ASTM B367-08

This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Because
it may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current version
of the standard as published by ASTM is to be considered the official document.
Designation:B367–06 Designation: B 367 – 08
Standard Specification for
1
Titanium and Titanium Alloy Castings
This standard is issued under the fixed designation B 367; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the Department of Defense.
1. Scope
1.1 This specification covers titanium and titanium alloy castings intended for general corrosion resistant and industrial
applications.
1.2 This specification is intended for use of purchasers and/or producers of reactive metal castings for defining the requirements
and assuring the properties of castings for unique corrosion-resistant applications, that is, not for commodity items which must
meet all potential purchasers’ requirements.
1.2.1 Users are advised to use the specification as a basis for obtaining castings which will meet minimum acceptance
requirements established and revised by consensus of the members of the committee.
1.2.2 User requirements considered more stringent may be met by the addition to the purchase order of one or more
supplementary requirements, which may include, but are not limited to, those listed in Sections S1 through S8.
1.3The values stated in inch-pound units are to be regarded as the standard. The values given in parentheses are for information
only.
1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical
conversions to SI units that are provided for information only and are not considered standard.
2. Referenced Documents
2
2.1 ASTM Standards:
A 802/A 802M Practice for Steel Castings, Surface Acceptance Standards, Visual Examination
E 8 Test Methods for Tension Testing of Metallic Materials
E 10 Test Method for Brinell Hardness of Metallic Materials
E 18 Test Methods for Rockwell Hardness of Metallic Materials
E 29 Practice for Using Significant Digits in Test Data to Determine Conformance with Specifications
E 94 Guide for Radiographic Examination
E 120 Test Methods for Chemical Analysis of Titanium and Titanium Alloys
3
E 142 Test Method for Controlling Quality of Radiographic Testing
E 165 Test Method for Liquid Penetrant Examination
E 446 Reference Radiographs for Steel Castings Up to 2 in. [51 mm] in Thickness
3. Terminology
3.1 Definitions of Terms Specific to This Standard:
3.1.1 lot, n—shall consist of all castings of the same design produced from the same pour.
3.1.2 pour, n—shall consist of all material melted and cast at one time.
4. Ordering Information
4.1 Orders for castings to this specification shall include the following as required, to describe the requirements adequately:
4.1.1 Description of the castings by pattern number or drawing. Dimensional tolerances shall be included on the casting
drawing,
4.1.2 Quantity,
1
This specification is under the jurisdiction of ASTM Committee B10 on Reactive and Refractory Metals and Alloys and is the direct responsibility of Subcommittee
B10.01 on Titanium.
Current edition approved March 1, 2006. Published March 2006. Originally approved in 1961. Last previous edition approved in 2005 as B367–05.
Current edition approved May 15, 2008. Published June 2008. Originally approved in 1961. Last previous edition approved in 2006 as B 367 – 06a.
2
For referencedASTM standards, visit theASTM website, www.astm.org, or contactASTM Customer Service at service@astm.org. For Annual Book of ASTM Standards
volume information, refer to the standard’s Document Summary page on the ASTM website.
3
Withdrawn.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
1

---------------------- Page: 1 ----------------------
B367–08
4.1.3 Grade designation (see Table 1),
4.1.4 Options in the specification, and
4.1.5 Supplementary requirements desired, including the standards of acceptance.
5. Materials and Manufacture
5.1 Materials for this specification shall be melted by conventional processes used for reactive metals. Typical methods include
the consumable electrode and induction-slag, plasma arc, induction-skull, and electron beam melting processes.
6. Chemical Composition
6.1 Pour Analysis—An analysis of each pour shall be made by the producer from a sample such as a casting or test bar that
is representative of the pour. The chemical
...