Rubber, vulcanized or thermoplastic — Determination of compression set — Part 1: At ambient or elevated temperatures

This document specifies methods for the determination of the compression set characteristics of vulcanized and thermoplastic rubbers at ambient (one method) or elevated temperatures (three methods, A, B, and C, depending on the way the test piece is released at the end of the test). The methods are intended to measure the ability of rubbers of hardness within the range 10 IRHD to 95 IRHD to retain their elastic properties at specified temperatures after prolonged compression at constant strain (normally 25 %) under one of the alternative sets of conditions described. For rubber of nominal hardness 80 IRHD and above, a lower compression strain is used: 15 % for a nominal hardness from 80 IRHD to 89 IRHD and 10 % for a nominal hardness from 90 IRHD to 95 IRHD. NOTE 1 When rubber is held under compression, physical or chemical changes that prevent the rubber returning to its original dimensions after release of the deforming force can occur. The result is a set, the magnitude of which depends on the time and temperature of compression as well as on the time, temperature, and conditions of recovery. At elevated temperatures, chemical changes become increasingly more important and lead to a permanent set. NOTE 2 Short-time compression set tests, typically for 24 h, at elevated temperatures are commonly used as a measure of the state of cure, a means of material classification, and a specification to ensure the quality of a compound. Longer tests, typically for 1 000 h, at elevated temperatures take account of the effect of ageing and are often used to predict service performance, including that of sealing materials. Short-time tests at ambient temperature show mainly the effect of physical changes (re-orientation of the molecular chains and the fillers).

Caoutchouc vulcanisé ou thermoplastique — Détermination de la déformation rémanente après compression — Partie 1: À températures ambiantes ou élevées

Le présent document spécifie des méthodes pour la détermination des caractéristiques de déformation rémanente après compression des caoutchoucs vulcanisés et thermoplastiques à températures ambiantes (une méthode) ou élevées (trois méthodes, A, B, et C, en fonction de la manière dont l'éprouvette est libérée à la fin de l'essai). Les méthodes sont destinées à mesurer l'aptitude des caoutchoucs de dureté comprise entre 10 DIDC et 95 DIDC, à conserver leurs propriétés élastiques à des températures spécifiées après compression prolongée à déformation constante (normalement 25 %) dans l'un des deux jeux de conditions d'essai décrits. Pour les caoutchoucs ayant une dureté égale ou supérieure à 80 DIDC, un taux de compression plus faible est utilisé: 15 % lorsque la dureté nominale est comprise entre 80 DIDC et 89 DIDC et 10 % lorsque la dureté nominale est comprise entre 90 DIDC et 95 DIDC. NOTE 1 Lorsqu'un caoutchouc est maintenu sous compression, des changements physiques ou chimiques peuvent se produire qui font que le caoutchouc, une fois relâché, ne recouvrera pas ses dimensions initiales. Il en résulte une déformation rémanente dont l'importance dépend à la fois de la durée et de la température de la compression et de la durée, de la température et des conditions de reprise élastique. A températures élevées, les changements chimiques deviennent de plus en plus importants et produisent une déformation permanente. NOTE 2 Des essais de déformation rémanente après compression de courte durée, habituellement 24 h, à températures élevées, sont couramment utilisés comme une mesure du degré de vulcanisation, c'est-à-dire comme un moyen de classification des matériaux et une spécification pour assurer la qualité d'un mélange. Des essais de plus longue durée, habituellement 1 000 h, à températures élevées, tiennent compte de l'effet de vieillissement et sont souvent utilisés pour prévoir les performances fonctionnelles, y compris celles des matériaux d'étanchéité. Des essais de courte durée, à température ambiante, montrent principalement l'effet des changements physiques (réorientation des chaînes moléculaires et des charges).

General Information

Status
Published
Publication Date
25-Nov-2019
Current Stage
9020 - International Standard under periodical review
Start Date
15-Jan-2024
Completion Date
15-Jan-2024
Ref Project

Relations

Buy Standard

Standard
ISO 815-1:2019 - Rubber, vulcanized or thermoplastic -- Determination of compression set
English language
14 pages
sale 15% off
Preview
sale 15% off
Preview
Standard
REDLINE ISO 815-1:2019 - Rubber, vulcanized or thermoplastic — Determination of compression set — Part 1: At ambient or elevated temperatures Released:11/26/2019
English language
14 pages
sale 15% off
Preview
sale 15% off
Preview
Standard
ISO 815-1:2019 - Caoutchouc vulcanisé ou thermoplastique -- Détermination de la déformation rémanente apres compression
French language
16 pages
sale 15% off
Preview
sale 15% off
Preview
Standard
REDLINE ISO 815-1:2019 - Rubber, vulcanized or thermoplastic — Determination of compression set — Part 1: At ambient or elevated temperatures Released:11/26/2019
French language
16 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (Sample)

INTERNATIONAL ISO
STANDARD 815-1
Third edition
2019-11
Rubber, vulcanized or
thermoplastic — Determination of
compression set —
Part 1:
At ambient or elevated temperatures
Caoutchouc vulcanisé ou thermoplastique — Détermination de la
déformation rémanente après compression —
Partie 1: À températures ambiantes ou élevées
Reference number
ISO 815-1:2019(E)
©
ISO 2019

---------------------- Page: 1 ----------------------
ISO 815-1:2019(E)

COPYRIGHT PROTECTED DOCUMENT
© ISO 2019
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication may
be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting
on the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address
below or ISO’s member body in the country of the requester.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: +41 22 749 01 11
Fax: +41 22 749 09 47
Email: copyright@iso.org
Website: www.iso.org
Published in Switzerland
ii © ISO 2019 – All rights reserved

---------------------- Page: 2 ----------------------
ISO 815-1:2019(E)

Contents Page
Foreword .iv
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 2
4 Principle . 2
5 Apparatus . 2
6 Calibration . 4
7 Test pieces . 4
7.1 Dimensions . 4
7.2 Preparation . 5
7.3 Number of test pieces . 5
7.4 Time interval between production and testing . 5
7.5 Conditioning . 5
8 Test conditions . 6
8.1 Duration of test . 6
8.2 Temperature of test . 6
9 Procedure. 6
9.1 Preparation of compression assembly .
...

ISO 815-1:2019(E) Style Definition: Footnote Text
Style Definition: Footnote
2019‐11
Reference
ISO TC 45/SC 2/WG 2
Secretariat: JISC
Rubber, vulcanized or thermoplastic — Determination of compression set — Part 1: At ambient
or elevated temperatures Formatted: Font: Not Bold

Caoutchouc vulcanisé ou thermoplastique — Détermination de la déformation
rémanente après compression — Partie 1: A températures ambiantes ou élevées
Formatted: Tab stops: 109.55 pt,
Left + Not at 487.6 pt

---------------------- Page: 1 ----------------------
ISO 815-1:2019(E)
Deleted: /FDIS
Contents Page
Foreword . iii  Deleted: Foreword iii¶
1 Scope 1¶
2 Normative references 1¶
1  Scope . 1
3 Terms and definitions 2¶
4 Principle 2¶
2  Normative references . 1
5 Apparatus 2¶
3  Terms and definitions . 2  6 Calibration 4¶
7 Test pieces 4¶
4  Principle . 2
7.1 Dimensions 4¶
7.2 Preparation 5¶
5  Apparatus . 2
7.3 Number of test pieces 5¶
7.4 Time interval between
6  Calibration . 4
production and testing 5¶
7.5 Conditioning 5¶
7  Test pieces. 4
8 Test conditions 6¶
7.1  Dimensions . 4
8.1 Duration of test 6¶
7.2  Preparation . 5
8.2 Temperature of test 6¶
7.3  Number of test pieces. 5
9 Procedure 6¶
7.4  Time interval between production and testing . 5
9.1 Preparation of
compression assembly 6¶
7.5  Conditioning . 5
9.2 Thickness
8  Test conditions . 6  measurement 6¶
9.3 Applying the
8.1  Duration of test . 6
compression 6¶
8.2  Temperature of test . 6
9.4 Starting the test 6¶
9.5 Terminating the test 7¶
9  Procedure . 6
9.5.1 At ambient
9.1  Preparation of compression assembly . 6
temperature 7¶
9.2  Thickness measurement . 6
9.5.2 At elevated
9.3  Applying the compression . 6
temperature 7¶
9.6 Internal examination 7¶
9.4  Starting the test . 6
10 Expression of results 7¶
9.5  Terminating the test . 7
11 Precision 8¶
9.5.1  At ambient temperature .
...

NORME ISO
INTERNATIONALE 815-1
Troisième édition
2019-11
Caoutchouc vulcanisé ou
thermoplastique — Détermination
de la déformation rémanente après
compression —
Partie 1:
À températures ambiantes ou élevées
Rubber, vulcanized or thermoplastic — Determination of
compression set —
Part 1: At ambient or elevated temperatures
Numéro de référence
ISO 815-1:2019(F)
©
ISO 2019

---------------------- Page: 1 ----------------------
ISO 815-1:2019(F)

DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2019
Tous droits réservés. Sauf prescription différente ou nécessité dans le contexte de sa mise en œuvre, aucune partie de cette
publication ne peut être reproduite ni utilisée sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique,
y compris la photocopie, ou la diffusion sur l’internet ou sur un intranet, sans autorisation écrite préalable. Une autorisation peut
être demandée à l’ISO à l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.
ISO copyright office
Case postale 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Genève
Tél.: +41 22 749 01 11
Fax: +41 22 749 09 47
E-mail: copyright@iso.org
Web: www.iso.org
Publié en Suisse
ii © ISO 2019 – Tous droits réservés

---------------------- Page: 2 ----------------------
ISO 815-1:2019(F)

Sommaire Page
Avant-propos .iv
1 Domaine d'application . 1
2 Références normatives . 1
3 Termes et définitions . 2
4 Principe . 2
5 Appareillage . 2
6 Étalonnage . 4
7 Éprouvettes . 4
7.1 Dimensions . 4
7.2 Préparation . 5
7.3 Nombre d'éprouvettes . 5
7.4 Délai entre la production et l'essai . 5
7.5 Conditionnement . 5
8 Conditions d'essai . 6
8.1 Durée de l'essai . 6
8.2 Température d'essai . 6
9 Mode opératoire. 6
9.1 Préparation de l'appareil de compression .
...

© ISO 2019 – Tous droits réservés
Deleted: © ISO 2019 – Tous droits
réservés
ISO/TC 45/SC 2
Date:  2019-08-13
Deleted: /FDIS
ISO 815-1:2019(F)
ISO/TC 45/SC 2/GT
Secrétariat:  JISC
Caoutchouc vulcanisé ou thermoplastique — Détermination de la déformation
rémanente après compression — Partie 1: A températures ambiantes ou élevées
Rubber, vulcanized or thermoplastic — Determination of compression set —
Part 1: At ambient and elevated temperatures
Deleted: Norme internationale
Deleted: (50) Approbation
Deleted: F
Deleted: STD Version 2.9a¶
Type du document: Norme internationale
Sous‐type du document:
Stade du document: (50) Approbation
Langue du document: F

STD Version 2.9a

---------------------- Page: 1 ----------------------
ISO 815-1:2019(F)
Deleted: ISO/FDIS 815-1:2019(F)
Formatted
DOCUMENT PROTÉGÉ PAR COPYRIGHT
Droits de reproduction réservés. Sauf indication contraire, aucune partie de cette publication ne
peut être reproduite ni utilisée sous quelque forme que ce soit et par aucun procédé, électronique
ou mécanique, y compris la photocopie, l’affichage sur l’internet ou sur un Intranet, sans
autorisation écrite préalable. Les demandes d’autorisation peuvent être adressées à l’ISO à
l’adresse ci‐après ou au comité membre de l’ISO dans le pays du demandeur.
ISO copyright office
Ch. de Blandonnet 8 • CP 401
CH‐1214 Vernier, Geneva, Switzerland
Tel. + 41 22 749 01 11
Fax + 41 22 749 09 47
copyright@iso.org
www.iso.org
Deleted: iv
Deleted: © ISO 2019 – Tous droits réservés
© ISO 2019 – Tous droits réservés
ii

---------------------- Page: 2 ----------------------
ISO 815-1:2019(F)
Deleted: ISO/FDIS 815-1:2019(F)
Sommaire Page
Avant-propos . iv
Deleted: Avant-propos iv¶
1 Domaine d'application 1¶
1  Domaine d'application . 1
2 Références normatives 2¶
3 Termes et définitions 2¶
2  Références normatives . 1
4 Principe 2¶
5 Appareillage 2¶
3  Termes et définitions . 2
6 Etalonnage 4¶
4  Principe . 2
7 Eprouvettes 4¶
7.1 Dimensions 4¶
5  Appareillage . 2
7.2 Préparation 5¶
7.3 Nombre
6  Étalonnage . 4
d'éprouvettes 5¶
7.4 Délai entre la production
7  Éprouvettes . 4
et l'essai 5¶
8  Conditions d'essai . 6
7.5 Conditionnement 6¶
8 Conditions d'essai 6¶
9  Mode opératoire . 6
8.1 Durée de l'essai 6¶
8.2 Température d'essai 6¶
10  Expression des résultats . 8
9 Mode opératoire 6¶
11  Fidélité . 8  9.1 Préparation de l'appareil
de compression 6¶
12  Rapport d'essai . 8
9.2 Mesurage de
l'épaisseur 7¶
Annexe A (informative) Fidélité . 10
9.3 Application de la
compression 7¶
Annexe B (informative) Programme d'étalonnage . 14
9.4 Démarrage de l'essai 7¶
Bibliographie . 17  9.5 Achèvement de
l'essai 7¶
9.5.1 A température
ambiante 7¶
9.5.2 A température
élev
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.