ISO 17640:2018
(Main)Non-destructive testing of welds — Ultrasonic testing — Techniques, testing levels, and assessment
Non-destructive testing of welds — Ultrasonic testing — Techniques, testing levels, and assessment
This document specifies techniques for the manual ultrasonic testing of fusion-welded joints in metallic materials of thickness ≥8 mm which exhibit low ultrasonic attenuation (especially that due to scatter) at object temperatures from 0 °C to 60 °C. It is primarily intended for use on full penetration welded joints where both the welded and parent material are ferritic. Where material-dependent ultrasonic values are specified in this document, they are based on steels having an ultrasonic sound velocity of (5 920 ± 50) m/s for longitudinal waves and (3 255 ± 30) m/s for transverse waves. This document specifies four testing levels, each corresponding to a different probability of detection of imperfections. Guidance on the selection of testing levels A, B, and C is given in Annex A. This document specifies that the requirements of testing level D, which is intended for special applications, be in accordance with general requirements. Testing level D can only be used when defined by specification. This includes tests of metals other than ferritic steel, tests on partial penetration welds, tests with automated equipment, and tests at object temperatures outside the range 0 °C to 60 °C. This document can be used for the assessment of discontinuities, for acceptance purposes, by either of the following techniques: a) evaluation based primarily on length and echo amplitude of the discontinuity; b) evaluation based on characterization and sizing of the discontinuity by probe movement techniques.
Essais non destructifs des assemblages soudés — Contrôle par ultrasons — Techniques, niveaux d'essai et évaluation
Le présent document spécifie des techniques de contrôle manuel par ultrasons des assemblages en matériaux métalliques soudés par fusion, d'épaisseur égale ou supérieure à 8 mm, présentant une atténuation relativement faible des ultrasons (en particulier celle due à la diffusion) à des températures d'objet comprises entre 0 °C et 60 °C. Elle vise particulièrement les assemblages soudés à pleine pénétration dont le métal de base et la soudure sont ferritiques. Lorsque les valeurs des caractéristiques ultrasonores dépendantes des matériaux sont précisées dans le présent document, elles concernent des aciers dans lesquels la vitesse des ondes ultrasonores est égale à (5 920 ± 50) m/s pour les ondes longitudinales et à (3 255 ± 30) m/s pour les ondes transversales. Le présent document spécifie quatre niveaux de contrôle, chacun correspondant à une probabilité différente de détection des défauts. Un guide du choix des niveaux de contrôle A, B et C est donné dans l'Annexe A. Le présent document spécifie que les exigences relatives au niveau de contrôle D, qui est prévu pour des applications spéciales, sont conformes aux exigences générales. Le niveau de contrôle D ne peut être utilisé que lorsqu'il est défini par une spécification. Cela inclut les contrôles de métaux autres que les aciers ferritiques, les contrôles sur des soudures à pénétration partielle, les contrôles avec des équipements automatisés, et les contrôles à des températures d'objet situées hors de la plage 0 °C à 60 °C. Le présent document peut être utilisé pour l'évaluation des discontinuités, aux fins d'acceptation, par l'une des techniques suivantes: a) évaluation fondée principalement sur la longueur et l'amplitude d'écho de la discontinuité; b) évaluation fondée sur la caractérisation et le dimensionnement de la discontinuité par des techniques de déplacement du traducteur.
General Information
Relations
Buy Standard
Standards Content (Sample)
INTERNATIONAL ISO
STANDARD 17640
Fourth edition
2018-10
Non-destructive testing of welds —
Ultrasonic testing — Techniques,
testing levels, and assessment
Essais non destructifs des assemblages soudés — Contrôle par
ultrasons — Techniques, niveaux d'essai et évaluation
Reference number
©
ISO 2018
© ISO 2018
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication may
be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting
on the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address
below or ISO’s member body in the country of the requester.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: +41 22 749 01 11
Fax: +41 22 749 09 47
Email: copyright@iso.org
Website: www.iso.org
Published in Switzerland
ii © ISO 2018 – All rights reserved
Contents Page
Foreword .iv
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 2
4 Symbols . 2
5 General . 3
6 Information required prior to testing . 3
6.1 Items to be specified . 3
6.2 Specific information required before testing . 4
6.3 Written test procedure . 4
7 Requirements for personnel and equipment . 4
7.1 Personnel qualifications . 4
7.2 Test equipment . 4
7.3 Probe parameters . 5
7.3.1 Test frequency . 5
7.3.2 Angles of incidence . 5
7.3.3 Transducer size . 5
7.3.4 Adaptation of probes to curved scanning surfaces . 5
7.3.5 Coupling media . 6
8 Testing volume . 6
9 Preparation of scanning surfaces . 6
10 Parent metal testing . 6
11 Range and sensitivity setting . 7
11.1 General . 7
11.2 Reference for sensitivity setting . 8
11.3 Evaluation levels . 9
11.4 Transfer correction . 9
11.5 Signal-to-noise ratio . 9
12 Testing levels . 9
13 Testing techniques .10
13.1 General .10
13.2 Manual scan path .10
13.3 Testing for imperfections perpendicular to the testing surface .10
13.4 Location of discontinuities .10
13.5 Evaluation of indications .10
13.5.1 General.10
13.5.2 Maximum echo amplitude .10
13.5.3 Discontinuity length.10
13.5.4 Discontinuity height . .10
13.5.5 Characterization of discontinuities .10
14 Test report .11
Annex A (normative) Testing levels for various types of welded joints .13
Bibliography .30
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out
through ISO technical committees. Each member body interested in a subject for which a technical
committee has been established has the right to be represented on that committee. International
organizations, governmental and non-governmental, in liaison with ISO, also take part in the work.
ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of
electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are
described in the ISO/IEC Directives, Part 1. In particular, the different approval criteria needed for the
different types of ISO documents should be noted. This document was drafted in accordance with the
editorial rules of the ISO/IEC Directives, Part 2 (see www .iso .org/directives).
Attention is drawn to the possibility that some of the elements of this document may be the subject of
patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of
any patent rights identified during the development of the document will be in the Introduction and/or
on the ISO list of patent declarations received (see www .iso .org/patents).
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation of the voluntary nature of standards, the meaning of ISO specific terms and
expressions related to conformity assessment, as well as information about ISO's adherence to the
World Trade Organization (WTO) principles in the Technical Barriers to Trade (TBT) see www .iso
.org/iso/foreword .html.
This document was prepared by Technical Committee ISO/TC 44, Welding and allied processes,
Subcommittee SC 5, Testing and inspection of welds.
Any feedback, question or request for official interpretation related to any aspect of this document
should be directed to the Secretariat of ISO/TC 44/SC 5 via your national standards body. A complete
listing of these bodies can be found at www .iso .org/members .html. Official interpretations, where they
exist, are available from this page: https: //committee .iso .org/sites/tc44/home/interpretation .html.
This fourth edition cancels and replaces the third edition (ISO 17640:2017), which has been technically
revised. The main change compared to the previous edition is that Figure A.4 a) and b) has been
corrected.
iv © ISO 2018 – All rights reserved
INTERNATIONAL STANDARD ISO 17640:2018(E)
Non-destructive testing of welds — Ultrasonic testing —
Techniques, testing levels, and assessment
1 Scope
This document specifies techniques for the manual ultrasonic testing of fusion-welded joints in metallic
materials of thickness ≥8 mm which exhibit low ultrasonic attenuation (especially that due to scatter)
at object temperatures from 0 °C to 60 °C. It is primarily intended for use on full penetration welded
joints where both the welded and parent material are ferritic.
Where material-dependent ultrasonic values are specified in this document, they are based on steels
having an ultrasonic sound velocity of (5 920 ± 50) m/s for longitudinal waves and (3 255 ± 30) m/s for
transverse waves.
This document specifies four testing levels, each corresponding to a different probability of detection of
imperfections. Guidance on the selection of testing levels A, B, and C is given in Annex A.
This document specifies that the requirements of testing level D, which is intended for special
applications, be in accordance with general requirements. Testing level D can only be used when defined
by specification. This includes tests of metals other than ferritic steel, tests on partial penetration welds,
tests with automated equipment, and tests at object temperatures outside the range 0 °C to 60 °C.
This document can be used for the assessment of discontinuities, for acceptance purposes, by either of
the following techniques:
a) evaluation based primarily on length and echo amplitude of the discontinuity;
b) evaluation based on characterization and sizing of the discontinuity by probe movement techniques.
2 Normative references
The following documents are referred to in the text in such a way that some or all of their content
constitutes requirements of this document. For dated references, only the edition cited applies. For
undated references, the latest edition of the referenced document (including any amendments) applies.
ISO 5577, Non-destructive testing — Ultrasonic testing — Vocabulary
ISO 9712, Non-destructive testing — Qualification and certification of NDT personnel
ISO 11666, Non-destructive testing of welds — Ultrasonic testing— Acceptance levels
ISO 16810, Non-destructive testing — Ultrasonic testing — General principles
ISO 16811, Non-destructive testing — Ultrasonic testing — Sensitivity and range setting
ISO 16826, Non-destructive testing — Ultrasonic testing — Examination for discontinuities perpendicular
to the s
...
NORME ISO
INTERNATIONALE 17640
Quatrième édition
2018-10
Essais non destructifs des
assemblages soudés — Contrôle par
ultrasons — Techniques, niveaux
d'essai et évaluation
Non-destructive testing of welds — Ultrasonic testing — Techniques,
testing levels, and assessment
Numéro de référence
©
ISO 2018
DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2018
Tous droits réservés. Sauf prescription différente ou nécessité dans le contexte de sa mise en œuvre, aucune partie de cette
publication ne peut être reproduite ni utilisée sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique,
y compris la photocopie, ou la diffusion sur l’internet ou sur un intranet, sans autorisation écrite préalable. Une autorisation peut
être demandée à l’ISO à l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.
ISO copyright office
Case postale 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Genève
Tél.: +41 22 749 01 11
Fax: +41 22 749 09 47
E-mail: copyright@iso.org
Web: www.iso.org
Publié en Suisse
ii © ISO 2018 – Tous droits réservés
Sommaire Page
Avant-propos .iv
1 Domaine d'application . 1
2 Références normatives . 1
3 Termes et définitions . 2
4 Symboles . 2
5 General . 3
6 Informations requises avant le contrôle . 3
6.1 Points à spécifier . 3
6.2 Informations spécifiques requises avant le contrôle . 4
6.3 Procédure de contrôle écrite . 4
7 Exigences relatives au personnel et au matériel . 4
7.1 Qualification du personnel . 4
7.2 Matériel d’essai . 5
7.3 Paramètres des traducteurs . 5
7.3.1 Fréquence d'essai . 5
7.3.2 Angles d'incidence . 5
7.3.3 Taille du transducteur . 5
7.3.4 Adaptation des traducteurs aux surfaces de balayage incurvées . 6
7.3.5 Milieu de couplage . . 6
8 Volume à contrôler . 6
9 Préparation des surfaces de balayage . 6
10 Contrôle du métal de base . 7
11 Réglage de la base de temps et de la sensibilité . 8
11.1 Généralités . 8
11.2 Référence pour le réglage de la sensibilité . 8
11.3 Niveaux d'évaluation . 9
11.4 Correction de transfert. 9
11.5 Rapport signal-bruit . 9
12 Niveaux de contrôle .10
13 Techniques de contrôle.10
13.1 Généralités .10
13.2 Exploration manuelle .10
13.3 Recherche des défauts perpendiculaires à la surface .10
13.4 Localisation des discontinuités .10
13.5 Évaluation des indications .11
13.5.1 Généralités .11
13.5.2 Amplitude maximale de l'écho .11
13.5.3 Longueur de la discontinuité .11
13.5.4 Hauteur de la discontinuité .11
13.5.5 Caractérisation des discontinuités .11
14 Rapport de contrôle .11
Annexe A (normative) Niveaux de contrôle pour différents types d'assemblages soudés .13
Bibliographie .27
Avant-propos
L'ISO (Organisation internationale de normalisation) est une fédération mondiale d'organismes
nationaux de normalisation (comités membres de l'ISO). L'élaboration des Normes internationales est
en général confiée aux comités techniques de l'ISO. Chaque comité membre intéressé par une étude
a le droit de faire partie du comité technique créé à cet effet. Les organisations internationales,
gouvernementales et non gouvernementales, en liaison avec l'ISO participent également aux travaux.
L'ISO collabore étroitement avec la Commission électrotechnique internationale (IEC) en ce qui
concerne la normalisation électrotechnique.
Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont
décrites dans les Directives ISO/IEC, Partie 1. Il convient, en particulier, de prendre note des différents
critères d'approbation requis pour les différents types de documents ISO. Le présent document a été
rédigé conformément aux règles de rédaction données dans les Directives ISO/IEC, Partie 2 (voir www
.iso .org/directives).
L'attention est attirée sur le fait que certains des éléments du présent document peuvent faire l'objet de
droits de propriété intellectuelle ou de droits analogues. L'ISO ne saurait être tenue pour responsable
de ne pas avoir identifié de tels droits de propriété et averti de leur existence. Les détails concernant
les références aux droits de propriété intellectuelle ou autres droits analogues identifiés lors de
l'élaboration du document sont indiqués dans l'Introduction et/ou dans la liste des déclarations de
brevets reçues par l'ISO (voir www .iso .org/brevets).
Les appellations commerciales éventuellement mentionnées dans le présent document sont données
pour information, par souci de commodité, à l’intention des utilisateurs et ne sauraient constituer un
engagement.
Pour une explication de la nature volontaire des normes, la signification des termes et expressions
spécifiques de l'ISO liés à l'évaluation de la conformité, ou pour toute information au sujet de l'adhésion
de l'ISO aux principes de l’Organisation mondiale du commerce (OMC) concernant les obstacles
techniques au commerce (OTC), voir www .iso .org/avant -propos.
Le présent document a été élaboré par le comité technique ISO/TC 44, Soudage et techniques connexes,
sous-comité SC 5, Essais et contrôle des soudures.
Il convient que l’utilisateur adresse tout retour d’information ou toute question concernant le présent
document au Secrétariat de l’ISO/TC 44/SC 5 par le biais de l’organisme national de normalisation de
son pays. Une liste exhaustive desdits organismes se trouve à l’adresse www .iso .org/fr/members .html.
Les interprétations officielles, lorsqu'elles existent sont disponibles depuis la page: https: //committee
.iso .org/sites/tc44/home/interpretation .html.
Cette troisième édition annule et remplace la deuxième édition (ISO 17640:2017), qui a fait l’objet d’une
révision technique. La principale modification par rapport à l’édition précédente concerne la correction
de la Figure A.4 a) et b).
iv © ISO 2018 – Tous droits réservés
NORME INTERNATIONALE ISO 17640:2018(F)
Essais non destructifs des assemblages soudés — Contrôle
par ultrasons — Techniques, niveaux d'essai et évaluation
1 Domaine d'application
Le présent document spécifie des techniques de contrôle manuel par ultrasons des assemblages en
matériaux métalliques soudés par fusion, d'épaisseur égale ou supérieure à 8 mm, présentant une
atténuation relativement faible des ultrasons (en particulier celle due à la diffusion) à des températures
d'objet comprises entre 0 °C et 60 °C. Elle vise particulièrement les assemblages soudés à pleine
pénétration dont le métal de base et la soudure sont ferritiques.
Lorsque les valeurs des caractéristiques ultrasonores dépendantes des matériaux sont précisées dans le
présent document, elles concernent des aciers dans lesquels la vitesse des ondes ultrasonores est égale
à (5 920 ± 50) m/s pour les ondes longitudinales et à (3 255 ± 30) m/s pour les ondes transversales.
Le présent document spécifie quatre niveaux de contrôle, chacun correspondant à une probabilité
différente de détection des défauts. Un guide du choix des niveaux de contrôle A, B et C est donné dans
l'Annexe A.
Le présent document spécifie que les exigences relatives au niveau de contrôle D, qui est prévu pour
des applications spéciales, sont conformes aux exigences générales. Le niveau de contrôle D ne peut
être utilisé que lorsqu'il est défini par une spécification. Cela inclut les contrôles de métaux autres
que les aciers ferritiques, les contrôles sur des soudures à pénétration partielle, les contrôles avec des
équipements automatisés, et les contrôles à des températures d'objet situées hors de la plage 0 °C à 60 °C.
Le présent document peut être utilisé pour l'évaluation des discontinuités, aux fins d'acceptation, par
l'une des techniques suivantes:
a) évaluation fondée principalement sur la longueur et l'amplitude d'écho de la discontinuité;
b) évaluation fondée sur la caractérisation et le dimensionnement de la discontinuité par des
techniques de déplacement du traducteur.
2 Références normatives
Les documents suivants cités dans le texte constituent, pour tout ou partie de leur contenu, des
exigences du présent document. Pour les références datées, seule l’édition citée s’applique. Pour les
références non datées, la dernière édit
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.