ISO 21068-1:2024
(Main)Chemical analysis of raw materials and refractory products containing silicon-carbide, silicon-nitride, silicon-oxynitride and sialon — Part 1: General information, terminology and sample preparation
Chemical analysis of raw materials and refractory products containing silicon-carbide, silicon-nitride, silicon-oxynitride and sialon — Part 1: General information, terminology and sample preparation
This document gives definitions and specifies techniques for the preparation of samples for the chemical analysis of silicon-carbide-containing raw materials and refractory products including: a) SiC raw materials; b) graphite brick containing silicon carbide; c) silicon carbide brick (includes the bricks containing silicon nitride, silicon oxynitride, sialon); d) refractories containing carbon and/or silicon carbide mixed with clay; e) refractories containing carbon and/or silicon carbide mixed with silica (and fused silica); f) refractories containing carbon and/or silicon carbide mixed with high alumina material; g) refractories containing carbon and/or silicon carbide mixed with magnesia (and dolomite); h) refractories containing carbon and/or silicon carbide mixed with chrome mineral or magnesia-chrome materials; i) refractories containing carbon and/or silicon carbide except those described in a) to h) above. The items of analysis described in ISO 21068-2, ISO 21068-3 and ISO 21068-4 are as follows: — loss on drying (LOD); — loss on ignition (LOI); — total carbon, Ctotal; — free carbon, Cfree; — silicon carbide, SiC; — free silicon (Sifree); — free aluminium (Alfree); — free magnesium (Mgfree); — free iron (Fefree); — silicon(IV) dioxide (SiO2); — aluminium(III) oxide (Al2O3); — iron(III) oxide (Fe2O3); — titanium(IV) oxide (TiO2); — calcium oxide (CaO); — magnesium oxide (MgO); — sodium oxide (Na2O); — potassium oxide (K2O); — chromium(III) oxide (Cr2O3); — zirconium(IV) oxide (ZrO2); — boron oxide (total boron calculated as B2O3); — nitrogen; — oxygen; — nitrides (undifferentiated: Si3N4, AlN, BN, sialon, oxy-nitrides, etc.); — mineralogical phases (XRD-methods).
Analyse chimique des matières premières et des produits réfractaires contenant du carbure de silicium, nitrure de silicium, oxynitrure de silicium et sialon — Partie 1: Informations générales, terminologie et préparation des échantillons
Le présent document donne des définitions et spécifie des techniques de préparation des échantillons pour l'analyse chimique des matières premières et des produits réfractaires contenant du carbure de silicium comprenant: a) matières premières contenant du carbure du silicium; b) brique de graphite contenant du carbure de silicium; c) brique de carbure de silicium (inclut les briques contenant du nitrure de silicium, de l’oxynitrure de silicium, du SIAlON); d) réfractaires contenant du carbone et/ou du carbure de silicium mélangés à de l’argile; e) réfractaires contenant du carbone et/ou du carbure de silicium mélangés à de la silice (et de la silice vitreuse); f) réfractaires contenant du carbone et/ou du carbure de silicium mélangés à des matériaux à haute teneur en alumine; g) réfractaires contenant du carbone et/ou du carbure de silicium mélangés à de la magnésie (ou de la dolomite); h) réfractaires contenant du carbone et/ou du carbure de silicium mélangés à des minéraux contenant du chrome ou des matériaux de magnésie-chrome; i) réfractaires contenant du carbone et/ou du carbure de silicium sauf ceux décrits ci-dessus en a) et h). L'ISO 21068-2, l'ISO 21068-3 et l'ISO 21068-4 décrivent des analyses chimiques sur: — la perte au séchage (LOD); — la perte au feu (LOI); — le carbone total, Ctotal; — le carbone libre, Clibre; — le carbure de silicium, SiC; — le silicium libre (Silibre); — l’aluminium libre (Allibre); — le magnésium libre (Mglibre); — le fer libre (Felibre); — l’oxyde de silicium (IV) (SiO2); — l’oxyde d'aluminium (Al2O3); — l’oxyde de fer (III) (Fe2O3); — l’oxyde de titane (IV) (TiO2); — l’oxyde de calcium (CaO); — l’oxyde de magnésium (MgO); — l’oxyde de sodium (Na2O); — l’oxyde de potassium (K2O); — l’oxyde de chrome (III) (Cr2O3); — l’oxyde de zirconium (ZrO2); — l’oxyde de bore (bore total calculé comme B2O3); — l’azote; — l’oxygène; — les nitrures (indifférencié: Si3N4, AlN, BN, SiAlON, oxynitrures, etc.); — les phases minéralogiques (méthodes de DRX).
General Information
Relations
Standards Content (Sample)
International
Standard
ISO 21068-1
Second edition
Chemical analysis of raw materials
2024-05
and refractory products containing
silicon-carbide, silicon-nitride,
silicon-oxynitride and sialon —
Part 1:
General information, terminology
and sample preparation
Analyse chimique des matières premières et des produits
réfractaires contenant du carbure de silicium, nitrure de silicium,
oxynitrure de silicium et sialon —
Partie 1: Informations générales, terminologie et préparation des
échantillons
Reference number
© ISO 2024
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication may
be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting on
the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address below
or ISO’s member body in the country of the requester.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: +41 22 749 01 11
Email: copyright@iso.org
Website: www.iso.org
Published in Switzerland
ii
Contents Page
Foreword .iv
Introduction .v
1 Scope . 1
2 Normative references . 2
3 Terms and definitions . 2
4 Sampling and preparation of the test sample . 4
4.1 General .4
4.2 Sample pre-treatment .4
4.2.1 General .4
4.2.2 Crushing .4
4.2.3 Thermal pre-treatment – Drying .4
5 Preliminary analyses . 5
6 Expression of results . 5
7 Test report . 5
Bibliography . 6
iii
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out through
ISO technical committees. Each member body interested in a subject for which a technical committee
has been established has the right to be represented on that committee. International organizations,
governmental and non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely
with the International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are described
in the ISO/IEC Directives, Part 1. In particular, the different approval criteria needed for the different types
of ISO document should be noted. This document was drafted in accordance with the editorial rules of the
ISO/IEC Directives, Part 2 (see www.iso.org/directives).
ISO draws attention to the possibility that the implementation of this document may involve the use of (a)
patent(s). ISO takes no position concerning the evidence, validity or applicability of any claimed patent
rights in respect thereof. As of the date of publication of this document, ISO had not received notice of (a)
patent(s) which may be required to implement this document. However, implementers are cautioned that
this may not represent the latest information, which may be obtained from the patent database available at
www.iso.org/patents. ISO shall not be held responsible for identifying any or all such patent rights.
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation of the voluntary nature of standards, the meaning of ISO specific terms and expressions
related to conformity assessment, as well as information about ISO's adherence to the World Trade
Organization (WTO) principles in the Technical Barriers to Trade (TBT), see www.iso.org/iso/foreword.html.
This document was prepared by Technical Committee ISO/TC 33, Refractories, in collaboration with the
European Committee for Standardization (CEN) Technical Committee CEN/TC 187, Refractory products
and materials, in accordance with the Agreement on technical cooperation between ISO and CEN (Vienna
Agreement).
This second edition cancels and replaces the first edition (ISO 21068-1:2008), which has been editorially
and technically revised.
The main changes are as follows:
— The Scope was adjusted according to the Scope of the revised versions of ISO 21068-2, ISO 21068-3 and
ISO 21068-4;
— Table 1 was removed as this is now part of the revised versions of ISO 21068-2, ISO 21068-3 and
ISO 21068-4;
— The list of documents in Clause 2 has been adjusted;
— Clause 3 was adjusted to the revised versions of ISO 21068-2, ISO 21068-3 and ISO 21068-4;
— The weighing procedure has been removed as it can be assumed as general knowledge of the user of the
ISO 21068 series;
— Bibliography was adjusted to this document.
Any feedback or questions on this document should be directed to the user’s national standards body. A
complete listing of these bodies can be found at www.iso.org/members.html.
iv
Introduction
[1]
The ISO 21068 series has been developed from the combination of EN 12698-1:2007 and EN 12698-
[2] [3] [4] [5]
2:2007 and ISO 21068-1:2008 , ISO 21068-2:2008 and ISO 21068-3:2008 . The last three standards
[6]
have been originally developed from the combination of Japanese standard JIS R 2011:2007 and work items
developed within CEN. Because there is a wide variety of laboratory equipment in use, the most commonly
used methods are described.
[2]
ISO 21068-4 is derived from EN 12698-2:2007 describing XRD methods for the determination of
mineralogical phases typically apparent in nitride and oxynitride bonded silicon carbide refractory products
using a Bragg-Brentano diffractometer.
[7]
The ISO 21068 series is applicable to the analysis of all refractory products as classified in ISO 10081-1 ,
[8] [9] [10] [11]
ISO 10081-2 , ISO 10081-3 and ISO 10081-4 (shaped) and ISO 1927-1 (unshaped) and raw materials
containing carbon and/or silicon carbide. Therefore, the ISO 21068 series covers the full range of analysis
from pure silicon carbide to oxide refractory composition with low-content silicon carbide and/or nitrides.
Primarily, the ISO 21068 series provides methods to distinguish between different carbon bound types
like total carbon (C ) and free carbon (C ) and derives from these two the silicon carbide content.
total free
ISO 21068-4 includes details of sample preparation and general principles for qualitative and quantitative
analysis of mineralogical phase composition. Quantitative determination of α-Si N , β-Si N , Si ON , AlN,
3 4 3 4 2 2
and SiAlON are described.
If free carbon is present, ISO 21068-2 includes different temperature treatments to determine the mass
changes gravimetrically. Frequently, the resulting residue is used for other determinations.
The determination of other groups of analytes described in the ISO 21068 series are free metals, free silicon
(Si ), free aluminium (Al ), free magnesium (Mg ), free iron (Fe ) and the group of oxides from main
free free free free
to trace components.
The ISO 21068 series also describes the determination of silicon dioxide, total silicon, oxygen and nitrogen
and other oxide bound metals that typically occur in the materials.
It represents a listing of analytical methods which is generally structured according to material composition.
However, it is still the user who should prove the applicability of the method depending on the material and
analytical requirements.
The most broadly used analytical techniques such as X-ray fluorescence spectroscopy (XRF) and inductively
coupled plasma-optical emission spectrometry (ICP-OES) suffer from the disadvantage that the analytical
results are chemical species independent. For carbon-containing ceramic raw materials and compositions,
the ISO 21068 series provides analytical methods for the determination of free carbon, and SiC in the
presence of oxide compounds in particular SiO .
Due to the diversity of laboratory equipment, the ISO 21068 series summarizes broadly used analytical
techniques which lead to equivalent results. For example, the determination of carbon is based on all
described methods on the reaction of carbon with oxygen at elevated temperatures to CO . Thus, carbon is
analysed as CO .
As well as carbon and carbide compounds, metallic silicon, aluminium and magnesium are considered. While
metallic silicon is mainly a precursor material which remains after the production process of SiC in the raw
material, metallic aluminium is added as an antioxidant in carbon-containing refractory formulations.
Mostly oxide bound components, such as Al O , CaO, MgO, TiO , Cr O , ZrO and alkalis, can be determined
2 3 2 2 3 2
[12] [13] [14]
by XRF, ICP-OES or wet chemical methods (see ISO 12677, ISO 26845 , ISO 21587-1 , ISO 21598-2
[15]
and ISO 21587-3 ). These results can be corrected by formulae provided by the ISO 21068 series, in
consideration of the values obtained by the determination of carbon, SiC, and metallic components.
The ISO 21068 series also provides methods for qualitative and quantitative determinations of the nitrogen
content and the determination of oxygen. Thereby only the total content of nitrogen and oxygen is given; a
precise determination of non-carbide components (oxides and nitrides) is not possible in this way.
v
The ISO 21068 series also provides methods to distinguish quantitatively between different varieties of
nitrides like silicon nitride, silicon oxy-nitride and sialon.
vi
International Standard ISO 21068-1:2024(en)
Chemical analysis of raw materials and refractory products
containing silicon-carbide, silicon-nitride, silicon-oxynitride
and sialon —
Part 1:
General information, terminology and sample preparation
1 Scope
This document gives definitions and specifies techniques for the preparation of samples for the chemical
analysis of silicon-carbide-containing raw materials and refractory products including:
a) SiC raw materials;
b) graphite brick containing silicon carbide;
c) silicon carbide brick (includes the bricks containing silicon nitride, silicon oxynitride, sialon);
d) refractories containing carbon and/or silicon carbide mixed with clay;
e) refractories containing carbon and/or silicon carbide mixed with silica (and fused silica);
f) refractories containing carbon and/or silicon carbide mixed with high alumina material;
g) refractories containing carbon and/or silicon carbide mixed with magnesia (and dolomite);
h) refractories containing carbon and/or silicon carbide mixed with chrome mineral or magnesia-chrome
mat
...
Norme
internationale
ISO 21068-1
Deuxième édition
Analyse chimique des matières
2024-05
premières et des produits
réfractaires contenant du carbure
de silicium, nitrure de silicium,
oxynitrure de silicium et sialon —
Partie 1:
Informations générales,
terminologie et préparation des
échantillons
Chemical analysis of raw materials and refractory products
containing silicon-carbide, silicon-nitride, silicon-oxynitride and
sialon —
Part 1: General information, terminology and sample preparation
Numéro de référence
DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2024
Tous droits réservés. Sauf prescription différente ou nécessité dans le contexte de sa mise en œuvre, aucune partie de cette
publication ne peut être reproduite ni utilisée sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique,
y compris la photocopie, ou la diffusion sur l’internet ou sur un intranet, sans autorisation écrite préalable. Une autorisation peut
être demandée à l’ISO à l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.
ISO copyright office
Case postale 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Genève
Tél.: +41 22 749 01 11
E-mail: copyright@iso.org
Web: www.iso.org
Publié en Suisse
ii
Sommaire Page
Avant-propos .iv
Introduction .v
1 Domaine d'application . 1
2 Références normatives . 2
3 Termes et définitions . 2
4 Échantillonnage et préparation de l'échantillon d'essai . 4
4.1 Généralités .4
4.2 Pré-traitement de l'échantillon .4
4.2.1 Généralités .4
4.2.2 Broyage .4
4.2.3 Pré-traitement thermique - Séchage .5
5 Analyses préalables . 5
6 Expression des résultats . 5
7 Rapport d'essai . 5
Bibliographie . 7
iii
Avant-propos
L'ISO (Organisation internationale de normalisation) est une fédération mondiale d'organismes nationaux
de normalisation (comités membres de l'ISO). L'élaboration des Normes internationales est en général
confiée aux comités techniques de l'ISO. Chaque comité membre intéressé par une étude a le droit de faire
partie du comité technique créé à cet effet. Les organisations internationales, gouvernementales et non
gouvernementales, en liaison avec l'ISO participent également aux travaux. L'ISO collabore étroitement avec
la Commission électrotechnique internationale (IEC) en ce qui concerne la normalisation électrotechnique.
Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont
décrites dans les Directives ISO/IEC, Partie 1. Il convient, en particulier, de prendre note des différents
critères d'approbation requis pour les différents types de documents ISO. Le présent document a
été rédigé conformément aux règles de rédaction données dans les Directives ISO/IEC, Partie 2 (voir
www.iso.org/directives).
L’ISO attire l’attention sur le fait que la mise en application du présent document peut entraîner l’utilisation
d’un ou de plusieurs brevets. L’ISO ne prend pas position quant à la preuve, à la validité et à l’applicabilité de
tout droit de propriété revendiqué à cet égard. À la date de publication du présent document, l’ISO n'avait pas
reçu notification qu’un ou plusieurs brevets pouvaient être nécessaires à sa mise en application. Toutefois,
il y a lieu d’avertir les responsables de la mise en application du présent document que des informations
plus récentes sont susceptibles de figurer dans la base de données de brevets, disponible à l'adresse
www.iso.org/brevets. L’ISO ne saurait être tenue pour responsable de ne pas avoir identifié tout ou partie de
tels droits de brevet.
Les appellations commerciales éventuellement mentionnées dans le présent document sont données pour
information, par souci de commodité, à l’intention des utilisateurs et ne sauraient constituer un engagement.
Pour une explication de la nature volontaire des normes, la signification des termes et expressions
spécifiques de l'ISO liés à l'évaluation de la conformité, ou pour toute information au sujet de l'adhésion de
l'ISO aux principes de l’Organisation mondiale du commerce (OMC) concernant les obstacles techniques au
commerce (OTC), voir www.iso.org/avant-propos.
Le présent document a été élaboré par le comité technique ISO/TC 33, Réfractaires, en collaboration avec
le comité technique CEN/TC 187 Matériaux et produits réfractaires, du Comité européen de normalisation
(CEN) conformément à l’Accord de coopération technique entre l’ISO et le CEN (Accord de Vienne).
Cette deuxième édition annule et remplace la première édition (ISO 21068-1:2008) qui a fait l’objet d’une
révision éditoriale et technique.
Les principales modifications par rapport à l’édition précédente sont les suivantes:
— Rectification du domaine d'application en fonction du domaine d'application des versions révisées de
l'ISO 21068-2, de l'ISO 21068-3 et de l'ISO 21068-4;
— Suppression du Tableau 1 car il fait désormais partie des versions révisées des normes ISO 21068-2,
ISO 21068-3 et ISO 21068-4;
— Rectification de la liste des documents de l’Article 2;
— Rectification de l’Article 3 pour correspondre aux versions révisées des normes ISO 21068-2, ISO 21068-3
et ISO 21068-4;
— Suppression de la procédure de pesage car elle peut être considérée comme une connaissance générale
de l'utilisateur de la série ISO 21068;
— La Bibliographie a été adaptée au présent document.
Il convient que l’utilisateur adresse tout retour d’information ou toute question concernant le présent
document à l’organisme national de normalisation de son pays. Une liste exhaustive desdits organismes se
trouve à l’adresse www.iso.org/fr/members.html.
iv
Introduction
[1] [2] [3]
L’ISO 21068 a été élaborée à partir de l’EN 12698-1:2007 et EN 12698-2:2007 , et EN 21068-1:2008 ,
[4] [5]
EN 21068-2:2008 , EN 21068-3:2008 . Les trois dernières normes ont été rédigées à l’origine en
[6]
combinant la norme japonaise JIS R 2011:2007 et des études menées au sein du CEN. Du fait du grand
nombre de matériels de laboratoire utilisés, les méthodes les plus couramment utilisées sont décrites.
[2]
L’ISO 21068-4, est fondée sur la Norme européenne EN 12698-2:2007 décrivant les méthodes de DRX
pour la détermination de phases minéralogiques généralement présentes dans les produits réfractaires de
carbure de silicium lié au nitrure et l’oxynitrure, à l’aide d’un diffractomètre à géométrie Bragg-Brentano.
[7]
L’ISO 21068 s'applique à l'analyse de tous les produits réfractaires tels qu'ils sont classés dans l'ISO 10081-1 ,
[8] [9] [10] [11]
l'ISO 10081-2 , l'ISO 10081-3 , l'ISO 10081-4 , (matériaux façonnés) et l'ISO 1927-1 , (matériaux
non façonnés) et des matériaux bruts contenant du carbone et/ou du carbure de silicium. Par conséquent,
l’ISO 21068, couvre toute l’étendue de l’analyse, du carbure de silicium pur à la composition des réfractaires
contenant de l’oxyde à faible teneur en nitrures et/ou en carbures de silicium. L’ISO 21068 fournie
principalement des méthodes permettant de faire une distinction entre les différents types de liaisons de
carbone comme le carbone total (C ) et le carbone libre (C ) et en tire la teneur en carbure de silicium.
total libre
L’iso 21068-4 contient des détails relatifs à la préparation des échantillons ainsi que des principes généraux
de l’analyse qualitative et quantitative de la composition des phases minéralogiques. La détermination
quantitative de α-Si N , β-Si N , Si ON , AlN, et SiAlON est décrite.
3 4 3 4 2 2
En présence de carbone libre, l'ISO 21068-2 inclut les différents traitements thermiques afin de déterminer
les variations de masse par une méthode gravimétrique. Le résidu obtenu est fréquemment utilisé pour
d'autres dosages.
L'ISO 21068 spécifie le dosage d’autres groupes de substances: les métaux libres, le silicium libre (Si ),
libre
l'aluminium libre (Al ), le magnésium libre (Mg ), le fer libre (Fe ) et le groupe des oxydes qu’il
libre libre libre
s’agisse de composés principaux ou présents à l'état de trace.
L’ISO 21068 décrit également le dosage du dioxyde de silicium, du silicium total, de l'oxygène, de l'azote et
d'autres métaux oxydés fréquemment retrouvés dans les matériaux.
Elle donne une liste de méthodes d'analyse généralement structurée selon la composition du matériau.
Cependant, il revient toujours à l'utilisateur d’apporter la démonstration de l’applicabilité de la méthode
selon le matériau et les exigences de l'analyse.
Les techniques analytiques les plus largement utilisées telles que la spectroscopie à fluorescence des
rayons X (FRX) et la spectroscopie d'émission optique avec plasma induit par haute fréquence (ICP-OES)
ont pour inconvénient que les résultats analytiques sont indépendants de l’espèce chimique. Pour les
matières premières céramiques et les compositions contenant du carbone, l'ISO 21068 fournit des méthodes
d’analyses pour le dosage du carbone libre, et du SiC en présence de composés oxydés, en particulier SiO .
En raison de la diversité de l'équipement de laboratoire, l'ISO 21068 récapitulent les techniques d’analyses
largement utilisées qui aboutissent à des résultats équivalents. Par exemple, le dosage du carbone repose
pour toutes les méthodes décrites sur la réaction du carbone avec l’oxygène à des températures élevées
2 2
conduisant à la formation de CO . Le dosage du carbone repose sur l’analyse du CO .
Outre le carbone et les composés de carbures, le silicium métallique, l'aluminium métallique et le magnésium
métallique sont également couverts. Tandis que le silicium métallique est principalement un matériau
précurseur qui demeure après le processus de production du SiC dans les matières premières, l'aluminium
métallique est ajouté comme antioxydant dans les formulations réfractaires contenant du carbone.
La plupart des composées oxydés, comme Al O , CaO, MgO, TiO , Cr O , ZrO et les alcalis, peuvent être
2 3 2 2 3 2
[12]
dosés par FRX, ICP-OES ou des méthodes chimiques par voies humides (voir l'ISO 12677, l'ISO 26845 ,
[13] [14] [15]
l'ISO 21587-1 , l'ISO 21587-2 et l'ISO 21587-3 ). Ces résultats peuvent être corrigés par des formules
fournies par l'ISO 21068 lors de la prise en compte des valeurs obtenues par le dosage du carbone, du SiC, et
des composants métalliques.
v
L'ISO 21068 fournit également des méthodes pour les déterminations qualitatives et quantitatives de la
teneur en azote et le dosage de l'oxygène. De ce fait, seulement la teneur totale en azote et en oxygène est
donnée; il est impossible de réaliser un dosage précis des composants sans carbure (oxydes et nitrures) de
cette façon.
L'ISO 21068, fournit des méthodes pour distinguer quantitativement les différentes variétés de nitrures
comme le nitrure de silicium, l’oxynitrure de silicium et le SIAlON.
vi
Norme internationale ISO 21068-1:2024(fr)
Analyse chimique des matières premières et des produits
réfractaires contenant du carbure de silicium, nitrure de
silicium, oxynitrure de silicium et sialon —
Partie 1:
Informations générales, terminologie et préparation des
échantillons
1 Domaine d'application
Le présent document donne des définitions et spécifie des techniques de préparation des échantillons pour
l'analyse chimique des matières premières et des produits réfractaires contenant du carbure de silicium
comprenant:
a) matières premières contenant du carbure du silicium;
b) brique de graphite contenant du carbure de silicium;
c) brique de carbure de silicium (inclut les briques contenant du nitrure de silicium, de l’oxynitrure de
silicium, du SIAlON);
d) réfractaires contenant du carbone et/ou du carbure de silicium mélangés à de l’argile;
e) réfractaires contenant du carbone et/ou du carbure de silicium mélangés à de la silice (et de la silice
vitreuse);
f) réfractaires contenant du carbone et/ou du carbure de silicium mélangés à des matériaux à haute teneur
en alumine;
g) réfractaires contenant du carbone et/ou du carbure de silicium mélangés à de la magnésie (ou de la
dolomite);
h) réfractaires contenant du carbone et/ou du carbure de silicium mélangés à des minéraux contenant du
chrome ou des matériaux de magnésie-chrome;
i) réfractaires contenant du carbone et/ou du carbure de silicium sauf ceux décrits ci-dessus en a) et h).
L'ISO 21068-2, l'ISO 21068-3 et l'ISO 21068-4 décrivent des analyses chimiques sur:
— la perte au séchage (LOD);
— la perte au feu (LOI);
— le carbone total, C ;
total
— le carbone libre, C ;
libre
— le carbure de silicium, SiC;
— le silicium libre (Si );
libre
— l’aluminium libre (Al );
libre
— le magnésium libre (Mg );
libre
— le fer libre (Fe );
libre
— l’oxyde de silicium (IV) (SiO );
— l’oxyde d'aluminium (Al O );
2 3
— l’oxyde de
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.
Loading comments...