ISO 6361-2:2014

INTERNATIONAL ISO
STANDARD 6361-2
Fourth edition
2014-09-15
Wrought aluminium and aluminium
alloys — Sheets, strips and plates —
Part 2:
Mechanical properties
Aluminium et alliages d’aluminium corroyés — Tôles, bandes et tôles
épaisses —
Partie 2: Propriétés mécaniques
Reference number
©
ISO 2014
© ISO 2014
All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized otherwise in any form
or by any means, electronic or mechanical, including photocopying, or posting on the internet or an intranet, without prior
written permission. Permission can be requested from either ISO at the address below or ISO’s member body in the country of
the requester.
ISO copyright office
Case postale 56 • CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax + 41 22 749 09 47
E-mail copyright@iso.org
Web www.iso.org
Published in Switzerland
ii © ISO 2014 – All rights reserved

Contents Page
Foreword .iv
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 1
4 Tensile testing . 1
5 Bend testing . 1
6 Mechanical properties . 2
6.1 Tensile test . 2
6.2 Bend test . 2
Annex A (normative) Rules for rounding results obtained by inspection and testing .50
Bibliography .51
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out
through ISO technical committees. Each member body interested in a subject for which a technical
committee has been established has the right to be represented on that committee. International
organizations, governmental and non-governmental, in liaison with ISO, also take part in the work.
ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of
electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are
described in the ISO/IEC Directives, Part 1. In particular the different approval criteria needed for the
different types of ISO documents should be noted. This document was drafted in accordance with the
editorial rules of the ISO/IEC Directives, Part 2 (see www.iso.org/directives).
Attention is drawn to the possibility that some of the elements of this document may be the subject of
patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of any
patent rights identified during the development of the document will be in the Introduction and/or on
the ISO list of patent declarations received (see www.iso.org/patents).
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation on the meaning of ISO specific terms and expressions related to conformity
assessment, as well as information about ISO’s adherence to the WTO principles in the Technical Barriers
to Trade (TBT) see the following URL: Foreword - Supplementary information
The committee responsible for this document is ISO/TC 79, Light metals and their alloys, Subcommittee
SC 6, Wrought aluminium and aluminium alloys.
This fourth edition cancels and replaces the third edition (ISO 6361-2:2011), which has been technically
revised.
ISO 6361 consists of the following parts, under the general title Wrought aluminium and aluminium
alloys — Sheets, strips and plates:
— Part 1: Technical conditions for inspection and delivery
— Part 2: Mechanical properties
— Part 3: Strips: Tolerances on shape and dimensions
— Part 4: Sheets and plates: Tolerances on shape and dimensions
— Part 5: Chemical composition
iv © ISO 2014 – All rights reserved

INTERNATIONAL STANDARD ISO 6361-2:2014(E)
Wrought aluminium and aluminium alloys — Sheets, strips
and plates —
Part 2:
Mechanical properties
1 Scope
In conjunction with ISO 6361-1, this part of ISO 6361 specifies the mechanical properties of wrought
aluminium and aluminium alloy sheets, strips, and plates for general engineering applications.
It applies to flat-rolled products.
The chemical composition of these materials is given in ISO 6361-5.
The designations of aluminium and aluminium alloys and the temper designations used in this part of
ISO 6361 are in accordance with ISO 2107.
NOTE In certain countries, for purposes of mechanical properties, the thickness limit can be lowered to
0,15 mm by agreement between the purchaser and the supplier, in the case of sheets and strips.
2 Normative references
The following documents, in whole or in part, are normatively referenced in this document and are
indispensable for its application. For dated references, only the edition cited applies. For undated
references, the latest edition of the referenced document (including any amendments) applies.
ISO 6361-1, Wrought aluminium and aluminium alloys — Sheets, strips and plates — Part 1: Technical
conditions for inspection and delivery
3 Terms and definitions
For the purposes of this document, the terms and definitions given in ISO 6361-1 apply.
4 Tensile testing
For the selection of the specimens and tensile testing, see ISO 6361-1.
5 Bend testing
For the selection of the specimens and bend testing, see ISO 6361-1.
6 Mechanical properties
6.1 Tensile test
Values for mechanical properties of aluminium and aluminium alloys are given in Tables 1 to 63.
For elongation, two different gauge lengths are used. The choice of the gauge length for elongation
measurements (A or A ) is at the discretion of the producer, unless otherwise agreed.
50mm
NOTE A is the percentage elongation on a gauge length of 56, 5 S . A is the percentage elongation on
50mm
o
a gauge length of 50 mm.
Test results shall be rounded in accordance with the rules given in Annex A.
6.2 Bend test
Sheet, strip, and plate shall be capable of being bent cold through an angle of 180°, as applicable, around
a pin having a radius equal to k times the thickness, t, of the sheet, strip, or plate (for example 0,5t)
without cracking. The values of the minimum bend radii for different alloys, tempers, and thicknesses
are given in Tables 1 to 63.
NOTE The explanations of the numbered notes in Tables 1 to 63 are given after Table 63.
Table 1 — Aluminium 1050
2)
Tensile test Bend test
1)
Specified thick- Tensile 0,2 % proof Elongation Specified
Temper ness strength stress min. thickness
Radius
mm MPa MPa % mm
over up to min. max. min. max. A A over up to
50mm
≥4,0 6,5 85 45 10
6,5 13,0 80 45 10
H112 13,0 25,0 70 35 16
25,0 50,0 65 30 22
50,0 75,0 65 20 22
≥0,2 0,5 60 100 15 ≥0,2 6,0 0t
0,5 0,8 60 100 20
O 0,8 1,3 60 100 20 25
1,3 6,5 60 100 20 30
6,5 50,0 60 100 20 28
≥0,2 0,3 80 120 2 ≥0,2 0,8 0t
0,3 0,5 80 120 3 0,8 6,0 0,5t
H12
0,5 0,8 80 120 4
or
3) 0,8 1,3 80 120 65 6
H22
1,3 2,9 80 120 65 8
2,9 12,0 80 120 65 9
≥0,2 0,3 95 125 1 ≥0,2 0,8 0,5t
0,3 0,5 95 125 2 0,8 6,0 1t
H14
0,5 0,8 95 125 3
or
3) 0,8 1,3 95 125 75 4
H24
1,3 2,9 95 125 75 5
2,9 12,0 95 125 75 6
2 © ISO 2014 – All rights reserved

Table 1 (continued)
2)
Tensile test Bend test
1)
Specified thick- Tensile 0,2 % proof Elongation Specified
Temper ness strength stress min. thickness
Radius
mm MPa MPa % mm
over up to min. max. min. max. A A over up to
50mm
≥0,2 0,5 120 145 1 ≥0,2 4,0 2t
H16
0,5 0,8 120 145 2
or
3) 0,8 1,3 120 145 85 3
H26
1,3 4,0 120 145 85 4
≥0,2 0,5 125 1
0,5 0,8 125 2
H18
0,8 1,3 125 3
1,3 3,0 125 4
Table 2 — Aluminium 1050A
2)
Tensile test Bend test
1)
Specified thick- Tensile 0,2 % proof Elongation Specified
Temper ness strength stress min. thickness
Radius
mm MPa MPa % mm
over up to min. max. min. max. A A over up to
50mm
≥0,2 0,5 65 95 20 20
0,5 1,5 65 95 20 22
1,5 3,0 65 95 20 26
O
3,0 6,0 65 95 20 29
6,0 12,5 65 95 20 35
12,5 25,0 65 95 20 32 32
≥0,2 0,5 105 145 85 2
0,5 1,5 105 145 85 3
H14
1,5 3,0 105 145 85 4
3,0 6,0 105 145 85 5
≥0,2 0,5 105 145 75 3
0,5 1,5 105 145 75 4
H24
1,5 3,0 105 145 75 5
3,0 6,0 105 145 75 8
≥0,2 0,5 140 120 120 1
H18 0,5 1,5 140 120 120 2
1,5 3,0 140 120 120 2
Table 3 — Aluminium 1070, 1080, and 1085
2)
Tensile test Bend test
1)
Specified thick- Tensile 0,2 % proof Elongation Specified
Temper ness strength stress min. thickness
Radius
mm MPa MPa % mm
over up to min. max. min. max. A A over up to
50mm
≥4,0 6,5 75 35 13
6,5 13,0 70 35 15
H112 13,0 25,0 60 25 20
25,0 50,0 55 20 25
50,0 75,0 55 15 25
≥0,2 0,3 55 95 15 ≥0,2 6,0 0t
0,3 0,5 55 95 20
0,5 0,8 55 95 25
O
0,8 1,3 55 95 15 30
1,3 13,0 55 95 15 35
13,0 50,0 55 95 15 30
≥0,2 0,3 70 110 2 ≥0,2 6,0 0t
0,3 0,5 70 110 3
H12
0,5 0,8 70 110 4
or
3) 0,8 1,3 70 110 55 6
H22
1,3 2,9 70 110 55 8
2,9 12,0 70 110 55 9
≥0,2 0,3 85 120 1 ≥0,2 0,8 0,5t
0,3 0,5 85 120 2 0,8 6,0 1t
H14
0,5 0,8 85 120 3
or
3) 0,8 1,3 85 120 65 4
H24
1,3 2,9 85 120 65 5
2,9 12,0 85 120 65 6
≥0,2 0,5 100 135 1 ≥0,2 0,8 1t
H16
0,5 0,8 100 135 2 0,8 6,0 1,5t
or
3) 0,8 1,3 100 135 75 3
H26
1,3 4,0 100 135 75 4
≥0,2 0,5 120 1
0,5 0,8 120 2
H18
0,8 1,3 120 3
1,3 3,0 120 4
4 © ISO 2014 – All rights reserved

Table 4 — Aluminium 1070A
2)
Tensile test Bend test
1)
Specified thick- Tensile 0,2 % proof Elongation Specified
Temper ness strength stress min. thickness
Radius
mm MPa MPa % mm
over up to min. max. min. max. A A over up to
50mm
0,2 0,5 60 90 15 23 0,2 0,5 0t
0,5 1,5 60 90 15 25 0,5 1,5 0t
1,5 3,0 60 90 15 29 1,5 3,0 0t
O/H111
3,0 6,0 60 90 15 32 3,0 6,0 0,5t
6,0 12,5 60 90 15 35 6,0 12,5 0,5t
12,5 25,0 60 90 15 32
≥6,0 12,5 70 20 20
H112
12,5 25,0 70 20
0,2 0,5 80 120 55 5 0,2 0,5 0,5t
0,5 1,5 80 120 55 6 0,5 1,5 0,5t
H12 1,5 3,0 80 120 55 7 1,5 3,0 0,5t
3,0 6,0 80 120 55 9
6,0 12,5 80 120 55 12
0,2 0,5 100 140 70 4 0,2 0,5 0,5t
0,5 1,5 100 140 70 4 0,5 1,5 0,5t
H14 1,5 3,0 100 140 70 5 1,5 3,0 1t
3,0 6,0 100 140 70 6
6,0 12,5 100 140 70 7
0,2 0,5 110 150 90 2 0,2 0,5 1t
H16 0,5 1,5 110 150 90 2 0,5 1,5 1t
1,5 4,0 110 150 90 3 1,5 4,0 1t
0,2 0,5 125 105 2
H18 0,5 1,5 125 105 2
1,5 3,0 125 105 2
0,2 0,5 80 120 50 7 0,2 0,5 0,5t
0,5 1,5 80 120 50 8 0,5 1,5 0,5t
H22 1,5 3,0 80 120 50 10 1,5 3,0 0,5t
3,0 6,0 80 120 50 12
6,0 12,5 80 120 50 15
0,2 0,5 100 140 60 5 0,2 0,5 0,5t
0,5 1,5 100 140 60 6 0,5 1,5 0,5t
H24 1,5 3,0 100 140 60 7 1,5 3,0 1t
3,0 6,0 100 140 60 9
6,0 12,5 100 140 60 11
0,2 0,5 110 150 80 3
H26 0,5 1,5 110 150 80 3
1,5 4,0 110 150 80 4
Table 5 — Aluminium 1080A
2)
Tensile test Bend test
1)
Specified thick- Tensile 0,2 % proof Elongation Specified
Temper ness strength stress min. thickness
Radius
mm MPa MPa % mm
over up to min. max. min. max. A A over up to
50mm
0,2 0,5 60 90 15 26 0,2 0,5 0t
0,5 1,5 60 90 15 28 0,5 1,5 0t
O/H111 1,5 3,0 60 90 15 31 1,5 3,0 0t
3,0 6,0 60 90 15 35 3,0 6,0 0,5t
6,0 12,5 60 90 15 35 6,0 12,5 0,5t
≥6,0 12,5 70 20
H112
12,5 25,0 70 20
0,2 0,5 80 120 55 5 0,2 0,5 0,5t
0,5 1,5 80 120 55 6 0,5 1,5 0,5t
H12 1,5 3,0 80 120 55 7 1,5 3,0 0,5t
3,0 6,0 80 120 55 9
6,0 12,5 80 120 55 12
0,2 0,5 100 140 70 4 0,2 0,5 0,5t
0,5 1,5 100 140 70 4 0,5 1,5 0,5t
H14 1,5 3,0 100 140 70 5 1,5 3,0 1t
3,0 6,0 100 140 70 6
6,0 12,5 100 140 70 7
0,2 0,5 110 150 90 2 0,2 0,5 1t
H16 0,5 1,5 110 150 90 2 0,5 1,5 1t
1,5 4,0 110 150 90 3 1,5 4,0 1t
0,2 0,5 125 105 2
H18 0,5 1,5 125 105 2
1,5 3,0 125 105 2
0,2 0,5 80 120 50 8 0,2 0,5 0,5t
0,5 1,5 80 120 50 9 0,5 1,5 0,5t
H22 1,5 3,0 80 120 50 11 1,5 3,0 0,5t
3,0 6,0 80 120 50 13
6,0 12,5 80 120 50 15
0,2 0,5 100 140 60 5 0,2 0,5 0,5t
0,5 1,5 100 140 60 6 0,5 1,5 0,5t
H24 1,5 3,0 100 140 60 7 1,5 3,0 1t
3,0 6,0 100 140 60 9
6,0 12,5 100 140 60 11
0,2 0,5 110 150 80 3
H26 0,5 1,5 110 150 80 3
1,5 4,0 110 150 80 4
6 © ISO 2014 – All rights reserved

Table 6 — Aluminium 1100, 1100A, 1200, and 1230A
2)
Tensile test Bend test
1)
Specified thick- Tensile 0,2 % proof Elongation Specified
Temper ness strength stress min. thickness
Radius
mm MPa MPa % mm
over up to min. max. min. max. A A over up to
50mm
≥4,0 6,5 95 50 9
6,5 13,0 90 50 9
H112
13,0 50,0 85 35 14
50,0 75,0 80 25 20
≥0,2 0,5 75 105 25 17 ≥0,2 6,0 0t
0,5 0,8 75 105 25 22
O 0,8 1,3 75 105 25 22
1,3 6,5 75 105 25 30
6,5 75,0 75 105 25 28 25
≥0,2 0,3 95 125 75 2 ≥0,2 6,0 0,5t
0,3 0,5 95 125 75 3
H12
0,5 0,8 95 125 75 4
or
3) 0,8 1,3 95 125 75 6
H22
1,3 2,9 95 125 75 8
2,9 12,0 95 125 75 9
≥0,2 0,3 120 145 95 1 ≥0,2 6,0 1t
0,3 0,5 120 145 95 2
H14
0,5 0,8 120 145 95 3
or
3) 0,8 1,3 120 145 95 4
H24
1,3 2,9 120 145 95 5
2,9 12,0 120 145 95 6
≥0,2 0,5 135 165 115 1 ≥0,2 4,0 2t
H16
0,5 0,8 135 165 115 2
or
3) 0,8 1,3 135 165 115 3
H26
1,3 4,0 135 165 115 4
≥0,2 0,5 150 130 1
0,5 0,8 150 130 2
H18
0,8 1,3 150 130 3
1,3 3,0 150 130 4
Table 7 — Alloy 2014
2)
Tensile test Bend test
1)
Specified thick- Tensile 0,2 % proof Elongation Specified
Temper ness strength stress min. thickness
Radius
mm MPa MPa % mm
over up to min. max. min. max. A A over up to
50mm
≥0,4 0,5 220 140 16 ≥0,4 1,6 0,5t
4)
O 0,5 13,0 220 140 16 1,6 2,9 1t
13,0 25,0 220 140 10 9 2,9 6,0 1,5t
Table 7 (continued)
2)
Tensile test Bend test
1)
Specified thick- Tensile 0,2 % proof Elongation Specified
Temper ness strength stress min. thickness
Radius
mm MPa MPa % mm
over up to min. max. min. max. A A over up to
50mm
≥0,4 0,5 395 245 14 ≥0,4 0,5 1,5t
0,5 6,0 395 245 14 0,5 1,6 2,5t
T3
6,0 6,3 395 240 14 1,6 2,9 3t
6,3 12,0 395 235 13 2,9 6,0 3,5t
≥0,4 0,5 395 240 14 ≥0,4 0,5 1,5t
0,5 6,0 395 240 14 0,5 1,6 2,5t
T4
6,0 6,3 400 250 14 1,6 2,9 3t
6,3 12,0 400 250 14 2,9 6,0 3,5t
≥6,0 13,0 400 250 14
13,0 25,0 400 250 14
5)
T451
25,0 50,0 400 250 12 10
50,0 80,0 395 250 8 7
≥0,4 0,5 400 14
6)
T42
0,5 25,0 400 235 14
≥0,4 0,5 440 390 6 ≥0,4 0,5 3t
0,5 1,0 440 390 6 0,5 1,6 3,5t
T6 1,0 6,0 440 390 7 1,6 2,9 4,5t
6,0 6,3 450 395 7 2,9 6,0 5t
6,3 12,0 450 395 7
≥0,4 0,5 440 6
0,5 1,0 440 390 6
7)
T62 1,0 6,5 460 400 7
6,5 13,0 460 410 7
13,0 25,0 460 410 6
≥6,0 13,0 460 405 7
13,0 25,0 460 405 7 6
25,0 50,0 460 405 4 5
T651
50,0 60,0 450 390 2 3
60,0 80,0 435 380 2 1
80,0 100,0 405 380 1
8 © ISO 2014 – All rights reserved

Table 8 — Alloy 2014A
2)
Tensile test Bend test
1)
Specified thick- Tensile 0,2 % proof Elongation Specified
Temper ness strength stress min. thickness
Radius
mm MPa MPa % mm
over up to min. max. min. max. A A over up to
50mm
≥0,35 3,2 220 140 16 13
3,2 6,0 220 140 16 12
O 6,0 12,0 220 140 16 12
12,0 12,5 220 140 16 12
12,5 25,0 220 140 12 9
≥0,35 0,5 395 240 14
0,5 1,0 395 240 14
T3
1,0 1,6 395 240 14
or
1,6 6,0 395 240 14
T4
6,0 6,3 395 240 14
6,3 12,0 395 235 13
≥0,35 0,5 440 380 6
0,5 1,0 440 380 6
1,0 1,6 440 380 7
T6
1,6 6,0 440 390 7
6,0 6,3 440 390 7
6,3 12,0 440 390 7
≥6,0 6,3 395 240 14
6,3 12,0 395 240 14
12,0 12,5 400 250 14
12,5 25,0 400 250 14 12
T451
25,0 40,0 400 250 10
40,0 50,0 400 250 8
50,0 60,0 395 250 7
60,0 80,0 390 240 7
≥6,0 6,3 450 395 7
6,3 12,0 450 395 7
12,0 12,5 450 395 7
12,5 25,0 460 405 7 6
T651 25,0 40,0 460 405 5
40,0 50,0 450 390 3
50,0 60,0 450 390 3
60,0 80,0 435 380 1
80,0 100,0 405 350 1
Table 9 — Alloy 2017
2)
Tensile test Bend test
1)
Specified thick- Tensile 0,2 % proof Elongation Specified
Temper ness strength stress min. thickness
Radius
mm MPa MPa % mm
over up to min. max. min. max. A A over up to
50mm
≥0,4 0,5 215 12 ≥0,4 1,6 0,5t
4)
O 0,5 25,0 215 110 12 1,6 2,9 1t
2,9 6,0 1,5t
≥0,4 0,5 375 12 ≥0,4 0,5 1,5t
0,5 1,6 375 215 15 0,5 1,6 2,5t
T3
1,6 2,9 375 215 17 1,6 2,9 3t
2,9 6,0 375 215 15 2,9 6,0 3,5t
≥6,0 25,0 375 215 12
25,0 50,0 375 215 12
T351
50,0 80,0 355 195 11
80,0 100,0 355 195 10
≥0,4 0,5 355 12 ≥0,4 0,5 1,5t
0,5 1,6 355 195 15 0,5 1,6 2,5t
T4
1,6 2,9 355 195 17 1,6 2,9 3t
2,9 6,0 355 195 15 2,9 6,0 3,5t
≥6,0 25,0 355 195 12
25,0 50,0 355 195 12
T451
50,0 80,0 355 195 11
80,0 100,0 355 195 10
≥0,4 0,5 355 12
0,5 1,6 355 195 15
6)
T42 1,6 2,9 355 195 17
2,9 6,5 355 195 15
6,5 25,0 335 195 12
Table 10 — Alloy 2017A
2)
Tensile test Bend test
1)
Specified thick- Tensile 0,2 % proof Elongation Specified
Temper ness strength stress min. thickness
Radius
mm MPa MPa % mm
over up to min. max. min. max. A A over up to
50mm
≥0,35 3,2 225 145 12
O 3,2 6,0 225 145 13
6,0 12,0 225 145 13
10 © ISO 2014 – All rights reserved

Table 10 (continued)
2)
Tensile test Bend test
1)
Specified thick- Tensile 0,2 % proof Elongation Specified
Temper ness strength stress min. thickness
Radius
mm MPa MPa % mm
over up to min. max. min. max. A A over up to
50mm
0,35 6,0 390 245 14
T4
6,0 12,0 390 260 13
6,0 12,0 390 260 13
12,0 25,0 390 250 13 12
25,0 40,0 390 250 12
T451 40,0 60,0 385 240 10
60,0 80,0 385 240 10
80,0 120,0 370 240 8
120,0 150,0 350 240 4
Table 11 — Alloy 2618A
2)
Tensile test Bend test
1)
Specified thick- Tensile 0,2 % proof Elongation Specified
Temper ness strength stress min. thickness
Radius
mm MPa MPa % mm
over up to min. max. min. max. A A over up to
50mm
≥6,0 12,5 420 375 5
12,5 40,0 420 375 5
T851 40,0 80,0 410 370 5
80,0 100,0 405 365 4
100,0 140,0 395 360 4
Table 12 — Alloy 2219
2)
Tensile test Bend test
1)
Specified thick- Tensile 0,2 % proof Elongation Specified
Temper ness strength stress min. thickness
Radius
mm MPa MPa % mm
over up to min. max. min. max. A A over up to
50mm
≥0,5 13,0 220 110 12 ≥0,5 6,5 2t
4)
O 13,0 50,0 220 110 11 10 6,5 13,0 3t
13,0 25,0 4t
≥0,5 1,0 315 200 8
9)
T31
1,0 6,5 315 195 10
≥6,5 12,5 315 195 10
12,5 50,0 315 195 10
8)
T351
50,0 80,0 305 195 10
80,0 100,0 290 195 9
Table 12 (continued)
2)
Tensile test Bend test
1)
Specified thick- Tensile 0,2 % proof Elongation Specified
Temper ness strength stress min. thickness
Radius
mm MPa MPa % mm
over up to min. max. min. max. A A over up to
50mm
≥0,5 1,0 340 260 6
1,0 12,5 340 255 6
10)
T37 12,5 60,0 340 255 5
60,0 80,0 325 250 5
80,0 100,0 310 240 3
≥0,5 1,0 370 250 6
1,0 6,5 370 250 7
7)
T62 6,5 13,0 370 250 8
13,0 25,0 370 250 8
25,0 50,0 370 250 7
≥0,5 1,0 425 315 6
T81
1,0 6,5 425 315 7
≥6,5 13,0 425 315 8
13,0 25,0 425 315 8 7
25,0 50,0 425 315 7 6
T851 50,0 80,0 425 310 6 5
80,0 100,0 415 305 5 4
100,0 130,0 405 295 4
130,0 150,0 395 290 3
≥0,5 1,0 440 360 5
1,0 12,5 440 350 6
12,5 60,0 440 350 7 6
T87
60,0 80,0 440 350 6 5
80,0 100,0 425 345 5 3
100,0 120,0 420 340 2
Table 13 — Alloy 2024
2)
Tensile test Bend test
1)
Specified thick- Tensile 0,2 % proof Elongation Specified
Temper ness strength stress min. thickness
Radius
mm MPa MPa % mm
over up to min. max. min. max. A A over up to
50mm
≥0,4 0,5 220 140 12 ≥0,4 0,5 0t
0,5 13,0 220 140 12 0,5 1,6 0,5t
4)
O
13,0 25,0 220 95 12 1,6 2,9 2t
25,0 45,0 220 10 2,9 6,0 3t
≥0,4 0,5 440 12 ≥0,4 0,5 2t
T3 0,5 6,5 440 295 15 0,5 2,9 3t
2,9 6,5 4t
12 © ISO 2014 – All rights reserved

Table 13 (continued)
2)
Tensile test Bend test
1)
Specified thick- Tensile 0,2 % proof Elongation Specified
Temper ness strength stress min. thickness
Radius
mm MPa MPa % mm
over up to min. max. min. max. A A over up to
50mm
≥6,5 13,0 440 290 12
13,0 25,0
435 290 8 7
25,0 40,0 425 290 7 6
40,0 50,0 425 290 6 5
8)
T351
50,0 80,0 415 290 4 3
80,0 100,0 395 285 4 3
100,0 120,0 395 285 2
120,0 150,0 380 260 2
≥0,4 0,5 460 8 ≥0,4 1,6 3t
0,5 1,6 460 345 8 1,6 2,9 4t
11)
T361
1,6 6,5 470 355 9 2,9 6,0 5t
6,5 12,0 460 345 9
≥0,4 0,5 425 275 12 ≥0,4 0,5 2t
T4 0,5 6,0 425 275 15 0,5 2,9 3t
2,9 6,0 4t
≥0,4 0,5 430 12
0,5 6,5 430 265 15
6)
T42
6,5 13,0 430 265 12
13,0 25,0 420 265 8
≥0,4 0,5 440 5
7)
T62 0,5 13,0 440 345 5
13,0 25,0 430 345 5
T81 ≥0,25 6,5 460 400 5
≥6,5 13,0 460 400 5
T851 13,0 25,0 455 400 5
25,0 40,0 455 395 5
≥0,4 0,5 480 3
0,5 1,6 480 430 3
T861
1,6 6,5 490 460 4
6,5 12,0 480 440 4
Table 14 — Alloy 2124
2)
Tensile test Bend test
1)
Specified thick- Tensile 0,2 % proof Elongation Specified
Temper ness strength stress min. thickness
Radius
mm MPa MPa % mm
over up to min. max. min. max. A A over up to
50mm
≥38,0 51,0 455 393 5
51,0 76,0 448 393 4
T851 76,0 102,0 448 386 4
102,0 127,0 441 379 4
127,0 152,0 434 372 4
Table 15 — Alloys 3003 and 3203
2)
Tensile test Bend test
1)
Specified thick- Tensile 0,2 % proof Elongation Specified
Temper ness strength stress min. thickness
Radius
mm MPa MPa % mm
over up to min. max. min. max. A A over up to
50mm
≥4,0 13,0 120 70 8
H112 13,0 50,0 110 40 12
50,0 75,0 100 40 18
≥0,2 0,3 95 135 18 ≥0,2 6,0 0t
0,3 0,8 95 135 35 20
O 0,8 1,3 95 135 35 22
1,3 6,5 95 135 35 25
6,5 75,0 95 135 35 23
≥0,2 0,3 120 155 2 ≥0,2 6,0 0,5t
0,3 0,5 120 155 3
0,5 0,8 120 155 4
H12
0,8 1,3 120 155 85 5
or
1,3 2,9 120 155 85 6
3)
H22
2,9 4,0 120 155 85 7
4,0 6,5 120 155 85 8
6,5 12,0 120 155 85 9
≥0,2 0,3 140 180 1 ≥0,2 2,9 1t
0,3 0,5 140 180 115 2 2,9 6,0 1,5t
0,5 0,8 140 180 115 3
H14
0,8 1,3 140 180 115 3
or
3) 1,3 2,9 140 180 115 5
H24
2,9 4,0 140 180 115 5
4,0 6,5 140 180 115 5
6,5 12,0 140 180 115 8
14 © ISO 2014 – All rights reserved

Table 15 (continued)
2)
Tensile test Bend test
1)
Specified thick- Tensile 0,2 % proof Elongation Specified
Temper ness strength stress min. thickness
Radius
mm MPa MPa % mm
over up to min. max. min. max. A A over up to
50mm
≥0,2 0,5 165 205 1 ≥0,2 1,3 2t
H16
0,5 0,8 165 205 2 1,3 2,9 2,5t
or
3) 0,8 1,3 165 205 145 3 2,9 4,0 3t
H26
1,3 4,0 165 205 145 4
≥0,2 0,5 180 165 1
0,5 0,8 180 165 2
H18
0,8 1,3 180 165 2
1,3 3,0 180 165 4
Table 16 — Alloy 3103
2)
Tensile test Bend test
1)
Specified thick- Tensile 0,2 % proof Elongation Specified
Temper ness strength stress min. thickness
Radius
mm MPa MPa % mm
over up to min. max. min. max. A A over up to
50mm
≥0,2 0,5 90 130 35 17
0,5 1,5 90 130 35 19
1,5 3,0 90 130 35 21
O
3,0 6,0 90 130 35 24
6,0 12,5 90 130 35 28
12,5 50,0 90 130 35 28 25
≥0,2 0,5 140 180 120 2
0,5 1,5 140 180 120 2
1,5 3,0 140 180 120 3
H14
3,0 6,0 140 180 120 4
6,0 12,5 140 180 120 5
12,5 25,0 140 180 120 5 5
≥0,2 0,5 140 180 110 4
0,5 1,5 140 180 110 4
3)
H24 1,5 3,0 140 180 110 5
3,0 6,0 140 180 110 6
6,0 12,5 140 180 110 8
≥0,2 0,5 185 165 1
H18 0,5 1,5 185 165 2
1,5 3,0 185 165 2
Table 17 — Alloys 3004 and 3104
2)
Tensile test Bend test
1)
Specified thick- Tensile 0,2 % proof Elongation Specified
Temper ness strength stress min. thickness
Radius
mm MPa MPa % mm
over up to min. max. min. max. A A over up to
50mm
≥0,2 0,5 155 195 10 ≥0,2 0,8 0t
0,5 0,8 155 195 14 0,8 3,0 0,5t
O
0,8 1,3 155 195 60 16
1,3 3,0 155 195 60 18
≥0,5 0,8 195 245 3 ≥0,5 0,8 0,5t
H12 or
3)
H22 0,8 1,3 195 245 145 4 0,8 3,0 1t
or H32
1,3 3,0 195 245 145 5
≥0,2 0,5 225 265 1 ≥0,2 0,8 1t
H14 or
0,5 0,8 225 265 3 0,8 3,0 1,5t
3)
H24
0,8 1,3 225 265 175 3
or H34
1,3 3,0 225 265 175 4
≥0,2 0,5 245 285 1 ≥0,2 0,8 2t
H16 or
0,5 0,8 245 285 2 0,8 3,0 2,5t
3)
H26
0,8 1,3 245 285 195 3
or H36
1,3 3,0 245 285 195 4
H18 or
≥0,2 0,5 265 215 1
3)
H28 or H38
H19 or
≥0,2 0,5 275 1
H29 or H39
Table 18 — Alloy 3005
2)
Tensile test Bend test
1)
Specified thick- Tensile 0,2 % proof Elongation Specified
Temper ness strength stress min. thickness
Radius
mm MPa MPa % mm
over up to min. max. min. max. A A over up to
50mm
≥0,3 0,5 120 165 14 ≥0,3 1,6 0t
O 0,5 0,8 120 165 16
0,8 1,6 120 165 45 18
≥0,3 0,5 135 185 1 ≥0,3 1,6 1t
H12
or 0,5 0,8 135 185 2
3)
H22
0,8 1,6 135 185 120 2
≥0,3 0,8 165 215 1 ≥0,3 0,8 1,5t
H14
3)
or H24
0,8 1,6 165 215 145 2 0,8 1,6 2t
≥0,3 0,8 195 245 1 ≥0,3 0,5 2t
H16
3)
or H26
0,8 1,6 195 245 165 2 0,8 1,6 3t
≥0,3 0,8 225 1
H18
0,8 1,6 225 205 2
16 © ISO 2014 – All rights reserved

Table 19 — Alloy 3105
2)
Tensile test Bend test
1)
Specified thick- Tensile 0,2 % proof Elongation Specified
Temper ness strength stress min. thickness
Radius
mm MPa MPa % mm
over up to min. max. min. max. A A over up to
50mm
0,2 0,5 100 155 40 14 0,2 0,5 0t
O/H111 0,5 1,5 100 155 40 15 0,5 1,5 0t
1,5 3,0 100 155 40 17 1,5 3,0 0,5t
0,2 0,5 130 180 105 3 0,2 0,5 1,5t
H12 0,5 1,5 130 180 105 4 0,5 1,5 1,5t
1,5 3,0 130 180 105 4 1,5 3,0 1,5t
0,2 0,5 150 200 130 2 0,2 0,5 2,5t
H14 0,5 1,5 150 200 130 2 0,5 1,5 2,5t
1,5 3,0 150 200 130 2 1,5 3,0 2,5t
0,2 0,5 175 225 160 1
H16 0,5 1,5 175 225 160 2
1,5 3,0 175 225 160 2
0,2 0,5 195 180 1
H18 0,5 1,5 195 180 1
1,5 3,0 195 180 1
0,2 0,5 215 190 1
H19
0,5 1,5 215 190 1
0,2 0,5 130 180 105 6
3)
H22 0,5 1,5 130 180 105 6
1,5 3,0 130 180 105 7
0,2 0,5 150 200 120 4 0,2 0,5 2,5t
3)
H24 0,5 1,5 150 200 120 4 0,5 1,5 2,5t
1,5 3,0 150 200 120 5 1,5 3,0 2,5t
0,2 0,5 175 225 150 3
3)
H26 0,5 1,5 175 225 150 3
1,5 3,0 175 225 150 3
0,2 0,5 195 170 2
H28
0,5 1,5 195 170 2
Table 20 — Alloy 4006
2)
Tensile test Bend test
1)
Specified thick- Tensile 0,2 % proof Elongation Specified
Temper ness strength stress min. thickness
Radius
mm MPa MPa % mm
over up to min. max. min. max. A A over up to
50mm
0,2 0,5 95 130 40 17 0,2 0,5 0t
0,5 1,5 95 130 40 19 0,5 1,5 0t
O
1,5 3,0 95 130 40 22 1,5 3,0 0t
3,0 6,0 95 130 40 25 3,0 6,0 1,0t
Table 20 (continued)
2)
Tensile test Bend test
1)
Specified thick- Tensile 0,2 % proof Elongation Specified
Temper ness strength stress min. thickness
Radius
mm MPa MPa % mm
over up to min. max. min. max. A A over up to
50mm
0,2 0,5 120 160 90 4 0,2 0,5 1,5t
H12 0,5 1,5 120 160 90 4 0,5 1,5 1,5t
1,5 3,0 120 160 90 5 1,5 3,0 1,5t
0,2 0,5 140 180 120 3 0,2 0,5 2,0t
H14 0,5 1,5 140 180 120 3 0,5 1,5 2,0t
1,5 3,0 140 180 120 3 1,5 3,0 2,0t
0,2 0,5 120 160 55 14
0,5 1,5 120 160 55 16
12)
T4
1,5 3,0 120 160 55 18
3,0 6,0 120 160 55 21
Table 21 — Alloy 4007
2)
Tensile test Bend test
1)
Specified thick- Tensile 0,2 % proof Elongation Specified
Temper ness strength stress min. thickness
Radius
mm MPa MPa % mm
over up to min. max. min. max. A A over up to
50mm
0,2 0,5 110 150 45 15
0,5 1,5 110 150 45 16
O/H111 1,5 3,0 110 150 45 19
3,0 6,0 110 150 45 21
6,0 12,5 110 150 45 25
0,2 0,5 140 180 110 4
H12 0,5 1,5 140 180 110 4
1,5 3,0 140 180 110 5
Table 22 — Alloy 4015
2)
Tensile test Bend test
1)
Specified thick- Tensile 0,2 % proof Elongation Specified
Temper ness strength stress min. thickness
Radius
mm MPa MPa % mm
over up to min. max. min. max. A A over up to
50mm
O/H111 0,2 3,0 150 45 20
0,2 0,5 120 175 90 4
H12
0,5 3,0 120 175 90 4
0,2 0,5 150 200 120 2
H14
0,5 3,0 150 200 120 3
0,2 0,5 170 220 150 1
H16
0,5 3,0 170 220 150 2
H18 0,2 3,0 200 250 180 1
18 © ISO 2014 – All rights reserved

Table 23 — Alloy 5005
2)
Tensile test Bend test
1)
Specified thick- Tensile 0,2 % proof Elongation Specified
Temper ness strength stress min. thickness
Radius
mm MPa MPa % mm
over up to min. max. min. max. A A over up to
50mm
≥4,0 13,0 120 8
H112 13,0 50,0 110 12
50,0 75,0 100 18
≥0,5 0,8 105 145 35 16 ≥0,5 6,0 0t
0,8 1,3 105 145 35 19
O
1,3 2,9 105 145 35 21
2,9 75,0 105 145 35 22 20
≥0,5 0,8 125 165 95 2 ≥0,5 6,0 0,5t
0,8 1,3 125 165 95 2
1,3 2,9 125 165 95 4
H12
2,9 4,0 125 165 95 5
4,0 6,5 125 165 95 5
6,5 12,0 125 165 95 7
≥0,5 0,8 120 155 3 ≥0,5 6,0 0,5t
0,8 1,3 120 155 85 4
3)
H22
1,3 2,9 120 155 85 6
or
2,9 4,0 120 155 85 7
H32
4,0 6,5 120 155 85 8
6,5 12,0 120 155 85 9
≥0,5 0,8 145 185 120 2 ≥0,5 2,9 1t
0,8 1,3 145 185 120 2 2,9 6,0 1,5t
1,3 2,9 145 185 120 3
H14
2,9 4,0 145 185 120 4
4,0 6,5 145 185 120 4
6,5 12,0 145 185 120 5
≥0,5 0,8 140 180 105 3 ≥0,5 2,9 1t
0,8 1,3 140 180 105 4 2,9 6,0 1,5t
3)
H24
1,3 2,9 140 180 105 5
or
2,9 4,0 140 180 105 5
H34
4,0 6,5 140 180 105 5
6,5 12,0 140 180 105 8
≥0,5 0,8 165 205 145 2 ≥0,5 1,3 2t
H16 0,8 1,3 165 205 145 2 1,3 2,9 2,5t
1,3 4,0 165 205 145 3 2,9 4,0 3t
≥0,5 0,8 155 195 1 ≥0,5 1,3 2t
3)
H26
or 0,8 1,3 155 195 125 2 1,3 2,9 2,5t
H36
1,3 4,0 155 195 125 3 2,9 4,0 3t
Table 23 (continued)
2)
Tensile test Bend test
1)
Specified thick- Tensile 0,2 % proof Elongation Specified
Temper ness strength stress min. thickness
Radius
mm MPa MPa % mm
over up to min. max. min. max. A A over up to
50mm
≥0,5 0,8 185 165 2
H18 0,8 1,3 185 165 2
1,3 3,0 185 165 2
≥0,5 0,8 180 165 2
H38 0,8 1,3 180 165 2
1,3 3,0 180 165 4
Table 24 — Alloy 5010
2)
Tensile test Bend test
1)
Specified thick- Tensile 0,2 % proof Elongation Specified
Temper ness strength stress min. thickness
Radius
mm MPa MPa % mm
over up to min. max. min. max. A A over up to
50mm
≥0,2 0,5 90 130 35 17 ≥0,2 0,5 0t
0,5 1,5 90 130 35 19 0,5 1,5 0t
O/H111
1,5 3,0 90 130 35 21 1,5 3,0 0t
3,0 6,0 90 130 35 24 3,0 6,0 1t
≥0,2 0,5 110 155 85 2 ≥0,2 0,5 1,5t
0,5 1,5 110 155 85 3 0,5 1,5 1,5t
H12
1,5 3,0 110 155 85 4 1,5 3,0 2t
3,0 6,0 110 155 85 5
≥0,2 0,5 140 175 115 2 ≥0,2 0,5 2t
0,5 1,5 140 175 115 2 0,5 1,5 2t
H14
1,5 3,0 140 175 115 3 1,5 3,0 2,5t
3,0 6,0 140 175 115 4
≥0,2 0,5 155 195 140 1 ≥0,2 0,5 2,5t
H16 0,5 1,5 155 195 140 2 0,5 1,5 2,5t
1,5 4,0 155 195 140 2 1,5 4,0 2,5t
≥0,2 0,5 175 160 1
H18 0,5 1,5 175 160 2
1,5 3,0 175 160 2
≥0,2 0,5 190 170 1
H19 0,5 1,5 190 170 1
1,5 3,0 190 170 1
≥0,2 0,5 110 155 75 4 ≥0,2 0,5 1t
0,5 1,5 110 155 75 5 0,5 1,5 1t
H22
1,5 3,0 110 155 75 6 1,5 3,0 1t
3,0 6,0 110 155 75 7
20 © ISO 2014 – All rights reserved

Table 24 (continued)
2)
Tensile test Bend test
1)
Specified thick- Tensile 0,2 % proof Elongation Specified
Temper ness strength stress min. thickness
Radius
mm MPa MPa % mm
over up to min. max. min. max. A A over up to
50mm
≥0,2 0,5 135 175 105 3 ≥0,2 0,5 1,5t
H24 0,5 1,5 135 175 105 4 0,5 1,5 1,5t
1,5 3,0 135 175 105 5 1,5 3,0 2t
≥0,2 0,5 155 195 130 2 ≥0,2 0,5 2t
H26 0,5 1,5 155 195 130 3 0,5 1,5 2t
1,5 4,0 155 195 130 3 1,5 4,0 2,5t
≥0,2 0,5 175 150 1
H28 0,5 1,5 175 150 2
1,5 3,0 175 150 3
Table 25 — Alloy 5110A
2)
Tensile test Bend test
1)
Specified thick- Tensile 0,2 % proof Elongation Specified
Temper ness strength stress min. thickness
Radius
mm MPa MPa % mm
over up to min. max. min. max. A A over up to
50mm
≥0,2 0,3 85 125 10 ≥0,2 6,0 0t
0,3 0,5 85 125 15
O
0,5 1,3 85 125 20
1,3 6,0 85 125 25
≥0,2 0,3 110 145 2 ≥0,2 6,0 0,5t
0,3 0,5 110 145 3
H12
0,5 0,8 110 145 4
or
3) 0,8 1,3 110 145 6
H22
1,3 2,9 110 145 8
2,9 6,0 110 145 9
≥0,2 0,3 125 165 1 ≥0,2 6,0 1t
0,3 0,5 125 165 2
H14
0,5 0,8 125 165 3
or
3) 0,8 1,3 125 165 4
H24
1,3 2,9 125 165 5
2,9 6,0 125 165 6
≥0,2 0,5 145 185 1 ≥0,2 4,0 2t
H16
0,5 0,8 145 185 2
or
3) 0,8 1,3 145 185 3
H26
1,3 4,0 145 185 4
≥0,2 0,5 165 1
0,5 0,8 165 2
H18
0,8 1,3 165 3
1,3 3,0 165 4
Table 26 — Alloy 5021
2)
Tensile test Bend test
1)
Specified thick- Tensile 0,2 % proof Elongation Specified
Temper ness strength stress min. thickness
Radius
mm MPa MPa % mm
over up to min. max. min. max. A A over up to
50mm
H18
≥0,15 0,5 260 3
or H38
H19
≥0,15 0,5 270 1
or H39
Table 27 — Alloy 5026
2)
Tensile test Bend test
1)
Specified thick- Tensile 0,2 % proof Elongation Specified
Temper ness strength stress min. thickness
Radius
mm MPa MPa % mm
over up to min. max. min. max. A A over up to
50mm
≥4,0 10,0 245 300 120 12
10,0 50,0 245 300 120 11
O/H111 50,0 100,0 245 300 120 10
100,0 200,0 230 285 120 9
200,0 350,0 210 270 90 6
≥5,0 12,5 250 300 200 10
H14
12,5 15,0 250 300 200 10
≥3,0 12,5 300 340 220 5
3)
H24
12,5 20,0 300 340 220 4
≥5,0 12,5 250 300 200 10
H34
12,5 15,0 250 300 200 10
Table 28 — Alloy 5040
2)
Tensile test Bend test
1)
Specified thick- Tensile 0,2 % proof Elongation Specified
Temper ness strength stress min. thickness
Radius
mm MPa MPa % mm
over up to min. max. min. max. A A over up to
50mm
3)
H24 /H34 ≥0,8 1,8 220 260 170 6
3)
H26 /H36 ≥1,0 2,0 240 280 205 5
22 © ISO 2014 – All rights reserved

Table 29 — Alloy 5042
2)
Tensile test Bend test
1)
Specified thick- Tensile 0,2 % proof Elongation Specified
Temper ness strength stress min. thickness
Radius
mm MPa MPa % mm
over up to min. max. min. max. A A over up to
50mm
H18
or ≥0,15 0,5 300 3
H38
H19
or ≥0,15 0,5 315 1
H39
Table 30 — Alloy 5049
2)
Tensile test Bend test
1)
Specified thick- Tensile 0,2 % proof Elongation Specified
Temper ness strength stress min. thickness
Radius
mm MPa MPa % mm
over up to min. max. min. max. A A over up to
50mm
0,2 0,5 190 240 80 12 0,2 0,5 0,5t
0,5 1,5 190 240 80 14 0,5 1,5 0,5t
1,5 3,0 190 240 80 16 1,5 3,0 1t
O/H111
3,0 6,0 190 240 80 18 3,0 6,0 1t
6,0 12,5 190 240 80 18
12,5 100,0 190 240 80 17
≥6,0 12,5 210 100 12
12,5 25,0 200 90 10
H112
25,0 40,0 190 80 12
40,0 80,0 190 80 14
0,2 0,5 220 270 170 4
0,5 1,5 220 270 170 5
1,5 3,0 220 270 170 6
H12
3,0 6,0 220 270 170 7
6,0 12,5 220 270 170 9
12,5 40,0 220 270 170 9
0,2 0,5 240 280 190 3
0,5 1,5 240 280 190 3
1,5 3,0 240 280 190 4
H14
3,0 6,0 240 280 190 4
6,0 12,5 240 280 190 5
12,5 25,0 240 280 190 5
0,2 0,5 265 305 220 2
0,5 1,5 265 305 220 3
H16
1,5 3,0 265 305 220 3
3,0 6,0 265 305 220 3
Table 30 (continued)
2)
Tensile test Bend test
1)
Specified thick- Tensile 0,2 % proof Elongation Specified
Temper ness strength stress min. thickness
Radius
mm MPa MPa % mm
over up to min. max. min. max. A A over up to
50mm
0,2 0,5 290 250 1
H18 0,5 1,5 290 250 2
1,5 3,0 290 250 2
0,2 0,5 220 270 130 7 0,2 0,5 1,5t
0,5 1,5 220 270 130 8 0,5 1,5 1,5t
1,5 3,0 220 270 130 10 1,5 3,0 2t
3)
H22 /H32
3,0 6,0 220 270 130 11
6,0 12,5 220 270 130 10
12,5 40,0 220 270 130 9
0,2 0,5 240 280 160 6 0,2 0,5 2,5t
0,5 1,5 240 280 160 6 0,5 1,5 2,5t
1,5 3,0 240 280 160 7 1,5 3,0 2,5t
3)
H24 /H34
3,0 6,0 240 280 160 8
6,0 12,5 240 280 160 10
12,5 25,0 240 280 160 8
0,2 0,5 265 305 190 4
0,5 1,5 265 305 190 4
3)
H26 /H36
1,5 3,0 265 305 190 5
3,0 6,0 265 305 190 6
0,2 0,5 290 230 3
3)
H28 /H38 0,5 1,5 290 230 3
1,5 3,0 290 230 4
Table 31 — Alloy 5449
2)
Tensile test Bend test
1)
Specified thick- Tensile 0,2 % proof Elongation Specified
Temper ness strength stress min. thickness
Radius
mm MPa MPa % mm
over up to min. max. min. max. A A over up to
50mm
0,5 1,5 190 240 80 14
O/H111
1,5 3,0 190 240 80 16
0,5 1,5 220 270 130 8
3)
H22
1,5 3,0 220 270 130 10
0,5 1,5 240 280 160 6
3)
H24
1,5 3,0 240 280 160 7
0,5 1,5 265 305 190 4
3)
H26
1,5 3,0 265 305 190 5
0,5 1,5 290 230 3
3)
H28
1,5 3,0 290 230 4
24 © ISO 2014 – All rights reserved

Table 32 — Alloy 5050
2)
Tensile test Bend test
1)
Specified thick- Tensile 0,2 % proof Elongation Specified
Temper ness strength stress min. thickness
Radius
mm MPa MPa % mm
over up to min. max. min. max. A A over up to
50mm
0,2 0,5 130 170 45 16 0,2 0,5 0t
0,5 1,5 130 170 45 17 0,5 1,5 0t
1,5 3,0 130 170 45 19 1,5 3,0 0,5t
O/H111
3,0 6,0 130 170 45 21
6,0 12,5 130 170 45 20
12,5 50,0 130 170 45 20
≥6,0 12,5 140 55 12
H112 12,5 40,0 140 55 10
40,0 80,0 140 55 10
0,2 0,5 155 195 130 2
H12 0,5 1,5 155 195 130 2
1,5 3,0 155 195 130 4
0,2 0,5 175 215 150 2
0,5 1,5 175 215 150 2
H14
1,5 3,0 175 215 150 3
3,0 6,0 175 215 150 4
0,2 0,5 195 235 170 1
0,5 1,5 195 235 170 2
H16
1,5 3,0 195 235 170 2
3,0 4,0 195 235 170 3
0,2 0,5 220 190 1
H18 0,5 1,5 220 190 2
1,5 3,0 220 190 2
0,2 0,5 155 195 110 4 0,2 0,5 1t
0,5 1,5 155 195 110 5 0,5 1,5 1t
3)
H22 /H32
1,5 3,0 155 195 110 7 1,5 3,0 1,5t
3,0 6,0 155 195 110 10
0,2 0,5 175 215 135 3 0,2 0,5 1,5t
0,5 1,5 175 215 135 4 0,5 1,5 1,5t
3)
H24 /H34
1,5 3,0 175 215 135 5 1,5 3,0 2t
3,0 6,0 175 215 135 8
0,2 0,5 195 235 160 2
0,5 1,5 195 235 160 3
3)
H26 /H36
1,5 3,0 195 235 160 4
3,0 4,0 195 235 160 6
0,2 0,5 220 180 1
3)
H28 /H38 0,5 1,5 220 180 2
1,5 3,0 220 180 3
Table 33 — Alloy 5251
2)
Tensile test Bend test
1)
Specified thick- Tensile 0,2 % proof Elongation Specified
Temper ness strength stress min. thickness
Radius
mm MPa MPa % mm
over up to min. max. min. max. A A over up to
50mm
0,2 0,5 160 200 60 13 0,2 0,5 0t
0,5 1,5 160 200 60 14 0,5 1,5 0t
1,5 3,0 160 200 60 16 1,5 3,0 0,5t
O/H111
3,0 6,0 160 200 60 18
6,0 12,5 160 200 60 18
12,5 50,0 160 200 60 18
0,2 0,5 190 230 150 3 0,2 0,5 2t
0,5 1,5 190 230 150 4 0,5 1,5 2t
1,5 3,0 190 230 150 5 1,5 3,0 2t
H12
3,0 6,0 190 230 150 8
6,0 12,5 190 230 150 10
12,5 25,0 190 230 150 10
0,2 0,5 210 250 170 2 0,2 0,5 2,5t
0,5 1,5 210 250 170 2 0,5 1,5 2,5t
H14 1,5 3,0 210 250 170 3 1,5 3,0 2,5t
3,0 6,0 210 250 170 4
6,0 12,5 210 250 170 5
0,2 0,5 230 270 200 1 0,2 0,5 3,5t
0,5 1,5 230 270 200 2 0,5 1,5 3,5t
H16
1,5 3,0 230 270 200 3 1,5 3,0 3,5t
3,0 4,0 230 270 200 3
0,2 0,5 255 230 1
H18 0,5 1,5 255 230 2
1,5 3,0 255 230 2
0,2 0,5 190 230 120 4 0,2 0,5 1,5t
0,5 1,5 190 230 120 6 0,5 1,5 1,5t
1,5 3,0 190 230 120 8 1,5 3,0 1,5t
3)
H22 /H32
3,0 6,0 190 230 120 10
6,0 12,5 190 230 120 12
12,5 25,0 190 230 120 12
0,2 0,5 210 250 140 3 0,2 0,5 2t
0,5 1,5 210 250 140 5 0,5 1,5 2t
3)
H24 /H34 1,5 3,0 210 250 140 6 1,5 3,0 2t
3,0 6,0 210 250 140 8
6,0 12,5 210 250 140 10
26 © ISO 2014 – All rights reserved

Table 33 (continued)
2)
Tensile test Bend test
1)
Specified thick- Tensile 0,2 % proof Elongation Specified
Temper ness strength stress min. thickness
Radius
mm MPa MPa % mm
over up to min. max. min. max. A A over up to
50mm
0,2 0,5 230 270 170 3 0,2 0,5 3t
0,5 1,5 230 270 170 4 0,5 1,5 3t
3)
H26 /H36
1,5 3,0 230 270 170 5 1,5 3,0 3t
3,0 4,0 230 270 170 7
0,2 0,5 255 200 2
3)
H28 /H38 0,5 1,5 255 200 3
1,5 3,0 255 200 3
Table 34 — Alloys 5052
2)
Tensile test Bend test
1)
Specified thick- Tensile 0,2 % proof Elongation Specified
Temper ness strength stress min. thickness
Radius
mm MPa MPa % mm
over up to min. max. min. max. A A over up to
50mm
4,0 6,5 195 110 9
6,5 13,0 195 110 7
H112
13,0 50,0 175 65 12
50,0 75,0 175 65 16
0,2 0,3 170 215 14 ≥0,2 0,8 0t
0,3 0,5 170 215 65 15 0,8 2,9 0,5t
0,5 0,8 170 215 65 17 2,9 6,0 1t
O 0,8 1,3 170 215 65 17
1,3 2,9 170 215 65 19
2,9 6,5 170 215 65 19
6,5 75,0 170 215 65 18
0,2 0,3 215 265 3 ≥0,2 0,8 0,5t
0,3 0,5 215 265 4 0,8 2,9 1t
0,5 0,8 215 265 5 2,9 6,0 1,5t
H12 or
3)
H22 0,8 1,3 215 265 155 5
or H32
1,3 2,9 215 265 155 7
2,9 6,5 215 265 155 9
6,5 12,0 215 265 155 11
0,2 0,5 235 285 180 3 ≥0,2 0,8 1t
0,5 0,8 235 285 180 4 0,8 2,9 1,5t
H14 or
0,8 1,3 235 285 180 4 2,9 6,0 2t
3)
H24
1,3 2,9 235 285 180 6
or H34
2,9 6,5 235 285 180 6
6,5 12,0 235 285 180 10
Table 34 (continued)
2)
Tensile test Bend test
1)
Specified thick- Tensile 0,2 % proof Elongation Specified
Temper ness strength stress min. thickness
Radius
mm MPa MPa % mm
over up to min. max. min. max. A A over up to
50mm
0,2 0,8 255 305 3 ≥0,2 0,8 2t
H16 or
3)
H26 0,8 4,0 255 305 205 4 0,8 1,3 2,5t
or H36
1,3 4,0 3t
0,2 0,8 270 220 3
H18 or
H38
0,8 3,0 270 220 4
H19 or H39 0,15 0,5 285 1
Table 35 — Alloys 5154 and 5254
2)
Tensile test Bend test
1)
Specified thick- Tensile 0,2 % proof Elongation Specified
Temper ness strength stress min. thickness
Radius
mm MPa MPa % mm
over up to min. max. min. max. A A over up to
50mm
≥4,0 6,5 235 125 8
6,5 13,0 225 125 8
H112
13,0 50,0 205 75 11
50,0 75,0 205 75 15
≥0,5 0,8 205 285 12 ≥0,5 0,8 1t
0,8 1,3 205 285 75 14 0,8 2,9 1,5t
O
1,3 2,9 205 285 75 16 2,9 6,0 2t
2,9 75,0 205 285 75 18
≥0,5 0,8 255 295 5 ≥0,5 0,8 1,5t
H12 or
0,8 1,3 255 295 175 5 0,8 2,9 2t
3)
H22
1,3 6,5 255 295 175 8 2,9 6,0 2,5t
or H32
6,5 12,0 255 295 175 12
≥0,5 0,8 275 315 4 ≥0,5 0,8 2t
0,8 1,3 275 315 205 4 0,8 2,9 2,5t
H14 or
3)
H24 1,3 4,0 275 315 205 6 2,9 6,0 3t
or H34
4,0 6,5 275 315 205 7
6,5 12,0 275 315 205 10
≥0,5 0,8 295 335 3 ≥0,5 0,8 3t
H16 or
0,8 1,3 295 335 225 3 0,8 1,3 3,5t
3)
H26
1,3 2,9 295 335 225 4 1,3 4,0 4t
or H36
2,9 4,0 295 335 225 5
≥0,5 0,8 315 3
H18 or
0,8 1,3 315 240 3
H38
1,3 3,0 315 240 4
28 © ISO 2014 – All rights reserved

Table 36 — Alloy 5154A
2)
Tensile test Bend test
1)
Specified thick- Tensile 0,2 % proof Elongation Specified
Temper ness strength stress min. thickness
Radius
mm MPa MPa % mm
over up to min. max. min. max. A A over up to
50mm
0,2 0,5 215 275 85 12 0,2 0,5 0,5t
0,5 1,5 215 275 85 13 0,5 1,5 0,5t
1,5 3,0 215 275 85 15 1,5 3,0 1t
O/H111
3,0 6,0 215 275 85 17
6,0 12,5 215 275 85 18
12,5 50,0 215 275 85 16
≥6,0 12,5 220 125 8
H112 12,5 40,0 215 90 9
40,0 80,0 215 90 13
0,2 0,5 250 305 190 3
0,5 1,5 250 305 190 4
1,5 3,0 250 305 190 5
H12
3,0 6,0 250 305 190 6
6,0 12,5 250 305 190 7
12,5 40,0 250 305 190 6
0,2 0,5 270 325 220 2
0,5 1,5 270 325 220 3
1,5 3,0 270 325 220 3
H14
3,0 6,0 270 325 220 4
6,0 12,5 270 325 220 5
12,5 25,0 270 325 220 4
0,2 0,5 310 270 1
H18 0,5 1,5 310 270 1
1,5 3,0 310 270 1
0,2 0,5 330 285 1
H19
0,5 1,5 330 285 1
0,2 0,5 250 305 180 5 0,2 0,5 1,5t
0,5 1,5 250 305 180 6 0,5 1,5 1,5t
1,5 3,0 250 305 180 7 1,5 3,0 2,0t
3)
H22 /H32
3,0 6,0 250 305 180 8
6,0 12,5 250 305 180 10
12,5 40,0 250 305 180 9
0,2 0,5 270 325 200 4 0,2 0,5 2,5t
0,
...