ASTM A312/A312M-08a

This document is not anASTM standard and is intended only to provide the user of anASTM standard an indication of what changes have been made to the previous version. Because
it may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current version
of the standard as published by ASTM is to be considered the official document.
Used in USDOE-NE standards
Designation:A 312/A 312M–08 Designation: A 312/A 312M – 08a
Standard Specification for
Seamless, Welded, and Heavily Cold Worked Austenitic
1
Stainless Steel Pipes
ThisstandardisissuedunderthefixeddesignationA312/A312M;thenumberimmediatelyfollowingthedesignationindicatestheyear
of original adoption or, in the case of revision, the year of last revision.Anumber in parentheses indicates the year of last reapproval.
A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the Department of Defense.
1. Scope*
2
1.1 This specification covers seamless, straight-seam welded, and heavily cold worked welded austenitic stainless steel pipe
intended for high-temperature and general corrosive service.
NOTE 1—When the impact test criterion for a low-temperature service would be 15 ft·lbf [20 J] energy absorption or 15 mils [0.38 mm] lateral
expansion, some of the austenitic stainless steel grades covered by this specification are accepted by certain pressure vessel or piping codes without the
necessity of making the actual test. For example, Grades TP304, TP304L, and TP347 are accepted by the ASME Pressure Vessel Code, Section VIII
Division 1, and by the Chemical Plant and Refinery Piping Code, ANSI B31.3, for service at temperatures as low as −425 °F [−250 °C] without
qualification by impact tests. OtherAISI stainless steel grades are usually accepted for service temperatures as low as −325 °F [−200 °C] without impact
testing. Impact testing may, under certain circumstances, be required. For example, materials with chromium or nickel content outside theAISI ranges,
and for material with carbon content exceeding 0.10 %, are required to be impact tested under the rules ofASME Section VIII Division 1 when service
temperatures are lower than −50 °F [−45 °C].
1.2 Grades TP304H, TP309H, TP309HCb, TP310H, TP310HCb, TP316H, TP321H, TP347H, and TP348H are modifications
of Grades TP304, TP309Cb, TP309S, TP310Cb, TP310S, TP316, TP321, TP347, and TP348, and are intended for service at
temperatures where creep and stress rupture properties are important.
1.3 Optional supplementary requirements are provided for pipe where a greater degree of testing is desired. These
supplementary requirements call for additional tests to be made and, when desired, it is permitted to specify in the order one or
more of these supplementary requirements.
1.4 Table X1.1 lists the standardized dimensions of welded and seamless stainless steel pipe as shown inANSI B36.19. These
dimensionsarealsoapplicabletoheavilycoldworkedpipe.Pipehavingotherdimensionsispermittedtobeorderedandfurnished
provided such pipe complies with all other requirements of this specification.
1.5 Grades TP321 and TP321H have lower strength requirements for pipe manufactured by the seamless process in nominal
3
wall thicknesses greater than ⁄8 in. [9.5 mm].
1.6 Thevaluesstatedineitherinch-poundunitsorSIunitsaretoberegardedseparatelyasstandard.Withinthetext,theSIunits
are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system must be used
independently of the other. Combining values from the two systems may result in nonconformance with the specification. The
inch-pound units shall apply unless the “M” designation of this specification is specified in the order.
NOTE 2—ThedimensionlessdesignatorNPS(nominalpipesize)hasbeensubstitutedinthisstandardforsuchtraditionaltermsas“nominaldiameter,”
“size,” and “nominal size.”
2. Referenced Documents
3
2.1 ASTM Standards:
A262 Practices for Detecting Susceptibility to Intergranular Attack in Austenitic Stainless Steels
A370 Test Methods and Definitions for Mechanical Testing of Steel Products
A941 Terminology Relating to Steel, Stainless Steel, Related Alloys, and Ferroalloys
A999/A999M Specification for General Requirements for Alloy and Stainless Steel Pipe
1
ThisspecificationisunderthejurisdictionofASTMCommitteeA01onSteel,StainlessSteelandRelatedAlloysandisthedirectresponsibilityofSubcommitteeA01.10
on Stainless and Alloy Steel Tubular Products.
Current edition approved MarchOct. 1, 2008. Published AprilOctober 2008. Originally approved in 1948. Last previous edition approved in 20072008 as
A312/A312M–078.
2
For ASME Boiler and Pressure Vessel Code applications see related Specification SA-312 in Section II of that Code.
3
ForreferencedASTMstandards,visittheASTMwebsite,www.astm.org,orcontactASTMCustomerServiceatservice@astm.org.For Annual Book of ASTM Standards
...

This document is not anASTM standard and is intended only to provide the user of anASTM standard an indication of what changes have been made to the previous version. Because
it may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current version
of the standard as published by ASTM is to be considered the official document.
Used in USDOE-NE standards
Designation:A312/A312M–08 Designation: A 312/A 312M – 08a
Standard Specification for
Seamless, Welded, and Heavily Cold Worked Austenitic
1
Stainless Steel Pipes
ThisstandardisissuedunderthefixeddesignationA312/A312M;thenumberimmediatelyfollowingthedesignationindicatestheyear
of original adoption or, in the case of revision, the year of last revision.Anumber in parentheses indicates the year of last reapproval.
A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the Department of Defense.
1. Scope*
2
1.1 This specification covers seamless, straight-seam welded, and heavily cold worked welded austenitic stainless steel pipe
intended for high-temperature and general corrosive service.
NOTE 1—When the impact test criterion for a low-temperature service would be 15 ft·lbf [20 J] energy absorption or 15 mils [0.38 mm] lateral
expansion, some of the austenitic stainless steel grades covered by this specification are accepted by certain pressure vessel or piping codes without the
necessity of making the actual test. For example, Grades TP304, TP304L, and TP347 are accepted by the ASME Pressure Vessel Code, Section VIII
Division 1, and by the Chemical Plant and Refinery Piping Code, ANSI B31.3, for service at temperatures as low as −425 °F [−250 °C] without
qualification by impact tests. OtherAISI stainless steel grades are usually accepted for service temperatures as low as −325 °F [−200 °C] without impact
testing. Impact testing may, under certain circumstances, be required. For example, materials with chromium or nickel content outside theAISI ranges,
and for material with carbon content exceeding 0.10 %, are required to be impact tested under the rules ofASME Section VIII Division 1 when service
temperatures are lower than −50 °F [−45 °C].
1.2 Grades TP304H, TP309H, TP309HCb, TP310H, TP310HCb, TP316H, TP321H, TP347H, and TP348H are modifications
of Grades TP304, TP309Cb, TP309S, TP310Cb, TP310S, TP316, TP321, TP347, and TP348, and are intended for service at
temperatures where creep and stress rupture properties are important.
1.3 Optional supplementary requirements are provided for pipe where a greater degree of testing is desired. These
supplementary requirements call for additional tests to be made and, when desired, it is permitted to specify in the order one or
more of these supplementary requirements.
1.4 Table X1.1 lists the standardized dimensions of welded and seamless stainless steel pipe as shown inANSI B36.19. These
dimensionsarealsoapplicabletoheavilycoldworkedpipe.Pipehavingotherdimensionsispermittedtobeorderedandfurnished
provided such pipe complies with all other requirements of this specification.
1.5 Grades TP321 and TP321H have lower strength requirements for pipe manufactured by the seamless process in nominal
3
wall thicknesses greater than ⁄8 in. [9.5 mm].
1.6 Thevaluesstatedineitherinch-poundunitsorSIunitsaretoberegardedseparatelyasstandard.Withinthetext,theSIunits
are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system must be used
independently of the other. Combining values from the two systems may result in nonconformance with the specification. The
inch-pound units shall apply unless the “M” designation of this specification is specified in the order.
NOTE 2—ThedimensionlessdesignatorNPS(nominalpipesize)hasbeensubstitutedinthisstandardforsuchtraditionaltermsas“nominaldiameter,”
“size,” and “nominal size.”
2. Referenced Documents
3
2.1 ASTM Standards:
A262 Practices for Detecting Susceptibility to Intergranular Attack in Austenitic Stainless Steels
A370 Test Methods and Definitions for Mechanical Testing of Steel Products
A941 Terminology Relating to Steel, Stainless Steel, Related Alloys, and Ferroalloys
A999/A999M Specification for General Requirements for Alloy and Stainless Steel Pipe
1
ThisspecificationisunderthejurisdictionofASTMCommitteeA01onSteel,StainlessSteelandRelatedAlloysandisthedirectresponsibilityofSubcommitteeA01.10
on Stainless and Alloy Steel Tubular Products.
Current edition approved MarchOct. 1, 2008. Published AprilOctober 2008. Originally approved in 1948. Last previous edition approved in 20072008 as
A312/A312M–078.
2
For ASME Boiler and Pressure Vessel Code applications see related Specification SA-312 in Section II of that Code.
3