ISO 10675-2:2010
(Main)Non-destructive testing of welds — Acceptance levels for radiographic testing — Part 2: Aluminium and its alloys
Non-destructive testing of welds — Acceptance levels for radiographic testing — Part 2: Aluminium and its alloys
ISO 10675:2010 specifies acceptance levels for indications from imperfections in aluminium butt welds detected by radiographic testing. If agreed, the acceptance levels may be applied to other types of welds or materials. The acceptance levels may be related to welding standards, application standards, specifications or codes. ISO 10675:2010 assumes that the radiographic testing has been carried out in accordance with ISO 17636. When assessing whether a weld meets the requirements specified for a weld quality level, the sizes of imperfections permitted by standards are compared with the dimensions of indications revealed by a radiograph made of the weld.
Essais non destructifs des assemblages soudés — Niveaux d'acceptation pour évaluation par radiographie — Partie 2: Aluminium et ses alliages
L'ISO 10675-2:2010 spécifie les niveaux d'acceptation des indications des défauts présents dans les assemblages soudés en aluminium et détectés par contrôle radiographique. En fonction des accords passés, les niveaux d'acceptation peuvent être appliqués à d'autres types d'assemblages soudés ou de matériaux. Les niveaux d'acceptation peuvent être reliés à des normes de soudage, des normes d'application, des spécifications ou des codes. L'ISO 10675-2:2010 présume que le contrôle par radiographie a été exécuté conformément à l'ISO 17636. Pour vérifier qu'une soudure satisfait aux exigences spécifiées pour un niveau de qualité de soudure, les dimensions des défauts permises par les normes sont comparées aux dimensions des indications révélées par la radiographie de la soudure.
General Information
Relations
Buy Standard
Standards Content (Sample)
INTERNATIONAL ISO
STANDARD 10675-2
First edition
2010-09-01
Non-destructive testing of welds —
Acceptance levels for radiographic
testing —
Part 2:
Aluminium and its alloys
Essais non destructifs des assemblages soudés — Niveaux
d'acceptation pour évaluation par radiographie —
Partie 2: Aluminium et ses alliages
Reference number
ISO 10675-2:2010(E)
©
ISO 2010
---------------------- Page: 1 ----------------------
ISO 10675-2:2010(E)
PDF disclaimer
This PDF file may contain embedded typefaces. In accordance with Adobe's licensing policy, this file may be printed or viewed but
shall not be edited unless the typefaces which are embedded are licensed to and installed on the computer performing the editing. In
downloading this file, parties accept therein the responsibility of not infringing Adobe's licensing policy. The ISO Central Secretariat
accepts no liability in this area.
Adobe is a trademark of Adobe Systems Incorporated.
Details of the software products used to create this PDF file can be found in the General Info relative to the file; the PDF-creation
parameters were optimized for printing. Every care has been taken to ensure that the file is suitable for use by ISO member bodies. In
the unlikely event that a problem relating to it is found, please inform the Central Secretariat at the address given below.
COPYRIGHT PROTECTED DOCUMENT
© ISO 2010
All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized in any form or by any means,
electronic or mechanical, including photocopying and microfilm, without permission in writing from either ISO at the address below or
ISO's member body in the country of the requester.
ISO copyright office
Case postale 56 CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax + 41 22 749 09 47
E-mail copyright@iso.org
Web www.iso.org
Published in Switzerland
ii © ISO 2010 – All rights reserved
---------------------- Page: 2 ----------------------
ISO 10675-2:2010(E)
Contents Page
Foreword.iv
1 Scope.1
2 Normative references.1
3 Radiographic technique.1
4 General.2
5 Acceptance levels.2
)
Annex A (informative) Guide to the limitations of radiographic testing .5
A.1 Volumetric imperfections in butt welds.5
A.2 Cracks in butt welds.5
A.3 Planar imperfections in butt welds .5
Annex B (informative) Examples for determination of percentage (%) of imperfections .6
Annex C (informative) Sum of acceptable areas.8
Bibliography .10
© ISO 2010 – All rights reserved iii
---------------------- Page: 3 ----------------------
ISO 10675-2:2010(E)
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies
(ISO member bodies). The work of preparing International Standards is normally carried out through ISO
technical committees. Each member body interested in a subject for which a technical committee has been
established has the right to be represented on that committee. International organizations, governmental and
non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the
International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization.
International Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part 2.
The main task of technical committees is to prepare International Standards. Draft International Standards
adopted by the technical committees are circulated to the member bodies for voting. Publication as an
International Standard requires approval by at least 75 % of the member bodies casting a vote.
Attention is drawn to the possibility that some of the elements of this document may be the subject of patent
rights. ISO shall not be held responsible for identifying any or all such patent rights.
ISO 10675-2 was prepared by the European Committee for Standardization (as EN 12517-2:2008) and was
adopted, under a special “fast-track procedure”, by Technical Committee ISO/TC 44, Welding and allied
processes, Subcommittee SC 5, Testing and inspection of welds, in parallel with its approval by the ISO
member bodies.
Request for official interpretations of any aspect of this part of ISO 10675 should be directed to the Secretariat
of ISO/TC 44/SC 5 via your national standards body. A complete listing of these bodies can be found at
www.iso.org.
iv © ISO 2010 – All rights reserved
---------------------- Page: 4 ----------------------
INTERNATIONAL STANDARD ISO 10675-2:2010(E)
Non-destructive testing of welds — Acceptance levels for
radiographic testing —
Part 2:
Aluminium and its alloys
1 Scope
This part of ISO 10675 specifies acceptance levels for indications from imperfections in aluminium butt
welds detected by radiographic testing. If agreed, the acceptance levels may be applied to other types of
welds or materials.
The acceptance levels may be related to welding standards, application standards, specifications or codes.
This part of ISO 10675 assumes that the radiographic testing has been carried out in accordance with
ISO 17636.
When assessing whether a weld meets the requirements specified for a weld quality level, the sizes of
imperfections permitted by standards are compared with the dimensions of indications revealed by a
radiograph made of the weld.
2 Normative references
The following referenced documents are indispensable for the application of this document. For dated
references, only the edition cited applies. For undated references, the latest edition of the referenced
document (including any amendments) applies.
ISO 6520-1, Welding and allied processes — Classification of geometric imperfections in metallic
materials — Part 1: Fusion welding
ISO 10042, Welding — Arc-welded joints in aluminium and its alloys — Quality levels for imperfections
ISO 17636, Non-destructive examination of welds — Radiographic examination of welded joints
3 Radiographic technique
Depending on the weld quality level, radiographic technique A or B in accordance with ISO 17636 shall be used
as shown in Table 1.
Table 1 — Radiographic testing
Quality levels in Testing techniques and Acceptance levels in
accordance with classes in accordance with accordance with
ISO 10042 ISO 17636 this part of ISO 10675
B B 1
a
C B 2
D A 3
a
However, the minimum number of exposure for circumferential weld testing may correspond to the
requirements of class A of ISO 17636.
© ISO 2010 – All rights reserved 1
---------------------- Page: 5 ----------------------
ISO 10675-2:2010(E)
4 General
Welded joints should be visually tested in accordance with ISO 17637 and evaluated before radiographic testing.
The acceptance levels in this part of ISO 10675 are basically valid for evaluation of imperfections which
cannot be detected and evaluated by visual testing (Table 2). Surface imperfections (Table 3; such as
undercut and excessive penetration, surface damage, weld spatter, etc.) which due to object geometry cannot
be evaluated, but where the interpreter suspects the ISO 10042 quality levels are not fulfilled, shall be
subject to more specific testing.
When quantification of undercut and/or excessive penetration by radiographic testing is required, specific
procedures using test exposures may be applied in o
...
NORME ISO
INTERNATIONALE 10675-2
Première édition
2010-09-01
Essais non destructifs des assemblages
soudés — Niveaux d'acceptation pour
évaluation par radiographie —
Partie 2:
Aluminium et ses alliages
Non-destructive testing of welds — Acceptance levels for radiographic
testing —
Part 2: Aluminium and its alloys
Numéro de référence
ISO 10675-2:2010(F)
©
ISO 2010
---------------------- Page: 1 ----------------------
ISO 10675-2:2010(F)
PDF – Exonération de responsabilité
Le présent fichier PDF peut contenir des polices de caractères intégrées. Conformément aux conditions de licence d'Adobe, ce fichier
peut être imprimé ou visualisé, mais ne doit pas être modifié à moins que l'ordinateur employé à cet effet ne bénéficie d'une licence
autorisant l'utilisation de ces polices et que celles-ci y soient installées. Lors du téléchargement de ce fichier, les parties concernées
acceptent de fait la responsabilité de ne pas enfreindre les conditions de licence d'Adobe. Le Secrétariat central de l'ISO décline toute
responsabilité en la matière.
Adobe est une marque déposée d'Adobe Systems Incorporated.
Les détails relatifs aux produits logiciels utilisés pour la création du présent fichier PDF sont disponibles dans la rubrique General Info
du fichier; les paramètres de création PDF ont été optimisés pour l'impression. Toutes les mesures ont été prises pour garantir
l'exploitation de ce fichier par les comités membres de l'ISO. Dans le cas peu probable où surviendrait un problème d'utilisation,
veuillez en informer le Secrétariat central à l'adresse donnée ci-dessous.
DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2010
Droits de reproduction réservés. Sauf prescription différente, aucune partie de cette publication ne peut être reproduite ni utilisée sous
quelque forme que ce soit et par aucun procédé, électronique ou mécanique, y compris la photocopie et les microfilms, sans l'accord écrit
de l'ISO à l'adresse ci-après ou du comité membre de l'ISO dans le pays du demandeur.
ISO copyright office
Case postale 56 • CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax + 41 22 749 09 47
E-mail copyright@iso.org
Web www.iso.org
Publié en Suisse
ii © ISO 2010– Tous droits réservés
---------------------- Page: 2 ----------------------
ISO 10675-2:2010(F)
Sommaire Page
Avant-propos .iv
1 Domaine d'application.1
2 Références normatives .1
3 Technique radiographique.1
4 Généralités .2
5 Niveaux d’acceptation.2
1)
Annexe A (informative) Guide pour les limitations du contrôle par radiographie .5
A.1 Défauts volumiques dans les soudures bout à bout .5
A.2 Fissures dans les assemblages bout à bout .5
A.3 Défauts plans dans les soudures bout à bout.5
Annexe B (informative) Exemples de détermination du pourcentage (%) de défauts .6
Annexe C (informative) Somme des surfaces acceptables . 8
Bibliographie.10
© ISO 2010 – Tous droits réservés iii
---------------------- Page: 3 ----------------------
ISO 10675-2:2010(F)
Avant-propos
L'ISO (Organisation internationale de normalisation) est une fédération mondiale d'organismes nationaux de
normalisation (comités membres de l'ISO). L'élaboration des Normes internationales est en général confiée
aux comités techniques de l'ISO. Chaque comité membre intéressé par une étude a le droit de faire partie du
comité technique créé à cet effet. Les organisations internationales, gouvernementales et non
gouvernementales, en liaison avec l'ISO participent également aux travaux. L'ISO collabore étroitement avec
la Commission électrotechnique internationale (CEI) en ce qui concerne la normalisation électrotechnique.
Les Normes internationales sont rédigées conformément aux règles données dans les Directives ISO/CEI,
Partie 2.
La tâche principale des comités techniques est d'élaborer les Normes internationales. Les projets de Normes
internationales adoptés par les comités techniques sont soumis aux comités membres pour vote. Leur
publication comme Normes internationales requiert l'approbation de 75 % au moins des comités membres
votants.
L'attention est appelée sur le fait que certains des éléments du présent document peuvent faire l'objet de
droits de propriété intellectuelle ou de droits analogues. L'ISO ne saurait être tenue pour responsable de ne
pas avoir identifié de tels droits de propriété et averti de leur existence.
L'ISO 10675-2 a été élaborée par le Comité européen de normalisation (CEN) (en tant que EN 12517-2:2010)
et adoptée, selon une procédure spéciale par «voie express», par le comité technique ISO/TC 44, Soudage et
techniques connexes, sous-comité SC 5, Essais et contrôle des soudures, parallèlement à son approbation
par les comités membres de l'ISO.
Il convient de faire parvenir les demandes d'interprétation officielles de l'un quelconque des aspects de la
présente partie de l'ISO 10675 au secrétariat de l'ISO/TC 44/SC 5 via votre organisme national de
normalisation. La liste exhaustive de ces organismes peut être trouvée à l'adresse www.iso.org.
iv © ISO 2010 – Tous droits réservés
---------------------- Page: 4 ----------------------
NORME INTERNATIONALE ISO 10675-2:2010(F)
Essais non destructifs des assemblages soudés — Niveaux
d'acceptation pour évaluation par radiographie —
Partie 2:
Aluminium et ses alliages
1 Domaine d'application
La présente partie de l'ISO 10675 spécifie les niveaux d'acceptation des indications des défauts présents dans
les assemblages soudés en aluminium et détectés par contrôle radiographique. En fonction des accords
passés, les niveaux d'acceptation peuvent être appliqués à d’autres types d'assemblages soudés ou de
matériaux.
Les niveaux d’acceptation peuvent être reliés à des normes de soudage, des normes d'application, des
spécifications ou des codes.
La présente partie de l'ISO 10675 présume que le contrôle par radiographie a été exécuté conformément à
l'ISO 17636.
Pour vérifier qu'une soudure satisfait aux exigences spécifiées pour un niveau de qualité de soudure, les
dimensions des défauts permises par les normes sont comparées aux dimensions des indications révélées
par la radiographie de la soudure.
2 Références normatives
Les documents de référence suivants sont indispensables pour l'application du présent document. Pour les
références datées, seule l'édition citée s'applique. Pour les références non datées, la dernière édition du
document de référence s'applique (y compris les éventuels amendements).
ISO 6520-1, Soudages et techniques connexes — Classification des défauts géométriques dans les
soudures des matériaux métalliques — Partie 1: Soudage par fusion
ISO 10042, Soudage — Assemblages en aluminium et alliages d'aluminium soudés à l'arc — Niveaux de
qualité par rapport aux défauts
ISO 17636, Contrôle non destructif des assemblages soudés — Contrôle par radiographie des assemblages
soudés par fusion
3 Technique radiographique
Selon le niveau de qualité de soudure, la technique radiographique A ou B conforme à l'ISO 17636 doit être
utilisée, comme indiqué au Tableau 1.
Tableau 1 — Essai par radiographie
Niveaux de qualité Techniques et niveaux Niveaux d’acceptation
conformément à d’examen conformément à conformément à la présente
l'ISO 10042 l'ISO 17636 partie de l'ISO 10675
B B 1
a
C B 2
D A 3
a
Cependant, le nombre minimal d’expositions peut, dans le cas du contrôle d’une soudure
circonférentielle, correspondre aux exigences du niveau d’examen A de l’ISO 17636.
© ISO 2010 – Tous droits réservés 1
---------------------- Page: 5 ----------------------
ISO 10675-2:2010(F)
4 Généralités
Il convient que les assemblages soudés soient contrôlés visuellement conformément à l’ISO 17637 et évalués
avant le contrôle par radiographie.
Les niveaux d’acceptation indiqués dans la présente partie de l'ISO 10675 sont fondamentalement valables
pour l’évaluation des défauts qui ne peuvent pas être détectés et évalués par un contrôle visuel (Tableau 2).
Les défauts de surface (Tableau 3 ; par exemple, les caniveaux et la pénétration excessive, les dégradations
de surface, les projections, etc.) qui, du fait de la géométrie de la pièce, ne peuvent pas être évalués mais
pour lesquels l’interprétateur suspecte le non-respect des niveaux de qualité de l’ISO 10042, doivent faire
l’objet d’un contrôle plus spécifique.
Dans le cas où la quantification des caniveaux et/ou des excès de pénétration par contrôle par radiographie
est exigée, des modes opératoires spécifiques faisant appel à d
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.