ASTM D6525/D6525M-17
(Test Method)Standard Test Method for Measuring Nominal Thickness of Rolled Erosion Control Products
Standard Test Method for Measuring Nominal Thickness of Rolled Erosion Control Products
SIGNIFICANCE AND USE
5.1 Thickness is one of the basic physical properties used to control the quality of rolled erosion control products. Thickness values may aid in the calculation of other rolled erosion control product parameters. Thickness however is not generally an indication of field performance and generally should not be used in specifications. This test method is developed to aid manufacturers, designers, and end users in comparing the thickness of rolled erosion control products through the use of an accepted ASTM standard.
5.2 The thickness of rolled erosion control products may vary considerably depending on the pressure applied to the specimen during measurement. Where observed changes occur, thickness decreases when applied pressure is increased. To minimize variation, specific sample size and applied pressure are indicated in this test method to ensure all results are comparable.
5.3 This test method may be used for acceptance testing of commercial shipments of rolled erosion control products, but caution is advised since information on between-laboratory precision is incomplete. Comparative tests in accordance with 5.3.1 may be advised.
5.3.1 In case of a dispute arising from differences in reported test results when using this test method for acceptance testing of commercial shipments, the purchaser and the supplier should conduct comparative tests to determine if there is a statistical bias between their laboratories. Competent statistical assistance is recommended for the investigation of bias. As a minimum, the two parties should take a group of test specimens that are as homogeneous as possible and that are formed from a lot of material of the type in question. The test specimens should be randomly assigned in equal numbers to each laboratory for testing. The average results from the two laboratories should be compared using Student’s t-test for unpaired data and an acceptable probability level chosen by the two parties before the testing is begun. If bia...
SCOPE
1.1 This test method covers the measurement of the nominal thickness of rolled erosion control products.
1.2 This test method does not provide thickness values for rolled erosion control products under variable compressive stresses. This test method determines nominal thickness, not necessarily minimum thickness.
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
General Information
Relations
Buy Standard
Standards Content (Sample)
NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation: D6525/D6525M − 17
Standard Test Method for
Measuring Nominal Thickness of Rolled Erosion Control
1
Products
This standard is issued under the fixed designation D6525/D6525M; the number immediately following the designation indicates the
year of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last
reapproval. A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope E691 Practice for Conducting an Interlaboratory Study to
Determine the Precision of a Test Method
1.1 Thistestmethodcoversthemeasurementofthenominal
thickness of rolled erosion control products.
3. Terminology
1.2 This test method does not provide thickness values for
3.1 Definitions:
rolled erosion control products under variable compressive
3.1.1 pressure, n—the force or load per unit area.
stresses. This test method determines nominal thickness, not
3.1.2 thickness—(1)thedistancebetweenoneplanarsurface
necessarily minimum thickness.
and its opposite parallel and planar surface; (2) in rolled
1.3 The values stated in either SI units or inch-pound units
erosion control products, the distance between the upper and
are to be regarded separately as standard. The values stated in
lower surfaces of the material, measured under a specified
each system may not be exact equivalents; therefore, each
pressure and time.
system shall be used independently of the other. Combining
values from the two systems may result in non-conformance
4. Summary of Test Method
with the standard.
4.1 Thenominalthicknessofrollederosioncontrolproducts
1.4 This standard does not purport to address all of the
is determined by observing the perpendicular distance that a
safety concerns, if any, associated with its use. It is the
movableplaneisdisplacedfromaparallelsurfacebytherolled
responsibility of the user of this standard to establish appro-
erosion control product while under a specified pressure of
priate safety and health practices and determine the applica-
0.2 kPa [0.029 psi] for 5 s.
bility of regulatory limitations prior to use.
1.5 This international standard was developed in accor-
5. Significance and Use
dance with internationally recognized principles on standard-
ization established in the Decision on Principles for the 5.1 Thickness is one of the basic physical properties used to
control the quality of rolled erosion control products. Thick-
Development of International Standards, Guides and Recom-
mendations issued by the World Trade Organization Technical ness values may aid in the calculation of other rolled erosion
control product parameters. Thickness however is not gener-
Barriers to Trade (TBT) Committee.
allyanindicationoffieldperformanceandgenerallyshouldnot
be used in specifications. This test method is developed to aid
2. Referenced Documents
2 manufacturers, designers, and end users in comparing the
2.1 ASTM Standards:
thickness of rolled erosion control products through the use of
D4354 Practice for Sampling of Geosynthetics and Rolled
an accepted ASTM standard.
Erosion Control Products (RECPs) for Testing
5.2 The thickness of rolled erosion control products may
E177 Practice for Use of the Terms Precision and Bias in
vary considerably depending on the pressure applied to the
ASTM Test Methods
specimenduringmeasurement.Whereobservedchangesoccur,
thickness decreases when applied pressure is increased. To
minimize variation, specific sample size and applied pressure
1
This test method is under the jurisdiction of ASTM Committee D35 on
are indicated in this test method to ensure all results are
Geosynthetics and is the direct responsibility of Subcommittee D35.05 on Geosyn-
thetic Erosion Control.
comparable.
Current edition approved July 1, 2017. Published July 2017. Originally approved
5.3 This test method may be used for acceptance testing of
in 2000. Last previous edition approved in 2016 as D6525/D6525M – 16. DOI:
10.1520/D6525_D6525M-17.
commercial shipments of rolled erosion control products, but
2
For referenced ASTM standards, visit the ASTM website, www.astm.org, or
caution is advised since information on between-laboratory
contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
precision is incomplete. Comparative tests in accordance with
Standards volume information, refer to the standard’s Document Summary page on
the ASTM website. 5.3.1 may be advised.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1
---------------------- Page: 1 ----------------------
D6525/D6525M − 17
5.3.1 In case of a dispute arising from differences in machine elements with no specimen taken nearer than 100 mm
reported test results when using this test method for acceptance [4 in.] from the roll
...
This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Because
it may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current version
of the standard as published by ASTM is to be considered the official document.
Designation: D6525/D6525M − 16 D6525/D6525M − 17
Standard Test Method for
Measuring Nominal Thickness of Rolled Erosion Control
1
Products
This standard is issued under the fixed designation D6525/D6525M; the number immediately following the designation indicates the
year of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last
reapproval. A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope
1.1 This test method covers the measurement of the nominal thickness of rolled erosion control products.
1.2 This test method does not provide thickness values for rolled erosion control products under variable compressive stresses.
This test method determines nominal thickness, not necessarily minimum thickness.
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each
system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the
two systems may result in non-conformance with the standard.
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility
of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory
limitations prior to use.
1.5 This international standard was developed in accordance with internationally recognized principles on standardization
established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued
by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
2. Referenced Documents
2
2.1 ASTM Standards:
D4354 Practice for Sampling of Geosynthetics and Rolled Erosion Control Products (RECPs) for Testing
E177 Practice for Use of the Terms Precision and Bias in ASTM Test Methods
E691 Practice for Conducting an Interlaboratory Study to Determine the Precision of a Test Method
3. Terminology
3.1 Definitions:
3.1.1 pressure, n—the force or load per unit area.
3.1.2 thickness—(1) the distance between one planar surface and its opposite parallel and planar surface; (2) in rolled erosion
control products, the distance between the upper and lower surfaces of the material, measured under a specified pressure and time.
4. Summary of Test Method
4.1 The nominal thickness of rolled erosion control products is determined by observing the perpendicular distance that a
movable plane is displaced from a parallel surface by the rolled erosion control product while under a specified pressure of 0.2 kPa
[0.029 psi] for 5 s.
5. Significance and Use
5.1 Thickness is one of the basic physical properties used to control the quality of rolled erosion control products. Thickness
values may aid in the calculation of other rolled erosion control product parameters. Thickness however is not generally an
1
This test method is under the jurisdiction of ASTM Committee D35 on Geosynthetics and is the direct responsibility of Subcommittee D35.05 on Geosynthetic Erosion
Control.
Current edition approved July 1, 2016July 1, 2017. Published July 2016July 2017. Originally approved in 2000. Last previous edition approved in 20142016 as
D6525/D6525M – 14.D6525/D6525M – 16. DOI: 10.1520/D6525_D6525M-16.10.1520/D6525_D6525M-17.
2
For referenced ASTM standards, visit the ASTM website, www.astm.org, or contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM Standards
volume information, refer to the standard’s Document Summary page on the ASTM website.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1
---------------------- Page: 1 ----------------------
D6525/D6525M − 17
indication of field performance and generally should not be used in specifications. This test method is developed to aid
manufacturers, designers, and end users in comparing the thickness of rolled erosion control products through the use of an
accepted ASTM standard.
5.2 The thickness of rolled erosion control products may vary considerably depending on the pressure applied to the specimen
during measurement. Where observed changes occur, thickness decreases when applied pressure is increased. To minimize
variation, specific sample size and applied pressure are indicated in this test method to ensure all results are comparable.
5.3 This test method may be used for acceptance testing of commercial
...
Questions, Comments and Discussion