ISO 10066:1991
(Main)Flexible cellular polymeric materials - Determination of creep in compression
Flexible cellular polymeric materials - Determination of creep in compression
Contains a procedure intended primarily for quality assurance in packaging applications. Describes the principle, the apparatus, the preparation of specimens, conditioning methods, the test procedure, and the contents of the test report.
Matériaux polymères alvéolaires souples — Détermination du fluage en compression
La présente Norme internationale décrit le mode opératoire pour déterminer le fluage d'un matériau polymère alvéolaire souple lorsqu'il est comprimé par une force statique, destiné principalement à l'assurance de la qualité des emballages. NOTE 1 L'essai peut aussi servir pour l'obtention de données de conception. Par exemple, un matériau montrant un fluage excessif ne devrait pas être choisi pour la fabrication de coussins destinés à supporter des objets emballés, à cause de la possibilité de glissement au cours du stockage. La quantité de fluage et la contrainte statique de sécurité admissibles dépendent de l'épaisseur du coussin, de la durée de vie de l'emballage et des conditions de stockage.
General Information
- Status
- Published
- Publication Date
- 13-Nov-1991
- Technical Committee
- ISO/TC 45/SC 4 - Products (other than hoses)
- Drafting Committee
- ISO/TC 45/SC 4/WG 8 - Flexible and semi-rigid cellular material
- Current Stage
- 9093 - International Standard confirmed
- Start Date
- 11-Sep-2023
- Completion Date
- 13-Dec-2025
Relations
- Consolidated By
ISO 3766:2003 - Construction drawings - Simplified representation of concrete reinforcement - Effective Date
- 06-Jun-2022
Overview
ISO 10066:1991 is a key international standard developed by ISO Technical Committee ISO/TC 45, focusing on flexible cellular polymeric materials. This standard outlines a comprehensive procedure for the determination of creep in compression of soft cellular polymer materials, primarily to support quality assurance in packaging applications. It details the principles, apparatus requirements, specimen preparation, conditioning methods, and test procedures necessary to measure and report the creep behavior of these materials under static compressive stress.
Accurately measuring and controlling creep in flexible cellular polymers is crucial for ensuring product performance, especially in cushioning packaging where excessive deformation can compromise protection. ISO 10066:1991 helps manufacturers and quality professionals ensure that materials meet necessary criteria for durability and reliability.
Key Topics
Scope and Application
The standard focuses on flexible cellular polymeric materials subjected to static compressive loads, providing a method to quantify deformation (creep) over time. While intended mainly for packaging quality assurance, its use extends to product design decisions where material creep may affect performance.Test Principle
Creep is measured as the variation in deformation of a sample under a prescribed static compressive stress, usually below 10 kPa, over time intervals (15 minutes to 72 hours). The test captures both the immediate and long-term compression behavior.Specimen Preparation
Test specimens are rectangular parallelepipeds, typically 50 mm by 50 mm in length and width, with thickness between 20 mm and 30 mm. Careful cutting methods avoiding heat or mechanical damage must be employed. Specimens may include surface skin if it forms an integral part of the material.Conditioning and Test Environment
Specimens are conditioned for a minimum of 16 hours under controlled temperature and humidity to ensure consistent testing conditions. Typical test conditions are 23°C ± 2°C and 50% ± 5% relative humidity for temperate climates or 27°C ± 2°C and 65% ± 5% humidity for tropical climates.Apparatus Requirements
The testing device includes two smooth parallel plates (at least one with automatic alignment) capable of applying and maintaining a uniform static compressive force with minimal variation (<1%) and measuring specimen thickness changes with 0.1 mm accuracy.Measurement and Calculation
Thickness measurements are taken initially, then after 15 minutes and 72 hours under compression, with a final measurement after 30 minutes of elastic recovery post-load removal. From these, percentage creep deformation and elastic recovery are calculated using standardized formulas.Test Report Contents
The standard specifies detailed reporting requirements including reference to the standard, material description, conditioning and test conditions, applied stress level, calculated creep and elastic recovery percentages, individual test results, and notes on specimen preparation such as presence/location of surface skin.
Applications
ISO 10066:1991 finds practical use in:
Packaging Industry
Ensuring that polymeric cushioning materials do not exhibit excessive long-term creep that would reduce protection during storage and transport.Material Quality Control
Verification of raw and finished material batches to maintain consistent and reliable mechanical properties.Product Development
Providing critical design input for selecting materials with appropriate compressive behavior over the expected product lifecycle.Compliance and Standardization
Facilitating uniform testing methods across manufacturers and suppliers, improving comparability and contractual quality assurance.
Related Standards
ISO 1923:1981
For determination of linear dimensions of cellular plastics and rubbers, referenced for specimen measurement techniques.ISO/TC 45 Series
Additional standards related to elastomers and elastomeric products may complement ISO 10066 for a fuller assessment of polymer properties.Packaging and Testing Standards
Depending on application, ISO 10066 results may be integrated with broader packaging performance standards to ensure overall package integrity.
Keywords: ISO 10066, flexible cellular polymeric materials, compression creep test, polymeric cushioning, packaging quality assurance, creep deformation, compression testing, specimen conditioning, test apparatus, polymer resilience, material quality control.
ISO 10066:1991 - Flexible cellular polymeric materials -- Determination of creep in compression
ISO 10066:1991 - Matériaux polymeres alvéolaires souples -- Détermination du fluage en compression
ISO 10066:1991 - Matériaux polymeres alvéolaires souples -- Détermination du fluage en compression
Frequently Asked Questions
ISO 10066:1991 is a standard published by the International Organization for Standardization (ISO). Its full title is "Flexible cellular polymeric materials - Determination of creep in compression". This standard covers: Contains a procedure intended primarily for quality assurance in packaging applications. Describes the principle, the apparatus, the preparation of specimens, conditioning methods, the test procedure, and the contents of the test report.
Contains a procedure intended primarily for quality assurance in packaging applications. Describes the principle, the apparatus, the preparation of specimens, conditioning methods, the test procedure, and the contents of the test report.
ISO 10066:1991 is classified under the following ICS (International Classification for Standards) categories: 83.100 - Cellular materials. The ICS classification helps identify the subject area and facilitates finding related standards.
ISO 10066:1991 has the following relationships with other standards: It is inter standard links to ISO 3766:2003. Understanding these relationships helps ensure you are using the most current and applicable version of the standard.
You can purchase ISO 10066:1991 directly from iTeh Standards. The document is available in PDF format and is delivered instantly after payment. Add the standard to your cart and complete the secure checkout process. iTeh Standards is an authorized distributor of ISO standards.
Standards Content (Sample)
INTERNATIONAL
STANDARD
First edition
1991-l 1-15
Flexible cellular polymeric materials -
Determination of creep in compression
Mat&-iaux polymkes alv6olaires souples - D6termination du fluage en
compression
Reference number
IS0 10066:1991(E)
IS0 10066:1991(E)
Foreword
IS0 (the International Organization for Standardization) is a worldwide
federation of national standards bodies (IS0 member bodies). The work
of preparing International Standards is normally carried out through IS0
technical committees. Each member body interested in a subject for
which a technical committee has been established has the right to be
represented on that committee. International organizations, govern-
mental and non-governmental, in liaison with ISO, also take part in the
work. IS0 collaborates closely with the International Electrotechnical
Commission (IEC) on all matters of electrotechnical standardization.
Draft International Standards adopted by the technical committees are
circulated to the member bodies for voting. Publication as an lnter-
national Standard requires approval by at least 75 % of the member
bodies casting a vote.
International Standard IS0 10066 was prepared by Technical Committee
ISO/TC 45, Rubber and rubber products.
0 IS0 1991
All rights reserved, No part of this publication may be reproduced or utilized in any form
or by any means, electronic or mechanical, including photocopying and microfilm, without
permission in writing from the publisher.
International Organization for Standardization
Case Postale 56 l CH-1211 Geneve 20 l Switzerland
Printed in Switzerland
ii
_-- -~
IS0 10066:1991 (E)
INTERNATIONAL STANDARD
Flexible cellular polymeric materials - Determination of
creep in compression
3.3 percentage compression after recovery: The
1 Scope
percentage loss in test piece thickness after 72 h
under static stress followed by a 30 min recovery
This International Standard describes the procedure
period.
for determining the creep of a flexible cellular
polymeric material when compressed by a static
force, intended primarily for quality assurance in
4 Principle
packaging applications.
The change in deformation under a static stress with
NOTE 1 The test may also be used to obtain design
time is measured.
data. For example, a material that shows excessive creep
is not likely to be selected for the manufacture of cushions
to support packaged items because of the possibility of
slippage during storage. The amount of creep and safe
5 Apparatus
static stress that can be allowed depends on cushion
thickness, package life and storage conditions.
The apparatus shall consist of two flat, smooth, but
not polished, plates, at least one of which shall be
2 Normative reference
self-aligning, so arranged that they compress the
test piece evenly in the vertical direction. The plates
The following standard contains provisions which,
shall be capable of being loaded so that during the
through reference in this text, constitute provisions
period of test the static stress does not change by
of this International Standard. At the time of publi-
more than + 1 %, and the separation of the plates
cation, the edition indicated was valid. All standards
shall be capable of being measured to within
are subject to revision, and parties to agreements
0,l mm. The compression stress required varies
based on this International Standard are encour-
with the material, but is usually less than 10 kPa.
aged to investigate the possibility of applying the
The apparatus shall be placed on a substantial sup-
most recent edition of the standard indicated below.
port to minimize the effects of vibration.
Members of IEC and IS0 maintain registers of cur-
rently valid International Standards.
6 Test piece
IS0 1923:1981, Cellular plastics and rubbers - De-
termination of linear dimensions.
6.1 The test piece shall be a right parallelepiped
with the following dimensions:
3 Definitions
length: 50 mm + 1 mm
-
For the purposes of this International Standard, the
following definitions apply.
width: 50 mm & 1 mm
3.1 percentage creep strain: The change in
mean thickness: within the range 20 mm to
compressive strain after 72 h exhibited by a test
30 mm
piece under the specified static stress as deter-
mined by measurements 15 min and 72 h after ap-
The thickness of the test piece shall be subject to a
plying the stress.
tolerance of + 1 mm about the selected mean value.
-
3.2 compression stress: The static force per unit The dimensions shall be measured in accordance
area of the original cro
...
ISO
NORME
INTERNATIONALE 10066
Premiere edition
1991-l l-15
Matériaux polymères alvéolaires souples -
Détermination du fluage en compression
Flexible cellular polymeric materials - Determination of creep in
compression
Numéro de référence
Avant-propos
L’ISO (Organisation internationale de normalisation) est une fédération
mondiale d’organismes nationaux de normalisation (comités membres
de I’ISO). L’élaboration des Normes internationales est en général
confiée aux comités techniques de I’ISO. Chaque comité membre inté-
ressé par une étude a le droit de faire partie du comité technique créé
à cet effet. Les organisations internationales, gouvernementales et non
gouvernementales, en liaison avec I’ISO participent également aux tra-
vaux. L’ISO collabore étroitement avec la Commission électrotechnique
internationale (CEI) en ce qui concerne la normalisation électrotech-
nique.
Les projets de Normes internationales adoptés par les comités techni-
ques sont soumis aux comités membres pour vote. Leur publication
comme Normes internationales requiert l’approbation de 75 % au moins
des comités membres votants.
La Norme internationale ISO 10066 a été élaborée par le comité techni-
que ISO/TC 45, Élastomères et produits à base d’élastoméres.
0 ISO 1991
Droits de reproduction réservés. Aucune partie de cette publication ne peut être repro-
duite ni utilisée sous quelque forme que ce soit et par aucun procédé, électronique ou
mécanique, y compris la photocopie et les microfilms, sans l’accord écrit de l’éditeur.
Organisation internationale de normalisation
Genève 20 * Suis se
Case Postale 56 l CH-1211
Imprimé en Suisse
ii
NORME INTERNATIONALE ISO 10066:1991(F)
Matériaux polymères alvéolaires souples - Détermination du
fluage en compression
minée lors de mesurages effectués 15 min et 72 h
1 Domaine d’application
après la mise sous contrainte.
La présente Norme internationale décrit le mode
3.2 contrainte en compression: Force statique par
opératoire pour déterminer le fluage d’un matériau
unité de surface de la section transversale initiale
polymère alvéolaire souple lorsqu’il est comprimé
de l’éprouvette.
destiné principalement à
par une force statique,
l’assurance de la qualité des emballages.
3.3 compression en pourcentage après reprise
élastique: Diminution en pourcentage de l’épaisseur
NOTE 1 L’essai peut aussi servir pour l’obtention de
de l’éprouvette au bout d’une période de 72 h sous
données de conception. Par exemple, un matériau mon-
trant un fluage excessif ne devrait pas être choisi pour la contrainte statique et après une période de reprise
fabrication de coussins destin& à supporter des objets
élastique de 30 min.
emballés, à cause de la possibilité de glissement au cours
du stockage. La quantite de fluage et la contrainte stati-
que de sécurité admissibles dépendent de l’épaisseur du
4 Principe
coussin, de la durée de vie de l’emballage et des condi-
tions de stockage.
On mesure la variation de la déformation d’une
éprouvette soumise à une contrainte statique en
fonction du temps.
2 Référence normative
La norme suivante contient des dispositions qui, par
5 Appareillage
suite de la référence qui en est faite, constituent des
dispositions valables pour la présente Norme inter-
L’appareillage doit comprendre deux plaques pla-
nationale. Au moment de la publication, l’édition in-
nes et lisses mais non polies, dont au moins une
diquée était en vigueur. Toute norme est sujette à
doit être à alignement automatique, disposées de
révision et les parties prenantes des accords fondés
manière à comprimer uniformément l’éprouvette en
sur la présente Norme internationale sont invitées
direction verticale. Les plaques doivent pouvoir être
à rechercher la possibilité d’appliquer l’édition la
mises sous contrainte de facon que la contrainte
plus récente de la norme indiquée ci-après. Les
statique ne varie pas de plus de + 1 % pendant
membres de la CEI et de I’ISO possèdent le registre
l’essai et de sorte que l’écart entre les plaques
des Normes internationales en vigueur à un moment
puisse être mesuré à 0,l mm près. La contrainte en
donné.
compression nécessaire dépend du matériau; tou-
tefois elle est, en général, inférieure à 10 kPa. L’ap-
ISO 1923: 1981, Plastiques et caoutchoucs alvéolaires
pareillage doit être placé sur un support solide afin
- Détermination des dimensions linéaires. ’
de réduire au maximum les effets de vibration.
3 Définitions
6 Éprouvette
Pour les besoins de la présente Norme internatio-
6.1 L’éprouvette doit avoir la forme d’un parallé-
nale, les définitions suivantes s’appliquent.
lépipède rectangle, avec les dimensions suivantes:
3.1 déformation au fluage en pourcentage: Va-
longueur: 50 mm + 1 mm
riation de la déformation en compression présentée
-
au bout de 72 h par une éprouvette soumise à la
largeur: 50 mm + 1 mm
contrainte statique prescrite, telle qu’elle est déter- -
épaisseur moyenne: comprise entre 20 mm et 8.3 Les éprouvettes doivent être c
...
ISO
NORME
INTERNATIONALE 10066
Premiere edition
1991-l l-15
Matériaux polymères alvéolaires souples -
Détermination du fluage en compression
Flexible cellular polymeric materials - Determination of creep in
compression
Numéro de référence
Avant-propos
L’ISO (Organisation internationale de normalisation) est une fédération
mondiale d’organismes nationaux de normalisation (comités membres
de I’ISO). L’élaboration des Normes internationales est en général
confiée aux comités techniques de I’ISO. Chaque comité membre inté-
ressé par une étude a le droit de faire partie du comité technique créé
à cet effet. Les organisations internationales, gouvernementales et non
gouvernementales, en liaison avec I’ISO participent également aux tra-
vaux. L’ISO collabore étroitement avec la Commission électrotechnique
internationale (CEI) en ce qui concerne la normalisation électrotech-
nique.
Les projets de Normes internationales adoptés par les comités techni-
ques sont soumis aux comités membres pour vote. Leur publication
comme Normes internationales requiert l’approbation de 75 % au moins
des comités membres votants.
La Norme internationale ISO 10066 a été élaborée par le comité techni-
que ISO/TC 45, Élastomères et produits à base d’élastoméres.
0 ISO 1991
Droits de reproduction réservés. Aucune partie de cette publication ne peut être repro-
duite ni utilisée sous quelque forme que ce soit et par aucun procédé, électronique ou
mécanique, y compris la photocopie et les microfilms, sans l’accord écrit de l’éditeur.
Organisation internationale de normalisation
Genève 20 * Suis se
Case Postale 56 l CH-1211
Imprimé en Suisse
ii
NORME INTERNATIONALE ISO 10066:1991(F)
Matériaux polymères alvéolaires souples - Détermination du
fluage en compression
minée lors de mesurages effectués 15 min et 72 h
1 Domaine d’application
après la mise sous contrainte.
La présente Norme internationale décrit le mode
3.2 contrainte en compression: Force statique par
opératoire pour déterminer le fluage d’un matériau
unité de surface de la section transversale initiale
polymère alvéolaire souple lorsqu’il est comprimé
de l’éprouvette.
destiné principalement à
par une force statique,
l’assurance de la qualité des emballages.
3.3 compression en pourcentage après reprise
élastique: Diminution en pourcentage de l’épaisseur
NOTE 1 L’essai peut aussi servir pour l’obtention de
de l’éprouvette au bout d’une période de 72 h sous
données de conception. Par exemple, un matériau mon-
trant un fluage excessif ne devrait pas être choisi pour la contrainte statique et après une période de reprise
fabrication de coussins destin& à supporter des objets
élastique de 30 min.
emballés, à cause de la possibilité de glissement au cours
du stockage. La quantite de fluage et la contrainte stati-
que de sécurité admissibles dépendent de l’épaisseur du
4 Principe
coussin, de la durée de vie de l’emballage et des condi-
tions de stockage.
On mesure la variation de la déformation d’une
éprouvette soumise à une contrainte statique en
fonction du temps.
2 Référence normative
La norme suivante contient des dispositions qui, par
5 Appareillage
suite de la référence qui en est faite, constituent des
dispositions valables pour la présente Norme inter-
L’appareillage doit comprendre deux plaques pla-
nationale. Au moment de la publication, l’édition in-
nes et lisses mais non polies, dont au moins une
diquée était en vigueur. Toute norme est sujette à
doit être à alignement automatique, disposées de
révision et les parties prenantes des accords fondés
manière à comprimer uniformément l’éprouvette en
sur la présente Norme internationale sont invitées
direction verticale. Les plaques doivent pouvoir être
à rechercher la possibilité d’appliquer l’édition la
mises sous contrainte de facon que la contrainte
plus récente de la norme indiquée ci-après. Les
statique ne varie pas de plus de + 1 % pendant
membres de la CEI et de I’ISO possèdent le registre
l’essai et de sorte que l’écart entre les plaques
des Normes internationales en vigueur à un moment
puisse être mesuré à 0,l mm près. La contrainte en
donné.
compression nécessaire dépend du matériau; tou-
tefois elle est, en général, inférieure à 10 kPa. L’ap-
ISO 1923: 1981, Plastiques et caoutchoucs alvéolaires
pareillage doit être placé sur un support solide afin
- Détermination des dimensions linéaires. ’
de réduire au maximum les effets de vibration.
3 Définitions
6 Éprouvette
Pour les besoins de la présente Norme internatio-
6.1 L’éprouvette doit avoir la forme d’un parallé-
nale, les définitions suivantes s’appliquent.
lépipède rectangle, avec les dimensions suivantes:
3.1 déformation au fluage en pourcentage: Va-
longueur: 50 mm + 1 mm
riation de la déformation en compression présentée
-
au bout de 72 h par une éprouvette soumise à la
largeur: 50 mm + 1 mm
contrainte statique prescrite, telle qu’elle est déter- -
épaisseur moyenne: comprise entre 20 mm et 8.3 Les éprouvettes doivent être c
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.
Loading comments...