ASTM A967-05e1

NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information.
´1
Designation: A967 – 05
Standard Specification for
1
Chemical Passivation Treatments for Stainless Steel Parts
This standard is issued under the fixed designation A967; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the Department of Defense.
1
´ NOTE—Section 6.1.1.1 was editorially corrected in July 2007.
1. Scope* concerns, if any, associated with its use. It is the responsibility
of the user of this standard to establish appropriate safety and
1.1 This specification covers several different types of
health practices and determine the applicability of regulatory
chemical passivation treatments for stainless steel parts. It
limitations prior to use.
includes recommendations and precautions for descaling,
cleaning, and passivation of stainless steel parts. It includes
2. Referenced Documents
several alternative tests, with acceptance criteria, for confirma-
2
2.1 ASTM Standards:
tion of effectiveness of such treatments for stainless steel parts.
A380 Practice for Cleaning, Descaling, and Passivation of
1.2 Practices for the mechanical and chemical treatments of
Stainless Steel Parts, Equipment, and Systems
stainless steel surfaces are discussed more thoroughly in
B117 Practice for Operating Salt Spray (Fog) Apparatus
Practice A380.
B254 Practice for Preparation of and Electroplating on
1.3 Several alternative chemical treatments are defined for
Stainless Steel
passivation of stainless steel parts. Appendix X1 gives some
3
2.2 Federal Specification:
nonmandatory information and provides some general guide-
QQ-P-35C Passivation Treatments for Corrosion-Resistant
lines regarding the selection of passivation treatment appropri-
Steels
ate to particular grades of stainless steel. It makes no recom-
mendations regarding the suitability of any grade, treatment, or
3. Terminology
acceptance criteria for any particular application or class of
3.1 Definition of Term Specific to This Standard—It is
applications.
necessary to define which of the several commonly used
1.4 Thetestsinthisspecificationareintendedtoconfirmthe
definitions of the term passivation will be used in this
effectiveness of passivation, particularly with regard to the
specification. (See Discussion.)
removal of free iron and other exogenous matter. These tests
3.1.1 Discussion—Stainlesssteelsareautopassivatinginthe
include the following practices:
sense that the protective passive film is formed spontaneously
1.4.1 Practice A—Water Immersion Test,
on exposure to air or moisture. The presence of exogenous
1.4.2 Practice B—High Humidity Test,
surface contamination, including dirt, grease, free iron from
1.4.3 Practice C—Salt Spray Test,
contact with steel tooling, and so forth, may interfere with the
1.4.4 Practice D—Copper Sulfate Test,
formation of the passive film. The cleaning of these contami-
1.4.5 Practice E—Potassium Ferricyanide–NitricAcidTest,
nants from the stainless steel surface will facilitate the spon-
and
taneous passivation by allowing the oxygen uniform access to
1.4.6 Practice F—Free Iron Test.
the surface. The passive film may be augmented by chemical
1.5 The values stated in inch-pound units are to be regarded
treatments that provide an oxidizing environment for the
as the standard. The SI units given in parentheses are for
stainless steel surface.
information only.
3.1.1.1 In this specification, passivation, unless otherwise
1.6 The following precautionary caveat pertains only to the
specified, is defined as the chemical treatment of a stainless
test method portions, Sections 14 through 18 of this specifica-
steel with a mild oxidant, such as a nitric acid solution, for the
tion: This standard does not purport to address all of the safety
1 2
This specification is under the jurisdiction of ASTM Committee A01 on Steel, For referenced ASTM standards, visit the ASTM website, www.astm.org, or
Stainless Steel and Related Alloys and is the direct responsibility of Subcommittee contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
A01.14 on Methods of Corrosion Testing. Standards volume information, refer to the standard’s Document Summary page on
Current edition approved Sept. 1, 2005. Published September 2005. Originally the ASTM website.
´1 3
approved in 1996. Last previous edition approved in 2001 as A967 – 01 . DOI: Available from Superintendent of Documents, U.S. Government Printing
10.1520/A0967-05E01. Office, Washington, DC 20402.
*A Summary of Changes section appears at the end of this standard.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C70
...