ISO 180:2019
(Main)Plastics — Determination of Izod impact strength
Plastics — Determination of Izod impact strength
1.1 This document specifies a method for determining the Izod impact strength of plastics under defined conditions. A number of different types of specimen and test configurations are defined. Different test parameters are specified according to the type of material, the type of test specimen and the type of notch. 1.2 The method is used to investigate the behaviour of specified types of specimen under the impact conditions defined and for estimating the brittleness or toughness of specimens within the limitations inherent in the test conditions. 1.3 The method is suitable for use with the following range of materials: — rigid thermoplastic moulding and extrusion materials, including filled and reinforced compounds in addition to unfilled types; rigid thermoplastics sheets; — rigid thermosetting moulding materials, including filled and reinforced compounds; rigid thermosetting sheets, including laminates; — fibre-reinforced thermosetting and thermoplastic composites incorporating unidirectional or non-unidirectional reinforcements such as mat, woven fabrics, woven rovings, chopped strands, combination and hybrid reinforcements, rovings and milled fibres and sheet made from pre-impregnated materials (prepregs); — thermotropic liquid-crystal polymers. 1.4 The method is not normally suitable for use with rigid cellular materials and sandwich structures containing cellular material. Notched specimens are also not normally used for long-fibre-reinforced composites or thermotropic liquid-crystal polymers. 1.5 The method is suited to the use of specimens which can be either moulded to the chosen dimensions, machined from the central portion of a standard multipurpose test specimen (see ISO 20753) or machined from finished or semi-finished products such as mouldings, laminates and extruded or cast sheet. 1.6 The method specifies preferred dimensions for the test specimen. Tests which are carried out on specimens of different dimensions or with different notches, or specimens which are prepared under different conditions, may produce results which are not comparable. Other factors, such as the energy capacity of the apparatus, its impact velocity and the conditioning of the specimens can also influence the results. Consequently, when comparative data are required, these factors are to be carefully controlled and recorded. 1.7 The method is not intended to be used as a source of data for design calculations. Information on the typical behaviour of a material can be obtained, however, by testing at different temperatures, by varying the notch radius and/or the thickness and by testing specimens prepared under different conditions.
Plastiques — Détermination de la résistance au choc Izod
1.1 Le présent document spécifié une méthode pour la détermination de la résistance au choc Izod des plastiques dans des conditions définies. De nombreux types de différentes éprouvettes et configurations d'essai sont définis. Divers paramètres d'essai sont spécifiés selon le type de matière, le type d'éprouvette et le type d'entaille. 1.2 La présente méthode est utilisée pour l'étude du comportement d'éprouvettes définies soumises à des conditions de choc déterminées et pour l'estimation de la fragilité ou de la ténacité des éprouvettes dans les limites inhérentes aux conditions d'essai. 1.3 La présente méthode est applicable à la gamme des matériaux suivants: — matières thermoplastiques rigides pour moulage et extrusion, y compris les compositions chargées et renforcées en plus des types non chargés; feuilles thermoplastiques rigides; — matières thermodurcissables rigides pour moulage, y compris les compositions chargées et renforcées; feuilles thermodurcissables rigides, y compris les stratifiés; — composites thermoplastiques et thermodurcissables renforcés de fibres comportant des renforts unidirectionnels ou multidirectionnels tels que mat, tissus, tissus stratifils, fils de base coupés, combinaison de renforcements et hybrides, stratifils et fibres broyées, feuilles réalisées à partir de matières préimprégnées (prepregs); — polymères de cristaux liquides thermotropes. 1.4 La présente méthode ne convient normalement pas à l'utilisation de matériaux alvéolaires rigides et de structures sandwichs contenant des matériaux alvéolaires. De même, les éprouvettes entaillées ne sont normalement pas utilisées pour les composites renforcés de longues fibres ou pour des polymères de cristaux liquides thermotropes. 1.5 La présente méthode est adaptée à l'utilisation d'éprouvettes qui sont moulées aux dimensions choisies, usinées à partir de la partie centrale de l'éprouvette normalisée à usages multiples (voir l'ISO 20753) ou encore usinées à partir de produits finis et semi-finis, tels que pièces moulées, stratifiées et feuilles extrudées ou coulées. 1.6 La présente méthode spécifie les dimensions préférentielles de l'éprouvette. Des essais réalisés avec des éprouvettes de dimensions et d'entailles différentes ou avec des éprouvettes préparées dans des conditions différentes, peuvent donner des résultats qui ne sont pas comparables. D'autres facteurs, tels que la capacité énergétique de l'appareillage, sa vitesse de percussion et le conditionnement des éprouvettes peuvent également avoir une répercussion sur les résultats. En conséquence, lorsque des résultats comparatifs sont nécessaires, ces facteurs devront être soigneusement contrôlés et enregistrés. 1.7 La présente méthode n'est pas destinée à être utilisée comme source de données pour les calculs relatifs à la conception. Cependant, des informations sur le comportement type de la matière peuvent être obtenues en effectuant l'essai à différentes températures, en faisant varier le rayon de l'entaille et/ou l'épaisseur, et en utilisant des éprouvettes préparées dans des conditions différentes.
General Information
Relations
Buy Standard
Standards Content (Sample)
INTERNATIONAL ISO
STANDARD 180
Fourth edition
2019-11
Plastics — Determination of Izod
impact strength
Plastiques — Détermination de la résistance au choc Izod
Reference number
ISO 180:2019(E)
©
ISO 2019
---------------------- Page: 1 ----------------------
ISO 180:2019(E)
COPYRIGHT PROTECTED DOCUMENT
© ISO 2019
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication may
be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting
on the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address
below or ISO’s member body in the country of the requester.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: +41 22 749 01 11
Fax: +41 22 749 09 47
Email: copyright@iso.org
Website: www.iso.org
Published in Switzerland
ii © ISO 2019 – All rights reserved
---------------------- Page: 2 ----------------------
ISO 180:2019(E)
Contents Page
Foreword .iv
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 2
4 Principle . 3
5 Apparatus . 3
5.1 Test machine . 3
5.2 Micrometers and gauges . 3
6 Test specimens. 3
6.1 Preparation . 3
6.1.1 Moulding and extrusion compounds . 3
6.1.2 Sheets . . . 6
6.1.3 Long-fibre-reinforced materials . 6
6.1.4 Checking . 6
6.1.5 Notching . 6
6.2 Anisotropy . 6
6.3 Shape and dimensions . 6
6.3.1 General. 6
6.3.2 Moulding and extrusion compounds . 7
6.3.3 Sheet materials, including long-fibre-reinforced materials . 7
6.4 Number of test specimens . 7
6.5 Conditioning . 7
7 Procedure. 7
8 Calculation and expression of results . 8
8.1 Unnotched specimens . 8
8.2 Notched specimens . 9
8.3 Statistical parameters . 9
8.4 Significant figures . 9
9 Precision . 9
10 Test report . 9
Annex A (informative) Precision statement .11
Bibliography .13
© ISO 2019 – All rights reserved iii
---------------------- Page: 3 ----------------------
ISO 180:2019(E)
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out
through ISO technical committees. Each member body interested in a subject for which a technical
committee has been established has the right to be represented on that committee. International
organizations, governmental and non-governmental, in liaison with ISO, also take part in the work.
ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of
electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are
described in the ISO/IEC Directives, Part 1. In particular, the different approval criteria needed for the
different types of ISO documents should be noted. This document was drafted in accordance with the
editorial rules of the ISO/IEC Directives, Part 2 (see www .iso .org/ directives).
Attention is drawn to the possibility that some of the elements of this document may be the subject of
patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of
any patent rights identified during the development of the document will be in the Introduction and/or
on the ISO list of patent declarations received (see www .iso .org/ patents).
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation of the voluntary nature of standards, the meaning of ISO specific terms and
expressions related to conformity assessment, as well as information about ISO's adherence to the
World Trade Organization (WTO) principles in the Technical Barriers to Trade (TBT), see www .iso .org/
iso/ foreword .html.
This document was prepared by Technical Committee ISO/TC 61, Plastics, Subcommittee SC 2,
Mechanical properties.
This fourth edition cancels and replaces the third edition (ISO 180:2000), of which it constitutes a minor
revision. It also incorporates the Amendments ISO 180:2000/Amd.1:2006 and ISO 180:2000/Amd.2:2013.
The changes compared to the previous edition are as follows:
— Clause 2 has been updated;
— the following clauses have been revised:
— Clause 5;
— Clause 6;
— Clause 7;
— Clause 8;
— Clause 9;
— a bibliography has been added.
Any feedback or questions on this document should be directed to the user’s national standards body. A
complete listing of these bodies can be found at www .iso .org/ members .html.
iv © ISO 2019 – All rights reserved
---------------------- Page: 4 ----------------------
INTERNATIONAL STANDARD ISO 180:2019(E)
Plastics — Determination of Izod impact strength
1 Scope
1.1 This document specifies a method for determining the Izod impact strength of plastics under defined
conditions. A number of different types of specimen and test configurations are defined. Different test
parameters are specified according to the type of material, the type of test specimen and the type of notch.
1.2 The method is used to investigate the behaviour of specified types of specimen under the impact
conditions defined and for estimating the brittleness or toughness of specimens within the limitations
inherent in the test conditions.
1.3 The method is suitable for use with the following range of materials:
— rigid thermoplastic moulding and extrusion materials, including filled and reinforced compounds
in addition to unfilled types; rigid thermoplastics sheets;
— rigid thermosetting moulding materials, including filled and reinforced compounds; rigid
thermosetting sheets, including laminates;
— fibre-reinforced thermosetting and thermoplastic composites incorporating unidirectional or
non-unidirectional reinforcements such as mat, woven fabrics, woven rovings, chopped strands,
combination and hybrid reinforcements, rovings and milled fibres and sheet made from pre-
impregnated materials (prepregs);
— thermotropic liquid-crystal polymers.
1.4 The method is not normally suitable for use with rigid cellular materials and sandwich structures
containing cellular material. Notched specimens are also not normally used for long-fibre-reinforced
composites or thermotropic liquid-crystal polymers.
1.5 The method is suited to the use of specimens which can be either moulded to the chosen dimensions,
machined from the central portion of a standard multipurpose test specimen (see ISO 20753) or machined
from finished or semi-finished products such as mouldings, laminates and extruded or cast sheet.
1.6 The method specifies preferred dimensions for the test specimen. Tests which are carried out on
specimens of different dimensions or with different notches, or specimens which are prepared under
different conditions, may produce results which are not comparable. Other factors, such as the energy
capacity of the apparatus, its impact velocity and the conditioning of the specimens can also influence the
results. Consequently, when comparative data are required, these factors are to be carefully controlled
and recorded.
1.7 The method is not intended to be used as a source of data for design calculations. Information
on the typical behaviour of a material can be obtained, however, by testing at different temperatures,
by varying the notch radius and/or the thickness and by testing specimens prepared under different
conditions.
2 Normative references
The following documents are referred to in the text in such a way that some or all of their content
constitutes requirements of this document. For dated references, only the edition cited applies. For
undated references, the latest edition of the referenced document (including any amendments) applies.
© ISO 2019 – All rights reserved 1
---------------------- Page: 5 ----------------------
ISO 180:2019(E)
ISO 291, Plastics — Standard atmospheres for conditioning and testing
ISO 293, Plastics — Compression moulding of test specimens of thermoplastic materials
ISO 294-1, Plastics — Injection moulding of test specimens of thermoplastic materials — Part 1: General
principles, and moulding of multipurpose and bar test specimens
ISO 295, Plastics — Compression moulding of test specimens of thermosetting materials
ISO 1268 (all parts), Fibre-reinforced plastics — Methods of producing test plates.
ISO 2602, Statistical interpretation of test results — Estimation of the mean — Confidence interval
ISO 2818, Plastics — Preparation of test specimens by machining
ISO 10724-1, Plastics — Injection moulding of test specimens of thermosetting powder moulding compounds
(PMCs) — Part 1: General principles and moulding of multipurpose test specimens
ISO 13802, Plastics — Verification of pendulum impact-testing machines — Charpy, Izod and tensile
impact-testing
ISO 20753, Plastics — Test specimens
3 Terms and definitions
For the purposes of this document, the following terms and definitions apply.
ISO and IEC maintain terminological databases for use in standardization at the following addresses:
— ISO Online browsing platform: available at https:// www .iso .org/ obp
— IEC Electropedia: available at http:// www .electropedia .org/
3.1
Izod unnotched impact strength
a
iU
impact energy absorbed in breaking an unnotched specimen, referred to the original cross-sectional
area of the specimen
2
Note 1 to entry: It is expressed in kilojoules per square metre (kJ/m ).
3.2
Izod notched impact strength
a
iN
impact energy absorbed in breaking a notched specimen, referred to the original cross-sectional area
of the specimen at the notch, with the pendulum striking the face containing the notch
2
Note 1 to entry: It is expressed in kilojoules per square metre (kJ/m ).
3.3
parallel impact
p
impact with the direction of blow parallel to the plane of reinforcement
Note 1 to entry: The direction of the blow in the Izod test is usually “edgewise parallel” (ep) (see Figure 1).
2 © ISO 2019 – All rights reserved
---------------------- Page: 6 ----------------------
ISO 180:2019(E)
3.4
normal impact
n
impact with the direction of blow normal to the plane of reinforcement
Note 1 to entry: This kind of impact is not usually used with the Izod test, but is indicated for the sake of
completion (see also Figure 1).
4 Principle
The test specimen, supported as a vertical cantilever beam, is broken by a single impact of a striker,
with the line of impact a fixed distance from the specimen clamp and, in the case of notched specimens,
from the centreline of the notch (see Figure 2).
5 Apparatus
5.1 Test machine
5.1.1 The principles, characteristics and verification of suitable test machines are detailed in
ISO 13802. ISO 13802 describes partial verification and full verification. In the case of full verification,
some items are difficult to verify when the apparatus is assembled. Such verifications are assumed to be
incumbent on the manufacturer.
5.1.2 Some plastics are sensitive to clamping pressure. When testing such materials, a means of
standardizing the clamping force shall be used and the clamping force shall be recorded in the test report.
The clamping force can be controlled by using a calibrated torque wrench or a pneumatic or hydraulic
device on the vice clamping screw.
5.2 Micrometers and gauges
Micrometers and gauges capable of measuring the essential dimensions of test specimens to an accuracy
of 0,02 mm are required. For measuring the dimension b of notched specimens, the micrometer shall
N
be fitted with an anvil of width 2 mm to 3 mm and of suitable
...
NORME ISO
INTERNATIONALE 180
Quatrième édition
2019-11
Plastiques — Détermination de la
résistance au choc Izod
Plastics — Determination of Izod impact strength
Numéro de référence
ISO 180:2019(F)
©
ISO 2019
---------------------- Page: 1 ----------------------
ISO 180:2019(F)
DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2019
Tous droits réservés. Sauf prescription différente ou nécessité dans le contexte de sa mise en œuvre, aucune partie de cette
publication ne peut être reproduite ni utilisée sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique,
y compris la photocopie, ou la diffusion sur l’internet ou sur un intranet, sans autorisation écrite préalable. Une autorisation peut
être demandée à l’ISO à l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.
ISO copyright office
Case postale 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Genève
Tél.: +41 22 749 01 11
Fax: +41 22 749 09 47
E-mail: copyright@iso.org
Web: www.iso.org
Publié en Suisse
ii © ISO 2019 – Tous droits réservés
---------------------- Page: 2 ----------------------
ISO 180:2019(F)
Sommaire Page
Avant-propos .iv
1 Domaine d’application . 1
2 Références normatives . 2
3 Termes et définitions . 2
4 Principe . 3
5 Appareillage . 3
5.1 Machine d’essai . 3
5.2 Micromètres et comparateurs . 3
6 Éprouvettes . 3
6.1 Préparation . 3
6.1.1 Compositions pour moulage et extrusion . 3
6.1.2 Feuilles . 7
6.1.3 Matériaux renforcés par de longues fibres. 7
6.1.4 Contrôle . 7
6.1.5 Préparation de l’entaille . 7
6.2 Anisotropie . 7
6.3 Formes et dimensions . 7
6.3.1 Généralités . 7
6.3.2 Compositions pour moulage et extrusion . 8
6.3.3 Matériaux sous forme de feuille, y compris les matériaux renforcés par de
longues fibres. 8
6.4 Nombre d’éprouvettes . 8
6.5 Conditionnement . 8
7 Mode opératoire. 9
8 Calcul et expression des résultats .10
8.1 Éprouvettes non entaillées .10
8.2 Éprouvettes entaillées .10
8.3 Paramètres statistiques .10
8.4 Chiffres significatifs .10
9 Fidélité .10
10 Rapport d’essai .10
Annexe A (informative) Données de fidélité .13
Bibliographie .15
© ISO 2019 – Tous droits réservés iii
---------------------- Page: 3 ----------------------
ISO 180:2019(F)
Avant-propos
L'ISO (Organisation internationale de normalisation) est une fédération mondiale d'organismes
nationaux de normalisation (comités membres de l'ISO). L'élaboration des Normes internationales est
en général confiée aux comités techniques de l'ISO. Chaque comité membre intéressé par une étude
a le droit de faire partie du comité technique créé à cet effet. Les organisations internationales,
gouvernementales et non gouvernementales, en liaison avec l'ISO participent également aux travaux.
L'ISO collabore étroitement avec la Commission électrotechnique internationale (IEC) en ce qui
concerne la normalisation électrotechnique.
Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont
décrites dans les Directives ISO/IEC, Partie 1. Il convient, en particulier de prendre note des différents
critères d'approbation requis pour les différents types de documents ISO. Le présent document a été
rédigé conformément aux règles de rédaction données dans les Directives ISO/IEC, Partie 2 (voir www
.iso .org/ directives).
L'attention est attirée sur le fait que certains des éléments du présent document peuvent faire l'objet de
droits de propriété intellectuelle ou de droits analogues. L'ISO ne saurait être tenue pour responsable
de ne pas avoir identifié de tels droits de propriété et averti de leur existence. Les détails concernant
les références aux droits de propriété intellectuelle ou autres droits analogues identifiés lors de
l'élaboration du document sont indiqués dans l'Introduction et/ou dans la liste des déclarations de
brevets reçues par l'ISO (voir www .iso .org/ brevets).
Les appellations commerciales éventuellement mentionnées dans le présent document sont données
pour information, par souci de commodité, à l’intention des utilisateurs et ne sauraient constituer un
engagement.
Pour une explication de la nature volontaire des normes, la signification des termes et expressions
spécifiques de l'ISO liés à l'évaluation de la conformité, ou pour toute information au sujet de l'adhésion
de l'ISO aux principes de l’Organisation mondiale du commerce (OMC) concernant les obstacles
techniques au commerce (OTC), voir le lien suivant: www .iso .org/ iso/ fr/ avant -propos.
Le présent document a été élaboré par le comité technique ISO/TC 61, Plastiques, sous-comité SC 2,
Comportement mécanique.
Cette quatrième édition annule et remplace la troisième édition (ISO 180:2000), qui a fait l’objet
d’une révision mineure. Elle incorpore également les Amendements ISO 180:2000/Amd.1:2006 et
ISO 180:2000/Amd.2:2013.
Les modifications par rapport à l’édition précédente sont les suivantes:
— l’Article 2 a été mis à jour;
— les articles suivants ont été révisés:
— Article 5;
— Article 6;
— Article 7;
— Article 8;
— Article 9;
— une Bibliographie a été ajoutée.
Il convient que l’utilisateur adresse tout retour d’information ou toute question concernant le présent
document à l’organisme national de normalisation de son pays. Une liste exhaustive desdits organismes
se trouve à l’adresse www .iso .org/ fr/ members .html.
iv © ISO 2019 – Tous droits réservés
---------------------- Page: 4 ----------------------
NORME INTERNATIONALE ISO 180:2019(F)
Plastiques — Détermination de la résistance au choc Izod
1 Domaine d’application
1.1 Le présent document spécifié une méthode pour la détermination de la résistance au choc Izod des
plastiques dans des conditions définies. De nombreux types de différentes éprouvettes et configurations
d'essai sont définis. Divers paramètres d'essai sont spécifiés selon le type de matière, le type d'éprouvette
et le type d'entaille.
1.2 La présente méthode est utilisée pour l'étude du comportement d'éprouvettes définies soumises à
des conditions de choc déterminées et pour l'estimation de la fragilité ou de la ténacité des éprouvettes
dans les limites inhérentes aux conditions d'essai.
1.3 La présente méthode est applicable à la gamme des matériaux suivants:
— matières thermoplastiques rigides pour moulage et extrusion, y compris les compositions chargées
et renforcées en plus des types non chargés; feuilles thermoplastiques rigides;
— matières thermodurcissables rigides pour moulage, y compris les compositions chargées et
renforcées; feuilles thermodurcissables rigides, y compris les stratifiés;
— composites thermoplastiques et thermodurcissables renforcés de fibres comportant des renforts
unidirectionnels ou multidirectionnels tels que mat, tissus, tissus stratifils, fils de base coupés,
combinaison de renforcements et hybrides, stratifils et fibres broyées, feuilles réalisées à partir de
matières préimprégnées (prepregs);
— polymères de cristaux liquides thermotropes.
1.4 La présente méthode ne convient normalement pas à l'utilisation de matériaux alvéolaires rigides
et de structures sandwichs contenant des matériaux alvéolaires. De même, les éprouvettes entaillées ne
sont normalement pas utilisées pour les composites renforcés de longues fibres ou pour des polymères
de cristaux liquides thermotropes.
1.5 La présente méthode est adaptée à l'utilisation d'éprouvettes qui sont moulées aux dimensions
choisies, usinées à partir de la partie centrale de l'éprouvette normalisée à usages multiples (voir
l’ISO 20753) ou encore usinées à partir de produits finis et semi-finis, tels que pièces moulées, stratifiées
et feuilles extrudées ou coulées.
1.6 La présente méthode spécifie les dimensions préférentielles de l’éprouvette. Des essais réalisés
avec des éprouvettes de dimensions et d'entailles différentes ou avec des éprouvettes préparées dans
des conditions différentes, peuvent donner des résultats qui ne sont pas comparables. D'autres facteurs,
tels que la capacité énergétique de l'appareillage, sa vitesse de percussion et le conditionnement des
éprouvettes peuvent également avoir une répercussion sur les résultats. En conséquence, lorsque des
résultats comparatifs sont nécessaires, ces facteurs devront être soigneusement contrôlés et enregistrés.
1.7 La présente méthode n’est pas destinée à être utilisée comme source de données pour les calculs
relatifs à la conception. Cependant, des informations sur le comportement type de la matière peuvent
être obtenues en effectuant l'essai à différentes températures, en faisant varier le rayon de l'entaille et/
ou l'épaisseur, et en utilisant des éprouvettes préparées dans des conditions différentes.
© ISO 2019 – Tous droits réservés 1
---------------------- Page: 5 ----------------------
ISO 180:2019(F)
2 Références normatives
Les documents suivants cités dans le texte constituent, pour tout ou partie de leur contenu, des
exigences du présent document. Pour les références datées, seule l’édition citée s’applique. Pour les
références non datées, la dernière édition du document de référence s’applique (y compris les éventuels
amendements).
ISO 291, Plastiques — Atmosphères normales de conditionnement et d'essai
ISO 293, Plastiques — Moulage par compression des éprouvettes en matières thermoplastiques
ISO 294-1, Plastiques — Moulage par injection des éprouvettes de matériaux thermoplastiques — Partie 1:
Principes généraux, et moulage des éprouvettes à usages multiples et des barreaux
ISO 295, Plastiques — Moulage par compression des éprouvettes de matériaux thermodurcissables
ISO 1268 (toutes les parties), Plastiques renforcés de fibres — Méthodes de fabrication de plaques d’essai
ISO 2602, Interprétation statistique de résultats d'essais — Estimation de la moyenne — Intervalle de
confiance
ISO 2818, Plastiques — Préparation des éprouvettes par usinage
ISO 10724-1, Plastiques — Moulage par injection d'éprouvettes en compositions de poudre à mouler (PMC)
thermodurcissables — Partie 1: Principes généraux et moulage d'éprouvettes à usages multiples
ISO 13802, Plastiques — Vérification des machines d'essai de choc pendulaire — Essais de choc Charpy,
Izod et de choc-traction
ISO 20753, Plastiques — Éprouvettes
3 Termes et définitions
Pour les besoins du présent document, les termes et définitions suivants s’appliquent.
L’ISO et l’IEC tiennent à jour des bases de données terminologiques destinées à être utilisées en
normalisation, consultables aux adresses suivantes:
— ISO Online browsing platform: disponible à l’adresse https:// www .iso .org/ obp
— IEC Electropedia: disponible à l’adresse http:// www .electropedia .org/
3.1
résistance au choc Izod d'éprouvettes non entaillées
a
iU
énergie de choc absorbée par la rupture d'une éprouvette non entaillée rapportée à la section droite
initiale de l'éprouvette
2
Note 1 à l'article: Elle est exprimée en kilojoules par mètre carré (kJ/m ).
3.2
résistance au choc Izod d'éprouvettes entaillées
a
iN
énergie de choc absorbée par la rupture d'une éprouvette entaillée rapportée à la section droite initiale
de l'éprouvette, le pendule percutant la face contenant l'entaille
2
Note 1 à l'article: Elle est exprimée en kilojoules par mètre carré (kJ/m ).
2 © ISO 2019 – Tous droits réservés
---------------------- Page: 6 ----------------------
ISO 180:2019(F)
3.3
choc parallèle
p
impact avec direction de la percussion parallèle au plan de
renforcement
Note 1 à l'article: Dans l'essai Izod, la direction de la percussion est normalement «position debout parallèle» (ep)
(voir Figure 1).
3.4
choc normal
n
impact avec direction de la percussion perpendiculaire au plan
de renforcement
Note 1 à l'article: Ce type de choc n'est normalement pas utilisé pour l'essai Izod mais il est indiqué dans un but de
clarification (voir aussi Figure 1).
4 Principe
L'éprouvette, supportée comme une poutre en console verticale, est rompue par un seul choc de
percuteur, la ligne de choc étant située à distance fixe du serrage de l'éprouvette, et en cas d'éprouvette
entaillée, de l'axe de l'entaille (voir Figure 2).
5 Appareillage
5.1 Machine d’essai
5.1.1 Les dispositions relatives aux principes, aux caractéristiques et à la vérification des machines
d’essai appropriées sont détaillées dans l’ISO 13802. L’ISO 13802 décrit la vérification partielle et la
vérification complète. Dans le cas d’une vérification complète, certains éléments sont difficiles à vérifier
une fois que l’appareil est assemblé. On considère que ces vérifications incombent au fabricant.
5.1.2 Certains plastiques sont sensibles à la pression de serrage. Lors de l'essai de ces matières, un
dispositif d’étalonnage de la force de serrage doit être utilisé et cette dernière doit être notée dans le
rapport d'essai. Le contrôle de la force de serrage peut s’effectuer au moyen d'une clé dynamométrique
étalonnée ou d'un appareil pneumatique ou hydraulique monté sur la vis du dispositif de serrage.
5.2 Micromètres et comparateurs
Les micromètres et comparateurs doivent pouvoir mesurer les principales dimensions des éprouvettes
avec une exactitude de 0,02 mm. Pour mesurer la dimension b d'une éprouvette entaillée, le micromètre
N
doit être équipé d'une enclume ayant une largeur de 2 mm à 3 mm et un profil convenable pour épouser
la forme de l'entaille.
6 Éprouvettes
6.1 Préparation
6.1.1 Compositions pour moulage et extrusion
Les éprouvettes doivent être préparées conformément à la spécification relative au matériau concerné.
En l'absence de spécification, ou sauf indication contraire, les éprouvettes doivent être soit directement
moulées par compression ou injection à partir de la matière conformément à l’ISO 293, l'ISO 294-1,
l'ISO 295 ou l'ISO 10724-1, selon le cas, soit usinées conformément à l'ISO 2818 à partir d’une feuille
© ISO 2019 – Tous droits réservés 3
---------------------- Page: 7 ----------------------
I
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.