EN 10327:2004
(Main)Continuously hot-dip coated strip and sheet of low carbon steels for cold forming - Technical delivery conditions
Continuously hot-dip coated strip and sheet of low carbon steels for cold forming - Technical delivery conditions
1.1 This European Standard specifies requirements for continuously hot-dip coated products made of low carbon steels for cold forming coated with zinc (Z), zinc-iron alloy (ZF), zinc-aluminium alloy (ZA), aluminium-zinc alloy (AZ) and aluminium-silicon alloy (AS) (see Table 1) with thicknesses of 0,35 mm to 3,0 mm unless otherwise agreed (see 1.2). The thickness is the final thickness of the delivered product after coating.
This European Standard applies to strip of all widths and to sheets cut from it (= 600 mm width) and cut lengths
(< 600 mm width).
1.2 If agreed at the time of enquiry and order, this European Standard may also be applied to continuously hot-dip coated flat products in thicknesses > 3,0 mm. In this case the mechanical property, adhesion of coating and surface condition requirements shall also be agreed at the time of enquiry and order.
1.3 The products covered by this European Standard are mainly used where cold formability and corrosion resistance are the most important factors. Corrosion resistance of the alloy is proportional to the coating thickness, hence to its mass (see also 7.3.2).
1.4 This European Standard is not applicable to:
· continuously hot-dip coated structural steel flat products (see prEN 10326);
· electrolytically zinc coated cold rolled steel flat products (see EN 10152);
· continuously organic coated (coil coated) steel flat products (see EN 10169-1, ENV 10169-2 and
EN 10169-3);
· continuously hot-dip coated strip and sheet of steels with higher yield strength for cold forming (see EN 10292).
Kontinuierlich schmelztauchveredeltes Band und Blech aus weichen Stählen zum Kaltumformen - Technische Lieferbedingungen
1.1 Dieses Dokument legt die Anforderungen an kontinuierlich schmelztauchveredelte Flacherzeugnisse aus weichen Stählen zum Kaltumformen mit Überzügen aus Zink (Z), Zink-Eisen-Legierung (ZF), Zink-Aluminium-Legierung (ZA), Aluminium-Zink-Legierung (AZ) und Aluminium-Silicium-Legierung (AS) (siehe Tabelle 1) in Dicken von 0,35 mm bis 3,0 mm fest, falls nicht anders vereinbart (siehe 1.2). Als Dicke gilt die Enddicke des gelieferten Erzeugnisses nach dem Schmelztauchveredeln.
Dieses Dokument gilt für Band aller Breiten sowie für daraus abgelängte Bleche (³ 600 mm Breite) und Stäbe (< 600 mm Breite).
1.2 Nach Vereinbarung bei der Anfrage und Bestellung kann dieses Dokument auch auf kontinuierlich schmelztauchveredelte Flacherzeugnisse in Dicken > 3,0 mm angewendet werden. Die Anforderungen an die mechanischen Eigenschaften, die Haftung des Überzugs und die Oberflächenbeschaffenheit sind in diesem Fall ebenfalls bei der Anfrage und Bestellung zu vereinbaren.
1.3 Die Erzeugnisse nach diesem Dokument eignen sich für Verwendungszwecke, bei denen die Kaltumformbarkeit und die Korrosionsbeständigkeit von vorrangiger Bedeutung sind. Der durch den Überzug bewirkte Korrosionsschutz ist der Überzugsdicke und damit der Auflagenmasse proportional (siehe auch 7.3.2).
1.4 Dieses Dokument gilt nicht für
· kontinuierlich schmelztauchverzinkte Flacherzeugnisse aus Baustählen (siehe EN 10326);
· elektrolytisch verzinkte kaltgewalzte Flacherzeugnisse aus Stahl (siehe EN 10152);
· kontinuierlich organisch beschichtete (bandbeschichtete) Flacherzeugnisse aus Stahl (siehe EN 10169-1,
ENV 10169-2 und EN 10169-3);
· kontinuierlich schmelztauchveredeltes Band und Blech aus Stählen mit hoher Streckgrenze zum Kaltumformen (siehe EN 10292).
Bandes et tôles en acier doux revêtues en continu par immersion à chaud pour formage à froid - Conditions techniques de livraison
1.1 Le présent document a pour objet de spécifier les exigences relatives aux produits en acier doux pour formage à froid revêtus par immersion à chaud en continu de zinc (Z), d'alliage de zinc et de fer (ZF), d'alliage de zinc et d'aluminium (ZA), d'alliage d'aluminium et de zinc (AZ) et d'alliage d'aluminium et de silicium (AS) (voir Tableau 1), avec des épaisseurs allant de 0,35 mm à 3,0 mm sauf indication contraire (voir 1.2). L'épaisseur considérée est l'épaisseur finale du produit livré après revêtement.
Le présent document est applicable aux bandes de toutes largeurs ainsi qu'aux tôles (largeur ³ 600 mm) et aux feuilles (largeur < 600 mm) qui y sont découpées.
1.2 Par accord lors de la commande, le présent document peut également être utilisé pour les produits plats en acier galvanisés à chaud en continu d'épaisseur > 3,0 mm. Dans ce cas, les propriétés mécaniques et les caractéristiques d'adhérence du revêtement et de finition doivent également faire l'objet d'un accord à la commande.
1.3 Les produits conformes au présent document sont principalement utilisés lorsque l'aptitude au formage et la résistance à la corrosion sont les facteurs primordiaux. La résistance du revêtement à la corrosion est proportionnelle à la masse du revêtement (voir aussi 7.3.2).
1.4 Le présent document ne s'applique pas :
- aux produits plats de bandes et tôles en acier de construction revêtus par immersion à chaud en continu pour formage à froid (voir EN 10326) ;
- aux produits plats en acier, laminés à froid, revêtus de zinc par voie électrolytique (voir EN 10152) ;
- aux produits plats en acier revêtus en continu de matières organiques (prélaqués) (voir EN 10169-1, ENV 10169-2 et EN 10169-3) ;
- bandes et tôles en acier à haute limite d'élasticité revêtues en continu par immersion à chaud pour formage à froid (voir EN 10292).
Kontinuirno vroče prevlečeni trakovi in pločevine iz jekel z majhnim deležem ogljika za hladno oblikovanje – Tehnični dobavni pogoji
General Information
Relations
Standards Content (Sample)
2003-01.Slovenski inštitut za standardizacijo. Razmnoževanje celote ali delov tega standarda ni dovoljeno.Continuously hot-dip coated strip and sheet of low carbon steels for cold forming - Technical delivery conditionsBandes et tôles en acier doux revetues en continu par immersion a chaud pour formage a froid - Conditions techniques de livraisonKontinuierlich schmelztauchveredeltes Band und Blech aus weichen Stählen zum Kaltumformen - Technische Lieferbedingungen77.140.50SROL]GHONLFlat steel products and semi-productsICS:SIST EN 10327:2004enTa slovenski standard je istoveten z:EN 10327:200401-november-2004SIST EN 10327:2004SLOVENSKI
STANDARDSIST EN 10214:1997SIST EN 10215:1998SIST EN 10142:2001SIST EN 10154:20031DGRPHãþD
EUROPEAN STANDARD NORME EUROPÉENNE EUROPÄISCHE NORM
EN 10327
July 2004 ICS 77.140.50 Supersedes EN 10142:2000,EN 10154:2002,EN 10214:1995,and EN 10215:1995English version
Continuously hot-dip coated strip and sheet of low carbon steels for cold forming - Technical delivery conditions
Bandes et tôles en acier doux revêtues en continu par immersion à chaud pour formage à froid - Conditions techniques de livraison
Kontinuierlich schmelztauchveredeltes Band und Blech aus weichen Stählen zum Kaltumformen - Technische Lieferbedingungen This European Standard was approved by CEN on 23 April 2004.
CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the Central Secretariat or to any CEN member.
This European Standard exists in three official versions (English, French, German). A version in any other language made by translation under the responsibility of a CEN member into its own language and notified to the Central Secretariat has the same status as the official versions.
CEN members are the national standards bodies of Austria, Belgium, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom.
EUROPEAN COMMITTEE FOR STANDARDIZATION COMITÉ EUROPÉEN DE NORMALISATION EUROPÄISCHES KOMITEE FÜR NORMUNG
Management Centre: rue de Stassart, 36
B-1050 Brussels © 2004 CEN All rights of exploitation in any form and by any means reserved worldwide for CEN national Members. Ref. No. EN 10327:2004: E
Reference method for determination of the zinc, zinc-aluminium and aluminium-zinc coating mass.20 Annex B (normative)
Reference method for determination of the aluminium-silicon coating mass.21 Annex C (normative)
Method for determination of the mass of the Al-Fe-Si alloy layer.22 Bibliography.23
This document specifies requirements for continuously hot-dip coated products made of low carbon steels for cold forming coated with zinc (Z), zinc-iron alloy (ZF), zinc-aluminium alloy (ZA), aluminium-zinc alloy (AZ) and aluminium-silicon alloy (AS) (see Table 1) with thicknesses of 0,35 mm to 3,0 mm unless otherwise agreed (see 1.2). The thickness is the final thickness of the delivered product after coating. This document applies to strip of all widths and to sheets cut from it (≥ 600 mm width) and cut lengths
(< 600 mm width). 1.2 If agreed at the time of enquiry and order, this document may also be applied to continuously hot-dip coated flat products in thicknesses > 3,0 mm. In this case the mechanical property, adhesion of coating and surface condition requirements shall also be agreed at the time of enquiry and order. 1.3 The products covered by this document are mainly used where cold formability and corrosion resistance are the most important factors. Corrosion resistance of the alloy is proportional to the coating thickness, hence to its mass (see also 7.3.2). 1.4
This document is not applicable to: • continuously hot-dip coated structural steel flat products (see EN 10326); • electrolytically zinc coated cold rolled steel flat products (see EN 10152); • continuously organic coated (coil coated) steel flat products (see EN 10169-1, ENV 10169-2 and
EN 10169-3); • continuously hot-dip coated strip and sheet of steels with higher yield strength for cold forming (see EN 10292). 2 Normative references The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments). EN 10002-1, Metallic materials – Tensile testing – Part 1: Method of test at ambient temperature. EN 10020:2000, Definition and classification of grades of steel. EN 10021:1993, General technical delivery requirements for steel and steel products. EN 10027-1, Designation systems for steels – Part 1: Steel names, principal symbols. EN 10027-2, Designation systems for steels – Part 2: Numerical system. EN 10079:1992, Definition of steel products. EN 10143, Continuously hot-dip metal coated steel sheet and strip - Tolerances on dimensions and shape. EN 10204:1991, Metallic products – Types of inspection documents. ISO 10113, Metallic materials – Sheet and strip – Determination of plastic strain ratio. ISO 10275, Metallic materials – Sheet and strip – Determination of tensile strain hardening exponent. CR 10260, Designation systems for steel – Additional symbols.
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.