ISO 4591:1992
(Main)Plastics - Film and sheeting - Determination of average thickness of a sample, and average thickness and yield of a roll, by gravimetric techniques (gravimetric thickness)
Plastics - Film and sheeting - Determination of average thickness of a sample, and average thickness and yield of a roll, by gravimetric techniques (gravimetric thickness)
Applies to all plastics films and sheeting and has special value when mechanical scanning is not sufficiently precise, particularly for measuring the thickness of embossed sheeting. The gravimetric thickness is calculated from measurements of mass, area and density of a sample.
Plastiques — Film et feuille — Détermination de l'épaisseur moyenne d'un échantillon, et de l'épaisseur moyenne d'un rouleau, ainsi que de sa surface par unité de masse, par mesures gravimétriques (épaisseur gravimétrique)
General Information
- Status
- Published
- Publication Date
- 02-Dec-1992
- Technical Committee
- ISO/TC 61/SC 11 - Products
- Drafting Committee
- ISO/TC 61/SC 11/WG 3 - Plastics films and sheeting
- Current Stage
- 9093 - International Standard confirmed
- Start Date
- 31-Aug-2022
- Completion Date
- 13-Dec-2025
Relations
- Effective Date
- 15-Apr-2008
Overview
ISO 4591:1992 is an international standard that specifies methods for determining the average thickness of plastic films and sheeting using gravimetric techniques. This standard provides a reliable means to measure the gravimetric thickness of samples and rolls by calculating thickness from mass, area, and density measurements. It is especially valuable for plastics where mechanical scanning is insufficiently accurate, such as embossed films or sheets. Governed by the International Organization for Standardization (ISO), this document ensures consistent and precise thickness measurement practices across the plastics industry.
Key Topics
Scope
ISO 4591:1992 applies to all plastics films and sheeting, emphasizing accuracy when mechanical methods fail-particularly for materials with embossed surfaces.Gravimetric Thickness Determination
The gravimetric thickness is calculated from:- Sample mass
- Sample area
- Sample density (as per ISO 1183)
Specimen Sampling
Samples must be cut from specified positions across the film or sheet, depending on the width to ensure representative measurements. For thin films with very low mass, combined specimens are used.Apparatus Required
Essential tools include:- Knife-edged punch or square template (100 cm² ± 0.5 cm²)
- Precision balance (accuracy of at least 0.0001 g)
Test Procedures
- Measure mass and density of specimens at controlled temperature and humidity.
- Calculate the gravimetric thickness of individual samples.
- Compute the average thickness from multiple specimens.
- For rolls, measure length, average width (per ISO 4592), net mass, and density to determine average thickness and yield.
Yield Calculation
Yield, defined as area per unit mass (m²/kg), is derived from roll dimensions, mass, and density, providing a critical parameter for quality control and material optimization.Precision and Reporting
Although no inter-laboratory precision data are available yet, the standard mandates detailed test reports including references, identification data, thickness results, and yield values (if applicable).
Applications
ISO 4591:1992 is crucial for manufacturers, quality assurance laboratories, and material inspectors involved with plastic films and sheeting. Its practical applications include:
Quality Control
Accurate measurement of film thickness ensures compliance with product specifications, affecting mechanical properties, durability, and processing parameters.Material Research & Development
Gravimetric techniques allow assessment of new polymer films, especially when surface textures complicate other thickness measurement methods.Process Optimization
Yield calculations enable manufacturers to optimize material usage, reducing waste and increasing cost efficiency.Embossed Sheetings Measurement
The method provides a reliable alternative to mechanical scanning for embossed films, which are commonly used in packaging and decorative applications.Compliance Testing
Supports adherence to regulatory and industry standards requiring verifiable thickness and yield values for plastic films.
Related Standards
For comprehensive testing and measurement of plastic films and sheeting, ISO 4591:1992 integrates with the following standards:
ISO 1183
Plastics - Methods for determining density and relative density of non-cellular plastics; essential for determining density in thickness calculations.ISO 4592
Plastics - Film and sheeting - Determination of length and width; used to measure physical dimensions of rolls for thickness and yield calculations.Additional Plastics Testing Standards
Complementary standards covering mechanical, thermal, and chemical properties support a holistic approach to plastic film evaluation.
By following these interrelated standards, organizations can maintain high levels of accuracy, reproducibility, and quality control in the production and testing of plastic films and sheeting.
Keywords: ISO 4591, plastics film thickness, gravimetric thickness, plastic sheeting measurement, plastic film yield, embossed sheeting, plastic film testing, ISO 1183, ISO 4592, quality control plastics, film thickness determination.
ISO 4591:1992 - Plastics -- Film and sheeting -- Determination of average thickness of a sample, and average thickness and yield of a roll, by gravimetric techniques (gravimetric thickness)
ISO 4591:1992 - Plastiques -- Film et feuille -- Détermination de l'épaisseur moyenne d'un échantillon, et de l'épaisseur moyenne d'un rouleau, ainsi que de sa surface par unité de masse, par mesures gravimétriques (épaisseur gravimétrique)
ISO 4591:1992 - Plastiques -- Film et feuille -- Détermination de l'épaisseur moyenne d'un échantillon, et de l'épaisseur moyenne d'un rouleau, ainsi que de sa surface par unité de masse, par mesures gravimétriques (épaisseur gravimétrique)
Frequently Asked Questions
ISO 4591:1992 is a standard published by the International Organization for Standardization (ISO). Its full title is "Plastics - Film and sheeting - Determination of average thickness of a sample, and average thickness and yield of a roll, by gravimetric techniques (gravimetric thickness)". This standard covers: Applies to all plastics films and sheeting and has special value when mechanical scanning is not sufficiently precise, particularly for measuring the thickness of embossed sheeting. The gravimetric thickness is calculated from measurements of mass, area and density of a sample.
Applies to all plastics films and sheeting and has special value when mechanical scanning is not sufficiently precise, particularly for measuring the thickness of embossed sheeting. The gravimetric thickness is calculated from measurements of mass, area and density of a sample.
ISO 4591:1992 is classified under the following ICS (International Classification for Standards) categories: 83.140.10 - Films and sheets. The ICS classification helps identify the subject area and facilitates finding related standards.
ISO 4591:1992 has the following relationships with other standards: It is inter standard links to ISO 4591:1979. Understanding these relationships helps ensure you are using the most current and applicable version of the standard.
ISO 4591:1992 is available in PDF format for immediate download after purchase. The document can be added to your cart and obtained through the secure checkout process. Digital delivery ensures instant access to the complete standard document.
Standards Content (Sample)
INTERNATIONAL ISO
STANDARD
Second edition
1992-12-01
Plastics - Film and sheeting -
Determination of average thickness of a
Sample, and average thickness and yield
of a roll, by gravimetric techniques
(gravimetric thickness)
Plas tiques - Film et feuille - Determination de I’epaisseur moyenne
d’un bchantillon, et de I’bpaisseur moyenne d’un rouleau, ainsi que de sa
surface par unit6 de masse, par mesures gravimetriques (6paisseur
gravime trique)
Reference number
ISO 4591 :1992(E)
Foreword
ISO (the International Organization for Standardization) is a worldwide
federation of national Standards bodies (ISO member bodies). The work
of preparing International Standards is normally carried out through ISO
technical committees. Esch member body interested in a subject for
which a technical committee has been established has the right to be
represented on that committee. International organizations, governmental
and non-governmental, in liaison with ISO, also take part in the work. ISO
collaborates closely with the International Electrotechnical Commission
(IEC) on all matters of electrotechnical standardization.
Draft International Standards adopted by the technical committees are
circulated to the member bodies for voting. Publication as an International
Standard requires approval by at least 75 % of the member bodies casting
a vote.
International Standard ISO 4591 was prepared by Technical Committee
lSO/TC 61, Plastics, Sub-Committee SC 11, Products.
This second edition cancels and replaces the first edition
(ISO 4591:1979), which has been technically revised.
0 ISO 1992
All rights reserved. No part of this publication may be reproduced or utilized in any form or
by any means, electronie or mechanical, including photocopying and microfilm, without per-
mission in writing from the publisher.
International Organization for Standardization
Case Postale 56 l CH-l 211 Geneve 20 l Switzerland
Printed in Switzerland
ii
INTERNATIONAL STANDARD
- Film and sheeting -
Plastics Determination of
average thickness of a Sample, and average thickness
and yield of a roll, by gravimetric techniques
(gravimetric thickness)
1 Scope 3 Determination of gravimetric
thickness of a Sample
This International Standard specifies
3.1 Principle
- a method for the determination of the gravimetric
thickness of a Sample of plastics film or sheeting
The gravimetric thickness of a Sample is calculated
(see clause 3);
from measurements of its mass, area and density.
- a method for the determination of the average
gravimetric thickness and, if required, the yield 3.2 Apparatus
(area per unit mass) of a roll of plastics film or
sheeting (see clause 4).
3.2.1 Knife-edged Punch, Square or circular, having
an area of 100 cm2 & 0,5 cm2, or
These methods are applicable to all plastics films and
sheeting, and have special value when mechanical
3.2.2 Square template, having an area of
scanning is not sufficiently precise, particularly for
100 cm2 + 0,5 cm2.
-
measuring the thickness of embossed sheeting.
3.2.3 Balance, accurate to 0,000 1 g.
3.3 Spetimens
Spetimens of area 100 cm2 + 0,5 cm2 shall be tut at
-
2 Normative references
positions approximately equally spaced across the
width of the Sample in each of two bands approxi-
The following Standards contain provisions which,
mately 1 m apart in the longitudinal direction.
through reference in this text, constitute provisions
of this International Standard. At the time of publica-
The minimum number of specimens taken from each
tion, the editions indicated were valid. All Standards
band across the film or sheeting shall be dependent
are subject to revision, and Parties to agreements
on the width of the Sample as follows:
based on this International Standard are encouraged
to investigate the possibility of applying the most re-
widths smaller than or equal to 1 000 mm 3
cent editions of the Standards indicated below.
widths greater than 1 000 mm and up to
Members of IEC and ISO maintain registers of cur-
1 500 mm 5
rently valid International Standards.
widths greater than 1 500 mm 10
ISO 1183:1987, Plastics - Methods for determining
the density and relative density of non-cellular In the case of very thin film, when the mass of a
specimen of area 100 cm2 + 0,5 cm2 is less than
plas tics.
1 g, two specimens locatediery close together on
the film in the longitudinal (extrusion/calender) direc-
ISO 4592:1992, Plastics - Film and sheeting - De-
termination of length and width. tion shall be used for
...
NORME ISO
INTERNATIONALE 4591
Deuxième édition
1992-l 2-01
Plastiques - Film et feuille -.
Détermination de l’épaisseur moyenne d‘un
échantillon, et de l’épaisseur moyenne d’un
rouleau, ainsi que de sa surface par unité
de masse, par mesures gravimétriques
(épaisseur gravimétrique)
P/as tics - Film and sheeting - Determination of average thickness of a
sample, and average thickness and yield of a roll, by gravimetric
techniques (gravimetric thickness)
Numéro de référence
ISO 4591 :1992(F)
Avant-propos
L’ISO (Organisation internationale de normalisation) est une fédération
mondiale d’organismes nationaux de normalisation (comités membres de
I’ISO). L’élaboration des Normes internationales est en général confiée aux
comités techniques de I’ISO. Chaque comité membre intéressé par une
Atude a le droit de faire partie du comité technique cree a cet effet. Les
organisations internationales, gouvernementales et non gouvernemen-
tales, en liaison avec I’ISO participent également aux travaux. L’ISO colla-
bore étroitement avec la Commission électrotechnique internationale (CEI)
en ce qui concerne la normalisation électrotechnique.
Les projets de Normes internationales adoptés par les comités techniques
sont soumis aux comités membres pour vote. Leur publication comme
Normes internationales requiert l’approbation de 75 % au moins des co-
mites membres votants.
La Norme internationale ISO 4591 a été élaborée par le comité technique
lSO/K 61, Plastiques, sous-comité SC 11, Produits.
Cette deuxième édition annule et remplace la première édition
(ISO 4591:1979), dont elle constitue une révision technique.
0 ISO 1992
Droits de reproduction réservés. Aucune partie de cette publication ne peut être reproduite
ni utilisee sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique,
y compris la photocopie et les microfilms, sans l’accord écrit de l’éditeur.
Organisation internationale de normalisation
Case Postale 56 l CH-121 1 Genève 20 l Suisse
Imprimé en Suisse
ii
NORME INTERNATIONALE ISO 4591:1992(F)
Plastiques - Film et feuille
- Détermination de
l’épaisseur moyenne d’un échantillon, et de l’épaisseur
moyenne d’un rouleau, ainsi que de sa surface par
unité de masse, par mesures gravimétriques (épaisseur
gravimétrique)
ISO 4592:1992, Plastiques - Film et feuille - Db-
1 Domaine d’application
termination de la longueur et de la largeur.
La présente Norme internationale prescrit
3 Détermination de l’épaisseur
- une méthode pour la détermination de l’épaisseur
gravimétrique d’un échantillon de film ou de feuille gravimétrique d’un échantillon
en plastique (voir article 3);
3.1 Principe
- une méthode pour la détermination de l’épaisseur
gravimétrique moyenne d’un rouleau de film ou de
L’épaisseur gravimétrique d’un échantillon est calcu-
feuille en plastique, ainsi que de sa surface par
lée à partir de mesures de masse, de surface et de
unité de masse si elle est exigée (voir article 4).
masse volumique.
Les méthodes sont applicables à tous les films ou
feuilles en plastique, mais présentent un intérêt parti-
3.2 Appareillage
culier lorsque la mesure mécanique de l’épaisseur
n’est pas suffisamment précise, particulièrement
3.2.1 Découpoir emporte-pièce, de forme carrée
lorsqu’il s’agit de mesurer l’épaisseur de feuilles
ou circulaire, d’une surface de 100 cm* & 0,5 cm*, ou
grainées.
3.2.2 Gabarit carré, d’une surface de
100 cm* + 0,5 cm*.
-
2 Références normatives
3.2.3 Balance, précise à 0,000 1 g.
Les normes suivantes contiennent des dispositions
qui, par suite de la référence qui en est faite, consti-
tuent des dispositions valables pour la présente
3.3 Éprouvettes
Norme internationale. Au moment de la publication,
les éditions indiquées étaient en vigueur. Toute
Des éprouvettes de 100 cm* + 0,5 cm* doivent être
norme est sujette à révision et les parties prenantes
découpées dans deux bandes transversales distantes
des accords fondés sur la présente Norme internatio-
d’environ 1 m l’une de l’autre dans le sens longitudi-
nale sont invitees a rechercher la possibilité d’appli-
nal, les prélèvements étant espacés de façon sensi-
quer les éditions les plus récentes des normes
blement régulière dans la largeur de l’échantillon.
indiquées ci-après. Les membres de la CEI et de I’ISO
possèdent le registre des Normes internationales en Le nombre minimal d’éprouvettes prélevées dans
vigueur a un moment donné. chaque bande transversale dépend de la largeur de
l’échantillon, à savoir:
ISO 1183:1987, Plastiques - Méthodes pour déter-
miner la masse volumique et la densité relative des 3 pour des largeurs inférieures ou égales à
plastiques non alvbolaires.
1 000 mm;
5 pour des largeurs supérieures a 1 000 mm et 3.7 Rapport d’essai
jusqu’à 1 500 mm;
Le rapport d’essai doit contenir les indications sui-
10 pour des largeurs supérieures à 1 500 mm.
vantes:
Dans le cas de films tres minces, si la masse d’un
...
NORME ISO
INTERNATIONALE 4591
Deuxième édition
1992-l 2-01
Plastiques - Film et feuille -.
Détermination de l’épaisseur moyenne d‘un
échantillon, et de l’épaisseur moyenne d’un
rouleau, ainsi que de sa surface par unité
de masse, par mesures gravimétriques
(épaisseur gravimétrique)
P/as tics - Film and sheeting - Determination of average thickness of a
sample, and average thickness and yield of a roll, by gravimetric
techniques (gravimetric thickness)
Numéro de référence
ISO 4591 :1992(F)
Avant-propos
L’ISO (Organisation internationale de normalisation) est une fédération
mondiale d’organismes nationaux de normalisation (comités membres de
I’ISO). L’élaboration des Normes internationales est en général confiée aux
comités techniques de I’ISO. Chaque comité membre intéressé par une
Atude a le droit de faire partie du comité technique cree a cet effet. Les
organisations internationales, gouvernementales et non gouvernemen-
tales, en liaison avec I’ISO participent également aux travaux. L’ISO colla-
bore étroitement avec la Commission électrotechnique internationale (CEI)
en ce qui concerne la normalisation électrotechnique.
Les projets de Normes internationales adoptés par les comités techniques
sont soumis aux comités membres pour vote. Leur publication comme
Normes internationales requiert l’approbation de 75 % au moins des co-
mites membres votants.
La Norme internationale ISO 4591 a été élaborée par le comité technique
lSO/K 61, Plastiques, sous-comité SC 11, Produits.
Cette deuxième édition annule et remplace la première édition
(ISO 4591:1979), dont elle constitue une révision technique.
0 ISO 1992
Droits de reproduction réservés. Aucune partie de cette publication ne peut être reproduite
ni utilisee sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique,
y compris la photocopie et les microfilms, sans l’accord écrit de l’éditeur.
Organisation internationale de normalisation
Case Postale 56 l CH-121 1 Genève 20 l Suisse
Imprimé en Suisse
ii
NORME INTERNATIONALE ISO 4591:1992(F)
Plastiques - Film et feuille
- Détermination de
l’épaisseur moyenne d’un échantillon, et de l’épaisseur
moyenne d’un rouleau, ainsi que de sa surface par
unité de masse, par mesures gravimétriques (épaisseur
gravimétrique)
ISO 4592:1992, Plastiques - Film et feuille - Db-
1 Domaine d’application
termination de la longueur et de la largeur.
La présente Norme internationale prescrit
3 Détermination de l’épaisseur
- une méthode pour la détermination de l’épaisseur
gravimétrique d’un échantillon de film ou de feuille gravimétrique d’un échantillon
en plastique (voir article 3);
3.1 Principe
- une méthode pour la détermination de l’épaisseur
gravimétrique moyenne d’un rouleau de film ou de
L’épaisseur gravimétrique d’un échantillon est calcu-
feuille en plastique, ainsi que de sa surface par
lée à partir de mesures de masse, de surface et de
unité de masse si elle est exigée (voir article 4).
masse volumique.
Les méthodes sont applicables à tous les films ou
feuilles en plastique, mais présentent un intérêt parti-
3.2 Appareillage
culier lorsque la mesure mécanique de l’épaisseur
n’est pas suffisamment précise, particulièrement
3.2.1 Découpoir emporte-pièce, de forme carrée
lorsqu’il s’agit de mesurer l’épaisseur de feuilles
ou circulaire, d’une surface de 100 cm* & 0,5 cm*, ou
grainées.
3.2.2 Gabarit carré, d’une surface de
100 cm* + 0,5 cm*.
-
2 Références normatives
3.2.3 Balance, précise à 0,000 1 g.
Les normes suivantes contiennent des dispositions
qui, par suite de la référence qui en est faite, consti-
tuent des dispositions valables pour la présente
3.3 Éprouvettes
Norme internationale. Au moment de la publication,
les éditions indiquées étaient en vigueur. Toute
Des éprouvettes de 100 cm* + 0,5 cm* doivent être
norme est sujette à révision et les parties prenantes
découpées dans deux bandes transversales distantes
des accords fondés sur la présente Norme internatio-
d’environ 1 m l’une de l’autre dans le sens longitudi-
nale sont invitees a rechercher la possibilité d’appli-
nal, les prélèvements étant espacés de façon sensi-
quer les éditions les plus récentes des normes
blement régulière dans la largeur de l’échantillon.
indiquées ci-après. Les membres de la CEI et de I’ISO
possèdent le registre des Normes internationales en Le nombre minimal d’éprouvettes prélevées dans
vigueur a un moment donné. chaque bande transversale dépend de la largeur de
l’échantillon, à savoir:
ISO 1183:1987, Plastiques - Méthodes pour déter-
miner la masse volumique et la densité relative des 3 pour des largeurs inférieures ou égales à
plastiques non alvbolaires.
1 000 mm;
5 pour des largeurs supérieures a 1 000 mm et 3.7 Rapport d’essai
jusqu’à 1 500 mm;
Le rapport d’essai doit contenir les indications sui-
10 pour des largeurs supérieures à 1 500 mm.
vantes:
Dans le cas de films tres minces, si la masse d’un
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.
Loading comments...