après,
soit d’un organisme membre de l’ISO dans le pays du demandeur. Aux États-Unis, les demandes doivent être adressées à ASTM
LES DESTINATAIRES DU PRÉSENT PROJET SONT
International.
INVITÉS À PRÉSENTER, AVEC LEURS OBSER-
VATIONS, NOTIFICATION DES DROITS DE PRO-
ISO copyright office ASTM International
PRIÉTÉ DONT ILS AURAIENT ÉVENTUELLEMENT
Case postale 401 • Ch. de Blandonnet 8 100 Barr Harbor Drive, PO Box C700
CONNAISSANCE ET À FOURNIR UNE DOCUMEN-
TATION EXPLICATIVE.
CH-1214 Vernier, Genève West Conshohocken, PA 19428-2959, USA
Tél.: +41 22 749 01 11 Tél.: +610 832 9634 OUTRE LE FAIT D’ÊTRE EXAMINÉS POUR
ÉTABLIR S’ILS SONT ACCEPTABLES À DES FINS
Fax: +41 22 749 09 47 Fax: +610 832 9635
INDUSTRIELLES, TECHNOLOGIQUES ET COM-
Numéro de référence
E-mail: copyright@iso.org E-mail: khooper@astm.org
MERCIALES, AINSI QUE DU POINT DE VUE
ISO/ASTM FDIS 52908:2023(F)
Web: www.iso.org Web: www.astm.org
DES UTILISATEURS, LES PROJETS DE NORMES
INTERNATIONALES DOIVENT PARFOIS ÊTRE
Publié en Suisse
CONSIDÉRÉS DU POINT DE VUE DE LEUR POSSI-
BILITÉ DE DEVENIR DES NORMES POUVANT
SERVIR DE RÉFÉRENCE DANS LA RÉGLEMENTA-
ii
© ISO/ASTM International 2023 – Tous droits réservés
TION NATIONALE. © ISO/ASTM International 2023
ISO/ASTM FDIS 52908:2023(F)
Sommaire Page
Avant-propos .v
Introduction . vi
1 Domaine d’application . 1
2 Références normatives .1
3 Termes et définitions . 2
4 Abréviations . 2
5 Qualification . 2
5.1 Généralités . 2
5.2 Validation de la pièce . 3
5.3 Documentation technique relative à la ou aux pièce(s) produite(s). 3
5.4 Documentation de l’installation . 3
5.4.1 Exigences de documentation des fabricants additifs . 3
5.4.2 Exigences de documentation des sous-traitants . 4
5.5 Documentation d’assurance qualité . 4
6 Post-traitement . 4
6.1 Généralités . 4
6.2 Activités de post-traitement . 4
6.3 Traitement thermique . 5
6.3.1 Généralités . 5
6.3.2 Réduction du stress résiduel . 5
6.3.3 Réduction de l’anisotropie . 5
6.3.4 Préparation du matériau pour le post-traitement mécanique . 5
6.3.5 Densification . 5
6.3.6 Recuit et vieillissement . 6
6.4 Séparation de la plateforme de fabrication et des structures support . 6
6.5 Finition de surface . 6
6.5.1 Opérations de finition de surface . 6
6.5.2 Tolérances d’usinage . 6
7 Inspection et essais . 7
7.1 Généralités . 7
7.2 Essais métallurgiques . 7
7.2.1 Objectif . 7
7.2.2 Sélection, conception, et préparation de l'éprouvette pour la caractérisation
de la pièce . 7
7.2.3 Méthodes d’essai, paramètres et éprouvettes. 9
7.2.4 Analyse chimique . 9
7.2.5 Propriétés métallurgiques . 9
7.2.6 Détermination de la teneur en inclusions non métalliques. 9
7.2.7 Analyse et rapport d’essai . 9
7.3 Essais de matériau. 10
7.3.1 Généralités . 10
7.3.2 Orientation dans l’espace de fabrication . 10
7.3.3 Géométrie et qualité de surface de l'éprouvette d'essai . 10
7.3.4 Densité (pièce) . 10
7.3.5 Méthode archimédienne .12
7.3.6 Analyse d’images d’éprouvettes métallographiques .13
7.4 Essai mécanique . 15
7.4.1 Essais statiques . 15
7.4.2 Essais dynamiques . 20
7.5 Inspection de la qualité de surface . 21
7.6 Inspection géométrique (forme, dimensions et tolérances) .22
7.7 Essais non destructifs .22
iii
© ISO/ASTM International 2023 – Tous droits réservés
ISO/ASTM FDIS 52908:2023(F)
Bibliographie .23
iv
© ISO/ASTM International 2023 – Tous droits réservés
ISO/ASTM FDIS 52908:2023(F)
Avant-propos
L’ISO (Organisation internationale de normalisation) est une fédération mondiale d’organismes
nationaux de normalisation (comités membres de l’ISO). L’élaboration des Normes internationales est
en général confiée aux comités techniques de l’ISO. Chaque comité membre intéressé par une étude
a le droit de faire partie du comité technique créé à cet effet. Les organisations internationales,
gouvernementales et non gouvernementales, en liaison avec l’ISO participent également aux travaux.
L’ISO collabore étroitement avec la Commission électrotechnique internationale (CEI) en ce qui
concerne la normalisation électrotechnique.
Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont
décrites dans les Directives ISO/IEC, Partie 1. Il convient, en particulier de prendre note des différents
critères d’approbation requis pour les différents types de document ISO. Le présent document a été
rédigé conformément aux règles de rédaction données dans les Directives ISO/IEC, Partie 2 (voir
www.iso.org/directives).
L’ISO attire l’attention sur le fait que la mise en application du présent document peut entraîner
l’utilisation d’un ou de plusieurs brevets. L’ISO ne prend pas position quant à la preuve, à la validité
et à l’applicabilité de tout droit de brevet revendiqué à cet égard. À la date de publication du présent
document, l’ISO n'avait pas reçu notification qu’un ou plusieurs brevets pouvaient être nécessaires à sa
mise en application. Toutefois, il y a lieu d’avertir les responsables de la mise en application du présent
document que des informations plus récentes sont
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.