SIST IEC 61089:1999/A1:1999

SLOVENSKI STANDARD
SIST IEC 61089:1999
01-november-1999
Round wire concentric lay overhead electrical stranded conductors - Amendment
A1
Round wire concentric lay overhead electrical stranded conductors
Ta slovenski standard je istoveten z: IEC 61089
ICS:
29.060.10 Žice Wires
29.240.20 Daljnovodi Power transmission and
distribution lines
SIST IEC 61089:1999 en
2003-01.Slovenski inštitut za standardizacijo. Razmnoževanje celote ali delov tega standarda ni dovoljeno.

---------------------- Page: 1 ----------------------

SIST IEC 61089:1999/A1:1999

---------------------- Page: 2 ----------------------

SIST IEC 61089:1999/A1:1999
CEI
NORME
IEC
INTERNATIONALE
1089
INTERNATIONAL
Première édition
STANDARD
First edition
1991-05
Conducteurs pour lignes aériennes
à brins circulaires, câblés en couches
concentriques
Round wire concentric lay overhead
electrical stranded conductors
© CEI 1991 Droits de reproducti réservés — Copyright — all rights reserved
on
or utilized in
Aucune partie de cette publication no peut être reproduite ni No part of this publication may be reproduced
utilisée sous quelque forme quo ce soit et par aucun pro- any tortu or by any means. electronic « mecharicai,
cédé. é ectrorêque
ou mêeanlw. y compds la photocopie et krekdlrg photocopying ad mkratikn, without pemdsslon
les microfilms. sans raccord écrit do l'éditeur.
In writing from the publisher.
Bureau Central de la Commission Electrotechnique Internationale 3, rue de Varembé Genève, Suisse
Commission Electrotechnique Internationale
CODE PRIX "
International Electrotechnical Commission
PRICE CODE V
Meautriapoanaa 3nearpoTexHwlecaaa H0Mttccua
IEC
• •
Pour pr&, voir catalogue en vigueur
For price, see current catalogue

---------------------- Page: 3 ----------------------

SIST IEC 61089:1999/A1:1999
1089©IEC – 3 –
CONTENTS
Page
5 FOREWORD
Clause

7
1 Scope

7
2 Normative references

9
3 Designation system

9
4 Definitions
11
5 Requirements for stranded conductors
11
5.1 Material
11
5.2 Conductor sizes
13
5.3 Surface
5.4 Stranding 13
13
5.5 Joints
15
5.6 Linear density – Mass per unit length
17
5.7 Conductor strength
19
6 Tests
6.1 Classification of tests 19
19
6.2 Test requirements
21
6.3 Sample size
21
6.4 Sample length
21
6.5 Type tests
6.6 Sample tests 23
25
6.7 Inspection
27
6.8 Acceptance or rejection
27
7 Packaging and marking
27
7.1 Packaging
27
7.2 Marking and tare
27
7.3 Random lengths
ANNEXES
A Information to be supplied by purchaser 29
B Stress-strain test method 31
C Nominal mass of grease for stranded conductors 39
D Recommended conductor sizes and tables of conductor properties 45

---------------------- Page: 4 ----------------------

SIST IEC 61089:1999/A1:1999
- 5 -
1089©IEC
COMMISSION
INTERNATIONAL ELECTROTECHNICAL
ROUND WIRE CONCENTRIC LAY OVERHEAD
ELECTRICAL STRANDED CONDUCTORS
FOREWORD
1) The formal decisions or agreements of the IEC on technical matters, prepared by Technical Committees on
which all the National Committees having a special interest therein are represented, express, as nearly as
possible, an international consensus of opinion on the subjects dealt with.
They have the form of recommendations for international use and they are accepted by the National
2)
Committees in that sense.
In order to promote international unification, the IEC expresses the wish that all National Committees
3)
should adopt the text of the IEC recommendation for their national rules in so far as national conditions will
permit. Any divergence between the IEC recommendation and the corresponding national rules should, as
far as possible, be clearly indicated in the latter.
This standard has been prepared by IEC Technical Committee No. 7: Bare aluminium
conductors.
The text of this standard is based on the following documents:
Report on Voting
Six Months' Rule Report on Voting Two Months' Procedure
7(00)431 7(00)433
7(00)429 7(00)430
Full information on the voting for the approval of this standard can be found in the Voting
Reports indicated in the above table.
This standard replaces the following publications:
IEC 207: 1966,
Aluminium stranded conductors.
IEC 208: 1966, Aluminium alloy stranded conductors (aluminium-magnesium-silicon type).
IEC 209: 1966, Aluminium conductors, steel-reinforced.
IEC 210: 1966, Aluminium alloy conductors, steel-reinforced.
Annexes A, B and C form an integral pa rt of this International Standard.
Annex D is for information only.

---------------------- Page: 5 ----------------------

SIST IEC 61089:1999/A1:1999
1089©IEC - 7 -
ROUND WIRE CONCENTRIC LAY OVERHEAD
ELECTRICAL STRANDED CONDUCTORS
1 Scope
1.1 This International Standard specifies the electrical and mechanical characteristics of
round wire concentric lay overhead electrical stranded conductors made of combinations
of any of the following metal wires:
a) hard-drawn aluminium as per IEC 889 designated Al*;
b) aluminium alloy type B as per IEC 104 designated A2*;
c) aluminium alloy type A as per IEC 104 designated A3* (and when applicable to the
following cores, as per IEC 888);
d) regular strength steel, designated S1A or S1 B, where A and B are zinc coating
classes, corresponding respectively to classes 1 and 2;
e) high strength steel, designated S2A or S2B;
f) extra high strength steel, designated S3A.
1.2 The conductor designations included in this standard are:
Al, A2, A3,
Al/S1A, Al/S1B, Al/S2A, Al/S2B, Al/S3A, A2/S1A,
A2/S 1 B, A2/S3A, A3/S 1 A,
A3/S 1 B, A3/S3A, Al /A2, A1 /A3.
2 Normative references
The following standards contain provisions which, through reference in this text, constitute
provisions of this International Standard. At the time of publication of this standard, the
editions indicated were valid. All standards are subject to revision, and parties to agree-
ments based on this International Standard are encouraged to investigate the possibility of
applying the most recent editions of the standards indicated below. Members of IEC and
ISO maintain registers of currently valid International Standards.
IEC 104: 1987, Aluminium-magnesium-silicon alloy wire for overhead line conductors.
IEC 888: 1987,
Zinc-coated steel wires for stranded conductors.
IEC 889: 1987,
Hard-drawn aluminium wire for overhead line conductors.
The resistivity of these metals is as follows (in increasing order):
Al: 28,264 nS1m (corresponding to 61% IACS),
A2: 32,530 nQm (corresponding to 53% IACS),
A3:
32,840 nam (corresponding to 52,5% IACS).

---------------------- Page: 6 ----------------------

SIST IEC 61089:1999/A1:1999
1089©IEC - 9 -
3 Designation system
3.1 A designation system is used to identify stranded conductors made of aluminium,
with or without steel wires.
3.2 Homogeneous aluminium conductors are designated Ax, where x identifies the type
of aluminium.
3.3 Composite aluminium conductors are designated Ax/Ay, where Ax identifies external
wires (or the envelope) and Ay identifies internal wires (or the core).
3.4 Composite aluminium-steel conductors are designated Ax/Syz, where Ax identifies
the external aluminium wires (envelope), and Syz identifies the steel core. In the
designation of steel wires, y represents the type of steel (regular, high or extra high
strength) and z represents the class of zinc coating (A or B).
3.5 Conductors are identified as follows:
a) a code number giving the equivalent conductive section of Al aluminium expressed
in mm2;
b) a designation identifying the type of wires constituting the conductor. For composite
conductors the first designation applies to the envelope and the second to the core;
c) one or two numbers giving the stranding of the conductor. For composite conduc-
tors, the first number identifies the number of wires of the envelope and the second
identifies the number of wires of the core.
Examples:
500-Al-37: Conductor made of 37 wires of Al aluminium. Its area is 500 mm2.
500-A2-37: Conductor made of 37 wires of A2 aluminium with a total conductive area
equivalent to 500 mm 2 of Al aluminium. From the tables of annex D we find its actual
area is equal to 575 mm2.
500-A1 /S1 A-45/7: Conductor made of 45 wires of Al aluminium and 7 wires of regular
strength steel with class 1 zinc coating. The area of Al aluminium is 500 mm 2 and, from
the tables of annex D, the area of S1 A steel is 34,6 mm2.
500-A3/S3A-54/7: Conductor made of 54 wires of A3 aluminium and 7 wires of extra
high strength steel with class 1 zinc coating. The A3 aluminium area is equivalent in
conductivity to 500 mm 2 of Al aluminium (the actual area of A3 aluminium is 581 mm2
and of steel is 75,3 mm 2, which can be obtained from the tables of annex D).
4 Definitions
The following definitions apply in this International Standard:
aluminium: All types of aluminium and aluminium alloys listed.
conductor: A material intended to be used for carrying electric current consisting of a
plurality of uninsulated wires twisted together.

---------------------- Page: 7 ----------------------

SIST IEC 61089:1999/A1:1999
- 11 -
1089 © IEC
concentric lay stranded conductor: A conductor composed of a central core surrounded
by one or more adjacent layers of wires being laid helically in opposite directions.
direction of lay: The direction of twist of a layer of wires as it moves away from the
viewer. A right-hand lay is a clockwise direction and a left-hand lay is an anti-clockwise
direction.
Alternative definition: The direction of lay is defined as right-hand or left-hand. With right-
hand lay, the wires conform to the direction of the central part of the letter Z when the
conductor is held vertically. With left-hand lay, the wires conform to the direction of the
central part of the letter S when the conductor is held vertically.
lay length: The axial length of one complete turn of the helix formed by an individual wire
in a stranded conductor.
lay ratio: Means the ratio of the lay length to the external diameter of the corresponding
layer of wires in the stranded conductor.
lot: A group of conductors manufactured by the same manufacturer under similar condi-
tions of production. A lot may consist of part or all of the purchased quantity.
nominal: The name or identifying value of a measurable property by which a conductor or
component of a conductor is identified and to which tolerances are applied. Nominal
values should be target values.
steel ratio: The ratio of steel area to aluminium area as a percentage in Ax/Syz
conductors.
wire: A filament of drawn metal having a constant circular cross-section.
5 Requirements for stranded conductors
5.1 Material
Stranded conductors shall be made up of round aluminium wires and, when applicable, of
round zinc-coated steel wires. All wires shall have before stranding the properties speci-
fied in IEC 104, IEC 888 and IEC 889.
5.2 Conductor sizes
A list of conductor sizes is given as guidance in annex D and it is recommended that for
new designs of conductor sizes should be selected from those listed. Conductors for
existing or established designs of overhead lines as well as sizes and strandings not
included in this standard may be designed and supplied as agreed upon by the manu-
facturer and purchaser and the relevant requirements of this standard shall apply.

---------------------- Page: 8 ----------------------

SIST IEC 61089:1999/A1:1999
1089 ©IEC - 13 -
5.3 Surface
rf rfections visible to the unaided eye
The su ace of the conductor shall be free from all impe
(normal corrective lenses accepted), such as nicks, indentations, etc., not consistent with
good commercial practice.
5.4 Stranding
5.4.1 All wires of the conductor shall be concentrically stranded.
5.4.2 Adjacent wire layers shall be stranded with reverse lay directions. The direction of
lay of the external layer shall be "right-hand" except when specifically indicated in the
purchase order.
5.4.3 The wires in each layer shall be evenly and closely stranded around the underlying
wire or wires.
5.4.4 The lay ratios for the zinc-coated steel wire layers shall be as follows:
the lay ratio for the six-wire layer of 7 and 19-wire steel cores shall be not less than
a)
16 nor more than 26;
b) the lay ratio for the 12-wire layer of 19-wire steel core shall be not less than 14 nor
more than 22.
5.4.5 The lay ratios for the aluminium layers of all types of conductor shall be as follows:
a) the lay ratio for the outside layer of aluminium wires shall be not less than 10 nor
more than 14;
b) the lay ratios for the inner layers of aluminium wires shall be not less than 10 nor
more than 16.
5.4.6 In a 19-wire steel core, the lay ratio of the 12-wire layer shall be not greater than
the lay ratio of the 6-wire layer. Similarly, in a conductor having multiple layers of alu-
minium wires, the lay ratio of any aluminium layer shall be not greater than the lay ratio of
the aluminium layer immediately beneath it.
5.4.7 All steel wires shall lie naturally in their position in the stranded core, and where
the core is cut, the wire ends shall remain in position or be readily replaced by hand and
then remain approximately in position. This requirement also applies to the outer layer of
aluminium wires of a conductor.
5.4.8 Before stranding, aluminium and steel wires shall have approximately uniform
temperatures.
5.5
Joints
5.5.1 There shall be no joints of any kind made in the zinc-coated steel core wire or wires
during stranding.
5.5.2 No more than one jointed aluminium finished wire as permitted in the references of
5.1 shall be used per length of conductor.

---------------------- Page: 9 ----------------------

SIST IEC 61089:1999/A1:1999
1089©IEC – 15 –
5.5.3 During stranding, no aluminium wire welds shall be made for the purpose of achiev-
ing the required conductor length.
5.5.4 Joints are permitted in aluminium wires unavoidably broken during stranding,
provided such breaks are not associated with either inherently defective wire or with the
use of short lengths of aluminium wires. Joints shall conform to the geometry of original
wire, i.e. joints shall be dressed smoothly with a diameter equal to that of the parent wires
and shall not be kinked.
Joints in aluminium wires shall not exceed those specified in table 1. These joints shall
not be closer than 15 m from a joint in the same wire or in any other aluminium wire of the
completed conductor.
Joints shall be made by electric butt welding, electric butt cold upset welding or cold
pressure welding (note 1) and other approved methods. These joints shall be made in
accordance with good commercial practice. The first type of joints shall be electrically
annealed for approximately 250 mm on both sides of the weld.
Table 1 – Number of joints permitted
in aluminium conductors
Number of aluminium Joints permitted per
layers conductor length
1 2
3
2
3 4
4 5
5.5.5 While the joints specified in 5.5.4 are not required to meet the requirements of un-
jointed wires (note 2), they shall withstand a stress of not less than 75 MPa for annealed
electric buttwelded joints, and not less than 130 MPa for cold pressure and electric butt
cold upset welded joints. The manufacturer shall demonstrate that the proposed welding
method is capable of meeting the specified strength requirements.
NOTES
1 It is a practice in some countries to require the annealing of cold pressure joints made in A2 or A3 material.
2 The behaviour of properly spaced wire joints in stranded conductor is related to both tensile strength
and elongation. Because of higher elongation properties, the lower strength annealed electric buttwelded
joint gives a similar overall pe rformance to that of a cold pressure or an electric butt cold upset welded
joint.
5.6
Linear density – Mass per unit length
5.6.1 The masses given in the tables of annex D have been calculated for each size and
stranding of conductor using densities for the aluminium and zinc-coated steel wires as
given in the standards listed in 5.1, the stranding increments given in table 2, and the
cross-sectional areas for aluminium and zinc-coated steel wires based on their theoretical
unrounded diameters.

---------------------- Page: 10 ----------------------

SIST IEC 61089:1999/A1:1999
1089©!EC - 17 --
5.6.2 The increments (note 1) in per cent, for mass due to stranding, based on the mean
lay ratios given in 5.4.4 and 5.4.5, shall be taken as given in table 2.
5.6.3 Whenever a conductor is to be greased (note 2), the nominal mass of grease shall
be calculated according to the method given in annex C.
NOTES
1 The mass of a stranded conductor is affected by the lay factor. With the exception of the centre wire,
all wires are longer than the stranded conductor and the increase in mass depends upon the lay ratio
employed.
2 Grease requirements are under consideration.
Table 2 - Standard* increments due to stranding
Increment (increase)
Stranding of conductor
Aluminium Steel Mass Electrical
resistance
Number of Number of Number of Number of
Aluminium Steel
wires layers** wires layers**
6 1 1 - 1,52 - 1,52
18 2 1 - 1,90 - 1,90
1,31
7 1 - - 1,31 -
18 1 - 1,90 - 1,90
2
22 2 7 1 2,04 0,43 2,04
26 2 7 1 2,16 0,43 2,16
19 - 1,80
2 - - 1,80
37 3 - - 2,04 - 2,04
61 4 - - 2,19 - 2,19
45 3 7 1 2,23 0,43 2,23
54 3 1 2,33
7 2,33 0,43
72 4 7 1 2,32 0,43 2,32
84 4 7 1 2,40 0,43 2,40
91 5 - - 2,30 - 2,30
54 2 2,33
3 19 2,33 0,77
72 4 19 2 2,32 0,77 2,32
84 4 19 2,40
2 0,77 2,40
* These increments have been calculated using average lay ratios for each applicable layer of aluminium or
steel.
** Number of layers of each type of wire not including the central wire.
5.7 Conductor strength
5.7.1 The rated tensile strength of a homogeneous aluminium conductor shall be taken as
the sum of the minimum tensile strength of all wires as defined in 5.7.4.
5.7.2 The rated tensile strength of composite Ax/Syz conductors shall be the sum of
the tensile strength of the aluminium po rt
ion plus the strength of steel corresponding
to an elongation compatible with that of aluminium at rupture load. For the purpose of

---------------------- Page: 11 ----------------------

SIST IEC 61089:1999/A1:1999
1089©IEC - 19 -
specification and practicability, this strength of steel is conservatively established as the
stress corresponding at 1% elongation in a 250 mm gauge length.
5.7.3 The rated tensile strength of composite aluminium conductors (Al/A2 or Al/A3)
shall be taken as the sum of the tensile strength of Al portion plus 95% of the tensile
strength of A2 or A3 portion.
5.7.4 The tensile strength of any single wire is the product of its nominal area and the
appropriate minimum stress given in the standards listed in 5.1.
6 Tests
6.1 Classification of tests
6.1.1
Type tests
Type tests are intended to verify the main characteristics of a conductor which depend
mainly on its design. They are carried out once for a new design or manufacturing process
of conductor and then subsequently repeated only when the design or manufacturing
process is changed.
Type tests shall be carried out only on a conductor which meets the requirements of all
the relevant sample tests.
6.1.2 Sample tests
Sample tests are intended to guarantee the quality of conductors and compliance with the
requirements of this standard.
6.2 Test requirements
Test requirements are as follows:
6.2.1 Type tests
a) joints in aluminium wires;
b) stress-strain curves;
c) breaking strength of conductor.
6.2.2
Sample tests
a) on wire before stranding:
- as per the applicable wire standards;
b) on the conductor:
- cross-sectional area;
- overall diameter;
- linear density;
-
surface condition;
- lay ratio and direction of lay.

---------------------- Page: 12 ----------------------

SIST IEC 61089:1999/A1:1999
1089©IEC -21 -
6.3 Sample size
Samples for the tests specified in 6.2.2 shall be taken at random from the outer end
ace condition of the
of 10% of the drums of conductor. However, the inspection of the su rf
conductor shall be carried out on every drum prior to lagging.
6.4 Sample length
6.4.1 Samples for tests on individual aluminium and zinc-coated steel core wires shall be
taken before stranding and tested in accordance with the standards listed in 5.1.
6.4.2 Samples for tests of individual wires after stranding when requested, shall consist
of a 1,5 m length or cut from the outer end of the coils or drums of conductors.
6.4.3 The sample length required for tensile and stress-strain tests shall be at least
400 times the diameter of the conductor but not less than 10 m.
The length of samples in this subclause is the minimum required for a good accuracy of
stress-strain curves. In cases where the manufacturer can demonstrate to the satisfaction
of the purchaser with significant comparative test results that a shorter length can give
equally accurate results then a short length of samples may be used.
6.5 Type tests
6.5.1 Stress-strain curves shall be supplied as a type test when requested by the
purchaser and shall represent the best knowledge of the behaviour of the purchased
conductor under load.
6.5.2 If agreed between purchaser and supplier when placing an order, stress-strain tests
shall be performed on the conductor and, when applicable, on the steel core, in
accordance with the method given in annex B.
6.5.3 Tensile test of the conductor
When tests for breaking strength of conductors are required, these shall withstand, without
the fracture of any wire not less than 95% of their rated tensile strength calculated accord-
ing to 5.7.
The breaking strength of conductors shall be determined by pulling a conductor in a
suitable tensile testing machine having an accuracy of at least ±1%. It is recommended
that the rate of increase of load should be as in B.6.8 of annex B. For the purposes of this
test, appropriate fittings shall be installed on the ends of the conductor samples. During
this test, the breaking strength of the conductor shall be determined by the load attained
at which one or more wires of the conductor are fractured. A retest, up to a total of three
tests, may be made if wire fracture occurs within 1 cm of the end fittings and the tensile
strength falls below the specified breaking strength requirements.

---------------------- Page: 13 ----------------------

SIST IEC 61089:1999/A1:1999
1089©IEC - 23 -
6.5.4
Welding of aluminium wires
The manufacturer shall demonstrate to the purchaser that the method used for jointing
aluminium wires meets the strength requirements of 5.5.5 by supplying recent test results
or by performing the necessary tests.
6.6
Sample tests
6.6.1 Cross-sectional area
rtion of a stranded conductor shall
6.6.1.1 The cross-sectional area of the aluminium po
be taken as the sum of the areas of the aluminium wires composing the conductor based
on the diameter measurements made in accordance with 6.6.1.3.
This area shall not vary from the nominal value by more than ±2% in any sample and by
more than ±1,5% for the average of any four measured values at locations selected at
random with a minimum spacing of 20 cm.
6.6.1.2 The area of steel core, where applicable, shall be taken as the sum of the areas
of the solid wires composing the steel core based on the diameter measurements made in
accordance with 6.6.1.3.
6.6.1.3 The diameter of a wire shall include the metallic coating, where applicable, and
shall be measured using a micrometer caliper having flat su rfaces on both the anvil and
the end of the spindle and graduated to be read in micrometres. The diameter d in milli-
metres shall be the average of three diameter measurements, each of which is the
average of the maximum and minimum readings at a point taken near each end and in the
centre of the sample.
6.6.2 Conductor diameter
The conductor diameter shall be measured midway between the closing die and the
capstan on the stranding machine.
Measurements shall be made with a caliper graduated to be read in 0,01 mm. The
diameter shall be the average of two readings, rounded to two decimals of a millimetre,
taken at right angles to each other at the same location.
The diameter of the conductor shall not vary by:
±1% for diameters larger than or equal to 10 mm;
±0,1 mm for diameters smaller than 10 mm.
6.6.3 Linear density - Mass per unit length
The linear density (mass per unit length) of the conductor shall be determined by using
apparatus capable of achieving an accuracy of ±0,1%.
The mass of the conductor per unit length without grease shall not vary from its nominal
value given in the tables by more than ±2%.
The mass of grease in a conductor shall be determined from the difference between the
mass of the conductor with grease and its mass after removing all the grease. The mass
of grease shall correspond at least to the minimum values specified in annex C.

---------------------- Page: 14 ----------------------

SIST IEC 61089:1999/A1:1999
1089 ©EC – 25 –
6.6.4 Breaking strength of wires
When required, breaking strength tests shall be made on wires obtained from conductors
after stranding. The specimen of wires shall be taken from the conductor sample and shall
be removed from its position and straightened, care being taken not to stretch it in so
doing.
The cross-sectional area of the wire is determined from the diameter measurements
indicated in 6.6.1.3. Then the straightened wire shall be installed in a suitable tensile test-
ing machine. The load shall be applied gradually with a rate of separation of the jaws not
less than 25 mm per minute and not greater than 100 mm per minute.
The load at failure divided by the cross-sectional area of the wire shall be not less than
95% of the applicable stress requirements prior to stranding. (The 5% reduction accounts
for handling and twisting of wires during stranding.)
6.6.5
Surface condition
The surface of the conductor shall comply with the requirements of 5.3.
6.6.6
Lay ratio and direction of lay
The lay ratio of each layer of the conductor shall be obtained through the ratio of the
measured lay length to the external diameter of the applicable layer.
The obtained values shall comply with the requirements of 5.4. In addition the direction of
each layer shall be noted and shall also comply with the requirements of 5.4.
6.7 Inspection
6.7.1 All tests and inspection shall be made at the manufacturer's plant prior to shipment
unless mutually agreed between the manufacturer and the purchaser at the time of pur-
chase and shall be so conducted as not to interfere unnecessarily with the manufacturer's
operations. The manufacturer shall afford the inspector, representing the purchaser, all
necessary and sufficient testing facilities in order to satisfy him that the material is being
furnished in accordance with this standard.
6.7.2 When inspection is to be made by the purchaser before shipment, the tests shall
all be made within 10 days after receipt of a notice by the purchaser that the material is
ready to test, and the material shall be accepted or rejected at the manufacturer's plant.
If the purchaser does not have a representative present at the manufacturer's plant to test
the material at the expiration of the said 10 days, the manufacturer shall make the tests
herein provided for and furnish to the purchaser, when requested, official copies of the
results of such tests, and the purchaser shall accept or reject the material in accordance
with the results of such tests. Alternatively, the manufacturer may provide relevant test
results if these have already been carried out in production.

---------------------- Page: 15 ----------------------

SIST IEC 61089:1999/A1:1999
1089 0O IEC – 27 –
6.8 Acceptance or rejection
6.8.1 Failure of a test specimen to comply with any one of the requirements of this
standard shall constitute grounds for rejection of the lot represented by the specimen.
6.8.2 If any lot is so rejected, the manufacturer shall have the right to test, only once, all
individual drums of conductors in the lot and submit those which meet the requirements for
acceptance.
7 Packaging and marking
7.1 Packaging
The conductor shall be suitably protected against damage which could occur in ordinary
handling and shipping.
NOTE - The following shall be agreed upon between the manufacturer and the purchaser at the time of
placing the order or at the earliest possible time:
a) the type and size of package and method of packing;
b) the packaging size and drum bore requirements and also the availability of the inner end of the conduc-
tor for grounding purposes, where conductor stringing practices require special consideration.
7.2 Marking and tare
The gross, net and tare weight, length (or length and number of pieces, if more than one
length is agreed upon to be supplied on the same drum), designation, and any other
necessary identification shall be suitably marked inside the package. This same inform-
ation, together with the purchase order number, the manufacturer's serial number (if any)
and all shipping marks and other information shall appear on the outside of each package.
7.3
Random lengths
Random lengths of conductors unavoidably obtained during production shall not exceed
5% of the length providing that no piece is less than 50% of the contractual length.

---------------------- Page: 16 ----------------------

SIST IEC 61089:1999/A1:1999
1089©IEC - 29 -
Annex A
(normative)
Information to be supplied by purchaser
When making an enquiry or placing an order the purchaser shall furnish the following
information:
a)
quantity of conductors;
b) cross-sectional area, designation and stranding of conductor;
c) length of conductor per drum, its tolerance, and where applicable, matching of
conductor lengths;
d) type and size of package and method of packing;
e) special packaging requirements, if any;
f) lagging requirements, if any;
g) if inspection is required and the place of inspection;
h) whether tests on wires after stranding are required;
i) whether conductor breaking strength tests are required;
j) whether c
...