ASTM B618/B618M-11

This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Because
it may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current version
of the standard as published by ASTM is to be considered the official document.
Designation:B618/B618M–10 Designation: B618/B618M – 11
Standard Specification for
1
Aluminum-Alloy Investment Castings
This standard is issued under the fixed designation B618/B618M; the number immediately following the designation indicates the year
of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.
A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the Department of Defense.
1. Scope*
1.1 This specification covers aluminum-alloy investment castings designated as shown in Table 1.
1.2This specification is not intended for aluminum-alloy investment castings used in aerospace applications.
1.2 This specification is for aluminum-alloy investment castings used in general purpose applications. It may not address the
mechanical properties integrity testing and verification required for highly loaded or safety critical applications.
1.3 Alloy and temper designations are in accordance withANSI H35.1/H35.1 (M). The equivalent Unified Numbering System
alloy designations are in accordance with Practice E527.
1.4 Unless the order specifies the “M” specification designation, the material shall be furnished to the inch-pound units.
1.5 For acceptance criteria for inclusion of new aluminum and aluminum alloys and their properties in this specification, see
Annex A1 and Annex A2.
1.6 Units—The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated
in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values
from the two systems may result in nonconformance with the standard.
1.7 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility
of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory
limitations prior to use.
2. Referenced Documents
2.1 The following documents of the issue in effect on the date of purchase form a part of this specification to the extent
referenced herein:
2
2.2 ASTM Standards:
B179 Specification for Aluminum Alloys in Ingot and Molten Forms for Castings from All Casting Processes
B275 Practice for Codification of Certain Nonferrous Metals and Alloys, Cast and Wrought
B557 Test Methods for Tension Testing Wrought and Cast Aluminum- and Magnesium-Alloy Products
B557M Test Methods for Tension Testing Wrought and Cast Aluminum- and Magnesium-Alloy Products (Metric)
B660 Practices for Packaging/Packing of Aluminum and Magnesium Products
B881 Terminology Relating to Aluminum- and Magnesium-Alloy Products
B917/B917M Practice for Heat Treatment of Aluminum-Alloy Castings from All Processes
D3951 Practice for Commercial Packaging
E29 Practice for Using Significant Digits in Test Data to Determine Conformance with Specifications
E34 Test Methods for Chemical Analysis of Aluminum and Aluminum-Base Alloys
E94 Guide for Radiographic Examination
E155 Reference Radiographs for Inspection of Aluminum and Magnesium Castings
E165 Practice for Liquid Penetrant Examination for General Industry
E527 Practice for Numbering Metals and Alloys in the Unified Numbering System (UNS)
E607 Test Method for Atomic Emission Spectrometric Analysis Aluminum Alloys by the Point to Plane Technique Nitrogen
Atmosphere
1
This specification is under the jurisdiction ofASTM Committee B07 on Light Metals andAlloys and is the direct responsibility of Subcommittee B07.01 onAluminum
Alloy Ingots and Castings.
Current edition approved Nov. 1, 2010.2011. Published December 2010.2011. Originally approved in 1977. Last previous edition approved in 20082010 as
B618/B618M – 108. DOI: 10.1520/B0618_B0618M-101.
2
For referencedASTM standards, visit theASTM website, www.astm.org, or contactASTM Customer Service at service@astm.org. For Annual Book of ASTM Standards
volume information, refer to the standard’s Document Summary page on the ASTM website.
*A Summary of Changes section appears at the end of this standard.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
1

---------------------- Page: 1 ----------------------
B618/B618M – 11
2
TABLE 1 Chemical Composition Requirements
NOTE 1—When single units are shown, these indicate the maximum amounts permitted.
NOTE 2—Analysis shall be made for the elements for which li
...

This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Because
it may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current version
of the standard as published by ASTM is to be considered the official document.
Designation:B618/B618M–10 Designation: B618/B618M – 11
Standard Specification for
1
Aluminum-Alloy Investment Castings
This standard is issued under the fixed designation B618/B618M; the number immediately following the designation indicates the year
of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.
A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the Department of Defense.
1. Scope*
1.1 This specification covers aluminum-alloy investment castings designated as shown in Table 1.
1.2This specification is not intended for aluminum-alloy investment castings used in aerospace applications.
1.2 This specification is for aluminum-alloy investment castings used in general purpose applications. It may not address the
mechanical properties integrity testing and verification required for highly loaded or safety critical applications.
1.3 Alloy and temper designations are in accordance withANSI H35.1/H35.1 (M). The equivalent Unified Numbering System
alloy designations are in accordance with Practice E527.
1.4 Unless the order specifies the “M” specification designation, the material shall be furnished to the inch-pound units.
1.5 For acceptance criteria for inclusion of new aluminum and aluminum alloys and their properties in this specification, see
Annex A1 and Annex A2.
1.6 Units—The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated
in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values
from the two systems may result in nonconformance with the standard.
1.7 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility
of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory
limitations prior to use.
2. Referenced Documents
2.1 The following documents of the issue in effect on the date of purchase form a part of this specification to the extent
referenced herein:
2
2.2 ASTM Standards:
B179 Specification for Aluminum Alloys in Ingot and Molten Forms for Castings from All Casting Processes
B275 Practice for Codification of Certain Nonferrous Metals and Alloys, Cast and Wrought
B557 Test Methods for Tension Testing Wrought and Cast Aluminum- and Magnesium-Alloy Products
B557M Test Methods for Tension Testing Wrought and Cast Aluminum- and Magnesium-Alloy Products (Metric)
B660 Practices for Packaging/Packing of Aluminum and Magnesium Products
B881 Terminology Relating to Aluminum- and Magnesium-Alloy Products
B917/B917M Practice for Heat Treatment of Aluminum-Alloy Castings from All Processes
D3951 Practice for Commercial Packaging
E29 Practice for Using Significant Digits in Test Data to Determine Conformance with Specifications
E34 Test Methods for Chemical Analysis of Aluminum and Aluminum-Base Alloys
E94 Guide for Radiographic Examination
E155 Reference Radiographs for Inspection of Aluminum and Magnesium Castings
E165 Practice for Liquid Penetrant Examination for General Industry
E527 Practice for Numbering Metals and Alloys in the Unified Numbering System (UNS)
E607 Test Method for Atomic Emission Spectrometric Analysis Aluminum Alloys by the Point to Plane Technique Nitrogen
Atmosphere
1
This specification is under the jurisdiction ofASTM Committee B07 on Light Metals andAlloys and is the direct responsibility of Subcommittee B07.01 onAluminum
Alloy Ingots and Castings.
Current edition approved Nov. 1, 2010.2011. Published December 2010.2011. Originally approved in 1977. Last previous edition approved in 20082010 as
B618/B618M – 108. DOI: 10.1520/B0618_B0618M-101.
2
For referencedASTM standards, visit theASTM website, www.astm.org, or contactASTM Customer Service at service@astm.org. For Annual Book of ASTM Standards
volume information, refer to the standard’s Document Summary page on the ASTM website.
*A Summary of Changes section appears at the end of this standard.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
1

---------------------- Page: 1 ----------------------
B618/B618M – 11
2
TABLE 1 Chemical Composition Requirements
NOTE 1—When single units are shown, these indicate the maximum amounts permitted.
NOTE 2—Analysis shall be made for the elements for which li
...